CN104059567A - 一种橡胶胶粘剂 - Google Patents
一种橡胶胶粘剂 Download PDFInfo
- Publication number
- CN104059567A CN104059567A CN201410291170.XA CN201410291170A CN104059567A CN 104059567 A CN104059567 A CN 104059567A CN 201410291170 A CN201410291170 A CN 201410291170A CN 104059567 A CN104059567 A CN 104059567A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- carbon black
- rubber adhesive
- ursol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于橡胶领域，具体涉及一种橡胶胶粘剂。本发明的橡胶胶粘剂包括下述重量份数的组分：氯丁橡胶20-100份、丁腈橡胶30-70份、聚氨酯橡胶20-50份、丙烯酸酯橡胶20-50份、纳米氧化锌2-10份、陶土2-4份、炭黑N10015-30份、古马隆树脂5-12份、硅藻土5-15份、硫磺5-10份、防老剂3-5份、叔丁酚甲醛树脂2-8份、机油2-6份、氧化镁1-3份、白炭黑2-5份、防焦剂2-5份、邻苯二甲酸二丁酯2-4份、二乙基二硫代氨基甲酸锌2-4份、2-硫醇基咪唑啉2-4份、二苯胍5-10份。本发明的有益效果在于，采用本发明的配方生产的橡胶胶粘剂，柔韧性好，具有优异的耐蠕变、耐挠曲及耐冲击震动等特性，能够适用于不同线膨胀系数材料之间及动态使用的部件或制品的胶接。
Description
技术领域
本发明属于橡胶领域，具体涉及一种橡胶胶粘剂。
背景技术
橡胶胶粘剂是以橡胶味基料配置而成的胶粘剂，几乎所有的天然橡胶和合成橡胶都可以用于配置胶粘剂，按照橡胶基料的组成，可分为天然橡胶胶粘剂和合成橡胶胶粘剂两大类。合成橡胶胶粘剂常用的品种有氯丁橡胶、丁腈橡胶、丁苯橡胶、硅橡胶等，其中氯丁橡胶粘合剂是合成橡胶胶粘剂中产量最大、用途最广的一个品种。橡胶是一种弹性体，不但在常温下具有显著的高弹性，而且能在很大温度范围内具有这种性质，变形性可达数倍。利用橡胶这一性质配制的胶粘剂，柔韧性优良，具有优异的耐蠕变、耐挠曲及耐冲击震动等特性，适用于不同线膨胀系数材料之间及动态使用的部件或制品的胶接，在工业生产中应该极为广泛。
发明内容
为了解决上述的技术问题，本发明提供了一种柔韧性好，耐蠕变、耐挠曲、耐冲击震动的橡胶胶粘剂。
本发明所采取的技术方案为：一种橡胶胶粘剂，包括下述重量份数的组分：氯丁橡胶20-100份、丁腈橡胶30-70份、聚氨酯橡胶20-50份、丙烯酸酯橡胶20-50份、纳米氧化锌2-10份、陶土2-4份、炭黑N100 15-30份、古马隆树脂5-12份、硅藻土5-15份、硫磺5-10份、防老剂3-5份、叔丁酚甲醛树脂2-8份、机油2-6份、氧化镁1-3份、白炭黑2-5份、防焦剂2-5份、邻苯二甲酸二丁酯2-4份、二乙基二硫代氨基甲酸锌2-4份、2-硫醇基咪唑啉2-4份、二苯胍5-10份。
上述的防老剂为N-苯基-2萘胺、2，2，4-三甲基1，2-二氢化喹聚合体、二芳基仲胺类防老剂、对苯二胺类、N-苯基-N’-异丙基-对苯二胺、N-N’-二苯基-对苯二胺、防老剂4020的至少一种。
本发明的有益效果在于，采用本发明的配方生产的橡胶胶粘剂，柔韧性好，具有优异的耐蠕变、耐挠曲及耐冲击震动等特性，能够适用于不同线膨胀系数材料之间及动态使用的部件或制品的胶接。
具体实施方式
下面结合具体实施方式，对本发明作进一步详细说明。
实施例1：一种橡胶胶粘剂，包括下述重量份数的组分：氯丁橡胶20份、丁腈橡胶30份、聚氨酯橡胶20份、丙烯酸酯橡胶20份、纳米氧化锌2份、陶土2份、炭黑N100 15份、古马隆树脂5份、硅藻土5份、硫磺5份、防老剂3份、叔丁酚甲醛树脂2份、机油2份、氧化镁1份、白炭黑2份、防焦剂2份、邻苯二甲酸二丁酯2份、二乙基二硫代氨基甲酸锌2份、2-硫醇基咪唑啉2份、二苯胍5份。
实施例2：一种橡胶胶粘剂，包括下述重量份数的组分：氯丁橡胶50份、丁腈橡胶50份、聚氨酯橡胶35份、丙烯酸酯橡胶25份、纳米氧化锌8份、陶土3份、炭黑N100 25份、古马隆树脂8份、硅藻土10份、硫磺8份、防老剂4份、叔丁酚甲醛树脂6份、机油4份、氧化镁2份、白炭黑3份、防焦剂4份、邻苯二甲酸二丁酯3份、二乙基二硫代氨基甲酸锌3份、2-硫醇基咪唑啉3份、二苯胍7份。
实施例3：一种橡胶胶粘剂，包括下述重量份数的组分：氯丁橡胶100份、丁腈橡胶70份、聚氨酯橡胶50份、丙烯酸酯橡胶50份、纳米氧化锌10份、陶土4份、炭黑N100 30份、古马隆树脂12份、硅藻土15份、硫磺10份、防老剂5份、叔丁酚甲醛树脂8份、机油6份、氧化镁3份、白炭黑5份、防焦剂5份、邻苯二甲酸二丁酯4份、二乙基二硫代氨基甲酸锌4份、2-硫醇基咪唑啉4份、二苯胍10份。
所述的防老剂为N-苯基-2萘胺、2，2，4-三甲基1，2-二氢化喹聚合体、二芳基仲胺类防老剂、对苯二胺类、N-苯基-N’-异丙基-对苯二胺、N-N’-二苯基-对苯二胺、防老剂4020的至少一种。
橡胶是一种弹性体，不但在常温下具有显著的高弹性，而且能在很大温度范围内具有这种性质，变形性可达数倍。
利用橡胶这一性质配制的胶粘剂，柔韧性优良，具有优异的耐蠕变、耐挠曲及耐冲击震动等特性，适用于不同线膨胀系数材料之间及动态使用的部件或制品的胶接。
本发明的采用的氯丁橡胶胶粘剂的主要成分是氯丁橡胶，是氯丁二烯的聚合物，其结构比较规整，分子上又有极性较大的氯原子，故结晶性强，在室温下就有较好的胶接性能和内聚力，非常适宜作胶粘剂。
其特点如下：
具有仅次于丁腈橡胶胶粘剂的高极性，故对极性物质的胶接性能良好；在常温不硫化也具有较高的内聚强度和粘附强度；具有优良的耐燃、耐臭氧、耐油、耐溶剂和化学试剂的性能。胶层弹性好，胶接体的抗冲击强度和剥离强度好；初粘性好，只需接触压力便能很好的胶接，特别适合一些形状特殊的表面胶贴；涂覆工艺性能好，使用简便。
当然上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改变、添加或替换，都应属于本发明的保护范围。
Claims (2)
1.一种橡胶胶粘剂，其特征在于：包括下述重量份数的组分：氯丁橡胶20-100份、丁腈橡胶30-70份、聚氨酯橡胶20-50份、丙烯酸酯橡胶20-50份、纳米氧化锌2-10份、陶土2-4份、炭黑N100 15-30份、古马隆树脂5-12份、硅藻土5-15份、硫磺5-10份、防老剂3-5份、叔丁酚甲醛树脂2-8份、机油2-6份、氧化镁1-3份、白炭黑2-5份、防焦剂2-5份、邻苯二甲酸二丁酯2-4份、二乙基二硫代氨基甲酸锌2-4份、2-硫醇基咪唑啉2-4份、二苯胍5-10份。
2.根据权利要求1所述的橡胶胶粘剂，其特征在于，所述的防老剂为N-苯基-2萘胺、2，2，4-三甲基1，2-二氢化喹聚合体、二芳基仲胺类防老剂、对苯二胺类、N-苯基-N’-异丙基-对苯二胺、N-N’-二苯基-对苯二胺、防老剂4020的至少一种。