CN108753078A - A kind of anti-Spider Webs survival-type wall finiss - Google Patents
A kind of anti-Spider Webs survival-type wall finiss Download PDFInfo
- Publication number
- CN108753078A CN108753078A CN201810320841.9A CN201810320841A CN108753078A CN 108753078 A CN108753078 A CN 108753078A CN 201810320841 A CN201810320841 A CN 201810320841A CN 108753078 A CN108753078 A CN 108753078A
- Authority
- CN
- China
- Prior art keywords
- parts
- essential oil
- wall finiss
- survival
- type wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to coating processing technique fields, and in particular to a kind of anti-Spider Webs survival-type wall finiss.The wall finiss includes following raw material：20~50 parts of deionized water, 10~30 parts of water soluble acrylic resin, 3~10 parts of sodium citrate, 3~10 parts of elastic resin, 1~5 part of nano-titanium dioxide, 1~9 part of emulsifier, 0.3~1 part of propylene glycol, 1~8 part of levelling agent, 10~25 parts of active carbon nanoparticles, 10~15 parts of modification infusorial earth, 1~8 part of titanium dioxide, 3~15 parts of plants essential oil；The wall finiss further includes 1~3 part of dispersant, 1~2 part of coalescents, 0.1~1 part of lubricant, 1~2 part of foam inhibitor, 1~3 part of antifoaming agent；Pass through in metope raw materials for varnish be added have inhibit spider activity smell plants essential oil and active carbon nanoparticles so that using wall finiss provided by the invention finishing after metope can slow release it is faint have inhibit the movable gas of spider, inhibit Spider Webs existence.
Description
Technical field
The present invention relates to coating processing technique fields, and in particular to a kind of anti-Spider Webs survival-type wall finiss.
Background technology
Wall finiss, that is, finishing coat, that is, it has often been said that emulsion paint, be in house decoration be used for metope main decoration materials
One of.Sizable ratio is accounted in basic decoration cost, select good wall finiss be it is very heavy, it is cohesive in order to reach
The main component of purpose, wall finiss is formaldehyde, can be firmly adhered on wall.In China, people traditionally set synthesis
Fat liquor is base-material, using water as decentralized medium, pigment, filler (also known as extender pigment) and auxiliary agent is added, through certain technical process
Manufactured coating is called emulsion paint, is also latex paint.
House fitting pollution refers to harmful gas that various building materials and ornament materials are released in fitment process
The chemicals that body and insecticide, deodorant, aromatic etc. largely use, the pollution caused by indoor environment.People learn indoors
The time of habit, work and life has accounted for the 80~90% of whole day, and " room air pollution " is paid attention to by more and more people,
And wall finiss pollution is the arch-criminal of indoor environmental pollution, binds and is formed whole very well with other materials coated on body surface
And the material of tough and tensile protective film is known as wall finiss.It is identical concept in the upper wall finiss of building and paint.Wall currently on the market
Finishing coat is broadly divided into waterborne wall surface paint and solvent type wall finiss.It just can detect that in the space air of brushing wall finiss a large amount of
50 gas chromatography such as benzene, toluene, ethylbenzene, dimethylbenzene, acetone, butyl acetate, acetaldehyde, butanol, formic acid generates organic solvent and waves
It sends out object (voc) and pollutes environment.Above-mentioned organic volatile contained by traditional solvent type wall finiss can damage the respiratory system of people, make
Blood function, immune system even result in the disease of certain heredity etc..
Due to environmentally friendly and health at home attention, waterborne wall surface paint gradually instead of traditional solvent-borne wall finiss,
Since the technology content of waterborne wall surface paint is higher, the production of most domestic manufacturers is difficult larger, solvent borne wall finiss still big row its
Road accounts for absolute mainstream.Activated carbon have powerful adsorption function before people be charcoal bag is placed on some position formaldehyde adsorption, but
It is limited in scope, cannot be adsorbed after saturation after all, become pollution sources, how to be quickly and effectively mesh by regenerating active carbon
The Main way of preceding research.
Simultaneously as the increase of operating pressure, contemporary many workers can not find time sweep roofing on time so that
Interior starts to grow a large amount of worm ants, the most serious is there are a large amount of cobwebs at corner or concealment or on windowsill, and has a large amount of
Spider survives, and psychological burden is caused to more and more young men.
Invention content
It is an object of the invention to：A kind of environment-friendly type aqueous wall finiss is provided, finishing pollution is solved from source, allows activity
Active ingredient of the charcoal as wall finiss realizes activated carbon rapid regeneration；Simultaneously depositing for indoor cobweb is solved from the angle of finishing
In problem.
The present invention is achieved by the following technical solutions：
A kind of anti-Spider Webs survival-type wall finiss, including following raw material：
20~50 parts of deionized water, 10~30 parts of water soluble acrylic resin, 3~10 parts of sodium citrate, elastic resin 3~
10 parts, 1~5 part of nano-titanium dioxide, 1~9 part of emulsifier, 0.3~1 part of propylene glycol, 1~8 part of levelling agent, active carbon nanoparticles 10
~25 parts, 10~15 parts of modification infusorial earth, 1~8 part of titanium dioxide, 3~15 parts of plants essential oil；The wall finiss further includes dispersant
1~3 part, 1~2 part of coalescents, 0.1~1 part of lubricant, 1~2 part of foam inhibitor, 1~3 part of antifoaming agent.
Preferably, the wall finiss includes following raw material：
23 parts of deionized water, 15 parts of water soluble acrylic resin, 5 parts of sodium citrate, 7 parts of elastic resin, nanometer titanium dioxide
3 parts of titanium, 4 parts of emulsifier, 0.6 part of propylene glycol, 5 parts of levelling agent, 18 parts of active carbon nanoparticles, 10 parts of modification infusorial earth, titanium dioxide 3
Part, 7 parts of plants essential oil；The wall finiss further includes 1 part of dispersant, 1 part of coalescents, 0.3 part of lubricant, 1 part of foam inhibitor, disappears
1 part of infusion.
Preferably, the plants essential oil includes following raw material：
1~3 part of galic essential oil, 5~8 parts of ginger essential oil, 1~5 part of wormwood essential oil, 3~5 parts of camphor tree essential oil, pine tree essence oil
0.5~2 part, 1~5 part of calcium carbonate.
Further, the plants essential oil processing method is as follows：
A large amount of fresh garlics, ginger, wormwood, camphortree bark, pine bark are taken respectively, extract plants essential oil；
The ground 400 mesh sieve of required weight parts of calcium carbonate is taken, takes lower part of screen point that the saturated salt solution of identical weight part is added,
3~5ml dilute hydrochloric acid is added dropwise again, heating water bath to calcium carbonate powder is completely dissolved, through filter paper mistake three times after being freely cooled to room temperature
Filter takes filtrate to be concentrated into the 1/10 of original volume, the camphor tree peel essential oil of the required weight part of addition, pine tree peel essential oil, ginger essential oil, garlic
Essential oil, wormwood essential oil, heating water bath stir, until each to dropwise addition 1~2ml dimethyl sulfoxide (DMSO)s after 40~45 DEG C in heating water bath
Stop heating after the complete mixing of essential oil, is placed in water-bath and is cooled to room temperature spare, 85~125r/min of mixing speed while stirring.
Preferably, the dispersant is the mixture of stearmide and hexylene glycol, mixed proportion 1:8.
Preferably, the modification infusorial earth be diatomite powder by being shaken after faintly acid copper-bath, through activated carbon
Drying is filtered after decoloration to be prepared.
Preferably, the coalescents are binary acid dibasic ester.
Preferably, the lubricant is the mixture of silicone oil, fatty acid amide, mixed proportion 1:5.
Preferably, the levelling agent be polyacrylic acid, any one in carboxymethyl cellulose or more than one.
In technical solution provided by the invention, the emulsifier is polyoxylethylene abietate.
In technical solution provided by the invention, the antifoaming agent is dimethyl silicone polymer, and foam inhibitor disappears for polyethers
Infusion.
In technical solution provided by the invention, the elastic resin is modified polyester resin.
In technical solution provided by the invention, the dispersant is the mixture of methyl anyl alcohol and cellulose derivative,
Mixed proportion 7:1.
The beneficial effects of the invention are as follows：
1, the present invention provides a kind of anti-Spider Webs survival-type wall finiss, have suppression by being added in metope raw materials for varnish
The plants essential oil and active carbon nanoparticles of spider activity smell processed so that can using the metope after wall finiss provided by the invention finishing
Faint the having of slow release inhibits the movable gas of spider, inhibits Spider Webs existence；
2, the present invention being used in mixed way by modification infusorial earth and active carbon nanoparticles, when the sodium bicarbonate using concentration 5%
Solution-wet metope can be such that active carbon nanoparticles therein regenerate, and effectively absorb formaldehyde gas, inertia that finishing material releases
Other harmful substances such as gas radon；
3, wall finiss provided by the invention selects qualified nuisanceless raw material, and finishing pollution, aqueous ring are reduced from source
It protects.
Specific implementation mode
The present invention is further described in detail With reference to embodiment, but technical solution provided by the invention
It include not only the content showed in embodiment.
Embodiment 1
Present embodiments provide one kind with the wall finiss for preventing Spider Webs from surviving disclosed by the invention effectively
Formula, specific proportioning are as follows：
23 parts of deionized water, 15 parts of water soluble acrylic resin, 5 parts of sodium citrate, 7 parts of elastic resin, nanometer titanium dioxide
3 parts of titanium, 4 parts of emulsifier, 0.6 part of propylene glycol, 5 parts of levelling agent, 18 parts of active carbon nanoparticles, 10 parts of modification infusorial earth, titanium dioxide 3
Part, 7 parts of plants essential oil；The wall finiss further includes 1 part of dispersant, 1 part of coalescents, 0.3 part of lubricant, 1 part of foam inhibitor, disappears
1 part of infusion.
In the present embodiment, the plants essential oil includes following raw material：
1 part of galic essential oil, 5 parts of ginger essential oil, 3 parts of wormwood essential oil, 3 parts of camphor tree essential oil, 1 part of pine tree essence oil, calcium carbonate 3
Part.
Further, the plants essential oil processing method is as follows：
A large amount of fresh garlics, ginger, wormwood, camphortree bark, pine bark are taken respectively, extract plants essential oil；
The ground 400 mesh sieve of required weight parts of calcium carbonate is taken, takes lower part of screen point that the saturated salt solution of identical weight part is added,
5ml dilute hydrochloric acid is added dropwise again, heating water bath to calcium carbonate powder is completely dissolved, and is filtered through filter paper three times after being freely cooled to room temperature,
Filtrate is taken to be concentrated into the 1/10 of original volume, the camphor tree peel essential oil of the required weight part of addition, pine tree peel essential oil, ginger essential oil, garlic essence
Oil, wormwood essential oil, heating water bath is stirred to dropwise addition 2ml dimethyl sulfoxide (DMSO)s after 45 DEG C in heating water bath, until each essential oil is completely mixed
Stop heating after even, is placed in water-bath and is cooled to room temperature spare, mixing speed 90r/min while stirring.
In the present embodiment, the dispersant is the mixture of stearmide and hexylene glycol, mixed proportion 1:8.
In the present embodiment, the modification infusorial earth is diatomite powder by being shaken after faintly acid copper-bath, is passed through
Drying is filtered after activated carbon decolorizing to be prepared.
In the present embodiment, the coalescents are binary acid dibasic ester.
In the present embodiment, the lubricant is the mixture of silicone oil, fatty acid amide, mixed proportion 1:5.
In the present embodiment, the levelling agent is carboxymethyl cellulose.
In the present embodiment, the emulsifier is polyoxylethylene abietate.
In the present embodiment, the antifoaming agent is dimethyl silicone polymer, and foam inhibitor is polyoxyethylene polyoxy propyl alcohol amidogen ether.
In the present embodiment, the elastic resin is modified polyester resin.
In the present embodiment, the dispersant is the mixture of methyl anyl alcohol and cellulose derivative, mixed proportion 7:1.
Embodiment 2
A kind of effective formula of anti-Spider Webs survival-type wall finiss is present embodiments provided, specific proportioning is as follows：
20 parts of deionized water, 25 parts of water soluble acrylic resin, 4 parts of sodium citrate, 8 parts of elastic resin, nanometer titanium dioxide
2 parts of titanium, 5 parts of emulsifier, 0.3 part of propylene glycol, 7 parts of levelling agent, 17 parts of active carbon nanoparticles, 10 parts of modification infusorial earth, titanium dioxide 3
Part, 10 parts of plants essential oil；The wall finiss further includes 1 part of dispersant, 1 part of coalescents, 0.3 part of lubricant, foam inhibitor 1.5
Part, 1 part of antifoaming agent.
In the present embodiment, the plants essential oil includes following raw material：
2 parts of galic essential oil, 7 parts of ginger essential oil, 3 parts of wormwood essential oil, 3 parts of camphor tree essential oil, 1 part of pine tree essence oil, calcium carbonate 3
Part.
Further, the plants essential oil processing method is as follows：
A large amount of fresh garlics, ginger, wormwood, camphortree bark, pine bark are taken respectively, extract plants essential oil；
The ground 400 mesh sieve of required weight parts of calcium carbonate is taken, takes lower part of screen point that the saturated salt solution of identical weight part is added,
4ml dilute hydrochloric acid is added dropwise again, heating water bath to calcium carbonate powder is completely dissolved, and is filtered through filter paper three times after being freely cooled to room temperature,
Filtrate is taken to be concentrated into the 1/10 of original volume, the camphor tree peel essential oil of the required weight part of addition, pine tree peel essential oil, ginger essential oil, garlic essence
Oil, wormwood essential oil, heating water bath is stirred to dropwise addition 1ml dimethyl sulfoxide (DMSO)s after 40 DEG C in heating water bath, until each essential oil is completely mixed
Stop heating after even, is placed in water-bath and is cooled to room temperature spare, mixing speed 125r/min while stirring.
In the present embodiment, the dispersant is the mixture of stearmide and hexylene glycol, mixed proportion 1:8.
In the present embodiment, the modification infusorial earth is diatomite powder by being shaken after faintly acid copper-bath, is passed through
Drying is filtered after activated carbon decolorizing to be prepared.
In the present embodiment, the coalescents are binary acid dibasic ester.
In the present embodiment, the lubricant is the mixture of silicone oil, fatty acid amide, mixed proportion 1:5.
In the present embodiment, the levelling agent is the mixture of polyacrylic acid, carboxymethyl cellulose, mixed proportion 1:2.
In the present embodiment, the emulsifier is polyoxylethylene abietate.
In the present embodiment, the antifoaming agent is dimethyl silicone polymer, and foam inhibitor is polyethers antifoaming agent.
In the present embodiment, the elastic resin is modified polyester resin.
In the present embodiment, the dispersant is the mixture of methyl anyl alcohol and cellulose derivative, mixed proportion 7:1.
In embodiment provided by the invention, the metope raw materials for varnish includes a large amount of levelling agents, lubricant, is effectively improved
The texture and smoothness of finished wall finishing coat increase knitmesh difficulty of the spider on metope.
In embodiment provided by the invention, appropriate plants essential oil is added in the metope raw materials for varnish, is knitted inhibiting spider
While net existence, the faint odor safety nuisance free discharged out, without any toxicity and side effects to human body.
In embodiment provided by the invention, the wall finiss safety and environmental protection is green non-poisonous, can be safe to use.
The above described is only a preferred embodiment of the present invention, being not intended to limit the present invention in any form, appoint
What without departing from technical solution of the present invention content, according to the technical essence of the invention to made by above example it is any modification, etc.
With variation and modification, in the range of still falling within technical solution of the present invention.
Claims (9)
1. a kind of anti-Spider Webs survival-type wall finiss, which is characterized in that including following raw material：
20~50 parts of deionized water, 10~30 parts of water soluble acrylic resin, 3~10 parts of sodium citrate, elastic resin 3~10
Part, 1~5 part of nano-titanium dioxide, 1~9 part of emulsifier, 0.3~1 part of propylene glycol, 1~8 part of levelling agent, active carbon nanoparticles 10~
25 parts, 10~15 parts of modification infusorial earth, 1~8 part of titanium dioxide, 3~15 parts of plants essential oil；The wall finiss further includes dispersant 1
~3 parts, 1~2 part of coalescents, 0.1~1 part of lubricant, 1~2 part of foam inhibitor, 1~3 part of antifoaming agent.
2. a kind of anti-Spider Webs survival-type wall finiss according to claim 1, which is characterized in that including following parts by weight
Raw material：
23 parts of deionized water, 15 parts of water soluble acrylic resin, 5 parts of sodium citrate, 7 parts of elastic resin, nano-titanium dioxide 3
Part, is planted at 4 parts of emulsifier, 0.6 part of propylene glycol, 5 parts of levelling agent, 18 parts of active carbon nanoparticles, 10 parts of modification infusorial earth, 3 parts of titanium dioxide
7 parts of object essential oil；The wall finiss further includes 1 part of dispersant, 1 part of coalescents, 0.3 part of lubricant, 1 part of foam inhibitor, antifoaming agent 1
Part.
3. a kind of anti-Spider Webs survival-type wall finiss according to claim 1~2 any one, which is characterized in that institute
It includes following raw material to state plants essential oil：
1~3 part of galic essential oil, 5~8 parts of ginger essential oil, 1~5 part of wormwood essential oil, 3~5 parts of camphor tree essential oil, pine tree essence oil 0.5~
2 parts, 1~5 part of calcium carbonate.
4. a kind of anti-Spider Webs survival-type wall finiss according to claim 3, which is characterized in that the plants essential oil adds
Work method is as follows：
A large amount of fresh garlics, ginger, wormwood, camphortree bark, pine bark are taken respectively, extract plants essential oil；
The ground 400 mesh sieve of required weight parts of calcium carbonate is taken, takes lower part of screen point that the saturated salt solution of identical weight part is added, then drip
Add 3~5ml dilute hydrochloric acid, heating water bath to calcium carbonate powder to be completely dissolved, filters, take through filter paper three times after being freely cooled to room temperature
Filtrate is concentrated into the 1/10 of original volume, be added needed for the camphor tree peel essential oil of weight part, pine tree peel essential oil, ginger essential oil, galic essential oil,
Wormwood essential oil, heating water bath stir, until each essential oil is complete to dropwise addition 1~2ml dimethyl sulfoxide (DMSO)s after 40~45 DEG C in heating water bath
Stop heating after full mixing, is placed in water-bath and is cooled to room temperature spare, 85~125r/min of mixing speed while stirring.
5. a kind of anti-Spider Webs survival-type wall finiss according to claim 1~2 any one, which is characterized in that institute
State the mixture that dispersant is stearmide and hexylene glycol, mixed proportion 1:8.
6. a kind of anti-Spider Webs survival-type wall finiss according to claim 1~2 any one, which is characterized in that institute
State modification infusorial earth be diatomite powder by being shaken after faintly acid copper-bath, after activated carbon decolorizing filter drying prepare
It forms.
7. a kind of anti-Spider Webs survival-type wall finiss according to claim 1~2 any one, which is characterized in that institute
It is binary acid dibasic ester to state coalescents.
8. a kind of anti-Spider Webs survival-type wall finiss according to claim 1~2 any one, which is characterized in that institute
State the mixture that lubricant is silicone oil, fatty acid amide, mixed proportion 1:5.
9. a kind of anti-Spider Webs survival-type wall finiss according to claim 1~2 any one, which is characterized in that institute
State levelling agent be polyacrylic acid, any one in carboxymethyl cellulose or more than one.