CN107266947A - A kind of emulsion paint of finishing and preparation method thereof - Google Patents
A kind of emulsion paint of finishing and preparation method thereof Download PDFInfo
- Publication number
- CN107266947A CN107266947A CN201710646834.3A CN201710646834A CN107266947A CN 107266947 A CN107266947 A CN 107266947A CN 201710646834 A CN201710646834 A CN 201710646834A CN 107266947 A CN107266947 A CN 107266947A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion
- paint
- emulsion paint
- finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of emulsion paint of finishing, according to the mass fraction, including following components：35 parts of 50 60 parts of latex paint emulsion, 10 15 parts of polyfunctionality acid allyl ester, 35 parts of thickener, 7 10 parts of talcum powder, 58 parts of pigment titanium white, 5 10 parts of high hydroscopic resin and modification infusorial earth.The invention also discloses the preparation method of above-mentioned emulsion paint.The emulsion paint adds modification infusorial earth and substantially increases adsorption efficiency of the emulsion paint to pernicious gas in domestic environment, and polyfunctionality acid allyl ester has lipophobic hydrophobic energy, avoid oily wastewater pollution thing to be attached on wall, build good domestic environment, environment protection health.
Description
Technical field
The present invention relates to finishing material field, specifically a kind of emulsion paint of finishing and preparation method thereof.
Background technology
With China's economy develop rapidly and people's living standard continuous improvement, pursuit of the people to quality of life
Also increasingly stricter, good home environment is the main target that people pursue now.
Existing people are fitted up before inhabitation to house, and Decoration Design field is calculated inside building trade at present
It is the showing tremendous enthusiasm industry of comparison, the personnel for being engaged in finishing also compare many, it is well known that in finishing field, emulsion paint is that one kind must
Indispensable finishing material, emulsion paint is mainly used in brushing on wall, still, after existing house decoration is completed, latex
Paint can not effectively adsorb the pernicious gas in living environment, have impact on the healthy of people.
The content of the invention
It is an object of the invention to provide a kind of emulsion paint of finishing and preparation method thereof, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides following technical scheme：
A kind of emulsion paint of finishing, according to the mass fraction, including following components：It is 50-60 parts of latex paint emulsion, multifunctional
Spend 10-15 parts of acid allyl ester, 3-5 parts of thickener, 7-10 parts of talcum powder, 5-8 parts of pigment titanium white, 5-10 parts of high hydroscopic resin and
3-5 parts of modification infusorial earth.
It is used as further scheme of the invention：The emulsion paint of above-mentioned finishing, according to the mass fraction, including following components：
53-58 parts of latex paint emulsion, 11-14 parts of polyfunctionality acid allyl ester, 4-5 parts of thickener, 8-9 parts of talcum powder, pigment titanium white
4-5 parts of 6-7 parts, 6-8 parts of high hydroscopic resin and modification infusorial earth.
It is used as further scheme of the invention：The emulsion paint of above-mentioned finishing, according to the mass fraction, including with the following group
Point：55 parts of latex paint emulsion, 13 parts of polyfunctionality acid allyl ester, 4 parts of thickener, 8 parts of talcum powder, 6 parts of pigment titanium white, high suction
4 parts of 7 parts of water-resin and modification infusorial earth.
It is used as further scheme of the invention：The polyfunctionality acid allyl ester is trimethylolpropane tris acrylic acid
Ester, pentaerythritol triacrylate, glycerol propoxylate triacrylate, ethoxyquin trimethylolpropane trimethacrylate, season penta
One or more in tetra-acrylate, ethoxyquin tetramethylol methane tetraacrylate and dipentaerythritol acrylate are mixed
Close.
It is used as further scheme of the invention：The modification infusorial earth is the complexing of tripolite loading copper ion modified
Thing.
A kind of preparation method of such as above-mentioned emulsion paint, is concretely comprised the following steps：
S1, diatomite modified：Diatomite particle is ground and sieved, diatomite powder is prepared, added in diatomite powder
Copper-bath, is placed in oscillator and shakes, and the concussion time is 1-2 hours, and drying vacuum is preserved, and prepares mixture A；
S2, addition polyfunctionality acid allyl ester, thickener, talcum powder, color titanium dioxide and high suction in latex paint emulsion
Water-resin, heating stirring, heating-up temperature is 100-200 DEG C, and mixing time is 30 minutes；
The mixture prepared in step S1 is added in S3, the mixed solution prepared in step s 2, heating stirring is made into
Product.
Compared with prior art, the beneficial effects of the invention are as follows：The emulsion paint adds modification infusorial earth and substantially increases breast
Shellac varnish is to the adsorption efficiency of pernicious gas in domestic environment, and polyfunctionality acid allyl ester has lipophobic hydrophobic energy, it is to avoid
Oily wastewater pollution thing is attached on wall, has built good domestic environment, environment protection health.
Embodiment
Technical scheme is described in more detail with reference to embodiment.
Embodiment 1
A kind of emulsion paint of finishing, according to the mass fraction, including following components：50 parts of latex paint emulsion, polyfunctionality
3 parts of 10 parts of acid allyl ester, 3 parts of thickener, 7 parts of talcum powder, 5 parts of pigment titanium white, 5 parts of high hydroscopic resin and modification infusorial earth.
Polyfunctionality acid allyl ester be trimethylolpropane trimethacrylate, pentaerythritol triacrylate, third oxidation it is sweet
Oily triacrylate, ethoxyquin trimethylolpropane trimethacrylate, tetramethylol methane tetraacrylate, ethoxyquin pentaerythrite four
One or more of mixing in acrylate and dipentaerythritol acrylate.
Modification infusorial earth is the complex compound of tripolite loading copper ion modified.
A kind of preparation method of such as above-mentioned emulsion paint, is concretely comprised the following steps：
S1, diatomite modified：Diatomite particle is ground and sieved, diatomite powder is prepared, added in diatomite powder
Copper-bath, is placed in oscillator and shakes, and the concussion time is 1-2 hours, and drying vacuum is preserved, and prepares mixture A；
S2, addition polyfunctionality acid allyl ester, thickener, talcum powder, color titanium dioxide and high suction in latex paint emulsion
Water-resin, heating stirring, heating-up temperature is 100-200 DEG C, and mixing time is 30 minutes；
The mixture prepared in step S1 is added in S3, the mixed solution prepared in step s 2, heating stirring is made into
Product.
Embodiment 2
A kind of emulsion paint of finishing, according to the mass fraction, including following components：55 parts of latex paint emulsion, polyfunctionality
4 parts of 13 parts of acid allyl ester, 4 parts of thickener, 8 parts of talcum powder, 6 parts of pigment titanium white, 7 parts of high hydroscopic resin and modification infusorial earth.
Polyfunctionality acid allyl ester be trimethylolpropane trimethacrylate, pentaerythritol triacrylate, third oxidation it is sweet
Oily triacrylate, ethoxyquin trimethylolpropane trimethacrylate, tetramethylol methane tetraacrylate, ethoxyquin pentaerythrite four
One or more of mixing in acrylate and dipentaerythritol acrylate.
Modification infusorial earth is the complex compound of tripolite loading copper ion modified.
A kind of preparation method of such as above-mentioned emulsion paint, is concretely comprised the following steps：
S1, diatomite modified：Diatomite particle is ground and sieved, diatomite powder is prepared, added in diatomite powder
Copper-bath, is placed in oscillator and shakes, and the concussion time is 1-2 hours, and drying vacuum is preserved, and prepares mixture A；
S2, addition polyfunctionality acid allyl ester, thickener, talcum powder, color titanium dioxide and high suction in latex paint emulsion
Water-resin, heating stirring, heating-up temperature is 100-200 DEG C, and mixing time is 30 minutes；
The mixture prepared in step S1 is added in S3, the mixed solution prepared in step s 2, heating stirring is made into
Product.
Embodiment 3
A kind of emulsion paint of finishing, according to the mass fraction, including following components：60 parts of latex paint emulsion, polyfunctionality
15 parts of acid allyl ester, 5 parts of thickener, 10 parts of talcum powder, 8 parts of pigment titanium white, 10 parts of high hydroscopic resin and modification infusorial earth 5
Part.
Polyfunctionality acid allyl ester be trimethylolpropane trimethacrylate, pentaerythritol triacrylate, third oxidation it is sweet
Oily triacrylate, ethoxyquin trimethylolpropane trimethacrylate, tetramethylol methane tetraacrylate, ethoxyquin pentaerythrite four
One or more of mixing in acrylate and dipentaerythritol acrylate.
Modification infusorial earth is the complex compound of tripolite loading copper ion modified.
A kind of preparation method of such as above-mentioned emulsion paint, is concretely comprised the following steps：
S1, diatomite modified：Diatomite particle is ground and sieved, diatomite powder is prepared, added in diatomite powder
Copper-bath, is placed in oscillator and shakes, and the concussion time is 1-2 hours, and drying vacuum is preserved, and prepares mixture A；
S2, addition polyfunctionality acid allyl ester, thickener, talcum powder, color titanium dioxide and high suction in latex paint emulsion
Water-resin, heating stirring, heating-up temperature is 100-200 DEG C, and mixing time is 30 minutes；
The mixture prepared in step S1 is added in S3, the mixed solution prepared in step s 2, heating stirring is made into
Product.
The better embodiment to the present invention is explained in detail above, but the present invention is not limited to above-mentioned embodiment party
, can also be on the premise of present inventive concept not be departed from formula, the knowledge that one skilled in the relevant art possesses
Various changes can be made.
Claims (6)
1. a kind of emulsion paint of finishing, it is characterised in that according to the mass fraction, including following components：Latex paint emulsion 50-60
Part, 10-15 parts of polyfunctionality acid allyl ester, 3-5 parts of thickener, 7-10 parts of talcum powder, 5-8 parts of pigment titanium white, super absorbent resin
3-5 parts of 5-10 parts of fat and modification infusorial earth.
2. the emulsion paint of a kind of finishing according to claim 1, it is characterised in that according to the mass fraction, including it is following
Component：53-58 parts of latex paint emulsion, 11-14 parts of polyfunctionality acid allyl ester, 4-5 parts of thickener, 8-9 parts of talcum powder, pigment titanium
4-5 parts of 6-7 parts of white powder, 6-8 parts of high hydroscopic resin and modification infusorial earth.
3. the emulsion paint of a kind of finishing according to claim 1, it is characterised in that according to the mass fraction, including it is following
Component：55 parts of latex paint emulsion, 13 parts of polyfunctionality acid allyl ester, 4 parts of thickener, 8 parts of talcum powder, 6 parts of pigment titanium white, height
4 parts of 7 parts of water-absorbing resin and modification infusorial earth.
4. a kind of emulsion paint of finishing according to claim 1, it is characterised in that the polyfunctionality acid allyl ester is
Trimethylolpropane trimethacrylate, pentaerythritol triacrylate, glycerol propoxylate triacrylate, ethoxyquin trihydroxy methyl
Propane triacrylate, tetramethylol methane tetraacrylate, ethoxyquin tetramethylol methane tetraacrylate and the propylene of dipentaerythritol six
One or more of mixing in acid esters.
5. the emulsion paint of a kind of finishing according to claim 1, it is characterised in that the modification infusorial earth is diatomite
Load the complex compound of copper ion modified.
6. a kind of preparation method of the emulsion paint of finishing as described in claim 1-3 is any, it is characterised in that specific steps
For：
S1, diatomite modified：Diatomite particle is ground and sieved, diatomite powder is prepared, sulfuric acid is added in diatomite powder
Copper solution, is placed in oscillator and shakes, and the concussion time is 1-2 hours, and drying vacuum is preserved, and prepares mixture A；
S2, addition polyfunctionality acid allyl ester, thickener, talcum powder, color titanium dioxide and super absorbent resin in latex paint emulsion
Fat, heating stirring, heating-up temperature is 100-200 DEG C, and mixing time is 30 minutes；
The mixture prepared in step S1 is added in S3, the mixed solution prepared in step s 2, finished product is made in heating stirring.