CN108748544A - A kind of purple willow peeling pre-treating method - Google Patents
A kind of purple willow peeling pre-treating method Download PDFInfo
- Publication number
- CN108748544A CN108748544A CN201810667511.7A CN201810667511A CN108748544A CN 108748544 A CN108748544 A CN 108748544A CN 201810667511 A CN201810667511 A CN 201810667511A CN 108748544 A CN108748544 A CN 108748544A
- Authority
- CN
- China
- Prior art keywords
- purple willow
- processing
- parts
- peeling
- treating method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of purple willow peeling pre-treating method, including following operating procedure：（1）Ozone Oxidation Treatment is passed through on purple willow surface after harvesting, it is 15-20% to be then dried to water content；（2）Step will be passed through（1）The purple willow of processing is put into peeling liquid, after immersion treatment 30-40min, takes out, dries processing, then carry out peeling processing.A kind of purple willow provided by the invention removes the peel pre-treating method, easy to operate, of low cost, and treatment effeciency is high, it can be achieved that continuous industrialized production, treated purple willow, and decortication effect is notable, and peeling is efficient, is not in wicker damage, blocks the case where skinning machine.
Description
Technical field
The invention belongs to purple willow processing technology fields, and in particular to a kind of purple willow peeling pre-treating method.
Background technology
Purple willow alias Salix suchowensis, round-bottomed basket willow and wicker belong to Salicaceae shrub, and resistance to moistening, resistance to carbuncle is thin, and clockwork spring rate is high, wicker
Thin and grow, rich in toughness, the strip after peeling is pure white smooth, is fabulous braided material.Currently, main point of domestic purple willow plantation
Cloth is on Shandong, Hebei, Shanxi, Inner Mongol, Heilungkiang and Jiangsu and other places, and since purple willow has preferable economic, society and ecology
Benefit, cultivated area are increasing year by year.Purple willow processing technology first has to peel off its exocuticle, but peeling labour is strong by hand
It spends big, time-consuming and misses farming season, and existing peeling equipment is not up to good effect, this seriously inhibits wickers and wicker plaiting article to produce
The development of industry.
Invention content
In order to solve the above-mentioned technical problem, a kind of purple willow of offer of the invention removes the peel pre-treating method.
The present invention is achieved by the following technical solutions.
A kind of purple willow peeling pre-treating method, including following operating procedure：
（1）Ozone Oxidation Treatment is passed through on purple willow surface after harvesting, it is 15-20% to be then dried to water content；
（2）Step will be passed through（1）The purple willow of processing is put into peeling liquid, after immersion treatment 30-40min, takes out, dries processing,
Then peeling processing is carried out, wherein peeling liquid is made of the component of following parts by weight：1-4 parts of tartaric acid oxygen antimony sodium, ammonium citrate
16-20 parts, 4-6 parts of potassium metabisulfite, 11-13 parts of sodium dimercaptosuccinate, 14-17 parts of methanesulfonic sodium, diphenylamine sulfonic acid sodium salt 22-
26 parts, 190-200 parts of water.
Specifically, above-mentioned steps（1）In, when ozone Oxidation Treatment, a concentration of 110-130ppm of ozone, the time of processing
For 10-15min.
Specifically, above-mentioned steps（1）In, the temperature of drying and processing is 70-80 DEG C, and the time of drying and processing is 3-4 hours.
Specifically, above-mentioned steps（2）In, the mass ratio of purple willow and peeling liquid is 1:8-10.
Specifically, the above-mentioned time for drying processing is 48-72 hours.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows：
A kind of purple willow provided by the invention removes the peel pre-treating method, easy to operate, of low cost, and treatment effeciency is high, it can be achieved that even
Continuous industrialized production, treated purple willow, decortication effect is notable, and peeling is efficient, is not in wicker damage, blocks peeling
The case where machine.Step（1）In, by carrying out oxidation processes to purple willow, the precision on purple willow surface can be effectively reduced, it is promoted
Laxity, and then be conducive to the operation of peeling；Step（2）In peeling liquid, can so that wicker skin between institutional framework it is loose,
Porosity is promoted, and then effectively reduces the cohesive force of wicker skin, improves the decortication effect of wicker skin.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, following embodiment carries out the present invention
It is further described.It should be appreciated that specific embodiment party example described herein is only used to explain the present invention, it is not used to limit
The fixed present invention.
Embodiment 1
A kind of purple willow peeling pre-treating method, including following operating procedure：
（1）Ozone Oxidation Treatment is passed through on purple willow surface after harvesting, it is 15% to be then dried to water content；
（2）Step will be passed through（1）The purple willow of processing is put into peeling liquid, after immersion treatment 30min, takes out, dries processing, then
Peeling processing is carried out, wherein peeling liquid is made of the component of following parts by weight：1 part of tartaric acid oxygen antimony sodium, 16 parts of ammonium citrate, coke
4 parts of potassium sulfite, 11 parts of sodium dimercaptosuccinate, 14 parts of methanesulfonic sodium, 22 parts of diphenylamine sulfonic acid sodium salt, 190 parts of water.
Specifically, above-mentioned steps（1）In, when ozone Oxidation Treatment, a concentration of 110ppm of ozone, the time of processing is
10min。
Specifically, above-mentioned steps（1）In, the temperature of drying and processing is 70 DEG C, and the time of drying and processing is 3 hours.
Specifically, above-mentioned steps（2）In, the mass ratio of purple willow and peeling liquid is 1:8.
Specifically, the above-mentioned time for drying processing is 48 hours.
Embodiment 2
A kind of purple willow peeling pre-treating method, including following operating procedure：
（1）Ozone Oxidation Treatment is passed through on purple willow surface after harvesting, it is 18% to be then dried to water content；
（2）Step will be passed through（1）The purple willow of processing is put into peeling liquid, after immersion treatment 35min, takes out, dries processing, then
Peeling processing is carried out, wherein peeling liquid is made of the component of following parts by weight：2 parts of tartaric acid oxygen antimony sodium, 18 parts of ammonium citrate, coke
5 parts of potassium sulfite, 12 parts of sodium dimercaptosuccinate, 16 parts of methanesulfonic sodium, 24 parts of diphenylamine sulfonic acid sodium salt, 195 parts of water.
Specifically, above-mentioned steps（1）In, when ozone Oxidation Treatment, a concentration of 120ppm of ozone, the time of processing is
13min。
Specifically, above-mentioned steps（1）In, the temperature of drying and processing is 75 DEG C, and the time of drying and processing is 3.5 hours.
Specifically, above-mentioned steps（2）In, the mass ratio of purple willow and peeling liquid is 1:9.
Specifically, the above-mentioned time for drying processing is 60 hours.
Embodiment 3
A kind of purple willow peeling pre-treating method, including following operating procedure：
（1）Ozone Oxidation Treatment is passed through on purple willow surface after harvesting, it is 20% to be then dried to water content；
（2）Step will be passed through（1）The purple willow of processing is put into peeling liquid, after immersion treatment 40min, takes out, dries processing, then
Peeling processing is carried out, wherein peeling liquid is made of the component of following parts by weight：4 parts of tartaric acid oxygen antimony sodium, 20 parts of ammonium citrate, coke
6 parts of potassium sulfite, 13 parts of sodium dimercaptosuccinate, 17 parts of methanesulfonic sodium, 26 parts of diphenylamine sulfonic acid sodium salt, 200 parts of water.
Specifically, above-mentioned steps（1）In, when ozone Oxidation Treatment, a concentration of 130ppm of ozone, the time of processing is
15min。
Specifically, above-mentioned steps（1）In, the temperature of drying and processing is 80 DEG C, and the time of drying and processing is 4 hours.
Specifically, above-mentioned steps（2）In, the mass ratio of purple willow and peeling liquid is 1:10.
Specifically, the above-mentioned time for drying processing is 72 hours.
It should be noted that the above examples are only used to illustrate the technical scheme of the present invention and are not limiting.Although with reference to compared with
Good embodiment describes the invention in detail, it will be understood by those of ordinary skill in the art that, it can be to the technology of invention
Scheme is modified or replaced equivalently, and without departing from the range of technical solution of the present invention, should all cover the power in the present invention
In sharp claimed range.
Claims (5)
1. a kind of purple willow removes the peel pre-treating method, which is characterized in that including following operating procedure：
（1）Ozone Oxidation Treatment is passed through on purple willow surface after harvesting, it is 15-20% to be then dried to water content；
（2）Step will be passed through（1）The purple willow of processing is put into peeling liquid, after immersion treatment 30-40min, takes out, dries processing,
Then peeling processing is carried out, wherein peeling liquid is made of the component of following parts by weight：1-4 parts of tartaric acid oxygen antimony sodium, ammonium citrate
16-20 parts, 4-6 parts of potassium metabisulfite, 11-13 parts of sodium dimercaptosuccinate, 14-17 parts of methanesulfonic sodium, diphenylamine sulfonic acid sodium salt 22-
26 parts, 190-200 parts of water.
2. a kind of purple willow according to claim 1 removes the peel pre-treating method, which is characterized in that above-mentioned steps（1）In, ozone
When oxidation processes, the time of a concentration of 110-130ppm of ozone, processing are 10-15min.
3. a kind of purple willow according to claim 1 removes the peel pre-treating method, which is characterized in that above-mentioned steps（1）In, drying
The temperature of processing is 70-80 DEG C, and the time of drying and processing is 3-4 hours.
4. a kind of purple willow according to claim 1 removes the peel pre-treating method, which is characterized in that above-mentioned steps（2）In, purple willow
Mass ratio with peeling liquid is 1:8-10.
5. a kind of purple willow according to claim 1 removes the peel pre-treating method, which is characterized in that the above-mentioned time for drying processing
It is 48-72 hours.