CN108745833A - A kind of general UV ordor removings coating construction process in sanitary ware industry bottom surface - Google Patents
A kind of general UV ordor removings coating construction process in sanitary ware industry bottom surface Download PDFInfo
- Publication number
- CN108745833A CN108745833A CN201810399741.XA CN201810399741A CN108745833A CN 108745833 A CN108745833 A CN 108745833A CN 201810399741 A CN201810399741 A CN 201810399741A CN 108745833 A CN108745833 A CN 108745833A
- Authority
- CN
- China
- Prior art keywords
- radium
- coating
- shine
- ordor
- roller
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of general UV ordor removings coating construction process in sanitary ware industry bottom surface, it is divided into clear-coated technique and white coating process, to sanitary ware industry bathroom cabinet plate, the disposable UV applications molding of cabinet back, suitable for different plates, its process characteristic adds radium-shine roller coating roll coating model to construct without spraying using common plain-barreled roll.Using that need not polish in technical solution of the present invention work progress, paint film is smooth, smooth, bright, strong covering power, good weatherability, and the complete ordor removing of paint film can reduce production process, production cost is greatly reduced, reduce environmental pollution, and improves production efficiency.
Description
Technical field
The present invention relates to the general UV ordor removings coating decorations of coating application technical field more particularly to a kind of sanitary ware industry bottom surface
Technique.
Background technology
Currently on the market production sanitary ware industry bathroom cabinet plate main technique be with after being polished after PE primer paintings again into
Row finishing coat application, or the use of UV roller coating applications constructed using common single roller or double roll coater roller coating multiple tracks, application comes out
Effect out-of-flatness, slivering weight, intermediate demand carry out multiple tracks polishing, and process is more, and working hour lengthens, and paint film is whole without ordor removing effect
Efficiency and benefit be not high, reduces the whole efficiency of application.It is painted using PE, a large amount of organic solvent pollution air of release,
Harmful substance is volatilized in production process, is seriously affected health, is not met National Environmental emission request, the production cycle is long, easily
The problems such as tangerine peel has occurred, and manual polishing difficulty is very big.
Invention content
In view of the deficiencies of the prior art, technical problem solved by the invention is to provide a kind of coating process and is not necessarily to sanding,
Application disposal molding, without the face of doing, paint film effect flat smooth, paint plate is tasteless, whiteness and the good construction work of color inhibition effect
Skill.
To solve above-mentioned technical problem the present invention provides a kind of general UV ordor removings coating construction process in sanitary ware industry bottom surface,
It is divided into clear-coated technique and white coating process, it is as follows respectively：
(1) clear-coated technique, includes the following steps：
1) base material is subjected to sanding dust removal process using tablet automatic sander with 240 mesh sandings；
2) putty roll coater roller coating UV ordor removing adhesive force is used to reinforce putty, coating weight is 20~25g/ ㎡, then with two
Mercury lamp carries out UV curing, and UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
3) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with a mercury lamp into
Row UV curing, UV solidification energies are 150mJ/cm2, drying time is 1~3 second；
4) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with a mercury lamp into
Row UV curing, UV solidification energies are 150mJ/cm2, drying time is 1~3 second；
5) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with three mercury lamps into
Row UV curing, UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
6) the disposable UV applications molding of cabinet back is completed to carry out overlay film protection, and cabinet plate front is carried out using automatic sander
Primary coat production is completed in sanding, dedusting.
In step 1), the base material includes plastic veneer or Wood veneer surfaced plate or paper overlay plate；
In step 3), 4) in, the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 50 lines；
In step 5), the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 65 lines.
(2) white coating process, includes the following steps：
1) base material is carried out carrying out sanding dust removal process with 240 mesh sandings using tablet automatic sander；
2) single roller roller coating UV ordor removing adhesive force reinforces priming paint, and coating weight is 15~20g/ ㎡, is then carried out with two mercury lamps
UV curing, UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
3) the radium-shine roller coating UV ordor removings color inhibition white primers of UV, coating weight is 40~50g/ ㎡, then with a gallium lamp, one
A mercury lamp carries out UV curing, and UV solidification energies are 350mJ/cm2, drying time is 3~5 seconds；
4) the radium-shine roller coating UV ordor removings color inhibition white primers of UV, coating weight is 40~50g/ ㎡, then with a gallium lamp, one
A mercury lamp carries out UV curing, and UV solidification energies are 350mJ/cm2, drying time is 3~5 seconds；
5) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with three mercury lamps into
Row UV curing, UV solidification energies are 350mJ/cm2, drying time is 3~5；
6) the disposable UV applications molding of cabinet back is completed to carry out overlay film protection, and cabinet plate front is carried out using automatic sander
Primary coat production is completed in sanding, dedusting.
In step 1), the base material includes plastic veneer or Wood veneer surfaced plate or paper overlay plate；
In step 3), 4) in, the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 50 lines；
In step 5), the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 65 lines.
The advantageous effect of technical solution of the present invention：
(1) coating process is not necessarily to sanding, application disposal molding, without the face of doing, paint film effect flat smooth, paint plate without
Taste, whiteness and color inhibition effect are good, efficient, environmentally friendly, at low cost, and paint film property such as hardness, wearability, brightness etc. obtain
Greatly promoted.
(2) thick painting may be implemented using radium-shine roller coating machine, efficiently.The complicated processes of application repeatedly are saved, film is more
Add smooth, richness is more preferable, can compare favourably with spraying effect.
(3) quantity of UV roll coating apparatus and its mating UV photo solidification machines and sander can be reduced, fund, place, people are saved
Member's cost input.
Specific implementation mode
The specific implementation mode of the present invention is further described with reference to embodiment, but is not the limit to the present invention
It is fixed.
Embodiment 1：
A kind of general clear-coated construction technology of UV ordor removings in sanitary ware industry bottom surface, includes the following steps：
1) base material is subjected to sanding dust removal process using tablet automatic sander with 240 mesh sandings；
2) putty roll coater roller coating UV ordor removing adhesive force is used to reinforce putty, coating weight is 20~25g/ ㎡, then with two
Mercury lamp carries out UV curing, and UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
3) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with a mercury lamp into
Row UV curing, UV solidification energies are 150mJ/cm2, drying time is 1~3 second；
4) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with a mercury lamp into
Row UV curing, UV solidification energies are 150mJ/cm2, drying time is 1~3 second；
5) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with three mercury lamps into
Row UV curing, UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
6) the disposable UV applications molding of cabinet back is completed to carry out overlay film protection, and cabinet plate front is carried out using automatic sander
Primary coat production is completed in sanding, dedusting.
In step 1), the base material includes plastic veneer or Wood veneer surfaced plate or paper overlay plate；
In step 3), 4) in, the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 50 lines；
In step 5), the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 65 lines.
Embodiment 2：
A kind of general UV ordor removings white coating construction process in sanitary ware industry bottom surface, includes the following steps：
1) base material is carried out carrying out sanding dust removal process with 240 mesh sandings using tablet automatic sander；
2) single roller roller coating UV ordor removing adhesive force reinforces priming paint, and coating weight is 15~20g/ ㎡, is then carried out with two mercury lamps
UV curing, UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
3) the radium-shine roller coating UV ordor removings color inhibition white primers of UV, coating weight is 40~50g/ ㎡, then with a gallium lamp, one
A mercury lamp carries out UV curing, and UV solidification energies are 350mJ/cm2, drying time is 3~5 seconds；
4) the radium-shine roller coating UV ordor removings color inhibition white primers of UV, coating weight is 40~50g/ ㎡, then with a gallium lamp, one
A mercury lamp carries out UV curing, and UV solidification energies are 350mJ/cm2, drying time is 3~5 seconds；
5) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight be 40~50g/ ㎡, then with three mercury lamps into
Row UV curing, UV solidification energies are 350mJ/cm2, drying time is 3~5；
6) the disposable UV applications molding of cabinet back is completed to carry out overlay film protection, and cabinet plate front is carried out using automatic sander
Primary coat production is completed in sanding, dedusting.
In step 1), the base material includes plastic veneer or Wood veneer surfaced plate or paper overlay plate；
In step 3), 4) in, the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 50 lines；
In step 5), the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 65 lines.
Detailed description is made that embodiments of the present invention above in association with embodiment, but the present invention be not limited to it is described
Embodiment.To those skilled in the art, without departing from the principles and spirit of the present invention, to these realities
The mode of applying carries out various change, modification, replacement and modification and still falls in protection scope of the present invention.
Claims (8)
1. a kind of general clear-coated construction technology of UV ordor removings in sanitary ware industry bottom surface, includes the following steps：
1) base material is subjected to sanding dust removal process using tablet automatic sander with 240 mesh sandings；
2) putty roll coater roller coating UV ordor removing adhesive force is used to reinforce putty, coating weight is 20~25g/ ㎡, then with two mercury lamps
UV curing is carried out, UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
3) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight are 40~50g/ ㎡, then carry out purple with a mercury lamp
Outside line is dried, and UV solidification energies are 150mJ/cm2, drying time is 1~3 second；
4) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight are 40~50g/ ㎡, then carry out purple with a mercury lamp
Outside line is dried, and UV solidification energies are 150mJ/cm2, drying time is 1~3 second；
5) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight are 40~50g/ ㎡, then carry out purple with three mercury lamps
Outside line is dried, and UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
6) the disposable UV applications molding of cabinet back is completed to carry out overlay film protection, and cabinet plate front carries out sand using automatic sander
Primary coat production is completed in light, dedusting.
2. the general clear-coated construction technology of UV ordor removings in sanitary ware industry bottom surface according to claim 1, it is characterised in that：?
In step 1), the base material includes plastic veneer or Wood veneer surfaced plate or paper overlay plate.
3. the general clear-coated construction technology of UV ordor removings in sanitary ware industry bottom surface according to claim 1, it is characterised in that：?
Step 3), 4) in, the rubber roller of the radium-shine roller is all made of the radium-shine rubber roller of 50 lines.
4. the general clear-coated construction technology of UV ordor removings in sanitary ware industry bottom surface according to claim 1, it is characterised in that：?
In step 5), the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 65 lines.
5. a kind of general UV ordor removings white coating construction process in sanitary ware industry bottom surface, includes the following steps：
1) base material is carried out carrying out sanding dust removal process with 240 mesh sandings using tablet automatic sander；
2) single roller roller coating UV ordor removing adhesive force reinforces priming paint, and coating weight is 15~20g/ ㎡, is then carried out with two mercury lamps ultraviolet
Line is dried, and UV solidification energies are 300mJ/cm2, drying time is 1~3 second；
3) the radium-shine roller coating UV ordor removings color inhibition white primers of UV, coating weight is 40~50g/ ㎡, then with a gallium lamp, a mercury
Lamp carries out UV curing, and UV solidification energies are 350mJ/cm2, drying time is 3~5 seconds；
4) the radium-shine roller coating UV ordor removings color inhibition white primers of UV, coating weight is 40~50g/ ㎡, then with a gallium lamp, a mercury
Lamp carries out UV curing, and UV solidification energies are 350mJ/cm2, drying time is 3~5 seconds；
5) the radium-shine roller coating UV ordor removings color inhibition high definition priming paint of UV, coating weight are 40~50g/ ㎡, then carry out purple with three mercury lamps
Outside line is dried, and UV solidification energies are 350mJ/cm2, drying time is 3~5；
6) the disposable UV applications molding of cabinet back is completed to carry out overlay film protection, and cabinet plate front carries out sand using automatic sander
Primary coat production is completed in light, dedusting.
6. the general UV ordor removings white coating construction process in sanitary ware industry bottom surface according to claim 5, it is characterised in that：?
In step 1), the base material includes plastic veneer or Wood veneer surfaced plate or paper overlay plate.
7. the general UV ordor removings white coating construction process in sanitary ware industry bottom surface according to claim 1, it is characterised in that：?
Step 3), 4) in, the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 50 lines.
8. the general UV ordor removings white coating construction process in sanitary ware industry bottom surface according to claim 5, it is characterised in that：?
In step 5), the rubber roller of the radium-shine roller uses the radium-shine rubber roller of 65 lines.