CN113019860A - UV film-coating bright surface-cleaning coating construction process for decorative plate - Google Patents
UV film-coating bright surface-cleaning coating construction process for decorative plate Download PDFInfo
- Publication number
- CN113019860A CN113019860A CN202110230321.0A CN202110230321A CN113019860A CN 113019860 A CN113019860 A CN 113019860A CN 202110230321 A CN202110230321 A CN 202110230321A CN 113019860 A CN113019860 A CN 113019860A
- Authority
- CN
- China
- Prior art keywords
- coating
- film
- decorative plate
- construction process
- bright
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The application discloses decorative board UV tectorial membrane bright light clear face application construction technology relates to coating construction technical field, includes following step: s1, performing surface cleaning treatment on the base material pasted with wood grains, stone grains and pure-color triamine paper by using a dust remover; s2, rolling a special UV attached bottom for a triamine layer; s3, roller coating the UV sanded bottom; s4, driving the abrasive belt to sand and remove dust by using a paint film sander; s5, rolling a UV coated bright clear surface, and enabling the plate to enter an UV automatic film press under the condition of wet film; s6, drying with strong mercury lamp in the film press; s7, the plate enters a strong gallium lamp and a strong mercury lamp for ultraviolet drying; and S8, finally, covering a protective film and packaging to finish the production. By utilizing the UV light curing principle, a paint film is instantly (1-3 s) dried in a UV drier, the coating efficiency is high, and the decorative plate has the characteristics of stain resistance, scratch resistance, tastelessness, safety, yellowing resistance, excellent hand feeling, long service life, environmental protection, strong sinking resistance and the like.
Description
Technical Field
The application relates to the technical field of coating construction, in particular to a UV (ultraviolet) film-coated bright surface-cleaning coating construction process for a decorative plate.
Background
At present, the bright coating effect of decorative plates on the market mainly comprises UV (ultraviolet) spraying bright clear surfaces and PET (polyethylene terephthalate) film flatly pasted on the surfaces of the decorative plates. The UV flow-coating bright clear top coat paint film has high plumpness, but has high requirements on paint and coating environment, and the paint film is thick, has easy edge breakage. The PET film with the flat-pasted board surface has strong anti-sinking capability, but the glue is not environment-friendly due to the use of the glue component, and is easy to delaminate and not resistant to yellowing after a long time. The UV film-coating bright surface-cleaning process can neutralize the advantages and disadvantages of the UV film-coating bright surface-cleaning process and the UV film-coating bright surface-cleaning process.
Disclosure of Invention
The invention aims to provide a UV film-coating bright surface-cleaning coating construction process for a decorative plate, which aims to solve the problems in the prior art in the background technology.
A UV film-coating bright surface-cleaning coating construction process for a decorative plate comprises the following steps:
s1, performing surface cleaning treatment on the base material pasted with wood grains, stone grains and pure-color triamine paper by using a dust remover;
s2, roller coating the special UV attached bottom for the triamine layer, and then carrying out ultraviolet drying by using a weak mercury lamp and a weak mercury lamp;
s3, roller coating a UV sanding bottom, and then carrying out ultraviolet drying by using a strong mercury lamp and a strong mercury lamp;
s4, driving the abrasive belt to sand and remove dust by using a paint film sander;
s5, rolling a UV coated bright clear surface, and enabling the plate to enter an UV automatic film press under the condition of wet film;
s6, performing ultraviolet drying in a film press by using a strong mercury lamp, enabling a wet film to pass through a lamp under the film pressure of the bright film to enable the paint film to be in a surface dry state for shaping, and then performing demoulding;
s7, the plate enters a strong gallium lamp and a strong mercury lamp to be subjected to ultraviolet drying, so that a paint film is in a full-dry state;
and S8, finally, covering a protective film and packaging to finish the production.
Preferably, the coating weight of the triamine layer in the S2 is 20-25 g per square meter, the ultraviolet drying strength is 200-250 mJ per square meter, and the drying time is 1-3 seconds.
Preferably, in the S3, the coating weight of the sanded sole is 35-40 g per square meter, the ultraviolet drying strength is 300-400 mJ per square meter, and the drying time is 1-3 seconds.
Preferably, in the step S5, the coating weight of the film-coated glossy clear surface is 70 to 75g per square meter.
Preferably, in the S6, the ultraviolet drying strength is 150-200 mJ/c square meter, and the drying time is 1-3 seconds.
Preferably, in the S7, the ultraviolet drying intensity is 600-800 mJ/c square meter, and the drying time is 1-3 seconds.
Preferably, the abrasive belts of the sander in the S4 are selected from 400# and 600 #.
Preferably, the paint film in S6 is added with organosilicon.
The invention has the beneficial effects that: by utilizing the UV light curing principle, a paint film is instantly (1-3 s) dried in a UV drier, the coating efficiency is high, and the decorative plate has the characteristics of stain resistance, scratch resistance, tastelessness, safety, yellowing resistance, excellent hand feeling, long service life, environmental protection, strong sinking resistance and the like.
Detailed Description
In order to make the objects, technical solutions and advantages of the present application more apparent, the technical solutions of the present application will be described in detail and completely with reference to the specific embodiments of the present application. It should be apparent that the described embodiments are only some of the embodiments of the present application, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present application.
The technical solutions provided in the embodiments of the present application are described in detail below.
A UV film-coating bright surface-cleaning coating construction process for a decorative plate comprises the following steps:
1. carrying out surface cleaning treatment on the base material stuck with wood grains, stone grains and pure-color triamine paper by using a dust remover;
2. the special UV attached bottom for the triamine layer is coated by roller, the coating amount is 20-25 g/square meter, then, a weak mercury lamp and a weak mercury lamp are used for carrying out ultraviolet drying, the drying strength is 200-250 mJ/square meter, and the drying time is 1-3 seconds;
3. roller coating of a UV sanded bottom, wherein the coating weight is 35-40 g/square meter, then carrying out ultraviolet drying by using a strong mercury lamp and a strong mercury lamp, the drying strength is 300-400 mJ/square meter, and the drying time is 1-3 seconds;
4. sanding and dedusting by using a paint film sander and using No. 400 and No. 600 abrasive belts;
5. the method comprises the following steps of roller coating UV (ultraviolet) coated film bright and clean surfaces, wherein the coating amount is 70-75 g/square meter, and the plate enters an UV automatic film press under the condition of wet film;
6. carrying out ultraviolet drying by using a strong mercury lamp in a film press, wherein the drying strength is 150-200 mJ/c square meter, the drying time is 1-3 seconds, a wet film passes through a lamp under the film pressure of a bright film to enable the paint film to be in a surface dry state for shaping (in the process, the surface effect of the bright film is transferred to the surface of the paint film), and then demoulding;
7. the plate enters a strong gallium lamp and a strong mercury lamp for ultraviolet drying, the drying strength is 600-800 mJ/c square meter, the drying time is 1-3 seconds, and the paint film is in a full-dry state;
8. and finally, coating a protective film and packaging to finish production.
In summary, the following steps: the UV film pressing process can reduce the interference of oxygen inhibition during the drying of the finish paint to a certain extent, the film pressing process can flatten dust points on the surface of a paint film to ensure that the surface of the paint film has no dust points, the flatness of the paint film is high, and the organosilicon is added into the UV finish paint, so that the hand feeling of the paint film is enhanced, and the adhesive density of the paint film can also be increased, thereby enhancing the scratch resistance and the wear resistance of the paint film.
The production efficiency is high: the UV coating paint film is dried by using a UV photocuring principle, and is dried instantly (1-3 s) in a UV dryer, so that the coating efficiency is high; production passes through the automatic mechanization UV production line, and material loading, unloading are automatic, remove artifical degree height, and the production efficiency is high for raw and other materials (substrate) end of the line promptly finished product.
The process selects UV film-coated bright clear-surface coating on a wood grain/stone grain/pure-color triamine plate, and the paint film has high yellowing resistance.
The large plate is coated, and then the material cutting and edge sealing are carried out, so that the edge sealing strip of the same type can be matched, and the grade is high.
The product is suitable for cabinet door plates of cabinets such as cabinets, wardrobes, bookcases and the like.
The above description is only an example of the present application and is not intended to limit the present application. Various modifications and changes may occur to those skilled in the art. Any modification, equivalent replacement, improvement, etc. made within the spirit and principle of the present application should be included in the scope of the claims of the present application.
Claims (8)
1. A UV film-coated bright surface-cleaning coating construction process for a decorative plate is characterized by comprising the following steps:
s1, performing surface cleaning treatment on the base material pasted with wood grains, stone grains and pure-color triamine paper by using a dust remover;
s2, roller coating the special UV attached bottom for the triamine layer, and then carrying out ultraviolet drying by using a weak mercury lamp and a weak mercury lamp;
s3, roller coating a UV sanding bottom, and then carrying out ultraviolet drying by using a strong mercury lamp and a strong mercury lamp;
s4, driving the abrasive belt to sand and remove dust by using a paint film sander;
s5, rolling a UV coated bright clear surface, and enabling the plate to enter an UV automatic film press under the condition of wet film;
s6, performing ultraviolet drying in a film press by using a strong mercury lamp, enabling a wet film to pass through a lamp under the film pressure of the bright film to enable the paint film to be in a surface dry state for shaping, and then performing demoulding;
s7, the plate enters a strong gallium lamp and a strong mercury lamp to be subjected to ultraviolet drying, so that a paint film is in a full-dry state;
and S8, finally, covering a protective film and packaging to finish the production.
2. The UV coating bright surface coating construction process for the decorative plate according to claim 1, which is characterized in that: the coating weight of the triamine layer in the S2 is 20-25 g per square meter, the ultraviolet drying strength is 200-250 mJ per square meter, and the drying time is 1-3 seconds.
3. The UV coating bright surface coating construction process for the decorative plate according to claim 1, which is characterized in that: in the S3, the coating weight of the sanded bottom is 35-40 g per square meter, the ultraviolet drying strength is 300-400 mJ per square meter, and the drying time is 1-3 seconds.
4. The UV coating bright surface coating construction process for the decorative plate according to claim 1, which is characterized in that: in the step S5, the coating weight of the film-coated bright clear surface is 70-75 g/square meter.
5. The UV coating bright surface coating construction process for the decorative plate according to claim 1, which is characterized in that: in the S6, the ultraviolet drying intensity is 150-200 mJ/c square meter, and the drying time is 1-3 seconds.
6. The UV coating bright surface coating construction process for the decorative plate according to claim 1, which is characterized in that: in the S7, the ultraviolet drying intensity is 600-800 mJ/c square meter, and the drying time is 1-3 seconds.
7. The UV coating bright surface coating construction process for the decorative plate according to claim 1, which is characterized in that: and abrasive belts of the sander in the S4 are selected from 400# and 600 #.
8. The UV coating bright surface coating construction process for the decorative plate according to claim 1, which is characterized in that: and the paint film in the S6 is added with organic silicon.