CN105413990A - LED-UV curing and coating method and application thereof - Google Patents
LED-UV curing and coating method and application thereof Download PDFInfo
- Publication number
- CN105413990A CN105413990A CN201510857038.5A CN201510857038A CN105413990A CN 105413990 A CN105413990 A CN 105413990A CN 201510857038 A CN201510857038 A CN 201510857038A CN 105413990 A CN105413990 A CN 105413990A
- Authority
- CN
- China
- Prior art keywords
- led
- solidifies
- coating
- coating process
- light source
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an LED-UV curing and coating method and application thereof. The method is characterized by including the following steps that firstly, wood is colored through a coloring agent; secondly, the polished wood is coated with UV-LED curing paint; and thirdly, the coated wood is subjected to UV-LED curing through a UV-LED light source. The method has the beneficial effects that energy consumption is low, products are not prone to deformation, operation cost is low, maintenance labor hours are reduced, no preheating is needed, preparation time is short, photo-initiation efficiency is high, harm to the health of operators is small, the UV-LED light source is free of mercury, ozone and other harmful gas cannot be generated, cold water can be used for cooling in the light curing process, environmental friendliness is facilitated, and noise pollution is reduced.
Description
Technical field
The present invention relates to a kind of coating process field, particularly relate to a kind of UV-LED and solidify coating process and application thereof.
Background technology
Wood decorative lamination decoration board utilizes natural seeds fancy veneer or artificial wooden fancy veneer by the veneer that accurate wound is cut or rotary-cut processing method is obtained, is attached on base material, adopts advanced adhesion process, through a kind of flawless finish sheet material that hot pressing is made.Decorative panel is as a kind of surface decoration material, can not be used alone, certain thickness can only be pasted onto and have on the backing material plate of some strength, as inorganic board, plastic plate, solid wood board, lumber core, multi-plywood, medium density fibre board (MDF) and particieboard etc., just can reasonably be utilized.Natural wood veneer veneer has natural wood decorative pattern, textured pattern nature, and variability is larger, random, and prosthetic is affected, and the sense of reality and third dimension by force, are widely used in interior decoration.As carried out UV application to timber, need to carry out UV solidification, and often use UV mercury lamp to have some defects as radiation source, the service life of UV mercury lamp is short, by mercury and as accessory substance ozone form the environmental problem that can cause.In addition, mercury lamp has lower energy conversion rate usually, needs preheating time, a large amount of heats can be produced during operation, need blower fan to cool, thus produce noise pollution, and heat-sensitive substrate material easily causes distortion after being heated, thus affects the attractive in appearance of product and quality, also limit it and use.Although UV-LED light source has extra long life, high, the customizable effective irradiation area of snap switch energy, not mercurous, also can not produce ozone, energy consumption low, to eyes and the plurality of advantages such as skin irritatin is little, but be mainly applied on widget now, as electronic applications, as on the parts such as optics, mobile phone, touch-screen, hard disk, encoder, thus limit its application.Although Chinese patent CN201080055758.5 discloses the LED solidification of radiation-hardenable floor paint, the patent provides a kind of be suitable for being solidified by LED radiation-hardenable floor paint and a kind of method with this coatings floor and a kind of coating floor of coating containing being prepared by this coating is provided, this coating process is only applicable to floor, and be not suitable for wooden decorative lamination decoration board, and and unresolved heat-sensitive substrate material cause after being heated be out of shape problem.
Summary of the invention
The technical problem to be solved in the present invention overcomes the deficiencies in the prior art, an object of the present invention is to provide a kind of UV-LED and solidify coating process, effectively can solve heat-sensitive substrate material because of yielding problem of being heated, but also there are energy-saving and environmental protection, not mercurous, also can not produce ozone, to eyes and the advantage such as skin irritatin is little.Another object of the present invention is also to provide above-mentioned UV-LED to solidify the application of coating process, and involved field comprises the production of decorative board for wall, solid wooden floor board, solid wood composite decorating board.
For solving said method problem, the present invention by the following technical solutions:
First timber is attached on base material, adopts advanced adhesion process to carry out gluing, and then carry out UV-LED solidification application.
A kind of UV-LED solidifies coating process, it is characterized in that: it comprises the following steps:
Step 1, employing colouring agent carry out painted to timber; Step 2, the timber after polishing to be carried out to application UV-LED coating material solidified; Step 3, carry out UV-LED solidification by UV-LED light source to being coated with the timber that installs.
Colouring agent described in step 1 is any one or more than one the mixing in the painted adhesive agent of water-based, water soluble dyestuffs or aqueous color paste, coated on timber by any one mode in spraying, showering, roller coat, brushing, obliterating, dip-coating and painted and Seal treatment is carried out to timber, and adopt far-infrared ray drying, infra-red drying, microwave drying or heated-air drying any one or more than one mode drying is carried out to the timber after painted, make it reach the effect of uniform coloring and closed timber pore simultaneously.Polishing can be carried out to wood surface after drying, remove wood thorn.
Application UV-LED described in step 2 is coating material solidified, comprise that UV-LED solidifies adhesion primer, UV-LED solidification infiltration priming paint, UV-LED curing transfer glue, UV-LED solidify putty, UV-LED curing transparent priming, UV-LED solidifies at the bottom of sanding priming paint, UV-LED solidified wear resistance, UV-LED solidifies showering varnish, UV-LED solidifies solid color enamel " comprise UV-LED and solidify white paint ", UV-LED solidify in finish paint any one or more than one, the number of channels of each coating be together or together more than, and the coating material solidified order of application UV-LED is according to needing suitably to adjust.
The coating material solidified total coating weight of UV-LED described in step 2 is 10-350g/m
2, every one coating weight can be 5-150g/m
2, the coating method of application is any one in showering, spraying, roller coat, brushing, obliterating, dip-coating, and wherein roll coating model comprises just against roller coat, common single and double in the same way roller coat, radium-shine single or two roller coat.
What the UV-LED light source described in step 3 adopted is wavelength is 260-450nm, and energy is 50-1000mj/cm
2uV-LED light source, the UV-LED light source of preferred wavelength to be 360-420nm or wavelength be 260-360nm, 1-2 UV lamp of arranging in pairs or groups, UV lamp comprises UV mercury lamp, UV gallium lamp or UV iron lamp.
UV-LED solidification process described in step 3 is cured on streamline with the speed of 1-20 m/min, and light application time is 1-20S.
There is the conventional light trigger of absorption bands between 360-450nm on the market now, select the light source efficiency of initiation of this wave band high, if wavelength is oversize, belong to visible region, in sunshine, the content of visible ray is up to 40%-55%, easily causes paint solidification, thus causes coating decoration inconvenient.
Described a kind of UV-LED solidifies coating process, except being applicable to the subsides wood finishing of inorganic board, stone material, is particularly useful for the subsides wood finishing of heat-sensitive substrate material.Heat-sensitive substrate material comprises plastic basis material, solid wood base material, lumber core, particieboard, moist-proof board, glued board, core-board medium density fibre board (MDF) or other hardboards.Because UV-LED belongs to cold light source, effectively can solve the problem of heat-sensitive substrate material because being out of shape after being heated, and UV-LED light source use procedure water cooling, effectively can solve UV mercury lamp solidification process needs to utilize blower fan to cool and the noise problem that produces.
Described UV-LED solidifies coating process application, involved field comprises decorative board for wall, the large plate of wood furniture, MDF decorate large plate " namely medium density fiber decorates large plate ", solid wood composite decorating board, melamine sticky paperboard, solid wooden compound floor, wood-plastic composite floor and other paste the heat-sensitive substrate material floor of wooden skin or the production of decorative panel.
Compared with prior art, the invention has the advantages that:
1, first coloring treatment is carried out to timber, reach the effect of uniform coloring and closed timber pore simultaneously, later stage application adopts UV-LED light source to be cured because UV-LED light source is cold light source, can effectively solve heat-sensitive substrate material because being heated yielding shortcoming.
2, adopt LED-UV solidification, than traditional UV mercury lamp solidification, can save energy 75%-90%.
3, the life-span of UV mercury lamp light source only has 1000-2000h, and LED-UV light source has extra long life, can reach 8-10 ten thousand hours, can significantly cut down operating cost and maintenance man-hours.
4, LED-UV light source snap switch energy high, namely to start shooting pass, without the need to preheating, exposure intensity can reach 8000mW/cm
2above.
5, the customizable effective irradiation area of LED-UV light source, improves light-initiated efficiency.
6, LED-UV light source without infra-red radiation, belong to direct light, to skin and eye irritation little, be conducive to workmen healthy.
Energy consumption of the present invention is low; product is not yielding, and operating cost is low, and maintenance man-hours is few; without the need to preheating; time is short, and light-initiated efficiency is high, little to operator ' s health infringement; LED-UV light source is not mercurous; also can not produce ozone and other pernicious gases, Light Curing can cool with cold water, is conducive to environmental protection and reduces noise pollution.
Detailed description of the invention
Below with reference to specific embodiment, the present invention is described in further detail.
Embodiment 1: be first attached on PVC stone-plastic plate by the wooden skin through rotary-cut, adopts moisture-curable Reactive hot melt adhesive (PUR adhesive) to carry out gluing, and then carries out UV-LED solidification application.
A kind of UV-LED solidifies coating process, comprises the following steps:
1, by painted for water-based adhesive agent is brushed on timber, painted and Seal treatment is carried out to timber, makes it reach the effect of uniform coloring and closed timber pore simultaneously;
2, microwave dryer is adopted to carry out microwave drying to the timber after painted;
3, polishing is carried out to wood surface, remove wood thorn;
4, carry out application UV-LED to the timber after polishing coating material solidified, coating squence is followed successively by:
1., roller coat one 40g/m
2uV-LED solidification infiltration priming paint, carry out levelling through levelling drying tunnel;
2., roller coat one 30g/m
2uV-LED solidify putty, the wavelength of UV-LED light source is 360-400nm, and energy is 100mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 5S;
3., roller coat one 50g/m
2uV-LED solidify sanding priming paint, the wavelength of UV-LED light source is 420-450nm, and energy is 80mj/cm
2, be cured on streamline with the speed of 5 ms/min, hardening time is 10S;
4., showering one 110g/m
2uV-LED solidification drench before white background, the wavelength of UV-LED light source is 380-410nm, and energy is 120mj/cm
2, be cured on streamline with the speed of 15 ms/min, hardening time is 4S;
5., showering one 120g/m
2uV-LED solidify showering height light face, the wavelength of UV-LED light source is 395-405nm, and energy is 110mj/cm
2, be cured on streamline with the speed of 12 ms/min, hardening time is 6S.
In the use procedure of above-mentioned UV-LED light source, adopt water cooling, effectively can solve UV mercury lamp solidification process needs to utilize blower fan to cool and the noise problem of generation.
Above-mentioned UV-LED solidifies the production that coating process can be applicable to decorative board for wall, solid wood composite decorating board.
Embodiment 2: be first attached in inorganic board by the wooden skin through slicing, adopts moisture-curable Reactive hot melt adhesive (PUR adhesive) to carry out gluing, and then carries out UV-LED solidification application.
A kind of UV-LED solidifies coating process, comprises the following steps:
1, pass through water soluble dyestuffs roller coat on timber, painted and Seal treatment is carried out to timber, makes it reach the effect of uniform coloring and closed timber pore simultaneously;
2, far-infrared drying technology is adopted to carry out drying to the timber after painted;
3, polishing is carried out to wood surface, remove wood thorn;
4, carry out application UV-LED to the timber after polishing coating material solidified, coating squence is followed successively by:
1., roller coat one 35g/m
2uV-LED solidification infiltration priming paint, carry out levelling through levelling drying tunnel;
2., roller coat one 20g/m
2uV-LED solidify putty, the wavelength of UV-LED light source is 360-380nm, and energy is 120mj/cm
2, be cured on streamline with the speed of 15 ms/min, hardening time is 5S;
3., roller coat one 60g/m
2uV-LED solidify sanding priming paint, the wavelength of UV-LED light source is 400-420nm, and energy is 120mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 8S;
4., roller coat three road 10g/m
2uV-LED solidify at the bottom of look, the wavelength of UV-LED light source is 360-370nm, and energy is 600mj/cm
2, be cured on streamline with the speed of 20 ms/min, hardening time is 5S;
5., roller coat one 50g/m
2uV-LED solidification just against the clear face of roller height light, the wavelength of UV-LED light source is 360-365nm, and energy is 800mj/cm
2, be cured on streamline with the speed of 14 ms/min, hardening time is 5S.
In the use procedure of above-mentioned UV-LED light source, adopt water cooling, effectively can solve UV mercury lamp solidification process needs to utilize blower fan to cool and the noise problem of generation.
Above-mentioned UV-LED solidifies the production that coating process can be applicable to decorative board for wall, solid wood composite decorating board.
Embodiment 3: be first attached on multi-plywood by the wooden skin through slicing, adopts silicone adhesive to carry out gluing, and then carries out UV-LED solidification application.
A kind of UV-LED solidifies coating process, comprises the following steps:
1, by will or aqueous color paste obliterating on timber, painted and Seal treatment is carried out to timber, makes it reach the effect of uniform coloring and closed timber pore simultaneously;
2, infra-red drying technology is adopted to carry out drying to the timber after painted;
3, polishing is carried out to wood surface, remove wood thorn;
4, carry out application UV-LED to the timber after polishing coating material solidified, coating squence is followed successively by:
1., roller coat one 45g/m
2uV-LED solidification infiltration priming paint, carry out levelling through levelling drying tunnel;
2., roller coat one 30g/m
2uV-LED solidify putty, the wavelength of UV-LED light source is 360-400nm, and energy is 100mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 10S;
3., showering one 90g/m
2uV-LED solidify sanding priming paint, the wavelength of UV-LED light source is 390-410nm, and energy is 150mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 6S;
4., roller coat one 10g/m
2uV-LED solidify roller coat priming paint, the wavelength of UV-LED light source is 405-445nm, and energy is 100mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 5S;
5., roller coat one 12g/m
2uV-LED solidified wear resistance priming paint, the wavelength of UV-LED light source is 415-425nm, and energy is 120mj/cm
2, be cured on streamline with the speed of 15 ms/min, hardening time is 6S;
6., roller coat one 10g/m
2uV-LED solidify high rigidity priming paint, the wavelength of UV-LED light source is 420-440nm, and energy is 120mj/cm
2, be cured on streamline with the speed of 15 ms/min, hardening time is 6S;
7., roller coat one 10g/m
2uV-LED solidify sanding priming paint, the wavelength of UV-LED light source is 390-430nm, and energy is 150mj/cm
2, be cured on streamline with the speed of 8 ms/min, hardening time is 10S;
8., roller coat twice 5g/m
2uV-LED solidify scratch-resistant finish paint, the wavelength of UV-LED light source is 380-420nm, and energy is 100mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 8S;
In the use procedure of above-mentioned UV-LED light source, adopt water cooling, effectively can solve UV mercury lamp solidification process needs to utilize blower fan to cool and the noise problem of generation.
Above-mentioned UV-LED solidifies the production that coating process can be applicable to solid wooden compound floor, solid wood composite decorating board.
Embodiment 4: be first attached on medium density fibre board (MDF) by the wooden skin through slicing, adopts white glue with vinyl to carry out gluing, and then carries out UV-LED solidification application.
A kind of UV-LED solidifies coating process, comprises the following steps:
1, by will or aqueous color paste dip-coating on timber, painted and Seal treatment is carried out to timber, makes it reach the effect of uniform coloring and closed timber pore simultaneously;
2, microwave drying technology is adopted to carry out microwave drying to the timber after painted;
3, polishing is carried out to wood surface, remove wood thorn;
4, carry out application UV-LED to the timber after polishing coating material solidified, coating squence is followed successively by:
1., roller coat one 45g/m
2uV-LED solidification infiltration priming paint, the wavelength of UV-LED light source is 395-400nm, and energy is 80mj/cm2, is cured on streamline with the speed of 10 ms/min, and hardening time is 5S;
2., roller coat one 20g/m
2uV-LED solidify dual anticracking priming paint, the wavelength of UV-LED light source is 390-400nm, and energy is 100mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 5S;
3., roller coat one 30g/m
2uV-LED solidify heavy putty, the wavelength of UV-LED light source is 380-390nm, and energy is 150mj/cm
2, be cured on streamline with the speed of 10 ms/min, hardening time is 6S;
4., roller coat one 20g/m
2uV-LED curing transparent putty, the wavelength of UV-LED light source is 405-435nm, and energy is 80mj/cm
2, be cured on streamline with the speed of 12 ms/min, hardening time is 5S;
5., roller coat one 15g/m
2uV-LED solidify roller coat priming paint, the wavelength of UV-LED light source is 380-390nm, and energy is 200mj/cm
2, be cured on streamline with the speed of 15 ms/min, hardening time is 5S;
6., roll off the production line and carry out offering tongue and groove, U-shaped or V-type chamfering can be offered in addition, with sand paper, paint film is polished.
7., roller coat one 15g/m
2uV-LED solidified wear resistance priming paint, the wavelength of UV-LED light source is 420-440nm, and energy is 150mj/cm
2, be cured on streamline with the speed of 15 ms/min, hardening time is 4S;
8., roller coat one 20g/m
2uV-LED solidify anticracking priming paint, the wavelength of UV-LED light source is 390-430nm, and energy is 120mj/cm
2, be cured on streamline with the speed of 14 ms/min, hardening time is 5S;
9., roller coat twice 12g/m
2uV-LED solidify sanding priming paint, the wavelength of UV-LED light source is 380-420nm, and energy is 500mj/cm
2, be cured on streamline with the speed of 8 ms/min, hardening time is 10S;
10., roller coat twice 5g/m
2uV-LED solidify scratch-resistant finish paint, the wavelength of UV-LED light source is 380-400nm, and energy is 1000mj/cm
2, be cured on streamline with the speed of 5 ms/min, hardening time is 10S;
In the use procedure of above-mentioned UV-LED light source, adopt water cooling, effectively can solve UV mercury lamp solidification process needs to utilize blower fan to cool and the noise problem of generation.
Above-mentioned UV-LED solidifies the production that coating process can be applicable to solid wooden compound floor.
Above-mentioned just preferred embodiment of the present invention, not does any pro forma restriction to the present invention.Although the present invention discloses as above with preferred embodiment, but and be not used to limit the present invention.Any those of ordinary skill in the art, when not departing from technical solution of the present invention scope, can utilize the technology contents of above-mentioned announcement to make many possible variations and modification to technical solution of the present invention, or being revised as the Equivalent embodiments of equivalent variations.Therefore, every content not departing from technical solution of the present invention, according to the technology of the present invention essence to any simple modification made for any of the above embodiments, equivalent variations and modification, all should drop in the scope of technical solution of the present invention protection.
Claims (10)
1. UV-LED solidifies a coating process, it is characterized in that: it comprises the following steps: step 1, adopts colouring agent to carry out painted to timber; Step 2, carries out application UV-LED to the timber after polishing coating material solidified; Step 3, carries out UV-LED solidification by UV-LED light source to being coated with the timber installed.
2. a kind of UV-LED according to claim 1 solidifies coating process, it is characterized in that: the colouring agent described in step 1 is any one or more than one the mixing in the painted adhesive agent of water-based, water soluble dyestuffs or aqueous color paste, coated on timber by any one mode in spraying, showering, roller coat, brushing, obliterating, dip-coating and painted and Seal treatment carried out to timber, and adopt far-infrared ray drying, infra-red drying, microwave drying or heated-air drying any one or more than one mode drying is carried out to the timber after painted.
3. a kind of UV-LED according to claim 1 solidifies coating process, it is characterized in that: the application UV-LED described in step 2 is coating material solidified, comprise that UV-LED solidifies adhesion primer, UV-LED solidification infiltration priming paint, UV-LED curing transfer glue, UV-LED solidify putty, UV-LED curing transparent priming, UV-LED solidifies at the bottom of sanding priming paint, UV-LED solidified wear resistance, UV-LED solidifies showering varnish, UV-LED solidifies solid color enamel, UV-LED solidify in finish paint any one or more than one, the number of channels of each coating be together or together more than.
4. a kind of UV-LED according to claim 1 solidifies coating process, it is characterized in that: the coating material solidified total coating weight of the UV-LED described in step 2 is 10-350g/ ㎡, and every one coating weight can be 5-150g/ ㎡.
5. a kind of UV-LED according to claim 1 solidifies coating process, it is characterized in that: the coating method of the application described in step 2 is any one in showering, spraying, roller coat, brushing, obliterating, dip-coating, and wherein roll coating model comprises just against roller coat, common single and double in the same way roller coat, radium-shine single or two roller coat.
6. a kind of UV-LED according to claim 1 solidifies coating process, it is characterized in that: what the UV-LED light source described in step 3 adopted is wavelength is 260-450nm, and energy is 50-1000mj/cm
2uV-LED light source, the UV-LED light source of preferred wavelength to be 360-420nm or wavelength be 260-360nm, 1-2 UV lamp of arranging in pairs or groups, UV lamp comprises UV mercury lamp, UV gallium lamp or UV iron lamp.
7. a kind of UV-LED according to claim 1 solidifies coating process, and it is characterized in that: the UV-LED solidification process described in step 3 is cured on streamline with the speed of 1-20 m/min, light application time is 1-20S.
8. a kind of UV-LED according to claim 1 solidifies coating process, it is characterized in that: described a kind of UV-LED solidifies coating process, except being applicable to the subsides wood finishing of inorganic board, stone material, is particularly useful for the subsides wood finishing of heat-sensitive substrate material.
9. a kind of UV-LED according to claim 8 solidifies coating process, it is characterized in that: described heat-sensitive substrate material comprises plastic basis material, solid wood base material, lumber core, particieboard, moist-proof board, glued board, core-board medium density fibre board (MDF) or other hardboards.
10. a kind of UV-LED according to claim 1 solidifies coating process, it is characterized in that: described UV-LED solidifies coating process application, involved field comprise decorative board for wall, the large plate of wood furniture, MDF decorate large plate " namely medium density fiber decorates large plate ", solid wood composite decorating board, melamine sticky paperboard, solid wooden compound floor, wood-plastic composite floor and other paste the heat-sensitive substrate material floor of wooden skin or the production of decorative panel.