CN108727620A - A kind of degradable plant mould plate material - Google Patents
A kind of degradable plant mould plate material Download PDFInfo
- Publication number
- CN108727620A CN108727620A CN201810665072.6A CN201810665072A CN108727620A CN 108727620 A CN108727620 A CN 108727620A CN 201810665072 A CN201810665072 A CN 201810665072A CN 108727620 A CN108727620 A CN 108727620A
- Authority
- CN
- China
- Prior art keywords
- parts
- steps
- plate material
- mould plate
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of degradable plant mould plate material, including plate body and face coat, the plate body each component substance and its mass fraction are：50~60 parts of Plant Powder, 20~30 parts of polyethylene, 4~6 parts of haloflex, 3~5 parts of stabilizer, 4~6 parts of lubrication prescription, 3~5 parts of titanium dioxide.Advantageous effect is：1, raw material convenient material drawing of the present invention, it is at low cost, it is easy to promote, the product made is lighter, environmental protection, degradable；2, modeling timber intensity of the invention is high, can recycle, can reuse；3, the advantages of present invention has moisture-proof, waterproof, light, convenient transportation, can be practical in packing case, fruit case, express box, household freezer etc. extensively.
Description
Technical field
The present invention relates to finishing material fields, more particularly to a kind of degradable plant mould plate material.
Background technology
Mould plate material is exactly the combination of timber and plastics, it combines the two-fold advantage of timber and plastics, both maintains paper
The compatibility of mould plate feels, and with good moisture-proof water-fast, and acid and alkali-resistance, restraining epiphyte is antistatic, the performances such as Anti-moth-eating, application
There is apparent advantage when bottom plate, decorative board material.Paper plate develops the waterproof and dampproof high-environmental of new direction, modeling wood at building materials industry
Plank combines the plurality of advantages of plant fiber and plastics high molecular material, can largely substitute timber, and it is gloomy China can be effectively relieved
Woods natural resources shortage, wood supply contradiction in short supply are a kind of low-carbons of great development prospect, green, are recycled renewable ecology
Plastic-wood material.
And as China is to the pay attention to day by day of environmental protection cause, the phenomenon that rural area crop straw burning, receives more the destruction of environment
Carry out more concerns, how to recycle stalk again, avoids generating economic benefit while environmental pollution, become one
A new issue, and the stalk generated in agricultural production is combined with modeling wood-based panel industry, not only reach stalk recycling
Purpose, produce economic benefit, while degradable function can also be provided for mould plate material, make mould plate material also have environmental protection
Property, it avoids discarded mould plate material from polluting environment, has achieved the purpose that kill two birds with one stone.
Invention content
The purpose of the present invention is that solve the above-mentioned problems and provides a kind of degradable plant mould plate material.
The present invention is achieved through the following technical solutions above-mentioned purpose：
A kind of degradable plant mould plate material, including plate body and face coat, the plate body each component substance and its quality point
Number is：50~60 parts of Plant Powder, 20~30 parts of polyethylene, 4~6 parts of haloflex, 3~5 parts of stabilizer, 4~6 parts of lubrication prescription,
3~5 parts of titanium dioxide.
The present invention is prepared by following steps：
A, drying：Plant Powder, polyethylene, haloflex, polyacrylate, stabilizer, lubrication prescription, titanium dioxide are sent into
It is adequately mixed in V-Mixer, and mixed material is sent into drying cylinder is dried after blending；
B, preplasticizing：Mixture after will be dry in a steps carries out heating stirring；It will mixing after heating stirring
Object carries out cooling and stirring, and the mixture of stirring is cooled to suitable temperature；
C, it stands：The mixture that the b step obtains is placed in ventilation to place；
D, extrusion forming：The mixture obtained in the step c is sent into screw extruder, it will by screw extruder
The mixture obtained in the step c is squeezed out, and is molded in a mold, semi-finished product are obtained；
E, it shapes：The semi-finished product obtained in the Step d are imported in stock mould, are allowed to cool to 35~45 DEG C, then
It places it in again in sink and is cooled further to 25~30 DEG C, the semi-finished product shaped；
F, it cuts：The semi-finished product for the sizing that the step e obtains are cut into preset length by cutting machine；
G, it is surface-treated：Semi-finished product after being cut in the f steps are polished, the burr generated after removal cutting；
H, it sprays：The face coat is fixed on to have been removed burr half obtained in the g steps by spraying
In finished product.
Further, in a steps, stalk wheat husk class may be used in Plant Powder, as rice straw, husk, straw, bamboo pole,
The stalk of the various crops such as sugarcane bar, maize straw, wheat straw can also use xylophyta, such as each trees, especially
Branch, dry, leaf, skin, root, stem for the xylophyta for being easy to materials.
Further, in a steps, the grain size of the Plant Powder of selection is 350~450 mesh.
Further, in the b step, whipping temp is 130~140 DEG C, and mixing time is 0.2~0.5 hour, mixing
The temperature of object is down to 25~30 DEG C.
Further, in the step c, it is 20~28 hours to stand ventilation time.
Further, in the step c, mixture water content is 2%~3% after standing ventilation.
Further, in the h steps, the spraying method used can be electrostatic spraying.
Further, in the h steps, the thickness of the face coat is in 0.2~0.4mm.
Compared with prior art, the beneficial effects of the present invention are：1, raw material convenient material drawing of the present invention, it is at low cost, it is easy
It promotes, the product made is lighter, environmental protection, degradable；2, modeling timber intensity of the invention is high, can recycle,
It can reuse；3, the present invention has moisture-proof, waterproof, light, the advantages of convenient transportation, can extensively it is practical packing case,
Fruit case, express box, household freezer etc..
Description of the drawings
Fig. 1 is a kind of front view of degradable plant mould plate material of the present invention.
The reference numerals are as follows：
1, plate body；2, face coat.
Specific implementation mode
Technical scheme of the present invention is purged below, is fully described by, it is clear that described embodiment is only this hair
Bright a part of the embodiment, instead of all the embodiments.Based on the embodiment of the present invention, those of ordinary skill in the art are not having
The every other embodiment obtained under the premise of creative work is made, shall fall within the protection scope of the present invention.
Embodiment one：
As shown in Figure 1, a kind of degradable plant mould plate material, including plate body 1 and face coat 2,1 each component object of the plate body
Matter and its mass fraction are：50 parts of Plant Powder, 20 parts of polyethylene, 4 parts of haloflex, 3 parts of stabilizer, 4 parts of lubrication prescription, titanium dioxide
3 parts of titanium.
The present invention is prepared by following steps：
A, drying：Plant Powder, polyethylene, haloflex, polyacrylate, stabilizer, lubrication prescription, titanium dioxide are sent into
It is adequately mixed in V-Mixer, and mixed material is sent into drying cylinder is dried after blending；
B, preplasticizing：Mixture after will be dry in a steps carries out heating stirring；It will mixing after heating stirring
Object carries out cooling and stirring, and the mixture of stirring is cooled to suitable temperature；
C, it stands：The mixture that the b step obtains is placed in ventilation to place；
D, extrusion forming：The mixture obtained in the step c is sent into screw extruder, it will by screw extruder
The mixture obtained in the step c is squeezed out, and is molded in a mold, semi-finished product are obtained；
E, it shapes：The semi-finished product obtained in the Step d are imported in stock mould, are allowed to cool to 35~45 DEG C, then
It places it in again in sink and is cooled further to 25~30 DEG C, the semi-finished product shaped；
F, it cuts：The semi-finished product for the sizing that the step e obtains are cut into preset length by cutting machine；
G, it is surface-treated：Semi-finished product after being cut in the f steps are polished, the burr generated after removal cutting；
H, it sprays：The face coat 2 is fixed on to have been removed burr half obtained in the g steps by spraying
In finished product.
In the present embodiment, in a steps, stalk wheat husk class may be used in Plant Powder, such as rice straw, husk, straw, bamboo
The stalk of the various crops such as pole, sugarcane bar, maize straw, wheat straw can also use xylophyta, such as each trees,
Branch, dry, leaf, skin, root, stem particular for the xylophyta for being easy to materials.
In the present embodiment, in a steps, the grain size of the Plant Powder of selection is 350~450 mesh.
In the present embodiment, in the b step, whipping temp is 130 DEG C, and mixing time is 0.2 hour, the temperature of mixture
It is down to 25~30 DEG C.
In the present embodiment, in the step c, it is 20 hours to stand ventilation time.
In the present embodiment, in the step c, mixture water content is 2%~3% after standing ventilation.
In the present embodiment, in the h steps, the spraying method used can be electrostatic spraying.
In the present embodiment, in the h steps, the thickness of the face coat 2 is in 0.2~0.4mm.
Embodiment two：
As shown in Figure 1, a kind of degradable plant mould plate material, including plate body 1 and face coat 2,1 each component object of the plate body
Matter and its mass fraction are：55 parts of Plant Powder, 25 parts of polyethylene, 5 parts of haloflex, 4 parts of stabilizer, 5 parts of lubrication prescription, titanium dioxide
4 parts of titanium.
The present invention is prepared by following steps：
A, drying：Plant Powder, polyethylene, haloflex, polyacrylate, stabilizer, lubrication prescription, titanium dioxide are sent into
It is adequately mixed in V-Mixer, and mixed material is sent into drying cylinder is dried after blending；
B, preplasticizing：Mixture after will be dry in a steps carries out heating stirring；It will mixing after heating stirring
Object carries out cooling and stirring, and the mixture of stirring is cooled to suitable temperature；
C, it stands：The mixture that the b step obtains is placed in ventilation to place；
D, extrusion forming：The mixture obtained in the step c is sent into screw extruder, it will by screw extruder
The mixture obtained in the step c is squeezed out, and is molded in a mold, semi-finished product are obtained；
E, it shapes：The semi-finished product obtained in the Step d are imported in stock mould, are allowed to cool to 35~45 DEG C, then
It places it in again in sink and is cooled further to 25~30 DEG C, the semi-finished product shaped；
F, it cuts：The semi-finished product for the sizing that the step e obtains are cut into preset length by cutting machine；
G, it is surface-treated：Semi-finished product after being cut in the f steps are polished, the burr generated after removal cutting；
H, it sprays：The face coat 2 is fixed on to have been removed burr half obtained in the g steps by spraying
In finished product.
In the present embodiment, in a steps, stalk wheat husk class may be used in Plant Powder, such as rice straw, husk, straw, bamboo
The stalk of the various crops such as pole, sugarcane bar, maize straw, wheat straw can also use xylophyta, such as each trees,
Branch, dry, leaf, skin, root, stem particular for the xylophyta for being easy to materials.
In the present embodiment, in a steps, the grain size of the Plant Powder of selection is 350~450 mesh.
In the present embodiment, in the b step, whipping temp is 135 DEG C, and mixing time is 0.4 hour, the temperature of mixture
It is down to 25~30 DEG C.
In the present embodiment, in the step c, it is 25 hours to stand ventilation time.
In the present embodiment, in the step c, mixture water content is 2%~3% after standing ventilation.
In the present embodiment, in the h steps, the spraying method used can be electrostatic spraying.
In the present embodiment, in the h steps, the thickness of the face coat 2 is in 0.2~0.4mm.
Embodiment three：
As shown in Figure 1, a kind of degradable plant mould plate material, including plate body 1 and face coat 2,1 each component object of the plate body
Matter and its mass fraction are：60 parts of Plant Powder, 30 parts of polyethylene, 6 parts of haloflex, 5 parts of stabilizer, 6 parts of lubrication prescription, titanium dioxide
5 parts of titanium.
The present invention is prepared by following steps：
A, drying：Plant Powder, polyethylene, haloflex, polyacrylate, stabilizer, lubrication prescription, titanium dioxide are sent into
It is adequately mixed in V-Mixer, and mixed material is sent into drying cylinder is dried after blending；
B, preplasticizing：Mixture after will be dry in a steps carries out heating stirring；It will mixing after heating stirring
Object carries out cooling and stirring, and the mixture of stirring is cooled to suitable temperature；
C, it stands：The mixture that the b step obtains is placed in ventilation to place；
D, extrusion forming：The mixture obtained in the step c is sent into screw extruder, it will by screw extruder
The mixture obtained in the step c is squeezed out, and is molded in a mold, semi-finished product are obtained；
E, it shapes：The semi-finished product obtained in the Step d are imported in stock mould, are allowed to cool to 35~45 DEG C, then
It places it in again in sink and is cooled further to 25~30 DEG C, the semi-finished product shaped；
F, it cuts：The semi-finished product for the sizing that the step e obtains are cut into preset length by cutting machine；
G, it is surface-treated：Semi-finished product after being cut in the f steps are polished, the burr generated after removal cutting；
H, it sprays：The face coat 2 is fixed on to have been removed burr half obtained in the g steps by spraying
In finished product.
In the present embodiment, in a steps, stalk wheat husk class may be used in Plant Powder, such as rice straw, husk, straw, bamboo
The stalk of the various crops such as pole, sugarcane bar, maize straw, wheat straw can also use xylophyta, such as each trees,
Branch, dry, leaf, skin, root, stem particular for the xylophyta for being easy to materials.
In the present embodiment, in a steps, the grain size of the Plant Powder of selection is 350~450 mesh.
In the present embodiment, in the b step, whipping temp is 140 DEG C, and mixing time is 0.5 hour, the temperature of mixture
It is down to 25~30 DEG C.
In the present embodiment, in the step c, it is 28 hours to stand ventilation time.
In the present embodiment, in the step c, mixture water content is 2%~3% after standing ventilation.
In the present embodiment, in the h steps, the spraying method used can be electrostatic spraying.
In the present embodiment, in the h steps, the thickness of the face coat 2 is in 0.2~0.4mm.
The basic principles, main features and advantages of the invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, and the above embodiments and description only describe the originals of the present invention
Reason, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes and improvements
It all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appending claims and equivalents circle
It is fixed.
Claims (8)
1. a kind of degradable plant mould plate material, it is characterised in that：A kind of degradable plant mould plate material, including plate body (1) and surface
Coating (2), plate body (1) each component substance and its mass fraction are：50~60 parts of Plant Powder, 20~30 parts of polyethylene, chlorine
Change 4~6 parts of polyethylene, 3~5 parts of stabilizer, 4~6 parts of lubrication prescription, 3~5 parts of titanium dioxide.
The present invention is prepared by following steps：
A, drying：Plant Powder, polyethylene, haloflex, polyacrylate, stabilizer, lubrication prescription, titanium dioxide are sent into V-type
It is adequately mixed in mixing machine, and mixed material is sent into drying cylinder is dried after blending；
B, preplasticizing：Mixture after will be dry in a steps carries out heating stirring；After heating stirring by mixture into
The mixture of stirring is cooled to suitable temperature by row cooling and stirring；
C, it stands：The mixture that the b step obtains is placed in ventilation to place；
D, extrusion forming：The mixture obtained in the step c is sent into screw extruder, it will be by institute by screw extruder
It states the mixture obtained in step c to squeeze out, and is molded in a mold, obtain semi-finished product；
E, it shapes：The semi-finished product obtained in the Step d are imported in stock mould, are allowed to cool to 35~45 DEG C, then again will
Its placement is cooled further to 25~30 DEG C in the sink, the semi-finished product shaped；
F, it cuts：The semi-finished product for the sizing that the step e obtains are cut into preset length by cutting machine；
G, it is surface-treated：Semi-finished product after being cut in the f steps are polished, the burr generated after removal cutting；
H, it sprays：The face coat (2) is fixed on by spraying obtained in the g steps have been removed the half of burr at
In product.
2. a kind of degradable plant mould plate material according to claim 1, it is characterised in that：In a steps, Plant Powder can
With use stalk wheat husk class, such as rice straw, husk, straw, bamboo pole, sugarcane bar, maize straw, the various crops of wheat straw straw
Stalk, can also use xylophyta, such as each trees, particular for the branch for the xylophyta for being easy to materials, dry, leaf, skin,
Root, stem.
3. a kind of degradable plant mould plate material according to claim 1, it is characterised in that：In a steps, the institute of selection
The grain size for the Plant Powder stated is 350~450 mesh.
4. a kind of degradable plant mould plate material according to claim 1, it is characterised in that：In the b step, whipping temp
It it is 130~140 DEG C, mixing time is 0.2~0.5 hour, and the temperature of mixture is down to 25~30 DEG C.
5. a kind of degradable plant mould plate material according to claim 1, it is characterised in that：In the step c, ventilation is stood
Time is 20~28 hours.
6. a kind of degradable plant mould plate material according to claim 1, it is characterised in that：In the step c, ventilation is stood
Mixture water content is 2%~3% afterwards.
7. a kind of degradable plant mould plate material according to claim 1, it is characterised in that：In the h steps, the spray of use
Painting mode can be electrostatic spraying.
8. a kind of degradable plant mould plate material according to claim 1, it is characterised in that：In the h steps, the surface
The thickness of coating (2) is in 0.2~0.4mm.