CN108716168A - Service plate manufacturing method - Google Patents

Service plate manufacturing method Download PDF

Info

Publication number
CN108716168A
CN108716168A CN201810757636.9A CN201810757636A CN108716168A CN 108716168 A CN108716168 A CN 108716168A CN 201810757636 A CN201810757636 A CN 201810757636A CN 108716168 A CN108716168 A CN 108716168A
Authority
CN
China
Prior art keywords
die
wet base
service plate
wet
dry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810757636.9A
Other languages
Chinese (zh)
Inventor
李学文
谢泰波
张海峰
叶建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Shaoneng Group Oasis Ecological Technology Co Ltd
Dongguan Runtitan Intelligent Polytron Technologies Inc Three
Original Assignee
Guangdong Shaoneng Group Oasis Ecological Technology Co Ltd
Dongguan Runtitan Intelligent Polytron Technologies Inc Three
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CN201810635783 priority Critical
Priority to CN2018106357839 priority
Application filed by Guangdong Shaoneng Group Oasis Ecological Technology Co Ltd, Dongguan Runtitan Intelligent Polytron Technologies Inc Three filed Critical Guangdong Shaoneng Group Oasis Ecological Technology Co Ltd
Publication of CN108716168A publication Critical patent/CN108716168A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of service plate manufacturing methods, including step to have:(1) slurries are molded wet base by wet blank forming machine structure;(2) wet base mechanism for picking declines and is resetted upwards after the wet base in the wet blank forming machine structure of vacsorb;(3) heating dry body lower die mechanism slides onto the underface of wet base mechanism for picking; wet base mechanism for picking declines to transfer to wet base at heating dry body lower die mechanism; after wet base transfers at heating dry body lower die mechanism, wet base mechanism for picking rises reset and heating dry body lower die mechanism retracts reset;(4) heating dry body upper die mechanism declines and is molded together with heating dry body lower die mechanism to compress and heat wet base, and wet base is made to form service plate first product, and heating dry body upper die mechanism rises reset after forming service plate first product;And (5) reclaimer robot captures service plate first product and is delivered at bead cutter, and trimming processing is carried out to service plate first product to process service plate by bead cutter.Slurries automatic moulding can be gone out service plate by the service plate manufacturing method of the present invention.

Description

Service plate manufacturing method
Technical field
The present invention relates to a kind of service plate manufacturing field more particularly to a kind of the slurries automatic moulding of plant fiber is gone out into service plate The service plate manufacturing method of first product.
Background technology
With the continuous development of economy and being constantly progressive for science and technology, extremely abundant substance is provided for people's lives The consumer goods, service plate are exactly one kind in many material consumption product.
It is well known that in service plate production process, it be unable to do without the wet base forming step of service plate, carries out wet base after molding It is dry to form dry body (referred to as service plate first product) the step of and by dry body trimming to form service plate the step of.Wherein, in service plate The forming process of first product causes the wet base for molding wet base to be molded since existing service plate former designs unreasonable Machine, the dry body molding machine for wet base to be dried and for being three mutually independent to the bead cutter of service plate first product trimming Machine is separately mounted to different places, so that disk is eaten, former be molded in wet base, is processed wet base with formation Dry body and continuity between service plate first product trimming are poor, therefore there are service plate Forming Quality difference and the defects of service plate shaping efficiency.
Therefore, it is necessary to provide the service plate manufacturing method that a kind of service plate Forming Quality is good and service plate shaping efficiency is high to overcome Above-mentioned defect.
Invention content
The purpose of the present invention is to provide the service plate manufacturing methods that a kind of service plate Forming Quality is good and service plate shaping efficiency is high.
To achieve the above object, the technical scheme is that:A kind of service plate manufacturing method is provided, including step has:(1) Slurries are molded wet base by wet blank forming machine structure;(2) be located at wet blank forming machine structure right over wet base mechanism for picking decline and it is true Suction takes the wet base in wet blank forming machine structure, and wet base mechanism for picking rises after the wet base of vacsorb to be resetted so that wet base and wet base Shaping mechanism is separated;(3) the heating dry body lower die mechanism of wet blank forming machine structure side slide onto wet base mechanism for picking just under Side, wet base mechanism for picking decline to transfer to wet base at heating dry body lower die mechanism, and heating dry body lower die is transferred in wet base After at mechanism, wet base mechanism for picking rises reset and heating dry body lower die mechanism retracts reset;(4) it is located at heating dry body lower die machine Heating dry body upper die mechanism right over structure declines and is molded together with heating dry body lower die mechanism to compress and heat wet base, makes For wet base dehydration and drying to form service plate first product, heating dry body upper die mechanism rises reset after forming service plate first product;And (5) take Material manipulator crawl service plate first product is simultaneously delivered at bead cutter, and trimming processing is carried out to service plate first product to process meal by bead cutter Disk.
Preferably, in step (4), heating dry body upper die mechanism is dry from heating by service plate first product while rising reset It is siphoned away at base lower die mechanism.
Preferably, reclaimer robot is taken away the service plate first product that dry body upper die mechanism is drawn is heated.
Preferably, during heating dry body upper die mechanism siphons away service plate first product, heating dry body upper die mechanism does vacuum suction Take and heat dry body lower die mechanism do blow match resultant motion.
Preferably, in step (3), wet base mechanism for picking blows and heats dry body lower die mechanism vacsorb and match Resultant motion, to make the wet base of wet base mechanism for picking transfer at heating dry body lower die mechanism.
Preferably, while executing step (4), slurries are also molded wet base by wet blank forming machine structure.
Preferably, while executing step (4), slurries are also molded wet base and wet base pickup machine by wet blank forming machine structure Structure also siphons away the wet base vacuum at wet blank forming machine structure.
Preferably, in step (1), slurries form wet base by the filter deposition in wet blank forming machine structure.
Preferably, in step (4), heating dry body upper die mechanism is to heat company of the liquid in heating dry body upper die mechanism Continue cycle and wet base is thermally dried.
Preferably, in step (4), heating dry body upper die mechanism is to heat company of the liquid in heating dry body lower die mechanism Continue cycle and wet base is thermally dried.
Compared with prior art, by step (1) to (5) so that the wet base that wet blank forming machine structure molds is picked up by wet base It takes mechanism to pick up away, then the wet base picked up away is transferred to the heating dry body immediately below wet base mechanism for picking by wet base mechanism for picking At lower die mechanism, and the heating dry body lower die mechanism equipped with wet base retracts the underface for being reset to heating dry body upper die mechanism again, Then by heating dry body upper die mechanism with heating dry body lower die mechanism together with mold, to while compressing wet base to wet base into Row heat drying is with the purpose of service plate first product;Finally, take and be delivered to service plate first product away bead cutter by reclaimer robot, by Bead cutter carries out trimming processing to form service plate to service plate first product.I other words service plate manufacturing method of the invention is picked up by wet base It takes mechanism and heats the cooperation of dry body lower die mechanism to realize that wet base is consistently transferred to heating dry body lower die mechanism with reality Existing wet base is transformed into the purpose of service plate first product, and service plate first product is transferred to bead cutter progress trimming by reclaimer robot and is added Work is to form service plate, thus the Forming Quality that improves service plate is good and the shaping efficiency of service plate is high.
Description of the drawings
Fig. 1 is the planar structure schematic diagram for the service plate molding machine for implementing the service plate manufacturing method of the present invention.
Fig. 2 is the flow chart of the service plate manufacturing method of the present invention.
Specific implementation mode
The embodiment of the present invention described referring now to the drawings, similar element numbers represent similar element in attached drawing.
As shown in Figure 1, implement the present invention service plate manufacturing method service plate molding machine 100 include wet blank forming machine structure 10, Wet base mechanism for picking 20, rack 30, heating dry body upper die mechanism 40, heating dry body lower die mechanism 50, the first driver, second drive Dynamic device, third driver, reclaimer robot 91 and bead cutter 92.Bead cutter 92 along rack 30 length direction and rack 30 side by side Arrangement, is preferably that bead cutter 92 is located at the right side of rack 30, and but not limited to this.Wet blank forming machine structure 10 is mounted on machine On frame 30, wet base mechanism for picking 20 is also located at the surface of wet blank forming machine structure 10.First driver is installed in rack 30 simultaneously For driving wet base mechanism for picking 20 to rise or fall.Heating dry body lower die mechanism 50 is slidedly arranged on along the length direction of rack 30 In rack 30.Second driver is installed on rack 30, and the second driver is for driving heating dry body lower die mechanism 50 to slide to or slide From the position between wet blank forming machine structure 10 and wet base mechanism for picking 20 so that be in the heating dry body lower die mechanism 50 of the position Positioned at the surface of wet base mechanism for picking 20, it is also located at the surface of wet blank forming machine structure 10.Heat 40 edge of dry body upper die mechanism The short transverse of rack 30 is slidedly arranged on rack 30 and positioned at the surface of heating dry body lower die mechanism 50.Third driver is installed on Rack 30 is simultaneously used to drive heating dry body upper die mechanism 40 to rise or fall.Reclaimer robot 91 is installed in rack 30 and carries The dry body for heating dry body upper die mechanism 40 or heating at dry body lower die mechanism 50 is transferred at bead cutter 92, it is right by bead cutter 92 Dry body carries out trimming processing to form service plate;Preferably it is that there is the length direction along rack 30 to arrange at the top of rack 30 Longitudinal rail 32, longitudinal rail 32 extend at bead cutter 92, and reclaimer robot 91 is slidedly arranged on longitudinal rail 32, are more conducive to take Material manipulator 91 dry body is transferred at bead cutter 92, and first to third driver be oil cylinder, certainly according to actual needs and It is selected as cylinder or other hydraulic cylinders, therefore is not limited.
In conjunction with Fig. 2, service plate manufacturing method of the invention includes the following steps:
Slurries are molded wet base by S001, wet blank forming machine structure 10, and specifically, in step S001, slurries pass through wet Filter deposition in blank forming machine structure 10 and form wet base, but not limited to this.
S002, the wet base mechanism for picking 20 right over wet blank forming machine structure 10 declines and the wet blank forming machine of vacsorb Wet base in structure 10, wet base mechanism for picking 20 rise reset so that wet base and wet 10 phase of blank forming machine structure after the wet base of vacsorb Separation;It will be appreciated that wet base mechanism for picking 20, which rises and declines, to be realized by the first driver 60.
S003, wet 10 side of blank forming machine structure heating dry body lower die mechanism 50 slide onto wet base mechanism for picking 20 just under Side, wet base mechanism for picking 20 decline to transfer to wet base at heating dry body lower die mechanism 50, and heating dry body is transferred in wet base After at lower die mechanism 50, wet base mechanism for picking 20 rises reset and heating dry body lower die mechanism 50 retracts reset;Specifically, in step In rapid S003, wet base mechanism for picking 20 blows and heats the resultant motion of matching that dry body lower die mechanism 50 does vacsorb, to make The wet base of wet base mechanism for picking 20 transfers at heating dry body lower die mechanism 50, further increases wet base and transfers under heating dry body Reliability at mold mechanism 50, but not limited to this;It will be appreciated that the sliding of heating dry body lower die mechanism 50 is by the second driving Device 70 is realized.
S004, the heating dry body upper die mechanism 40 right over heating dry body lower die mechanism 50 decline and with heating dry body Lower die mechanism 50 is molded together to compress and heat wet base, is made wet base dehydration and drying to form service plate first product, is heated dry body upper mold Mechanism 40 rises reset after forming service plate first product;Specifically, in step S004, heating dry body upper die mechanism 40 is rising again Position while by service plate first product from heating dry body lower die mechanism 50 from siphon away, in order to by service plate first product from heating dry body lower die machine It is siphoned away at structure 50;Preferably it is, during heating dry body upper die mechanism 40 siphons away service plate first product, heating dry body upper die mechanism 40 It does vacsorb and heats dry body lower die mechanism 50 and do the resultant motion of matching blown, so that service plate first product is more reliably adsorbed in It heats at dry body upper die mechanism 40;More specifically, in step S004, heating dry body upper die mechanism 40 is to heat liquid (deep fat) Wet base is thermally dried in the continuous cycle heated in dry body upper die mechanism 40, heating dry body lower die mechanism 50 is with heating Liquid is thermally dried wet base in the continuous cycle heated in dry body lower die mechanism 50, to improve the efficiency of heating surface, but not It is limited to this;It will be appreciated that the rising and decline of heating dry body upper die mechanism 50 are realized by third driver 80.And
S005, reclaimer robot 91 capture service plate first product and are delivered at bead cutter 92, by bead cutter 92 to service plate first product Trimming processing is carried out to process service plate;Specifically, the service plate that reclaimer robot 91 is drawn heating dry body upper die mechanism 40 First product is taken away, in order to which service plate first product is taken away.
Wherein, while executing step S004, wet blank forming machine structure 10 can also continue to slurries molding wet base, together When, wet base mechanism for picking 20 also siphons away the wet base vacuum at wet blank forming machine structure 10, significantly shortens wet blank forming machine structure 10 and wet base mechanism for picking 20 heating dry body upper die mechanism 40 and heating dry body lower die mechanism 50 wet base is dried together To form the stand-by period of service plate first product, the shaping efficiency of service plate first product is further increased, but not limited to this.
Compared with prior art, by step S001 to S004 so that the wet base that wet blank forming machine structure 10 molds is wet Base mechanism for picking 200 is walked, then is transferred to the wet base picked up away immediately below wet base mechanism for picking 20 by wet base mechanism for picking 20 Heating dry body lower die mechanism 50 at, and equipped with wet base heating dry body lower die mechanism 50 retract again be reset to heating dry body upper mold The underface of mechanism 40 is finally molded by heating dry body upper die mechanism 40 and heating dry body lower die mechanism 50, together to press Wet base is thermally dried with the purpose of service plate first product while tight wet base;Finally, by reclaimer robot 91 by service plate first product It takes away and is delivered at bead cutter 92, trimming processing is carried out to form service plate to service plate first product by bead cutter 92.I other words this hair Bright service plate manufacturing method realizes that wet base connects by the cooperation of wet base mechanism for picking 20 and heating dry body lower die mechanism 50 It is transferred to heating dry body lower die mechanism 50 with passing through to realize that wet base is transformed into the purpose of service plate first product, and by reclaimer robot 91 By service plate first product transfer at bead cutter 92 carry out trimming processing to form service plate, thus the Forming Quality for improving service plate it is good with The shaping efficiency of service plate is high.
The person of being worth noting, in order to enable serum recycle, therefore the top of rack 30 is equipped with liquid storage container 94, liquid storage container 94, it is docked and connected by external pipe 95 between 113 three of stock inlet pipeline 12 and slurries wastewater outlet, i.e. liquid storage container 94 outlet is connected to by an external pipe 95 with stock inlet pipeline 12, and slurries wastewater outlet 113 passes through another external pipe again 95 are connected to the entrance of liquid storage container 94, and are equipped with circulating pump on external pipe 95, to realize the serum recycle between three Flowing, but not limited to this.
Upper disclosed is merely a preferred embodiment of the present invention, and cannot limit the right model of the present invention with this certainly It encloses, therefore according to equivalent variations made by scope of the present invention patent, is still within the scope of the present invention.

Claims (10)

1. a kind of service plate manufacturing method, which is characterized in that include the following steps:
(1) slurries are molded wet base by wet blank forming machine structure;
(2) it is located at wet in the decline of wet base mechanism for picking and the wet blank forming machine structure of vacsorb right over wet blank forming machine structure Base, wet base mechanism for picking rises after the wet base of vacsorb to be resetted so that wet base is separated with wet blank forming machine structure;
(3) the heating dry body lower die mechanism of wet blank forming machine structure side slides onto the underface of wet base mechanism for picking, wet base pickup Mechanism declines to transfer to wet base at heating dry body lower die mechanism, wet after wet base transfers at heating dry body lower die mechanism Base mechanism for picking rises reset and heating dry body lower die mechanism retracts reset;
(4) be located at heating dry body lower die mechanism right over heating dry body upper die mechanism decline and with heating dry body lower die mechanism one Molding is played to compress and heat wet base, makes wet base dehydration and drying to form service plate first product, heating dry body upper die mechanism is eaten in formation Rise after disk first product and resets;And
(5) reclaimer robot captures service plate first product and is delivered at bead cutter, and trimming processing is carried out to service plate first product by bead cutter To process service plate.
2. service plate manufacturing method according to claim 1, which is characterized in that in step (4), heat dry body upper die mechanism Service plate first product is siphoned away at heating dry body lower die mechanism while rising reset.
3. service plate manufacturing method according to claim 2, which is characterized in that reclaimer robot will heat dry body upper die mechanism The service plate first product drawn is taken away.
4. service plate manufacturing method according to claim 2, which is characterized in that at the beginning of heating dry body upper die mechanism siphons away service plate During product, heating dry body upper die mechanism do vacsorb and heat dry body lower die mechanism do blow match resultant motion.
5. service plate manufacturing method according to claim 1, which is characterized in that in step (3), wet base mechanism for picking, which is done, to be blown Gas and heat the resultant motion of matching that dry body lower die mechanism does vacsorb, it is dry to make the wet base of wet base mechanism for picking transfer to heating At base lower die mechanism.
6. service plate manufacturing method according to claim 1, which is characterized in that while executing step (4), wet base molding Slurries are also molded wet base by mechanism.
7. service plate manufacturing method according to claim 1, which is characterized in that while executing step (4), wet base molding Slurries are also molded wet base and wet base mechanism for picking and also siphon away the wet base vacuum at wet blank forming machine structure by mechanism.
8. service plate manufacturing method according to claim 1, which is characterized in that in step (1), slurries by wet base at Type filter deposition within the organization and form wet base.
9. service plate manufacturing method according to claim 1, which is characterized in that in step (4), heat dry body upper die mechanism Wet base is thermally dried in the continuous cycle heated in dry body upper die mechanism with heating liquid.
10. service plate manufacturing method according to claim 1, which is characterized in that in step (4), heat dry body lower die machine Structure is thermally dried wet base in the continuous cycle heated in dry body lower die mechanism with heating liquid.
CN201810757636.9A 2018-06-20 2018-07-11 Service plate manufacturing method Pending CN108716168A (en)