CN108716133A - It imitates the low solid content of nylon feel and applies silver color fourth cloth and its production technology - Google Patents
It imitates the low solid content of nylon feel and applies silver color fourth cloth and its production technology Download PDFInfo
- Publication number
- CN108716133A CN108716133A CN201810482327.5A CN201810482327A CN108716133A CN 108716133 A CN108716133 A CN 108716133A CN 201810482327 A CN201810482327 A CN 201810482327A CN 108716133 A CN108716133 A CN 108716133A
- Authority
- CN
- China
- Prior art keywords
- cloth
- fabric
- parts
- feel
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, includes the following steps:A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；B. the fabric after desizing is subjected to overflow dyeing processing；C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven, and control temperature at 200-210 DEG C；D. finishing agent is added in the fabric after pre-setting, sizing treatment in progress, wherein setting temperature are controlled at 186-192 DEG C；By weight percentage, the finishing agent includes waterproofing agent 2-4%, fabric moisture leavening agent 1-2% and feel leavening agent 1.3-1.7%；E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth.Shaping process in increasing after the presetting technology that the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology in the present invention, so that Se Dingbu yarns fully open the node of fiber interweaving under the action of feel leavening agent and hygroscopic agent, come flexibility and fluffy sense to webbing.
Description
Technical field
The present invention relates to textile production fields, and in particular to a kind of low solid content of imitative nylon feel apply silver color fourth cloth and its
Production technology.
Background technology
With the development of the stamp umbrella cloth market demand, demand of the client to product additional function is higher and higher, especially
Se Dingbu applies silver products and requires the stringent performance for increasing umbrella cloth by nylon feel, and applying silver reduction cloth cover using low solid content helps
The standards such as agent residual.240TH washs its fabric of Se Dingyin and uses the woven satin face class fabric of twill intertexture method, fabric fine in weaving
Dimension more slightly causes cloth cover entirety feel relatively stiffening, it is difficult to reach the soft feeling of customer demand.From the angle analysis for making umbrella, face
Expect that preferable feel flexility promotes umbrella folding effect, improves umbrella service life.
The existing patent document application No. is CN201010600939.3 discloses《A kind of color fourth imitates the printer of number
Skill》, which includes：Make plain net halftone, modulation sizing liquor, 4）Stamp is evaporated, is washed and setting process；The work
The obtained product feel of skill is harder, and fold resistant, does not cause service life relatively low.
Invention content
（One）Technical problems to be solved
The object of the present invention is to provide a kind of low solid contents of imitative nylon feel to apply silver color fourth cloth and its production technology, solves existing
Se Dingbu printing technologies the harder defect of product feel is made.
（Two）Technical solution
In order to solve the above technical problem, the present invention provides a kind of low solid content of imitative nylon feel apply silver color fourth cloth and its production
Technique, it includes base cloth layer, the primer coating positioned at base fabric layer surface that the low solid content of the imitative nylon feel, which applies silver color fourth cloth,；It is given birth to
Production. art includes the following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven, and control temperature
At 200-210 DEG C；
D. finishing agent, sizing treatment in progress are added in the fabric after pre-setting；
E. the gluing configured is coated on press polish treated fabric, obtains applying gel coating cloth；By weight, the gluing
Including：90-110 parts of cyanoacrylate adhesives, 25-35 parts of SS-2050 epitheliums glue, 2-4 parts of smooth, soft agent, 8-10 parts of hands
Feel leavening agent, 4-6 parts of bridging agents and 20-25 parts of toluene solvants.More preferably, cyanoacrylate adhesive uses 100% dosage
XF-3388 glue.
Increase after the presetting technology that the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology in the present invention
Add middle shaping process, and finishing agent is added in middle sizing so that Se Dingbu yarns are under the action of feel leavening agent and hygroscopic agent
The node for fully opening fiber interweaving, comes flexibility and fluffy sense to webbing.Coating of the present invention is viscous using cyanoacrylate
Mixture configuration enables its feel to reach best pliability and epithelium sense, and coating product feel is similar to the sense of touch of nylon facing material.
The present invention folds 100 comparisons after umbrella by making new product and conventional products, new product folding line slightly and
Without silver-colored light leakage phenomenon is fallen, conventional products folding line is serious and has degumming phenomenon（Glued membrane fastness is bad）.New product advantage protrudes.Product
Feel flexibility applies silver-colored feel close to nylon product feel, far superior to conventional color fourth.Color fastness Indexs measure：It is new by detecting
Product and conventional products comparison, new product dry and wet colorfastness to rubbing want 1-2 grades high.More preferably, gluing further includes 5-10 parts of second
Alcohol.The toluene solvant for taking away part in the present invention using ethyl alcohol, improves the organic efficiency of toluene solvant, reduces first in finished product
The residual of benzene solvent.
Preferably, in the predetermined process, control setting temperature is at 200-210 DEG C；Above and below the cloth feeding area of forming machine
Overfeeding is 1.1-1.2%.Pre-setting temperature is adjusted to 200-210 DEG C by the present invention by conventional 220 DEG C, and it is hard to fabric to reduce high temperature
The facilitation of change.Meanwhile overfeeding is adjusted to 1.2% up and down in cloth feeding area, mitigating over-stressed stretching causes fabric distortion existing
As.
Preferably, in the middle setting process, setting temperature is controlled at 186-192 DEG C；By weight percentage, the arrangement
Agent includes waterproofing agent 2-4%, fabric moisture leavening agent 1-2% and feel leavening agent 1.3-1.7%.More preferably, add in the finishing agent
Enter 1-2% antioxidants and the ethyl alcohol of 5-10%.Antioxidant, which is added, can increase high temperature resistant of the fabric in subsequent coating process
Oxidation resistant performance.The ethyl alcohol that 5-10% is added makes antioxidant, waterproofing agent, fabric moisture leavening agent and feel leavening agent more
It is disperse easily in water phase so that above-mentioned auxiliary agent is evenly dispersed in fabric, improves finishing effect, further improves fabric
Flexibility and fluffy sense, while the azeotropic effect of water and ethyl alcohol so that moisture quickly evaporates in type-approval process, improves
The efficiency of arrangement；Remaining ethyl alcohol is retained in coating process in middle setting process, is further taken away the toluene solvant of part, is carried
The high organic efficiency of toluene solvant, reduces the residual of toluene solvant in finished product.
Preferably, it is additionally provided with calendering operation after the coating procedure, the calendering operation is：Gel coating cloth will be applied to carry out
Calendering is handled, and wherein calendering is 95-125 DEG C of temperature, and pressure 80-120kg/cm, calendering speed control is in 10-25m/ min.
Preferably, the calendering operation is divided into two stages, and first stage wherein calendering is to slowly warm up to for 95 DEG C by temperature
120 DEG C, pressure 80-110kg/cm, calendering speed control is in 16-25m/ min；Second stage, control calendering temperature are 120 ± 1
DEG C, 115 ± 2kg/cm of pressure2, calendering speed is 15-17m/ min.Calendering operation part two benches of the present invention carry out, wherein the
The medium temperature calendering of two-stage is handled, and thick and solid degree unavoidably is rolled thin so that the flexibility of feel increases.
Preferably, the slurry groove temperature that moves back is 98-100 DEG C；The speed of desizing vehicle is 50-70m/min, and padding machine pressure is
1.5-2.0kg/cm2。
Preferably, desizing mixed liquor is added in the desizing process, by weight, the desizing mixed liquor includes 45-50
Part desizing agent, 40-60 parts of liquid caustic soda, 1-2 parts of refining agents and 1-2 parts of hydrogen peroxide.
Preferably, the desizing agent is added at one time 15-20 parts in charging, and follow-up every myriametre is continuous to add 10 parts.
（Three）Advantageous effect
A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, has the following advantages：
1, increase after the presetting technology that the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology in the present invention
Middle shaping process, and finishing agent is added in middle sizing so that Se Dingbu yarns fill under the action of feel leavening agent and hygroscopic agent
Divide the node for opening fiber interweaving, comes flexibility and fluffy sense to webbing.Coating of the present invention is bonded using cyanoacrylate
Agent configuration enables its feel to reach best pliability and epithelium sense, and coating product feel is similar to the sense of touch of nylon facing material.
The present invention folds 100 comparisons after umbrella by making new product and conventional products, new product folding line slightly and
Without silver-colored light leakage phenomenon is fallen, conventional products folding line is serious and has degumming phenomenon（Glued membrane fastness is bad）.New product advantage protrudes.Product
Feel flexibility applies silver-colored feel close to nylon product feel, far superior to conventional color fourth.Color fastness Indexs measure：It is new by detecting
Product and conventional products comparison, new product dry and wet colorfastness to rubbing want 1-2 grades high.
The coating of the present invention enables its feel to reach best pliability and skin using cyanoacrylate adhesive configuration
Film sense, coating product feel are similar to the sense of touch of nylon facing material.More preferably, gluing further includes 5-10 parts of ethyl alcohol.In the present invention
The toluene solvant that part is taken away using ethyl alcohol improves the organic efficiency of toluene solvant, reduces the residual of toluene solvant in finished product
It stays.
2, the property of fire-resistant oxidation resistant of the fabric in subsequent coating process can be increased by antioxidant being added in the present invention
Energy.The ethyl alcohol that 5-10% is added makes antioxidant, waterproofing agent, fabric moisture leavening agent and feel leavening agent be more easily dispersed in
Water phase so that above-mentioned auxiliary agent is evenly dispersed in fabric, improves finishing effect, further improve fabric flexibility and
Fluffy sense, while the azeotropic effect of water and ethyl alcohol so that moisture quickly evaporates in type-approval process, improves the effect of arrangement
Rate；Remaining ethyl alcohol is retained in coating process in middle setting process, is further taken away the toluene solvant of part, is improved toluene
The organic efficiency of solvent reduces the residual of toluene solvant in finished product.
3, calendering operation part two benches of the invention carry out, wherein the medium temperature calendering processing of second stage, by thickness unavoidably
Solidity is rolled thin so that the flexibility of feel increases.
4, pre-setting temperature is adjusted to 200-210 DEG C by the present invention by conventional 220 DEG C, reduces the rush that high temperature hardens fabric
Into effect.Meanwhile overfeeding is adjusted to 1.2% up and down in cloth feeding area, mitigating over-stressed stretching leads to fabric distortion phenomenon.
Description of the drawings
Fig. 1 is that the low solid content of imitative nylon feel of the present invention applies the process flow diagram of silver color fourth cloth production technology.
Specific implementation mode
With reference to the accompanying drawings and examples, the specific implementation mode of the present invention is described in further detail.Following instance
For illustrating the present invention, but it is not limited to the scope of the present invention.
Antioxidant in the present invention uses the antioxygen of Guangzhou Jin Yue textile auxiliaries Co., Ltd JINCOLOR T01
Change auxiliary agent.Cyanoacrylate adhesive uses the Ailete3388 glue of Ai Lete companies in the present invention.Waterproof in the present invention
Agent uses methyl type silicone oil.Fabric moisture leavening agent takes the multi-functional leavening agent of Nanjing Chinese olive Chemical Co., Ltd..Feel is fluffy
Loose agent uses the TF-432 leavening agents of Haicheng City Ze Hang trade Co., Ltds sale.Refining agent uses Dongguan Foster textile finishing
The product of agent Co., Ltd.Bridging agent uses the product of Quzhou Shun Tai rubber and plastics Science and Technology Ltd..Desizing agent uses Jiaxing Hua Sheng
The product of Auxiliaries Industry Co., Ltd.Smooth, soft agent uses the product of Hangzhou Hua Xin Trade Co., Ltd.s.
Embodiment 1：A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, described
It includes base cloth layer, the primer coating positioned at base fabric layer surface to imitate the low solid content of nylon feel and apply silver color fourth cloth；Its production technology packet
Include following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；The slurry groove temperature that moves back is 98-100 DEG C；The speed of desizing vehicle is
50m/min, padding machine pressure are 1. kg/cm2.Desizing mixed liquor is added in the desizing process, by weight, the desizing is mixed
It includes 45 parts of desizing agents, 40 parts of liquid caustic soda, 1 part of refining agent and 1 part of hydrogen peroxide to close liquid；The desizing agent disposably adds in charging
Enter 15 parts, follow-up every myriametre is continuous to add 10 parts.
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven；Wherein, it controls
Setting temperature processed is at 200 DEG C；The overfeeding up and down in the cloth feeding area of forming machine is 1.1%.
D. finishing agent is added in the fabric after pre-setting, sizing treatment in progress, wherein setting temperature are controlled 186
℃；By weight percentage, the finishing agent includes waterproofing agent 2%, fabric moisture leavening agent 1% and feel leavening agent 1.3%；
E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth.Add in the coating procedure
The gluing entered, by weight, including：90 parts of cyanoacrylate adhesives, 25 parts of SS-2050 epitheliums glue, 2 parts of smooth, softs
Agent, 8 parts of feel leavening agents, 4 parts of bridging agents and 20 parts of toluene solvant
F. gel coating cloth will be applied and carry out calendering processing, wherein calendering is 95 DEG C of temperature, and pressure 80kg/cm, calendering speed control exists
10m/ min.Wherein, calendering operation is divided into two stages, and first stage wherein calendering is to slowly warm up to 120 for 95 DEG C by temperature
DEG C, pressure 80kg/cm, calendering speed control is in 16m/ min；Second stage, control calendering temperature are 120 ± 1 DEG C, pressure 115
± 2kg/cm, calendering speed are 15m/ min.
Embodiment 2：A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, including
Following steps:
A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, the imitative nylon feel are low
It includes base cloth layer, the primer coating positioned at base fabric layer surface that solid content, which applies silver color fourth cloth,；Its production technology includes the following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；The slurry groove temperature that moves back is 100 DEG C；The speed of desizing vehicle is 70m/
Min, padding machine pressure are 2.0kg/cm2.Desizing mixed liquor, by weight, the desizing mixed liquor are added in the desizing process
Including 50 parts of desizing agents, 60 parts of liquid caustic soda, 2 parts of refining agents and 2 parts of hydrogen peroxide；The desizing agent is added at one time 20 in charging
Part, follow-up every myriametre is continuous to add 10 parts.
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven；Wherein, it controls
Setting temperature processed is at 210 DEG C；The overfeeding up and down in the cloth feeding area of forming machine is 1.2%.
D. finishing agent is added in the fabric after pre-setting, sizing treatment in progress, wherein setting temperature are controlled 192
℃；By weight percentage, the finishing agent includes waterproofing agent 4%, fabric moisture leavening agent 2% and feel leavening agent 1.7%；
E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth.Add in the coating procedure
The gluing entered, by weight, including：110 parts of cyanoacrylate adhesives, 35 parts of SS-2050 epitheliums glue, 4 parts of smooth, softs
Agent, 10 parts of feel leavening agents, 6 parts of bridging agents and 25 parts of toluene solvants.
F. gel coating cloth will be applied and carry out calendering processing, wherein calendering is 125 DEG C of temperature, pressure 120kg/cm, calendering speed
Control is in 25m/ min.Wherein, calendering operation is divided into two stages, first stage wherein calendering, by 95 DEG C of slowly heatings of temperature
To 120 DEG C, pressure 110kg/cm, calendering speed control is in 25m/ min；Second stage, control calendering temperature are 120 ± 1 DEG C,
115 ± 2kg/cm of pressure, calendering speed are 17m/ min.
Embodiment 3：A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, described
It includes base cloth layer, the primer coating positioned at base fabric layer surface to imitate the low solid content of nylon feel and apply silver color fourth cloth；Its production technology packet
Include following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；The slurry groove temperature that moves back is 99 DEG C；The speed of desizing vehicle is 60m/
Min, padding machine pressure are 1.75kg/cm2.Desizing mixed liquor, by weight, the desizing mixed liquor are added in the desizing process
Including 47.5 parts of desizing agents, 50 parts of liquid caustic soda, 1.5 parts of refining agents and 1.5 parts of hydrogen peroxide.The desizing agent is disposable in charging
17.5 parts are added, follow-up every myriametre is continuous to add 10 parts.
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven, it is described pre-
Shaping process, control setting temperature is at 205 DEG C；The overfeeding up and down in the cloth feeding area of forming machine is 1.15%.
D. finishing agent is added in the fabric after pre-setting, sizing treatment in progress, wherein setting temperature are controlled 189
℃；By weight percentage, the finishing agent include waterproofing agent 2-4%, fabric moisture leavening agent 1.5%, feel leavening agent 1.5%,
1.5% antioxidant and 7.5% ethyl alcohol；
E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth.Add in the coating procedure
The gluing entered, by weight, including：100 parts of XF-3388 glue, 30 parts of SS-2050 epitheliums glue, 3 parts of smooth, soft agent, 9 parts of feels
Leavening agent, 5 parts of bridging agents, 22.5 parts of toluene solvants and 7.5 parts of ethyl alcohol.
F. gel coating cloth will be applied and carry out calendering processing, wherein calendering is 110 DEG C of temperature, pressure 100kg/cm, calendering speed
Control is in 17.5m/ min.The calendering operation is divided into two stages, first stage wherein calendering, by 95 DEG C of slowly heatings of temperature
To 120 DEG C, pressure 95kg/cm, calendering speed control is in 20m/ min；Second stage, control calendering temperature are 119 DEG C, pressure
113kg/cm, calendering speed are 16m/ min.
Embodiment 4：A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, described
It includes base cloth layer, the primer coating positioned at base fabric layer surface to imitate the low solid content of nylon feel and apply silver color fourth cloth；Its production technology packet
Include following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；The slurry groove temperature that moves back is 99 DEG C；The speed of desizing vehicle is 60m/
Min, padding machine pressure are 1.75kg/cm2.Desizing mixed liquor, by weight, the desizing mixed liquor are added in the desizing process
Including 47.5 parts of desizing agents, 50 parts of liquid caustic soda, 1.5 parts of refining agents and 1.5 parts of hydrogen peroxide.The desizing agent is disposable in charging
17.5 parts are added, follow-up every myriametre is continuous to add 10 parts.
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven, it is described pre-
Shaping process, control setting temperature is at 205 DEG C；The overfeeding up and down in the cloth feeding area of forming machine is 1.15%.
D. finishing agent is added in the fabric after pre-setting, sizing treatment in progress, wherein setting temperature are controlled 189
℃；By weight percentage, the finishing agent include waterproofing agent 2-4%, fabric moisture leavening agent 1.5%, feel leavening agent 1.5%,
1.5% antioxidant and 7.5% ethyl alcohol；
E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth.Add in the coating procedure
The gluing entered, by weight, including：100 parts of XF-3388 glue, 30 parts of SS-2050 epitheliums glue, 3 parts of smooth, soft agent, 9 parts of feels
Leavening agent, 5 parts of bridging agents, 22.5 parts of toluene solvants and 7.5 parts of ethyl alcohol.
F. gel coating cloth will be applied and carry out calendering processing, wherein calendering is 110 DEG C of temperature, pressure 100kg/cm, calendering speed
Control is in 17.5m/ min.The calendering operation is divided into two stages, first stage wherein calendering, by 95 DEG C of slowly heatings of temperature
To 120 DEG C, pressure 95kg/cm, calendering speed control is in 20m/ min；Second stage, control calendering temperature are 121 DEG C, pressure
117kg/cm, calendering speed are 16m/ min.
Comparative example 1：A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, described
It includes base cloth layer, the primer coating positioned at base fabric layer surface to imitate the low solid content of nylon feel and apply silver color fourth cloth；Its production technology packet
Include following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；The slurry groove temperature that moves back is 98-100 DEG C；The speed of desizing vehicle is
40m/min, padding machine pressure are 1.4kg/cm2.Desizing mixed liquor is added in the desizing process, by weight, the desizing is mixed
It includes 44 parts of desizing agents, 61 parts of liquid caustic soda, 0.9 part of refining agent and 0.9 part of hydrogen peroxide to close liquid.The desizing agent is primary in charging
Property be added 14 parts, it is follow-up continuous per myriametre plus 9 parts.
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven, it is described pre-
Shaping process, control setting temperature is at 198 DEG C；The overfeeding up and down in the cloth feeding area of forming machine is 1.0%.
D. finishing agent is added in the fabric after pre-setting, sizing treatment in progress, wherein setting temperature are controlled 185
℃；By weight percentage, the finishing agent includes waterproofing agent 1%, fabric moisture leavening agent 0.9%, feel leavening agent 1.2%, 0.9%
Antioxidant and 4% ethyl alcohol；
E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth.Add in the coating procedure
The gluing entered, by weight, including：88 parts of cyanoacrylate adhesives, 24 parts of SS-2050 epitheliums glue, 1 part of smooth, soft
Agent, 7 parts of feel leavening agents, 3 parts of bridging agents, 18 parts of toluene solvants and 4 parts of ethyl alcohol.
F. gel coating cloth will be applied and carry out calendering processing, wherein calendering is 94 DEG C of temperature, pressure 78kg/cm, calendering speed control
System is in 9m/ min.The calendering operation is divided into two stages, and first stage wherein calendering is to slowly warm up to 120 for 95 DEG C by temperature
DEG C, pressure 78kg/cm, calendering speed control is in 15m/ min；Second stage, control calendering temperature are 118 DEG C, pressure 112kg/
Cm, calendering speed are 14m/ min.
Comparative example 2：A kind of low solid content of imitative nylon feel provided by the invention applies silver color fourth cloth and its production technology, described
It includes base cloth layer, the primer coating positioned at base fabric layer surface to imitate the low solid content of nylon feel and apply silver color fourth cloth；Its production technology packet
Include following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；The slurry groove temperature that moves back is 102 DEG C；The speed of desizing vehicle is 71m/
Min, padding machine pressure are 2.1kg/cm2.Desizing mixed liquor, by weight, the desizing mixed liquor are added in the desizing process
Including 51 parts of desizing agents, 38 parts of liquid caustic soda, 3 parts of refining agents and 3 parts of hydrogen peroxide.The desizing agent is added at one time 21 in charging
Part, follow-up every myriametre is continuous to add 11 parts.
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven, it is described pre-
Shaping process, control setting temperature is at 211 DEG C；The overfeeding up and down in the cloth feeding area of forming machine is 1.13%.
D. finishing agent is added in the fabric after pre-setting, sizing treatment in progress, wherein setting temperature are controlled 193
℃；By weight percentage, the finishing agent includes that waterproofing agent 5%, fabric moisture leavening agent 3%, feel leavening agent 2%, 3% are anti-oxidant
Agent and 11% ethyl alcohol；
E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth.Add in the coating procedure
The gluing entered, by weight, including：112 parts of cyanoacrylate adhesives, 37 parts of SS-2050 epitheliums glue, 5 parts of smooth, softs
Agent, 11 parts of feel leavening agents, 7 parts of bridging agents, 26 parts of toluene solvants and 11 parts of ethyl alcohol.
F. gel coating cloth will be applied and carry out calendering processing, wherein calendering is 126 DEG C of temperature, pressure 121kg/cm, calendering speed
Control is in 26m/ min.The calendering operation is divided into two stages, and first stage wherein calendering is to slowly warm up to for 95 DEG C by temperature
120 DEG C, pressure 112kg/cm, calendering speed control is in 26m/ min；Second stage, control calendering temperature are 122 DEG C, pressure
120kg/cm, calendering speed are 18m/ min.
Above-described embodiment 1, embodiment 2, embodiment 3, embodiment 4 and textile made from comparative example 1, comparative example 2（Umbrella cover
Cloth）Performance parameter be compared as follows：Wherein color fastness uses GB/T 5713-2013（Textile color stability tests resistance to water colour
Fastness）It is detected.It is the experimental data after folding 100 times that glued membrane fastness, which uses company standard, the glued membrane fastness data,.Weaving
The complete performance of product takes GB/T18318.4-2009《The measurement of textile bending property》It is detected；Wherein, bending stiffness
（B）Square is lagged with bending（HB）It is detected using bending property tester.Solvent detection limit takes paper《Textile is harmful
The study on determination method of volatile matter residual quantity and the amount of migration》（46-50 pages of weaving university's flow separation Zhen）In solvent detection method
It is operated.
| Product index project | Dry and wet colorfastness to rubbing | Flexility（Soft grade） | Glued membrane fastness after folding 100 times | Crease-flex test | Bending stiffness（B） | Bending lag square（HB） | Dissolvent residual detects |
| Embodiment 1 | 5.0 grade | 1 | 520gf | Folding line is slight and nothing falls silver-colored light leakage phenomenon | 0.151 | 0.278 | 1 sample exceeds detection limit |
| Embodiment 2 | 5.0 grade | 1 | 518gf | Folding line is slight and nothing falls silver-colored light leakage phenomenon | 0.167 | 0.289 | Without departing from detection limit |
| Embodiment 3 | 5.5 grade | 1 | 640gf | Folding line is slight and nothing falls silver-colored light leakage phenomenon | 0.148 | 0.252 | Without departing from detection limit |
| Embodiment 4 | 5.5 grade | 1 | 650gf | Folding line is slight and nothing falls silver-colored light leakage phenomenon | 0.137 | 0.241 | Without departing from detection limit |
| Comparative example 1 | 3.5 grade | 4 | 320gf | Folding line is serious and has degumming phenomenon | 0.536 | 0.624 | 10 samples exceed detection limit |
| Comparative example 2 | 3.5 grade | 3 | 330gf | Folding line is serious and has degumming phenomenon | 0.533 | 0.610 | 10 samples exceed detection limit |
| Market colouring fourth cloth | 3.5 grade | 4 | 380gf | Folding line is serious and has degumming phenomenon | 0.455 | 0.526 | 8 samples exceed detection limit |
In conclusion using the embodiment 1 of present invention process, embodiment 2, embodiment 3, embodiment 4 its product obtained it is dry
Wet friction color fastness, soft grade, fold 100 times after glued membrane fastness, crease-flex test, bending stiffness（B）Square is lagged with bending
（HB）It is better than comparative example 1, comparative example 2 and market colouring fourth cloth beyond processing range.Especially take optimize technique
Embodiment 3, embodiment 4, dry and wet colorfastness to rubbing is than 2 high 2 grades of embodiment 1, embodiment, soft grade, after folding 100 times
Glued membrane fastness, crease-flex test, bending stiffness（B）Square is lagged with bending（HB）Also it is superior to the experiment number of embodiment 1 and implementation 2
According to；Existing Se Dingbu folding resistances can worse, bending stiffness（B）Square is lagged with bending（HB）It is worse than the product of the present invention.
Present invention process be added ethyl alcohol after toluene solvant residue detection statistics indicate that, improve toluene volatility, reduce toluene
Detection limit.
The various embodiments described above are merely to illustrate the present invention, wherein the structure of each component, connection type etc. are all can be
Variation, every equivalents carried out based on the technical solution of the present invention and improvement should not be excluded the present invention's
Except protection domain.
Claims (8)
1. a kind of low solid content of imitative nylon feel applies silver color fourth cloth and its production technology, which is characterized in that the imitative nylon feel
It includes base cloth layer, the primer coating positioned at base fabric layer surface that low solid content, which applies silver color fourth cloth,；
Its production technology includes the following steps:
A. color fourth embryo cloth is entered into desizing machine and carries out boiling-off pre-treatment；
B. the fabric after desizing is subjected to overflow dyeing processing；
C. the fabric of dyeing is subjected to washing process, pre-setting processing then is carried out to the fabric in an oven；
D. finishing agent, sizing treatment in progress are added in the fabric after pre-setting；
E. the gluing configured is coated on press polish treated fabric；It obtains applying gel coating cloth；By weight, the gluing
Including：90-110 parts of cyanoacrylate adhesives, 25-35 parts of SS-2050 epitheliums glue, 2-4 parts of smooth, soft agent, 8-10 parts of hands
Feel leavening agent, 4-6 parts of bridging agents and 20-25 parts of toluene solvants.
2. the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology as described in claim 1, which is characterized in that institute
Predetermined process is stated, control setting temperature is at 200-210 DEG C；The overfeeding up and down in the cloth feeding area of forming machine is 1.1-1.2%.
3. the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology as described in claim 1, which is characterized in that institute
It states in setting process, setting temperature is controlled at 186-192 DEG C；By weight percentage, the finishing agent include waterproofing agent 2-4%,
Fabric moisture leavening agent 1-2% and feel leavening agent 1.3-1.7%.
4. the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology as described in claim 1, which is characterized in that institute
It states coating procedure and is additionally provided with calendering operation later, the calendering operation is：Gel coating cloth will be applied and carry out calendering processing, wherein calendering
For 95-125 DEG C of temperature, pressure 80-120kg/cm2, calendering speed control is in 10-25m/ min.
5. the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology as claimed in claim 4, which is characterized in that institute
It states calendering operation and is divided into two stages, first stage wherein calendering is to slowly warm up to 120 DEG C for 95 DEG C, pressure 80- by temperature
110kg/cm2, calendering speed control is in 16-25m/ min；Second stage, control calendering temperature are 120 ± 1 DEG C, pressure 115 ±
2kg/cm2, calendering speed is 15-17m/ min.
6. the low solid content of imitative nylon feel as described in claims 1 or 2 or 3 or 4 or 5 applies silver color fourth cloth and its production technology,
It is characterized in that, the slurry groove temperature that moves back is 98-100 DEG C；The speed of desizing vehicle is 50-70m/min, and padding machine pressure is 1.5-
2.0kg/cm2。
7. the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology as claimed in claim 6, which is characterized in that institute
Addition desizing mixed liquor in desizing process is stated, by weight, the desizing mixed liquor includes 45-50 parts of desizing agents, 40-60 parts of liquid
Alkali, 1-2 part refining agent and 1-2 parts of hydrogen peroxide.
8. the low solid content of imitative nylon feel applies silver color fourth cloth and its production technology as claimed in claim 7, which is characterized in that institute
It states desizing agent and is added at one time 15-20 parts in charging, follow-up every myriametre is continuous to add 10 parts.