CN107603442A - A kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating and its Waterborne synthetic leather bass of preparation - Google Patents
A kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating and its Waterborne synthetic leather bass of preparation Download PDFInfo
- Publication number
- CN107603442A CN107603442A CN201710810891.0A CN201710810891A CN107603442A CN 107603442 A CN107603442 A CN 107603442A CN 201710810891 A CN201710810891 A CN 201710810891A CN 107603442 A CN107603442 A CN 107603442A
- Authority
- CN
- China
- Prior art keywords
- synthetic leather
- aqueous polyurethane
- bamboo charcoal
- friendly type
- polyurethane coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to synthetic leather field, more particularly to a kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating and its Waterborne synthetic leather bass of preparation.The present invention is foamed using bamboo vinegar, the generation of acetic acid foaming microcellular structure structure is avoided, and tensile strength, Tear strength and wearability have all reached the level using the foaming of DMF wet methods, and manufactured finished product has soft handle, quality is fine and smooth, the advantages that good permeability.For whole production process without using DMF, solvent is water, has non-ignitable, safe and environment-friendly, cost-effective performance.Formaldehyde, DMF are not detected in obtained synthetic leather product, meet the requirement of ecological synthetic leather.
Description
Technical field
The present invention relates to synthetic leather field, more particularly to a kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating and
Its Waterborne synthetic leather bass prepared.
Background technology
The production method of wet polyurethane synthetic leather be will be added in polyurethane wet resin DMF solvent and other fillers,
Mixed liquor is made in auxiliary agent, after vacuum machine deaeration, dipping or coated in base fabric, being then placed in and solvent（DMF）With parent
And property, and with the incompatible water of polyurethane resin, solvent（DMF）Replaced by water, polyurethane resin gradually solidifies, so as to be formed
Porous epithelium, i.e. microvoid polyurethane grain layer, traditionally referred to as bass (English BASS transliteration), its connotation are base materials (half
Resultant Leather) the meaning, bass by dry method veneer or surface after ornamenting, such as surface printing, embossing, mill skin technique after,
Synthetic Leather finished product can be turned into.
Typical synthetic leather wet processing includes：To the N,N-dimethylformamide of oiliness polyurethane resin（DMF）Solution
Add middle adding assistant, slurry is made, by impregnating slurry or coated in base fabric, then by the 25% DMF aqueous solution wash admittedly
Change, then by hot wash, processing is then dried by baking oven, so as to form with loose structure, flexible and flesh
Product-bass of skin sense.Its principle is：Contain a large amount of DMF in oiliness Polyurethane resin slurry, DMF has extremely strong hydrophilic
Property, the DMF in slurry is replaced under hygrometric state by water, so that oiliness polyurethane resin precuring；Interior aqueous precuring
Bass forms with loose structure, flexible and skin sense bass product after drying.
At present, from the point of view of with regard to the development of synthetic leather technology, the major technology bottleneck of synthetic leather rapid industrial development is hindered
Problem has two：First, problem of environmental pollution caused by solvent-borne type production system, rough calculation, China's conventional synthesis leather industry
The demand to solvent type resin is more than 200 ten thousand tons every year, and this means that annual about 1,500,000 tons poisonous and harmful substances
Volatile emission is into air, so huge discharge amount of exhaust gas, seriously pollutes environment in the fabrication process and to execute-in-place
The health of personnel is threatened, and particularly synthetic leather factory surrounding area is produced and had a strong impact on.Second, due to using molten
The production system of formulation, synthesize the residual of residual, particularly solvent dimethylformamide (DMF) that solvent is had in leather goods
Can be exceeded, it is difficult to meet the requirement of ecological synthetic leather.
Under the overall situation of current national requirements energy-saving and emission-reduction, the substitute for developing solvent borne polyurethane has been general trend of events institute
Become.Aqueous polyurethane is using water as solvent, nontoxic non-hazardous, does not produce waste water, waste gas, free from environmental pollution, is the poly- ammonia of solvent-borne type
The preferable alternative materials of ester, it is the needs for realizing the production of artificial leather industry environmental health metaplasia.
The Chinese invention patent of inventor herein Guan Ningzhang applications（Application number CN200610053939.X, the applying date
2006.10.24）Disclose kind of environment-friendly type use for synthetic leather urethane composition and synthetic leather prepared therefrom and the system of the synthetic leather
Preparation Method.Include following composition by weight percentage：Polyurethane resin 35%~60%, powdered carbon 10%~35%, solidification
Agent 0.8%~3%, NN- dimethylformamides 1%~10% and acetone 15%~35%.It can in addition contain add 1%~
12% function nano material.The patent replaces lignin with powdered carbon, can be absorbed in the stirring of dispensing stove harmful in dispensing
Material and gas, be advantageous to environmental protection and the health of worker.Meanwhile be combined together powdered carbon and synthetic leather, make the essence of charcoal
Function is fully played in synthetic leather.This method belongs to oiliness production technology, employs N, N- bis- in process of production
NMF（DMF）Solvent, it is unavoidable also to have brought micro DMF into synthetic leather（DMF）.
《University Of Nanchang》Master's thesis in 2011《Aqueous polyurethane acid bath cohesion film forming is probed into》Paper discloses use
Acetic acid frothed aqueous polyurethane emulsion prepares synthetic leather, but goes back document and also disclose that WPU acid baths demulsification method surface and section have
Many microcellular structures, wherein plus wood powder it is more rich relative to its microcellular structure that with the addition of wood powder, but no matter which
Kind, compared with solvent-borne type PU wet methods, microcellular structure also differs obvious, and therefore, WPU acid baths are demulsified method from theory into action
It is required for making further research.
The content of the invention
In order to solve above-mentioned technical problem, it is an object of the present invention to provide a kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather
Aqueous polyurethane coating.Second object of the present invention is to provide Waterborne synthetic leather shellfish prepared by above-mentioned aqueous polyurethane coating
This, the present invention is foamed using bamboo vinegar, is avoided acetic acid and is foamed the generation of microcellular structure structure, and tensile strength, tears
Split strength and wearability has all reached the level to be foamed using DMF wet methods, whole production process is without using DMF, obtained synthesis
Formaldehyde, DMF are not detected in leather product, meet the requirement of ecological synthetic leather.
In order to realize first above-mentioned purpose, present invention employs following technical scheme：
A kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating, aqueous polyurethane coating by mass percentage include with
Lower component：
Aqueous polyurethane emulsion 20 ~ 60%
Wood powder and/or wood pulp 5 ~ 15%
Bamboo charcoal 2.0 ~ 20%
Calcium carbonate 0 ~ 20%
Lubricant 1.0 ~ 5.0%
Organic silicone oil 1.0 ~ 5.0%
White oil 0.5 ~ 3.0%
Glycerine and/or ethylene glycol 1.0 ~ 5.0%
Processing aid 0.1 ~ 2.0%
Water 20 ~ 50%.
Preferably, aqueous polyurethane coating includes following components by mass percentage：
Aqueous polyurethane emulsion 30 ~ 50%
Wood powder and/or wood pulp 8 ~ 12%
Bamboo charcoal 2.0 ~ 10%
Calcium carbonate 0 ~ 20%
Lubricant 1.5 ~ 4.0%
Organic silicone oil 1.5 ~ 4.0%
White oil 0.8 ~ 2.0%
Glycerine and/or ethylene glycol 1.5 ~ 4.0%
Processing aid 0.5 ~ 1.5%
Water 25 ~ 45%.
As further preferably, above-mentioned bamboo charcoal powder is the bamboo charcoal powder of 600~2000 mesh.
Preferably, one or more mixing in described lubricant preferably talc powder, zinc oxide；Organic silicone oil is preferred
Aqueous emulsifying silicone oil.
Preferably, aqueous polyurethane coating also includes toner 0.01 ~ 1.0%.
Preferably, aqueous polyurethane coating also includes function nano material 1.0 ~ 5.0%；It is preferred that function nano material is
Nano titanium oxide, nano silicon, nano zine oxide and nano-aluminium oxide are a kind of or 2 kinds mix；As it is further preferred that
Above-mentioned function nano material is 2 kinds of mixing of nanometer anatase titania and nano silicon, dichloride in anatase type dioxy
Change titanium and account for the 0.4%~5% of gross weight, nano silicon accounts for the 0.8%~5% of gross weight.
Preferably, processing aid includes levelling agent, defoamer and thickener；It is preferred that levelling agent 0.1 ~ 0.5%, defoamer
0.01 ~ 0.1% and thickener 0.1 ~ 0.5%.
In order to realize second above-mentioned purpose, present invention employs following technical scheme：
A kind of environment-friendly type aqueous synthetic leather bass of bamboo Charcoal Adsorption, it is characterised in that the Waterborne synthetic leather bass is using above-mentioned any
It is made after aqueous polyurethane coating coating base fabric described in one technical scheme using bamboo vinegar foaming；Preferably, bamboo vinegar
PH be 1.0 ~ 4.5；PH as preferred bamboo vinegar is 1.8 ~ 3.5.
Preferably, the coating weight of aqueous polyurethane layer is 20 ~ 200g/m2；As further preferably, the painting of aqueous polyurethane layer
Cloth amount is 30 ~ 100g/m2。
To be preferred, water-based aliphaic polyurethane breast of the aqueous polyurethane from 30 ~ 50% solid contents in aqueous polyurethane coating
Liquid；Base fabric selects superfine fibre cloth.
Preferably, base fabric is soaked using bamboo vinegar before base fabric is coated, base fabric is impregnated with bamboo vinegar, then extract.
Present invention base fabric before blade coating is soaked using bamboo vinegar, base fabric is impregnated with bamboo vinegar, is easy to aqueous polyurethane coating starching.
The invention also discloses environment-friendly water-based polyurethane synthetic leather bass made from described method.
A kind of environment-friendly water-based polyurethane synthetic leather fabric, the fabric use described bass surface treated to be made.Table
Face processing includes but is not limited to transfer, embossing, oiling.
The lubricant that the present invention adds is used for the weight for increasing leather, feel.Organic silicone oil increase pliability, increase intensity
And toughness, increase leather surface scratch resistance degree.White oil increases the brightness of leather, prevents from bonding when embossing.Glycerine and/or second
Glycol can adjust the humidity of leather, increase the feel and pliability of leather.Function nano material of the present invention can adsorb
In the hole of charcoal, the absorption property of original charcoal is not only remained, and can be killed in the presence of light using function nano material
Dead bacterium, virus and by poisonous and harmful substance（Such as formaldehyde, benzene）It is decomposed into carbon dioxide and water.In addition, the present invention also designs
Strong light temperature control production line, produce synthetic leather when, solvent volatilization, the absorption of function nano material is forced in the hole of charcoal
Interior, the harmful substance in production process can be resolved into carbon dioxide and water by function nano material due to strong light action.
The present invention is foamed using bamboo vinegar as a result of above-mentioned technical scheme, avoids acetic acid foaming micropore
The generation of structure structure, and tensile strength, Tear strength and wearability have all reached the level using the foaming of DMF wet methods, system
Into finished product there is soft handle, quality is fine and smooth, the advantages that good permeability.For whole production process without using DMF, solvent is water, tool
There is non-ignitable, safe and environment-friendly, cost-effective performance.Formaldehyde, DMF are not detected in obtained synthetic leather product, meet that ecology is closed
The requirement of finished leather.Present invention process is workable, production efficiency is high, cost is low, it is environmentally friendly, can be achieved industrialized production.Separately
Outside, the natural component of bamboo vinegar can be brought into naturally in the product（Certainly, it is undesirable that the taste for having bamboo vinegar can also be through
Repeatedly washing is crossed to wash away bamboo vinegar）, bamboo vinegar contains nearly 300 kinds of natural polymer organic compounds, there is organic acid, alcohol
Class, ketone, aldehydes, esters and micro alkaline components etc..With anti-mildew, antibacterial, inoxidizability, methanol, formaldehyde can be removed
Etc. harmful substance, the effect of synthesis is reformed is assigned.
Brief description of the drawings
Fig. 1 is synthetic leather prepared by the water-soluble polyurethane leather beth of the embodiment of the present invention 1.
Fig. 2 is synthetic leather prepared by the water-soluble polyurethane leather beth of the embodiment of the present invention 2.
Fig. 3 is synthetic leather prepared by the water-soluble polyurethane leather beth of the embodiment of the present invention 3.
Embodiment
Embodiment 1
The formula of aqueous polyurethane coating is as follows：
| Aqueous polyurethane emulsion | 45.0% |
| Wood powder | 8.5% |
| Bamboo charcoal powder | 10.0% |
| Calcium carbonate | 15.5% |
| Talcum powder | 2.5% |
| Glycerine | 4.0% |
| Organic silicone oil | 0.5% |
| White oil | 1.5% |
| Nano titanium oxide | 2.5% |
| Levelling agent | 0.2% |
| Defoamer | 0.01% |
| Thickener | 0.2% |
| Toner | 0.1% |
| Water | Surplus |
A kind of production method of environment-friendly water-based polyurethane synthetic leather bass, this method comprise the following steps：
1）Base fabric is soaked using bamboo vinegar before blade coating, and bamboo vinegar pH is 3.5, base fabric is impregnated with bamboo vinegar, then extracts；
2）Base fabric carries out scratching above-mentioned aqueous polyurethane coating, solidifies to form aqueous polyurethane layer in scrim surfaces, extracts；
3）After extracting, foamed into bamboo vinegar, bamboo vinegar pH is 3.2, foamed time 2min, forms porous poly- ammonia
Ester coating, the coating weight of aqueous polyurethane layer is 40g/m2；
4）Washed after the completion of foaming, dry the waterborne polyurethane synthetic leather for being made described.
It is as shown in Figure 1 to adopt the water-soluble polyurethane leather beth being prepared with the aforedescribed process.
After testing, indices are as follows for the water-soluble polyurethane leather beth：
1st, color fastness is dry-cleaned（AS2001.4.16-1981)
Discoloration 3-4 as former state
Cotton staining 4
Nylon staining 4-5
Remarks：Gray card is rated one to Pyatyi, and 1 grade is worst, and 5 grades are best.
2nd, light shine color fastness（AS2001.4.B02-2001；Use atmosphere arc lamp）
6 grade 4 of illumination
Grading（Standard blue wool）.
3rd, tensile strength（Ref, AS2001.2.3.2-2001;InstronCRE-25mm grab methods）
Length direction（N) 1000
Width（N) 600.
4th, Tear strength（Ref.AS2001.2.8:2001)
Tear length direction（N）This direction is horizontal to tear
Tear cross direction（N) 39；
5th, wearability（AS2001.2.25-2:2006)
Terminal coating comes off at 15000 turns.
6th, hydrolysis and free formaldehyde
Method of testing：According to 150,4184-,:201 ,-textile-formaldehyde examination-Part I：Hydrolysis and free formaldehyde（Water extracts
Follow the example of）；Analyzed with UVNIS；
Formaldehyde remarks：Do not detect
lppm=1mg/kg
Detection limit=16mg/kg.
7th, the pH value of textile
Method of testing：According to 1503071:2005 (0.lmol/L potassium chloride）
As a result：PH value 7.5
Note:Extract pH value 5.5
14.0 DEG C of extract temperature；
8th, azo dyes
Method of testing：Textile：According to EN14362-1:2012- is analyzed using GC-MS/HPLC-DAD.
Remarks：Method detection is limited to 5mg/kg（Single aromatic amine）
Maximum limitation：30mg/kg（Single aromatic amine）；
9th, pentachlorophenol（PCP)
Method of testing：Analysis is carried out using the MS of GC mono-
Test event:Pentachlorophenol（PCP)
As a result:ND
Remarks：MDL（Detection limits）=0.05mg/kg
ND=is not detected（<MDL)
10th, N,N-dimethylformamide（DMF)
Method of testing：With reference to USEPA3550C:2007 and USEPA8270D:2014 methods determine, and are analyzed using the MS of GC mono-；
Test event CASNO.68-12-2
As a result：N,N-dimethylformamide（DMF) ND
Remarks：
MOL（Method test limit）:5mg/kg, NO=are not detected（<MDL).
Embodiment 2
The formula of aqueous polyurethane coating is as follows：
| Aqueous polyurethane emulsion | 40.5% |
| Wood pulp | 5.5% |
| Bamboo charcoal powder | 18.5% |
| Talcum powder | 2.5% |
| Glycerine | 2.5% |
| Organic silicone oil | 1.5% |
| White oil | 2.0% |
| Nano titanium oxide | 3.5% |
| Levelling agent | 0.2% |
| Defoamer | 0.02% |
| Thickener | 0.1% |
| Toner | 0.5% |
| Water | Surplus |
A kind of production method of environment-friendly water-based polyurethane synthetic leather bass, this method comprise the following steps：
1）Base fabric is soaked using bamboo vinegar before blade coating, and bamboo vinegar pH is 3.5, base fabric is impregnated with bamboo vinegar, then extracts；
2）Base fabric carries out scratching above-mentioned aqueous polyurethane coating, solidifies to form aqueous polyurethane layer in scrim surfaces, extracts；
3）After extracting, foamed into bamboo vinegar, bamboo vinegar pH is 3.2, foamed time 2min, forms porous poly- ammonia
Ester coating, the coating weight of aqueous polyurethane layer is 40g/m2；
4）Washed after the completion of foaming, dry the waterborne polyurethane synthetic leather for being made described.
Waterborne polyurethane synthetic leather prepared by the method for embodiment 2 waterborne polyurethane synthetic leather with embodiment 1 after testing
With it is identical the effect of, and also there is absorption ammonia, formaldehyde, benzene and the effect of toluene.
Detect foundation：《Public place method for determining formaldehyde in air》 GB/T18204.26- 2000、《Public place is empty
Ammonia assay method in gas》GB/T18204.25- 2000.
Testing conditions：1st, synthetic leather obtained above is cut into fragment；2nd, experimental temperature：31 ± 1 DEG C, relative humidity：66
± 2%；3rd, 2 volumes are 1M3Closed container, air pressure 1004.5hPa.
Method of testing：1st, the synthetic leather fragment for being adsorbed with ammonia and formaldehyde is tested and analyzed respectively every 2h（It is parallel
Experiment）, the ammonia of its absorption and the quality of formaldehyde are tested, untill the gross mass of charcoal no longer changes；2nd, in closed container ammonia and
The concentration of formaldehyde standard gas is respectively：1.25g/m3、1.2g/m3。
Testing result see the table below：
| Time | 1h | 3h | 5h | 7h |
| The adsorbance of ammonia（mg/g） | 25.15 | 55.78 | 83.35 | 82.83 |
| The adsorbance of formaldehyde（mg/g） | 21.34 | 42.23 | 75.23 | 71.46 |
Detect foundation：With reference to GB/T12496.5-1999《Wood activated charcoal test method-carbon tetrachloride adsorption rate（Activity）'s
Measure》Method determines, and replaces carbon tetrachloride to carry out adsorption test with benzene, toluene.
Testing conditions：1st, 150 × 3mm of synthetic leather strip sheet；2nd, experimental temperature：28 ± 1 DEG C, relative humidity：80 ± 2%；
3rd, gas flow：60±5ml/min；4th, adsorption time：30min.
Testing result：Absorption of the synthetic leather to benzene and toluene, is adsorbed by 30min, and it is the .25mg/g of benzene 75 to inhale a value,
Toluene 54.23mg/g.
Embodiment 3
The formula of aqueous polyurethane coating is as follows：
| Aqueous polyurethane emulsion | 50.5% |
| Wood powder | 5.0% |
| Ag+-SiO2 | 1.2% |
| Calcium carbonate | 10.2% |
| Bamboo charcoal powder | 8.6% |
| Talcum powder | 2.5% |
| Ethylene glycol | 2.5% |
| Organic silicone oil | 1.5% |
| White oil | 2.5% |
| Nano titanium oxide | 1.5% |
| Levelling agent | 0.1% |
| Defoamer | 0.02% |
| Thickener | 0.3% |
| Toner | 0.05% |
| Water | Surplus |
A kind of production method of environment-friendly water-based polyurethane synthetic leather bass, this method comprise the following steps：
1）Base fabric is soaked using bamboo vinegar before blade coating, and bamboo vinegar pH is 3.5, base fabric is impregnated with bamboo vinegar, then extracts；
2）Base fabric carries out scratching above-mentioned aqueous polyurethane coating, solidifies to form aqueous polyurethane layer in scrim surfaces, extracts；
3）After extracting, foamed into bamboo vinegar, bamboo vinegar pH is 3.2, foamed time 2min, forms porous poly- ammonia
Ester coating, the coating weight of aqueous polyurethane layer is 40g/m2；
4）Washed after the completion of foaming, dry the waterborne polyurethane synthetic leather for being made described.
Waterborne polyurethane synthetic leather prepared by the method for embodiment 3 waterborne polyurethane synthetic leather with embodiment 1 after testing
With it is identical the effect of, and also there is absorption ammonia, formaldehyde, benzene and the effect of toluene.
Claims (10)
1. a kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating, it is characterised in that aqueous polyurethane coating presses quality
Percentages include following components：
Aqueous polyurethane emulsion 20 ~ 60%
Wood powder and/or wood pulp 5 ~ 15%
Bamboo charcoal 2.0 ~ 20%
Calcium carbonate 0 ~ 20%
Lubricant 1.0 ~ 5.0%
Organic silicone oil 1.0 ~ 5.0%
White oil 0.5 ~ 3.0%
Glycerine and/or ethylene glycol 1.0 ~ 5.0%
Processing aid 0.1 ~ 2.0%
Water 20 ~ 50%.
A kind of 2. bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating according to claim 1, it is characterised in that water
Property polyurethane coating includes following components by mass percentage：
Aqueous polyurethane emulsion 30 ~ 50%
Wood powder and/or wood pulp 8 ~ 12%
Bamboo charcoal 2.0 ~ 10%
Calcium carbonate 0 ~ 20%
Lubricant 1.5 ~ 4.0%
Organic silicone oil 1.5 ~ 4.0%
White oil 0.8 ~ 2.0%
Glycerine and/or ethylene glycol 1.5 ~ 4.0%
Processing aid 0.5 ~ 1.5%
Water 25 ~ 45%.
3. a kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating according to claim 1 or 2, its feature exist
In bamboo charcoal powder is the bamboo charcoal powder of 600~2000 mesh.
A kind of 4. bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating according to claim 1, it is characterised in that institute
One or more mixing in the lubricant preferably talc powder stated, zinc oxide；The preferred aqueous emulsifying silicone oil of organic silicone oil.
A kind of 5. bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating according to claim 1, it is characterised in that water
Property polyurethane coating also includes toner 0.01 ~ 1.0%.
A kind of 6. bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating according to claim 1, it is characterised in that water
Property polyurethane coating also includes function nano material 1.0 ~ 5.0%；It is preferred that function nano material is nano titanium oxide, nanometer two
Silica, nano zine oxide and nano-aluminium oxide are a kind of or 2 kinds mix；As it is further preferred that above-mentioned function nano material
For 2 kinds of mixing of nanometer anatase titania and nano silicon, nanometer anatase titania accounts for the 0.4% of gross weight
~5%, nano silicon accounts for the 0.8%~5% of gross weight.
7. a kind of bamboo Charcoal Adsorption environment-friendly type synthetic leather aqueous polyurethane coating according to claim 1, it is characterised in that add
Work auxiliary agent includes levelling agent, defoamer and thickener；It is preferred that levelling agent 0.1 ~ 0.5%, defoamer 0.01 ~ 0.1% and thickener
0.1~0.5%。
8. a kind of environment-friendly type aqueous synthetic leather bass of bamboo Charcoal Adsorption, it is characterised in that the Waterborne synthetic leather bass will using right
The aqueous polyurethane coating described in 1 ~ 7 any one claim is asked to be made after coating base fabric using bamboo vinegar foaming；As excellent
Choosing, the pH of bamboo vinegar is 1.0 ~ 4.5；As further preferably, the pH of bamboo vinegar is 1.8 ~ 3.5.
A kind of 9. environment-friendly type aqueous synthetic leather bass of bamboo Charcoal Adsorption according to claim 1, it is characterised in that water-based poly- ammonia
The coating weight of ester layer is 20 ~ 200g/m2；As further preferably, the coating weight of aqueous polyurethane layer is 30 ~ 100g/m2；Water-based poly- ammonia
Aqueous polyurethane selects the Aliphatic Polyester Aqueous Polyurethane Dispersions of 30 ~ 50% solid contents in ester paint；Base fabric selects superfine fibre cloth.
10. the environment-friendly type aqueous synthetic leather bass of a kind of bamboo Charcoal Adsorption according to claim 1, it is characterised in that coating
Base fabric is soaked using bamboo vinegar before base fabric, base fabric is impregnated with bamboo vinegar, is then extracted.