CN109137550A - A kind of PU coating fabric manufacture craft of high water pressure resistance height tearing - Google Patents
A kind of PU coating fabric manufacture craft of high water pressure resistance height tearing Download PDFInfo
- Publication number
- CN109137550A CN109137550A CN201810948712.4A CN201810948712A CN109137550A CN 109137550 A CN109137550 A CN 109137550A CN 201810948712 A CN201810948712 A CN 201810948712A CN 109137550 A CN109137550 A CN 109137550A
- Authority
- CN
- China
- Prior art keywords
- resin
- pressure resistance
- water pressure
- tearing
- high water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing, mainly comprises the steps that 1) stained clot-h water-sprinkling setting treatment；2) press polish processing before gluing；3) aqueous PU resin bottoming processing: aqueous PU resinous coat is carried out in trowel finish, carries out incomplete maturation drying and processing later；4) two knife solvent type PU resin treatment: successively applying solvent type PU resin primer layer and solvent type PU resin face glue-line on aqueous PU resinous coat face, and carries out drying maturation processing.This case uses first with aqueous PU resin bottoming, then is aided with two knife solvent type PU resinous coats, reaches high water pressure resistance and high tearing effects, can effectively improve traditional tearing of degradation because of coating, and the higher tearing of hydraulic pressure declines more severe problem.This case technology can be applied to the production production of the products such as the water-proof jacket that high tearing high water pressure resistance requires and tent material.
Description
Technical field
The present invention relates to the PU coating fabric production that fabric Manufacturing Techniques, in particular to a kind of high water pressure resistance height are torn
Technique.
Background technique
At present due to the prevalence of outdoor sports, the performance of the eager intended motion fabric of consumer can be promoted effectively.And
PU coating fabric is favored since sexual valence is more excellent by the majority of consumers.However, the bottleneck that current PU resinous coat is encountered
Be exactly fabric water pressure resistance it is higher, resin coating weight when coating is higher, and the gap that sizing material penetrates into fabric is more, thus
Lead to the degradation of tearing.If one hide to pursue addition tearing promoting agent when being lifted at water-sprinkling of the tearing of base fabric, most
It will lead to the then bad of sizing material and cloth afterwards.Therefore the performance of the two has no idea completely to take into account.
In consideration of it, inventor furthers investigate the above problem, and propose a kind of PU of high water pressure resistance height tearing
Thus coating fabric manufacture craft, this case generate.
Summary of the invention
The purpose of the present invention is to provide a kind of PU coating fabric manufacture crafts of high water pressure resistance height tearing, overcome above-mentioned lack
Point can take into account water pressure resistance performance and tear resistance, under the premise of keeping high tearing, reach higher water pressure resistance effect.
In order to achieve the above objectives, solution of the invention is:
A kind of PU coating fabric manufacture craft of high water pressure resistance height tearing, mainly comprises the steps that
1) stained clot-h water-sprinkling setting treatment；
2) press polish processing before gluing；
3) aqueous PU resin bottoming processing: aqueous PU resinous coat is carried out in the trowel finish of stained clot-h, is carried out later endless
It is well done at drying and processing；
4) two knife solvent type PU resin treatment: successively applied on aqueous PU resinous coat face solvent type PU resin primer layer and
Solvent type PU resin face glue-line, and carry out drying maturation processing.
3) in the step, aqueous PU resinous coat is grouped as by following mass fraction group: 100 parts of aqueous PU resin, frame
1-3 parts of bridge agent, promoting agent 10-15 parts is torn, water；The dosage of water is subject to the viscosity of glue and is added, and wherein the viscosity of glue is
15000cps。
3) in the step, incomplete maturation drying and processing is carried out, four sections are arranged in baking oven, and temperature is set gradually are as follows: 80 DEG C,
100 DEG C, 120 DEG C, 140 DEG C.
3) in the step, the coating weight of aqueous PU resinous coat is 13-15G/Y.
4) in the step, solvent type PU resin primer layer is grouped as by following mass fraction group: two liquid type polyurethane tree
100 parts of rouge, 1.5-2.5 parts of bridging agent, 0.75-1.25 parts of bridge formation promotor, MEK solvent 8-12.
4) in the step, solvent type PU resin face glue-line is grouped as by following mass fraction group: a fluid polyurethane tree
100 parts of rouge, 35-40 parts of TOL solvent, dry and comfortable dose 1.5-2.5 parts.
4) in the step, three section baking ovens are arranged in the drying and processing of solvent type PU resin primer layer, and temperature is set gradually are as follows:
80℃,100℃,120℃；Four section baking ovens are arranged in the drying and processing of solvent type PU resin face glue-line, and temperature is set gradually are as follows: 100
℃、120℃、150℃、160℃。
4) in the step, the wet glue coating weight of solvent type PU resin primer layer is 100-110G/Y, solvent type PU resin
The wet glue coating weight of face glue-line is 80-90G/Y.
1) dyeing processing is also carried out before the step, throws base 70D, 190T semi-gloss nylon taffeta plain fabric, it is advanced
Row matches cloth desizing, using 7 slot compact form continuous annealing desizing machine desizing；BEAM dyeing is carried out later, and concrete technology is adding assistant under room temperature
And acid dyes, heating curve are that 0.5 DEG C/min rises to 70 DEG C, acid control pH is 7.0, and constant temperature 20min, then 0.5 DEG C/min rise to
90 DEG C of constant temperature 20min, then 0.5 DEG C/min rise to 100 degree, constant temperature 30min；Drain is carried out later, and water inlet room temperature washing 4min is simultaneously
Drain；Fixation is finally carried out, is dehydrated, drying.
1) in the step, stained clot-h water-sprinkling setting treatment, water-sprinkling formula: the volume of total solution is added with the amount of 50L,
First plus water 30L, IPA bleeding agent 30-40G/L, softening agent 4-8G/L, water-sprinkling agent 15-20G/L；It is suitable by water-sprinkling formula front and back
Sequence is successively at the uniform velocity added, and is slowly stirred, and the volume for finally adding water to total solution is 50L, is stirred evenly.
After adopting the above scheme, a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing of the present invention, relative to existing
Have the beneficial effect of technology to be: the coating way that is mainly characterized by of this case PU coating fabric manufacture craft uses first with aqueous
PU resin bottoming, then be aided with two knife solvent type PU resinous coats, using aqueous PU resin to the lesser feature of fabric permeability, with
It is arranged as coating bottoming, then cooperates two knife solvent type PU resins, reaches high water pressure resistance and high tearing effects, can be effective
Improve traditional tearing of degradation because of coating, the higher tearing of hydraulic pressure declines more severe problem.This case technology can
To be applied to the production production of the products such as the water-proof jacket for thering is high tearing high water pressure resistance to require and tent material.
Specific embodiment
This case is described in further detail With reference to embodiment.
This case is related to a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing, mainly comprises the steps that
1) stained clot-h water-sprinkling setting treatment；
2) press polish processing before gluing；
3) aqueous PU resin bottoming processing: aqueous PU resinous coat is carried out in trowel finish, carries out incomplete maturation baking later
Dry-cure；
4) two knife solvent type PU resin treatment: the successively coating solvent type PU resin primer layer on aqueous PU resinous coat face
With solvent type PU resin face glue-line, and carry out drying maturation processing.
This case PU coating fabric manufacture craft is mainly characterized by the PU resin painting that including step 3) and 4) the two cooperates
The innovative design of layer reaches the performance of fabric high water pressure resistance height tearing, i.e. coating design use elder generation with aqueous PU resin bottoming,
Using aqueous PU resin to the lesser feature of fabric permeability, it is arranged using it as coating bottoming, then be aided with two knife solvent type PU
Resinous coat, thus obtained PU coating fabric can overcome in traditional technology that both water pressure resistance performance and tear resistance can not
The problem of taking into account reaches high water pressure resistance and high tearing effects.
Preferably, 3) in the step, aqueous PU resinous coat is grouped as by following mass fraction group: aqueous PU resin
100 parts, 1-3 parts of bridging agent, promoting agent 10-15 parts is torn, water.Wherein, the dosage of water is subject to the viscosity of glue and is added, wherein glue
Viscosity be 15000cps.
Preferably, 3) in the step, incomplete maturation drying and processing is carried out, specifically, four sections, temperature is arranged in baking oven
It sets gradually are as follows: 80 DEG C, 100 DEG C, 120 DEG C, 140 DEG C.Incomplete maturation drying and processing, is conducive to and the solvent type PU in step 4)
Resinous coat then, promotes then performance, ensures and realizes high water pressure resistance and high tearing effect while fabric physical property is excellent.
Preferably, 3) in the step, the coating weight of aqueous PU resinous coat is that (G/Y refers to every 1 plaiting to 13-15G/Y
The sizing material grammes per square metre value being coated with).Select blade type: 0.5R, speed: 40M/MIN.
Preferably, 4) in the step, solvent type PU resin primer layer is grouped as by following mass fraction group: two-liquid type is poly-
100 parts of urethane resin, 1.5-2.5 parts of bridging agent, 0.75-1.25 parts of bridge formation promotor, MEK solvent 8-12.Solvent type PU resin
Face glue-line is grouped as by following mass fraction group: 100 parts of a fluid polyurethane resin, and 35-40 parts of TOL solvent, dry and comfortable dose of 1.5-
2.5 part.
Preferably, 4) in the step, three section baking ovens are arranged in the drying and processing of solvent type PU resin primer layer, and temperature is successively
Setting are as follows: 80 DEG C, 100 DEG C, 120 DEG C；Four section baking ovens are arranged in the drying and processing of solvent type PU resin face glue-line, and temperature is set gradually
Are as follows: 100 DEG C, 120 DEG C, 150 DEG C, 160 DEG C.
Preferably, 4) in the step, the wet glue coating weight of solvent type PU resin primer layer is 100-110G/Y, solvent type
The wet glue coating weight of PU resin face glue-line is 80-90G/Y.
Preferably, 1) dyeing processing is also carried out before the step, throws base 70D, 190T semi-gloss nylon taffeta plain weave face
Material is first carried out with cloth desizing, using 7 slot compact form continuous annealing desizing machine desizing, carries out BEAM dyeing later, concrete technology is room temperature
Lower adding assistant and acid dyes, heating curve are that 0.5 DEG C/min rises to 70 DEG C, and acid controls pH as 7.0, constant temperature 20min, then 0.5 DEG C/
Min rises to 90 DEG C of constant temperature 20min, then 0.5 DEG C/min rises to 100 degree, constant temperature 30min；Drain, water inlet room temperature washing are carried out later
4min and drain；Fixation is finally carried out, is dehydrated, drying.
Preferably, 1) in the step, stained clot-h water-sprinkling setting treatment, water-sprinkling formula:
The volume of total solution is added with the amount of 50L, first plus water 30L, IPA bleeding agent 30-40G/L, softening agent 4-8G/L,
Water-sprinkling agent 15-20G/L；It successively at the uniform velocity adds, and is slowly stirred by water-sprinkling formula tandem, finally add water to total solution
Volume be 50L, stir evenly.
Particular preferred embodiment, a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing, processing step are as follows:
1, base is thrown
70D, 190T semi-gloss nylon taffeta plain fabric；
2, it dyes
Desizing, using 7 slot compact form continuous annealing desizing machine desizing；
Then carry out BEAM dyeing, concrete technology is adding assistant and acid dyes under room temperature, heating curve be 0.5 DEG C/
Min rises to 70 DEG C, and acid control pH is 7.0, constant temperature 20min, then 0.5 DEG C/min rises to 90 DEG C of constant temperature 20min, then 0.5 DEG C/min liter
To 100 degree, constant temperature 30min；Drain, water inlet room temperature washing 4min and drain are carried out later；Fixation is then carried out, is dehydrated, drying.
3. stained clot-h water-sprinkling setting treatment
Water-sprinkling formula, by following formulas from top to bottom at the uniform velocity plus, and be slowly stirred；
Water: 30L
IPA bleeding agent: 40G/L
Softening agent: 12/L
Water-sprinkling agent: 20G/L
Water: X (X is the total volume 50L for making last solution)
Forming machine temperature is with 160 DEG C DEG C, speed 40M/min, air quantity 90%, overfeeding 3%.
Then detection water-sprinkling
| Test item | Test method | Benchmark | As a result | Determine |
| Water-sprinkling degree | ISO4920 | 3 | 4 | PASS |
4. press polish processing before gluing
Glue face pressure light, calendaring technology: 140 DEG C of roads * 150N/MM*30M/MIN*2；
5. functional coating is handled
1) permit and receive benchmark
| Project | Test method | Numerical value |
| Hydraulic pressure (MMH2O) | ISO811(60CM/MIN) | 10000 |
| It tears (N) | ISO13937.2 | 30 |
| It slides (mm) | ISO13936.2(100N) | 3 |
| Water-cleaning appearance | ISO6330.4N*10 times | Not degumming |
| Joint strip | 490℃ | 0.7KG |
2) coating processing conditions
A, with aqueous PU resin bottoming
B, again with the one bottom one side operation of solvent type PU resin
3, it detects
| Test item | Test method | Test content | Test value | Standard | Determine |
| It tears (N)) | ISO13937.2 | Through to/broadwise | 34.8/32.3 | 30 | PASS |
| Suture slides (MM) | ISO13936.2(100N) | Through to/broadwise | 1.1/1.3 | 3 | PASS |
| Hydraulic pressure (MMH2O) | ISO811(60CM/MIN) | As a result | 13268 | 10000 | PASS |
| Water-cleaning appearance | ISO6330.4N*10 times | As a result | Not degumming | Not degumming | PASS |
Coating fabric of the present invention is not limited by citing, can be any chemical fibre shuttle-woven fabric.It is of the present invention
Functional high water pressure resistance and the specific value of high tearing are not limited by citing, 10000 or more water pressure resistance range (ISO811), tearing
3KG(ISO13937.2)。
One embodiment of the present invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, all equivalent changes and modification done with scope of the invention as claimed should all
Belong to the range of the claims in the present invention.
Claims (10)
1. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing, which is characterized in that mainly comprise the steps that
1) stained clot-h water-sprinkling setting treatment；
2) press polish processing before gluing；
3) aqueous PU resin bottoming processing: aqueous PU resinous coat is carried out in trowel finish, is carried out at incomplete maturation drying later
Reason；
4) solvent type PU resin primer layer and solvent successively two knife solvent type PU resin treatment: are applied on aqueous PU resinous coat face
Type PU resin face glue-line, and carry out drying maturation processing.
2. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
3) in step, aqueous PU resinous coat is grouped as by following mass fraction group: 100 parts of aqueous PU resin, is torn by 1-3 parts of bridging agent
10-15 parts of promoting agent are split, water；The dosage of water is subject to the viscosity of glue and is added, and wherein the viscosity of glue is 15000cps.
3. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
3) in step, incomplete maturation drying and processing is carried out, four sections are arranged in baking oven, and temperature is set gradually are as follows: 80 DEG C, 100 DEG C, 120 DEG C,
140℃。
4. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
3) in step, the coating weight of aqueous PU resinous coat is 13-15G/Y.
5. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
4) in step, solvent type PU resin primer layer is grouped as by following mass fraction group: 100 parts of two liquid type polyurethane resin, being built bridge
1.5-2.5 parts of agent, 0.75-1.25 parts of bridge formation promotor, MEK solvent 8-12.
6. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
4) in step, solvent type PU resin face glue-line is grouped as by following mass fraction group: 100 parts of a fluid polyurethane resin, TOL is molten
35-40 parts of agent, dry and comfortable dose 1.5-2.5 parts.
7. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
4) in step, three section baking ovens are arranged in the drying and processing of solvent type PU resin primer layer, and temperature is set gradually are as follows: 80 DEG C, 100 DEG C,
120℃；Four section baking ovens are arranged in the drying and processing of solvent type PU resin face glue-line, and temperature is set gradually are as follows: 100 DEG C, 120 DEG C, 150
℃、160℃。
8. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
4) in step, the wet glue coating weight of solvent type PU resin primer layer is 100-110G/Y, the wet glue of solvent type PU resin face glue-line
Coating weight is 80-90G/Y.
9. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that described
1) dyeing processing is also carried out before step, throws base 70D, 190T semi-gloss nylon taffeta plain fabric, first carries out adopting with cloth desizing
With 7 slot compact form continuous annealing desizing machine desizing, carry out BEAM dyeing later, concrete technology is, concrete technology is, under room temperature adding assistant and
Acid dyes, heating curve are that 0.5 DEG C/min rises to 70 DEG C, and acid control pH is 7.0, and constant temperature 20min, then 0.5 DEG C/min rise to 90
DEG C constant temperature 20min, then 0.5 DEG C/min rise to 100 degree, constant temperature 30min；Drain is carried out later, and water inlet room temperature washing 4min is side by side
Liquid；Fixation is finally carried out, is dehydrated, drying.
10. a kind of PU coating fabric manufacture craft of high water pressure resistance height tearing as described in claim 1, which is characterized in that institute
State in 1) step, stained clot-h water-sprinkling setting treatment, water-sprinkling formula: the volume of total solution is added with the amount of 50L, first plus water 30L,
IPA bleeding agent 30-40G/L, softening agent 4-8G/L, water-sprinkling agent 15-20G/L；Tandem is formulated successively at the uniform velocity by the water-sprinkling
Addition, and be slowly stirred, the volume for finally adding water to total solution is 50L, is stirred evenly.