CN108703424A - A kind of flame-retardant garment plus material - Google Patents
A kind of flame-retardant garment plus material Download PDFInfo
- Publication number
- CN108703424A CN108703424A CN201810497815.3A CN201810497815A CN108703424A CN 108703424 A CN108703424 A CN 108703424A CN 201810497815 A CN201810497815 A CN 201810497815A CN 108703424 A CN108703424 A CN 108703424A
- Authority
- CN
- China
- Prior art keywords
- fiber
- flame
- parts
- retardant
- length
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of flame-retardant garment plus materials, by the PSA fiber of 20-30 parts by weight, the carbon fiber of 30-40 parts by weight, the conductive fiber of 10-20 parts by weight, the melamine fiber of 5-10 parts by weight, the spandex fibre of the 5-10 parts by weight and flame retardant viscose fiber of 40-60 parts by weight is blended is prepared, the length of the PSA fiber is 200-250nm, the length of the carbon fiber is 100-150nm, the length of the conductive fiber is 50-100nm, the length of the melamine fiber is 150-200nm, the length of the spandex fibre is 150-180nm, the length of the flame retardant viscose fiber is 300-350nm.By the above-mentioned means, flame-retardant garment plus material provided by the invention, has higher flame retardant property, and wear comfortable, relative inexpensiveness.
Description
Technical field
The present invention relates to fabric fields, more particularly to a kind of flame-retardant garment plus material.
Background technology
With the raising of living standard, requirement of the people to textile is no longer limited to warming, comfortable etc. original
Fundamental characteristics.According to the different purposes of textile, it is also desirable that it is with specific functions such as health care, safety, such as antibacterial, anti-
Mite, anion, far infrared, antiultraviolet, gas defence, fire-retardant, anti-electromagnetic radiation, magnetic therapy, fragrance, moisture absorbing and sweat releasing, grease-proof and waterproof
Deng.Existing flame-retardant garment plus material flame retardant property is relatively low, and it is higher to wear uncomfortable and cost.
Invention content
The invention mainly solves the technical problem of providing a kind of flame-retardant garment plus materials, have higher flame retardant property, and
Wear comfortable, relative inexpensiveness.
In order to solve the above technical problems, one aspect of the present invention is：A kind of flame-retardant garment plus material is provided, by
The three of the PSA fiber of 20-30 parts by weight, the carbon fiber of 30-40 parts by weight, the conductive fiber of 10-20 parts by weight, 5-10 parts by weight
The flame retardant viscose fiber of poly cyanamid fiber, the spandex fibre of 5-10 parts by weight and 40-60 parts by weight is blended to be prepared, the virtue
The length of sulfone synthetic fibre is 200-250nm, and the length of the carbon fiber is 100-150nm, and the length of the conductive fiber is 50-
The length of 100nm, the melamine fiber are 150-200nm, and the length of the spandex fibre is 150-180nm, the resistance
The length for firing viscose rayon is 300-350nm.
In a preferred embodiment of the present invention, fire retardant accounts for the flame retardant viscose fiber in the flame retardant viscose fiber
Mass percentage 8-10%.
In a preferred embodiment of the present invention, the fire retardant is selected from antimony trichloride, ammonium sulfate, magnesium hydroxide and phosphorus
It is one or more in acid dihydride ammonium.
In a preferred embodiment of the present invention, the fire retardant is grouped as by the group of following parts by weight：Antimony trichloride
40-50 parts of 10-20 parts, 20-25 parts of ammonium sulfate, 30-40 parts of magnesium hydroxide and ammonium dihydrogen phosphate.
In a preferred embodiment of the present invention, the flame-retardant garment plus material thickness is 0.9-0.95mm.
The beneficial effects of the invention are as follows：A kind of flame-retardant garment plus material that the present invention points out has higher flame retardant property, and
Wear comfortable, relative inexpensiveness.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
All other embodiment that technical staff is obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1：
It weighs：40 kilograms of 10 kilograms of antimony trichloride, 20 kilograms of ammonium sulfate, 30 kilograms of magnesium hydroxide and ammonium dihydrogen phosphate, stirring are mixed
Close uniformly obtained composite flame-retardant agent.
Above-mentioned composite flame-retardant agent is mixed with viscose solution, routinely wet spinning spinneret technological forming, you can institute is made
Flame retardant viscose fiber is stated, the length of flame retardant viscose fiber is 350nm, wherein the matter of fire retardant in finished product flame retardant viscose fiber is made
It is 9% to measure percentage composition.
It weighs：20 kilograms of PSA fiber, 30 kilograms of carbon fiber, 10 kilograms of conductive fiber, 5 kilograms of melamine fiber, spandex
8 kilograms of fiber and 40 kilograms of flame retardant viscose fiber obtained above, wherein the length of PSA fiber is 200nm, the length of carbon fiber
Length for 150nm, conductive fiber is 100nm, and the length of melamine fiber is 200nm, and the length of spandex fibre is
180nm is combed into the PSA fiber carded sliver, the carbon fiber carded sliver, conductive fiber life then in shredding pretreatment respectively on carding machine
Item, the melamine fiber carded sliver, the spandex fibre carded sliver and the flame retardant viscose fiber carded sliver, then by drawing frame combination system at ripe bar,
It carries out stretching on fly frame leading and twisting, is finally further stretched on spinning frame and lead twisting, mixed yarn is made, then mixed yarn is adopted
It is weaved with large circle machine weft knitting manufacturing method, the final flame-retardant garment plus material that the present invention is made.
Embodiment 2：
It is substantially the same manner as Example 1, only difference is that, the fire retardant, which is that both antimony trichloride and ammonium sulfate are compound, to be mixed
Fire retardant is closed, rather than by antimony trichloride, ammonium sulfate, magnesium hydroxide and the compound mixing fire retardant of ammonium dihydrogen phosphate.
Embodiment 3：
It is substantially the same manner as Example 1, only difference is that, the fire retardant is that both antimony trichloride and magnesium hydroxide are compound
Fire retardant is mixed, rather than by antimony trichloride, ammonium sulfate, magnesium hydroxide and the compound mixing fire retardant of ammonium dihydrogen phosphate.
Embodiment 4：
It is substantially the same manner as Example 1, only difference is that, the fire retardant is the mixing resistance of antimony trichloride and ammonium dihydrogen phosphate
Agent is fired, rather than by antimony trichloride, ammonium sulfate, magnesium hydroxide and the compound mixing fire retardant of ammonium dihydrogen phosphate.
Test case：
Respectively to flame retardant viscose fiber made from embodiment 1-4 and and flame-retardant garment plus material progress flame retardant property test.
In conclusion a kind of flame-retardant garment plus material that the present invention points out, has higher flame retardant property, and dress is comfortable,
Relative inexpensiveness.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (5)
1. a kind of flame-retardant garment plus material, which is characterized in that by the PSA fiber of 20-30 parts by weight, 30-40 parts by weight carbon fiber,
The conductive fiber of 10-20 parts by weight, the melamine fiber of 5-10 parts by weight, the spandex fibre of 5-10 parts by weight and 40-60 weights
The flame retardant viscose fiber of amount part is blended to be prepared, and the length of the PSA fiber is 200-250nm, and the length of the carbon fiber is
The length of 100-150nm, the conductive fiber are 50-100nm, and the length of the melamine fiber is 150-200nm, described
The length of spandex fibre is 150-180nm, and the length of the flame retardant viscose fiber is 300-350nm.
2. flame-retardant garment plus material according to claim 1, which is characterized in that fire retardant accounts for institute in the flame retardant viscose fiber
State the mass percentage 8-10% of flame retardant viscose fiber.
3. flame-retardant garment plus material according to claim 2, which is characterized in that the fire retardant, selected from antimony trichloride, sulfuric acid
It is one or more in ammonium, magnesium hydroxide and ammonium dihydrogen phosphate.
4. flame-retardant garment plus material according to claim 2, which is characterized in that the fire retardant, by the group of following parts by weight
It is grouped as：40-50 parts of 10-20 parts of antimony trichloride, 20-25 parts of ammonium sulfate, 30-40 parts of magnesium hydroxide and ammonium dihydrogen phosphate.
5. flame-retardant garment plus material according to claim 1, which is characterized in that the flame-retardant garment plus material thickness is 0.9-
0.95mm。