CN108698886A - 降低二氧化硅颗粒的碳含量和石英玻璃体的制备 - Google Patents

降低二氧化硅颗粒的碳含量和石英玻璃体的制备 Download PDF

Info

Publication number
CN108698886A
CN108698886A CN201680082012.0A CN201680082012A CN108698886A CN 108698886 A CN108698886 A CN 108698886A CN 201680082012 A CN201680082012 A CN 201680082012A CN 108698886 A CN108698886 A CN 108698886A
Authority
CN
China
Prior art keywords
range
less
quartz glass
silica
content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201680082012.0A
Other languages
English (en)
Chinese (zh)
Inventor
M·欧特
W·莱曼
M·胡乃曼
N·C·尼尔森
N·R·惠比
B·格罗曼
A-G·柯佩巴尼
T·凯瑟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Heraeus Quarzglas GmbH and Co KG
Original Assignee
Heraeus Quarzglas GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heraeus Quarzglas GmbH and Co KG filed Critical Heraeus Quarzglas GmbH and Co KG
Publication of CN108698886A publication Critical patent/CN108698886A/zh
Pending legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00—Silicon; Compounds thereof
    • C01B33/113—Silicon oxides; Hydrates thereof
    • C01B33/12—Silica; Hydrates thereof, e.g. lepidoic silicic acid
    • C01B33/18—Preparation of finely divided silica neither in sol nor in gel form; After-treatment thereof
    • C01B33/181—Preparation of finely divided silica neither in sol nor in gel form; After-treatment thereof by a dry process
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B17/00—Forming molten glass by flowing-out, pushing-out, extruding or drawing downwardly or laterally from forming slits or by overflowing over lips
    • C03B17/04—Forming tubes or rods by drawing from stationary or rotating tools or from forming nozzles
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B19/00—Other methods of shaping glass
    • C03B19/10—Forming beads
    • C03B19/1005—Forming solid beads
    • C03B19/106—Forming solid beads by chemical vapour deposition; by liquid phase reaction
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B19/00—Other methods of shaping glass
    • C03B19/10—Forming beads
    • C03B19/1095—Thermal after-treatment of beads, e.g. tempering, crystallisation, annealing
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B20/00—Processes specially adapted for the production of quartz or fused silica articles, not otherwise provided for
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C1/00—Ingredients generally applicable to manufacture of glasses, glazes, or vitreous enamels
    • C03C1/02—Pretreated ingredients
    • C03C1/022—Purification of silica sand or other minerals
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C12/00—Powdered glass; Bead compositions
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/06—Glass compositions containing silica with more than 90% silica by weight, e.g. quartz
    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
    • G02B6/10—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings of the optical waveguide type
    • G02B6/12—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings of the optical waveguide type of the integrated circuit kind
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/51—Particles with a specific particle size distribution
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/10—Solid density
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/11—Powder tap density
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/12—Surface area
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/80—Compositional purity
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2201/00—Type of glass produced
    • C03B2201/06—Doped silica-based glasses
    • C03B2201/07—Impurity concentration specified
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2201/00—Type of glass produced
    • C03B2201/06—Doped silica-based glasses
    • C03B2201/07—Impurity concentration specified
    • C03B2201/075—Hydroxyl ion (OH)
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/30—For glass precursor of non-standard type, e.g. solid SiH3F
    • C03B2207/32—Non-halide
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B2207/00—Glass deposition burners
    • C03B2207/36—Fuel or oxidant details, e.g. flow rate, flow rate ratio, fuel additives
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2201/00—Glass compositions
    • C03C2201/02—Pure silica glass, e.g. pure fused quartz
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2201/00—Glass compositions
    • C03C2201/06—Doped silica-based glasses
    • C03C2201/08—Doped silica-based glasses containing boron or halide
    • C03C2201/11—Doped silica-based glasses containing boron or halide containing chlorine
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2201/00—Glass compositions
    • C03C2201/06—Doped silica-based glasses
    • C03C2201/20—Doped silica-based glasses containing non-metals other than boron or halide
    • C03C2201/26—Doped silica-based glasses containing non-metals other than boron or halide containing carbon
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2201/00—Glass compositions
    • C03C2201/06—Doped silica-based glasses
    • C03C2201/30—Doped silica-based glasses containing metals
    • C03C2201/32—Doped silica-based glasses containing metals containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2201/00—Glass compositions
    • C03C2201/06—Doped silica-based glasses
    • C03C2201/30—Doped silica-based glasses containing metals
    • C03C2201/54—Doped silica-based glasses containing metals containing beryllium, magnesium or alkaline earth metals
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2203/00—Production processes
    • C03C2203/10—Melting processes
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2203/00—Production processes
    • C03C2203/40—Gas-phase processes
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2203/00—Production processes
    • C03C2203/40—Gas-phase processes
    • C03C2203/42—Gas-phase processes using silicon halides as starting materials
    • C03C2203/44—Gas-phase processes using silicon halides as starting materials chlorine containing
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2203/00—Production processes
    • C03C2203/50—After-treatment
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N21/00—Investigating or analysing materials by the use of optical means, i.e. using sub-millimetre waves, infrared, visible or ultraviolet light
    • G01N21/17—Systems in which incident light is modified in accordance with the properties of the material investigated
    • G01N21/41—Refractivity; Phase-affecting properties, e.g. optical path length
    • G01N21/412—Index profiling of optical fibres
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P40/00—Technologies relating to the processing of minerals
    • Y02P40/50—Glass production, e.g. reusing waste heat during processing or shaping
    • Y02P40/57—Improving the yield, e-g- reduction of reject rates

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Physics & Mathematics (AREA)
  • Manufacturing & Machinery (AREA)
  • Inorganic Chemistry (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Thermal Sciences (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • General Physics & Mathematics (AREA)
  • Optics & Photonics (AREA)
  • Glass Compositions (AREA)
  • Glass Melting And Manufacturing (AREA)
  • Optical Integrated Circuits (AREA)
  • Silicon Compounds (AREA)
CN201680082012.0A 2015-12-18 2016-12-16 降低二氧化硅颗粒的碳含量和石英玻璃体的制备 Pending CN108698886A (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP15201098 2015-12-18
EP15201098.9 2015-12-18
PCT/EP2016/081520 WO2017103167A2 (de) 2015-12-18 2016-12-16 Verringern des kohlenstoffgehalts von siliziumdioxidgranulat und herstellung eines quarzglaskörpers

Publications (1)

Publication Number Publication Date
CN108698886A true CN108698886A (zh) 2018-10-23

Family

ID=54850382

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201680082012.0A Pending CN108698886A (zh) 2015-12-18 2016-12-16 降低二氧化硅颗粒的碳含量和石英玻璃体的制备

Country Status (6)

Country Link
US (1) US20190077672A1 (https=)
EP (1) EP3390307A2 (https=)
JP (1) JP6912098B2 (https=)
CN (1) CN108698886A (https=)
TW (1) TWI764879B (https=)
WO (1) WO2017103167A2 (https=)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017103160A1 (de) 2015-12-18 2017-06-22 Heraeus Quarzglas Gmbh & Co. Kg Herstellung von quarzglaskörpern aus siliziumdioxidgranulat
US11053152B2 (en) 2015-12-18 2021-07-06 Heraeus Quarzglas Gmbh & Co. Kg Spray granulation of silicon dioxide in the preparation of quartz glass
JP7044454B2 (ja) 2015-12-18 2022-03-30 ヘレウス クワルツグラス ゲーエムベーハー ウント コンパニー カーゲー 石英ガラス調製時の中間体としての炭素ドープ二酸化ケイ素造粒体の調製
US10676388B2 (en) 2015-12-18 2020-06-09 Heraeus Quarzglas Gmbh & Co. Kg Glass fibers and pre-forms made of homogeneous quartz glass
WO2017103115A2 (de) 2015-12-18 2017-06-22 Heraeus Quarzglas Gmbh & Co. Kg Herstellung eines quarzglaskörpers in einem schmelztiegel aus refraktärmetall
US11952303B2 (en) 2015-12-18 2024-04-09 Heraeus Quarzglas Gmbh & Co. Kg Increase in silicon content in the preparation of quartz glass
EP3390290B1 (de) 2015-12-18 2023-03-15 Heraeus Quarzglas GmbH & Co. KG Herstellung eines opaken quarzglaskörpers
TWI794149B (zh) 2015-12-18 2023-03-01 德商何瑞斯廓格拉斯公司 石英玻璃粉粒、不透明成型體及彼等之製備方法
US11492282B2 (en) 2015-12-18 2022-11-08 Heraeus Quarzglas Gmbh & Co. Kg Preparation of quartz glass bodies with dew point monitoring in the melting oven
CN108698894A (zh) 2015-12-18 2018-10-23 贺利氏石英玻璃有限两合公司 在多腔式烘箱中制备石英玻璃体
CN112236392B (zh) * 2019-03-22 2024-02-02 瓦克化学股份公司 用于生产工业硅的方法
CN112390261A (zh) * 2019-08-13 2021-02-23 斯特里特技术有限公司 气相二氧化硅颗粒分离脱氢的系统和方法
EP4030204B1 (de) * 2021-01-19 2023-09-20 Heraeus Quarzglas GmbH & Co. KG Mikrostrukturierte optische faser und vorform dafür
WO2025057938A1 (ja) * 2023-09-15 2025-03-20 日本板硝子株式会社 ガラス粉体

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4650511A (en) * 1984-06-04 1987-03-17 Shin-Etsu Chemical Co., Ltd. Method for the preparation of a dehydrated quartz glass material for light transmission
CN1134399A (zh) * 1995-02-04 1996-10-30 底古萨股份公司 基于热解制备的二氧化硅的颗粒、其制备方法及其应用
EP0890555A1 (de) * 1997-07-10 1999-01-13 Heraeus Quarzglas GmbH Verfahren zur Herstellung von SiO2-Granulat
US6136736A (en) * 1993-06-01 2000-10-24 General Electric Company Doped silica glass
EP1088789A2 (en) * 1999-09-28 2001-04-04 Heraeus Quarzglas GmbH & Co. KG Porous silica granule, its method of production and its use in a method for producing quartz glass
EP1167309A1 (en) * 2000-06-28 2002-01-02 Mitsubishi Materials Quartz Corporation Synthetic quartz powder, its production process, and synthetic quartz crucible
US20030129153A1 (en) * 2001-12-22 2003-07-10 Degussa Ag Silicon-titanium mixed oxide powder prepared by flame hydrolysis, which is surface-enriched with silicon dioxide, and the preparation and use thereof
CN1757598A (zh) * 2005-10-26 2006-04-12 太原理工大学 一种超细疏水性二氧化硅的制取方法
CN103717531A (zh) * 2011-07-29 2014-04-09 莫门蒂夫性能材料股份有限公司 制造高质量金属氧化物颗粒的方法和制造其的材料

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2925797B2 (ja) * 1991-07-30 1999-07-28 古河電気工業株式会社 光ファイバ用多孔質母材の精製方法
JP3751326B2 (ja) * 1994-10-14 2006-03-01 三菱レイヨン株式会社 高純度透明石英ガラスの製造方法
DE10019693B4 (de) * 2000-04-20 2006-01-19 Heraeus Quarzglas Gmbh & Co. Kg Verfahren zur Herstellung eines Bauteils aus opakem, synthetischen Quarzglas, nach dem Verfahren hergestelltes Quarzglasrohr, sowie Verwendung desselben
US20040118155A1 (en) * 2002-12-20 2004-06-24 Brown John T Method of making ultra-dry, Cl-free and F-doped high purity fused silica
JP4470479B2 (ja) * 2003-12-17 2010-06-02 旭硝子株式会社 光学部材用合成石英ガラスおよびその製造方法
US7166963B2 (en) * 2004-09-10 2007-01-23 Axcelis Technologies, Inc. Electrodeless lamp for emitting ultraviolet and/or vacuum ultraviolet radiation
US7452518B2 (en) * 2004-12-28 2008-11-18 Momentive Performance Materials Inc. Process for treating synthetic silica powder and synthetic silica powder treated thereof
JPWO2009096557A1 (ja) * 2008-01-30 2011-05-26 旭硝子株式会社 エネルギー伝送用または紫外光伝送用光ファイバプリフォームおよびその製造方法
US8925354B2 (en) * 2009-11-04 2015-01-06 Corning Incorporated Methods for forming an overclad portion of an optical fiber from pelletized glass soot
DE102011121153B3 (de) * 2011-12-15 2013-03-21 Heraeus Quarzglas Gmbh & Co. Kg Verfahren zur Herstellung von synthetischem Quarzglas sowie Quarzglas für den Einsatz als Mantelmaterial einer optischen Faser
DE102012008437B3 (de) * 2012-04-30 2013-03-28 Heraeus Quarzglas Gmbh & Co. Kg Verfahren zur Herstellung synthetischer Quarzglaskörnung
CN105722788B (zh) * 2014-01-29 2018-04-03 三菱综合材料株式会社 合成非晶质二氧化硅粉末及其制造方法
EP3000790B2 (de) * 2014-09-29 2023-07-26 Heraeus Quarzglas GmbH & Co. KG Verfahren für die Herstellung von Bauteilen aus synthetischem Quarzglas aus SiO2-Granulat

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4650511A (en) * 1984-06-04 1987-03-17 Shin-Etsu Chemical Co., Ltd. Method for the preparation of a dehydrated quartz glass material for light transmission
US6136736A (en) * 1993-06-01 2000-10-24 General Electric Company Doped silica glass
CN1134399A (zh) * 1995-02-04 1996-10-30 底古萨股份公司 基于热解制备的二氧化硅的颗粒、其制备方法及其应用
EP0890555A1 (de) * 1997-07-10 1999-01-13 Heraeus Quarzglas GmbH Verfahren zur Herstellung von SiO2-Granulat
EP1088789A2 (en) * 1999-09-28 2001-04-04 Heraeus Quarzglas GmbH & Co. KG Porous silica granule, its method of production and its use in a method for producing quartz glass
EP1167309A1 (en) * 2000-06-28 2002-01-02 Mitsubishi Materials Quartz Corporation Synthetic quartz powder, its production process, and synthetic quartz crucible
US20030129153A1 (en) * 2001-12-22 2003-07-10 Degussa Ag Silicon-titanium mixed oxide powder prepared by flame hydrolysis, which is surface-enriched with silicon dioxide, and the preparation and use thereof
CN1757598A (zh) * 2005-10-26 2006-04-12 太原理工大学 一种超细疏水性二氧化硅的制取方法
CN103717531A (zh) * 2011-07-29 2014-04-09 莫门蒂夫性能材料股份有限公司 制造高质量金属氧化物颗粒的方法和制造其的材料

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
谢洪勇主编: "《粉体力学与工程》", 31 July 2007, 北京：化学工业出版社 *

Also Published As

Publication number Publication date
TWI764879B (zh) 2022-05-21
US20190077672A1 (en) 2019-03-14
WO2017103167A2 (de) 2017-06-22
JP2019502631A (ja) 2019-01-31
TW201733924A (zh) 2017-10-01
WO2017103167A3 (de) 2017-11-23
JP6912098B2 (ja) 2021-07-28
EP3390307A2 (de) 2018-10-24

Similar Documents

Publication Publication Date Title
TWI720090B (zh) 於石英玻璃之製備中作為中間物之經碳摻雜二氧化矽顆粒的製備
TWI840318B (zh) 石英玻璃體、光導、施照體、成型體及製備彼等之方法及矽組分之用途
TWI794150B (zh) 自二氧化矽顆粒製備石英玻璃體
TWI728018B (zh) 自二氧化矽粉末製備石英玻璃體
TWI794148B (zh) 於懸掛式燒結坩堝中製備石英玻璃體
TWI793065B (zh) 用於熔融烘箱的氣體沖洗及製備石英玻璃之方法
TWI764879B (zh) 降低二氧化矽顆粒之碳含量及石英玻璃體之製備
TWI813534B (zh) 利用露點監測在熔融烘箱中製備石英玻璃體
TWI808933B (zh) 石英玻璃體、二氧化矽顆粒、光導、施照體、及成型體及其製備方法
TWI812586B (zh) 石英玻璃體、其製備方法與應用、及用於控制烘箱出口處之露點
TWI794149B (zh) 石英玻璃粉粒、不透明成型體及彼等之製備方法
CN108698894A (zh) 在多腔式烘箱中制备石英玻璃体
CN108779014A (zh) 于立式烧结坩埚中制备石英玻璃体
CN108698896A (zh) 石英玻璃体的制备与后处理
CN108698889A (zh) 在悬挂式金属片坩埚中制备石英玻璃体
CN108698882A (zh) 石英玻璃制备中的二氧化硅粉末的氨处理
CN108698880A (zh) 不透明石英玻璃体的制备
CN108698884A (zh) 石英玻璃制备中的二氧化硅粉末的蒸汽处理
CN110740978A (zh) 石英玻璃体的制备

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination
RJ01 Rejection of invention patent application after publication
RJ01 Rejection of invention patent application after publication

Application publication date: 20181023