CN108695688A - The preparation method of module occurs for a kind of negative oxygen ion - Google Patents
The preparation method of module occurs for a kind of negative oxygen ion Download PDFInfo
- Publication number
- CN108695688A CN108695688A CN201810500203.5A CN201810500203A CN108695688A CN 108695688 A CN108695688 A CN 108695688A CN 201810500203 A CN201810500203 A CN 201810500203A CN 108695688 A CN108695688 A CN 108695688A
- Authority
- CN
- China
- Prior art keywords
- negative oxygen
- oxygen ion
- powder
- layer
- aloe vera
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of negative oxygen ions, and module occurs, which is characterized in that structure includes:Electric membranous layer (5), negative oxygen ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8);The electric membranous layer (5), negative oxygen ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8) are arranged in order.The present invention has many advantages, such as that simple in structure, cheap, easy for installation, purification efficiency is high, and non-secondary pollution, energy conservation and environmental protection are capable of providing the negative oxygen ion for being beneficial to health.
Description
The application be application No. is:201710450239.2, the divisional application that the applying date is on 06 14th, 2017.
Technical field
The invention belongs to air cleaning facility technical fields, and in particular to the preparation side of module occurs for a kind of negative oxygen ion
Method.
Background technology
Negative aeroion refers to molecule or atom negatively charged in air.Negative aeroion is known as " long in air
Shou Su ", " air vitamin ", the content concn of negative aeroion, directly related with health level in human habitat.
Ion medical investigator thinks, the energy of nature is given to life entity --- negative aeroion is (since the air of the Nature is negative
Ion has prodigious antioxidant effect and reducing power, so Ku Kou Noboru doctors are named as reduction ion again), ring can be made to give birth to brokenly
It orders the factors such as acidity, oxidation, active oxygen, the lactic acid of body health to gradually decrease, life entity is given in the metabolism of active cell tissue
The good environment of internal invention to the restoring force for reinforcing life entity itself and natural healing ability, and then overcomes disease, brings up
The body of health.The main component of air is nitrogen (accounting for about 78%) and oxygen (accounting for about 21%), and usual nitrogen, oxygen molecule institute are with positive and negative
Charge is equal, and electrical property is in neutrality.But after the electronics overwhelming majority that air molecule ionization generates is by oxygen muon capture, you can shape
At the negative oxygen ion that chemical property is active.
Nature air anion has three big mechanism:
1. air is by ultraviolet light, cosmic ray, radiogen, thunderstorm, storm, the shadow of the factors such as soil and air radioactive ray
It rings the electronics that ionization occurs and is released to combine with the neutral molecule in air quickly, and becomes anion, or be the moon
Ion.
2. waterfall impacts, ripple push away volume heavy rain fall mistake etc. in natural processes water under the effect of gravity, flow at high speed, hydrone
It cracks and generates anion.
3. the photoelectric effect that the trees of forest, leaf branch point discharge and green plants photosynthesis are formed, makes air ionization
And the anion generated.
In nature, there are some rays or thunderstorm waterfall etc. that can make partial air molecular ionization and generate negative oxygen ion.Cause
This, people by the sea, waterfall, after the places such as forest or thunderstorm, feel that air is fresh, breathing is happy.Usual mountain forest, beach
The air-anion concentration in area is 2500~5000/cm3, hot spring and waterfall are nearby up to 5000~20000/cm3, and it is big
City room is generally then 40~50/cm3, big arenas is only 10~30/cm3。
Negative oxygen ion is to human body and those benefitsNegative oxygen ion can lead to before fast reaction does not occur with other substances
It crosses breathing, nerve and hematological system and acts on human body, promote the metabolism of each system in vivo, excite incretory function, increase
Into appetite, dispelling fatigue.Anion moral is in the presence of productions such as polluter, nitrogen oxides, the cigarettes that can be restored from air in air
Harm of the raw active oxygen (oxygen radical), the excessive active oxygen of reduction to human body;After positively charged floating dust in air is neutralized without charge
Sedimentation, makes air be purified.
Negative oxygen ion is shown in medical field " air vitamin " its main function of being known as:
1. being the influence to nervous system.Cerebral cortex function and mental activity can be made to reinforce, in high spirits, working efficiency
It improves, sleep quality can be made to be improved.Anion can also be such that the oxidation process dynamics of brain tissue reinforces, and brain tissue is made to obtain more
More oxygen.
2. being the influence to cardiovascular system.It is observed according to scholar, negative oxygen ion plays the role of obviously expanding blood vessel, can release
Arteries spasm achievees the purpose that reduce blood pressure, and negative oxygen ion also has greatly for improving cardiac function and improving myocardial nutrition
Benefit, the state of an illness for being conducive to hypertension and cardio-cerebrovascular disorder patient are restored.
3. being the influence to hematological system.Research confirm, negative oxygen ion have make blood pool flow velocity it is slack-off, extend blood coagulation when
Between effect, oxygen content can be made to increase in blood, be conducive to blood oxygen conveying, absorb and utilize.
4. influence of the negative oxygen ion to respiratory system is most apparent.This is because negative oxygen ion is to enter human body by respiratory tract
, it can improve the lung capacity of people.Someone once tested, and air negative oxgyen ion was sucked in glass mask 30 minutes, can make
Pulmonary absorption amount of oxygen increases by 20%, and amount of carbon dioxide, which is discharged, can increase by 14.5%, therefore negative oxygen ion has improvement and increases lung
The effect of function.
In addition to this, air negative oxgyen ion also has calm, hypnosis effect.If we suck daily suitable negative oxygen from
Son is persevered, of great advantage to health:Make one full of vitality, dispelling fatigue and burnout improve working efficiency.Improve sleep,
Eliminate neurasthenia.Reduce disease incidence, preventing cold and breathing problem.Improve the symptom of Cardial or cerebral vascular diseases.Negative
Under oxonium ion effect, the excitability of bone can be made to increase, movement duration reduction contributes to sportsman to improve results, especially pair
Some projects that need to be reacted rapidly, such as dash, swimming.Just because of there are a large amount of negative oxygen ions in sweat-steaming house, it is possible to
Improve our sub-health condition of human body, disease can also be prevented, and improves itself constitution.
We only know with the presence of a large amount of negative oxygen ion in sweat-steaming house, then these negative oxygen ions are from what again
ComeWe know about the presence for having tourmaline and negative oxygen ion powder in sweat-steaming house.Tourmaline, negative oxygen ion powder is in sweat-steaming house
It is interior and play the role of thoseNegative oxygen ion is worked in the form of what kind of on earth in sweat-steaming house
One, tourmaline
Tourmaline is the natural minerals of permanent releasing negative oxygen ion, with the artificial method phase for obtaining negative oxygen ion
Than tourmaline releasing negative oxygen ion does not consume energy, and does not generate ozone and active oxygen, and soft decoration textile is made, and can improve indoor small
The air quality of environment is ideal green material.The mechanism of the permanent releasing negative oxygen ion of tourmaline has several solutions at present
It releases, one of them is attributed to electrolysis of the tourmaline to water:4H2O is electrolysed OH-+H+, and hydrogen ion is by between tourmaline electrode
Weak current in obtain electronics;2H++2e→H2↑, hydroxide ion forms air negative oxgyen ion with water molecules;OH-+
nH2O→OH-(H2O) for n according to this theory, the concentration of tourmaline releasing negative oxygen ion is related with its spontaneous polarization effect power,
Necessary condition is to contain moisture in air.
Two, negative oxygen ion powder
Negative oxygen ion powder is to pass through nanotechnology elaborate by natural material.Scientific investigations showed that negative oxygen ion powder
Energetic is kept to human body and has great help to the improvement of human residential environment.The characteristics of series of products is
Naturally, tasteless, nontoxic, have a safety feature.The effect of negative oxygen ion powder is as follows:
1. function occurs for permanent air negative oxgyen ion
In air gas molecule ionize mechanism, mainly by extraneous ionizer to gas act on as a result, ionizer has purple
Outside line, radioactive ray, photoelectric effect etc..Ingredient in negative oxygen ion powder has pyroelectricity and a piezoelectricity, thus have temperature and
(even if small variation) can cause the potential difference between ingredient crystal, this electrostatic to be up to 1,000,000 in the case of pressure change
Electron-volt, to make air ionize, that is hit is electronically attached to neighbouring water and oxygen molecule and it is made to be converted into
Negative aeroion, i.e. negative oxygen ion.
2. stronger far-infrared transmitting function
Ingredient in ion powder is the silicate material of aluminium characterized by boracic, sodium, iron, lithium cyclic structure, class matter
With as development, because of its pyroelectricity and piezoelectricity, its polar ion is made to be vibrated in equilbrium position and dipole moment variation is caused to generate far
The electromagnetic radiation of infrared band, if being added in product (such as fiber) by a certain percentage, make it through itself free ion,
Impurity ion and ionic substance, impurity and two, three phonon sympathetic responses generate radiation, affect it is organic interlink with inorganic molecule from
Sub-key polarity is vibrated, and stronger radiation broadband is formd, and is 90% or more to the emissivity of far infrared according to test anion powder.
The far infrared performance of anion powder mainly has the following aspects to the health care of human body and other effects:
1. far infrared can accelerate moisture movement, light water is made to become active water, to make the penetration of water, extension,
Dissolving power, metabolism power enhancing, and generate water conservation film.
2. far infrared can play expansion capillary for the circulatory system, enhance blood circulation, boost metabolism, increases
The effect of strong Lymphatic Circulation.
3. far infrared can make cell activation for cell tissue, so that old dead cell is drained or assign power of regeneration, can enhance
Cellular energy, the effects that enhancing the function and vigor of cell.
3. excellent antibiotic and sterilizing function
The negative oxygen ion generated in anion powder has higher activity, has very strong redox, can destroy
The cell membrane of bacterium or the activity of cellular plasm organized enzyme, to achieve the purpose that antibiotic and sterilizing.
4. purposes
(1) movement is that " is presented to the anion in purificationization negative aeroion powder in air;Z"Font.And it conveys
Negative electrical charge is to bacterium, dust, smoke particles and water droplet etc., this particle phase of charge and this is sunk in conjunction with ball is polymerized to, to reach
To the purpose of purification air.
(2) eliminate what the art work that foreign flavor indoors and various pernicious gases use in fitment process indoors evaporated
Leftovers leftovers acid smell in the irritative gas such as benzene, formaldehyde, ketone, ammonia and daily life, cigarette etc. to the harmful peculiar smell of people's sheet,
With wall cloth, curtain containing anion powder etc. or the coating containing anion powder, the negative aeroion of release can be effectively
It is eliminated.
(3) fabric that health-care effect is processed through negative-ion fiber such as clothes, sheet and the wallpaper of indoor decoration, carpet,
Or the coating etc. containing anion powder, all there is health care and environmentally friendly dual function, such as be made in automobile and knitted with negative-ion fiber
Object, can eliminate peculiar smell in automobile, and purification air, the excitement for adjusting driver's nervous system and holddown improve cerebral cortex
Function keeps the good state of mind.
(4) water process anion powder is added filtering material and is used for water dispenser filtration core, can kill bacterium in water, increase
Oxygen in water is made bathroom towel with negative-ion fiber or is used for bathroom water process, can accelerate moisture movement, make light water
Become active water.Increase energy, easily removes human body dirt, dispelling fatigue.Treated water is used for high-grade green plants room
Interior culture, can improve the survival rate of plant, and shorten the maturity period, be sprayed onto the blade face of flowers, and the freshness date of flowers can be made to extend
5-10 times.
5. the additive amount suggestion of anion powder, between 3-15%, this value can be adjusted flexibly according to the difference of product.
Therefore, the research and application of negative oxygen ion come into doctor U.S. and health field, and people are for rich negative oxygen ion sky
Between construction demand increase, however since the points such as the problems such as period of construction is long, cost is high and service life also counteract house
The marketing in front yard richness negative oxygen ion space.It is therefore desirable to invent a kind of preparation method it is simple, it is cheap and use the longevity
Order long negative oxygen ion generating device.
Invention content
To overcome prior art defect, present invention employs following technical schemes:
The present invention provides a kind of negative oxygen ions, and module occurs, which is characterized in that structure includes:Electric membranous layer (5), negative oxygen
Ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8);It is the electric membranous layer (5), negative
Oxonium ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8) are arranged in order;The negative oxygen
It is 4.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for ion3~1.0 × 106A/cm3。
Preferably, it is 2.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for the negative oxygen ion5~1.0 × 106
A/cm3;It is further preferred that it is 8.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for the negative oxygen ion5~1.0
×106A/cm3。
Preferably, module occurs for the negative oxygen ion, which is characterized in that structure further includes:Reflective film layer (4);Institute
It is the reflective film layer (4) stated, electric membranous layer (5), negative oxygen ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative
Oxonium ion coating (8) is arranged in order.
Preferably, module occurs for the negative oxygen ion, which is characterized in that concrete structure further includes:Film layer
(1), thermal insulation board layer (2), refractory heat-insulating cotton layer (3) and the identical interface (9) of power supply;The film layer (1), heat preservation
Plate layer (2), refractory heat-insulating cotton layer (3), reflective film layer (4), electric membranous layer (5), negative oxygen ion powder Aloe Vera Gel mixture layer
(6), negative oxygen ion brick layer (7), negative oxygen ion coating (8) are arranged in order, and the identical interface of power supply is set on negative oxygen ion coating (8)
(9)。
It is further preferred that the thermal insulation board is that (hereinafter referred to as XPS is kept the temperature extrusion moulding type polystyrene heat insulating board
Plate) or polyurethane thermal insulation board;
Preferably, the reflective film layer is made of upper, middle and lower-ranking, and upper layer is also constituted by three layers, be arranged in order for
Bidirectional stretching polypropylene film material layer (hereinafter referred to as BOPP material layers) (10), aluminium foil layer (11) and base fabric (12),
Middle level is ethene-vinyl acetate copolymer foamed cotton layer (hereinafter referred to as EVA foamed cottons layer) (13), and lower layer is also three-layer type knot
Structure is arranged in order as base fabric (12), aluminium foil layer (11) and BOPP material layers (10);
Preferably, after the negative oxygen ion powder Aloe Vera Gel mixture layer is sieved respectively by tourmaline powder and rare earth powder, with
Aloe Vera Gel is mixed in a certain ratio, and is then wrapped up heat-generating pipe and is made, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are
1:(50~500):(10~50);Preferably, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(100~
300):(10~30);It is further preferred that wherein, tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:250:20.
Preferably, the negative oxygen ion brick is mixed by tourmaline powder, rare earth powder with adhesive, at 1000~1500 DEG C
It fires, wherein tourmaline powder, rare earth powder, adhesive proportions are 1:(50~1000):(10~100);Preferably,
The tourmaline powder, rare earth powder, adhesive proportions are 1:(500~1000):(10~60);It is further preferred that institute
The tourmaline powder stated, rare earth powder, adhesive proportions are 1:600:30.
It is further preferred that firing temperature is 1250 DEG C;
It is further preferred that the adhesive is Aloe Vera Gel, clay or pulverized limestone;
Preferably, after the negative oxygen ion coating is sieved respectively by tourmaline powder and rare earth powder, with Aloe Vera Gel by certain
Ratio is mixed, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(50~500):(10~50);It is preferred that
, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(100~300):(10~30);It is further preferred that its
In, tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:250:20.
Preferably, the identical interface of the power supply is made of fine copper.
Preferably, module occurs for the negative oxygen ion, which is characterized in that a height of 100~200CM;It is further preferred that
A height of 120CM;
Preferably, module occurs for the negative oxygen ion, which is characterized in that width is 50~100CM;It is further preferred that
Width is 80CM.
The present invention also provides the preparation methods that module occurs for a kind of negative oxygen ion, which is characterized in that including:
Electric membranous layer (5), negative oxygen ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion is taken to apply
Layer (8), be arranged in order bonding to get;The negative oxygen ion occur the releasable negative oxygen ion number of module be 4.0 ×
103~1.0 × 106A/cm3。
Preferably, it is 2.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for the negative oxygen ion5~1.0 × 106
A/cm3;Preferably, it is 8.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for the negative oxygen ion5~1.0 × 106
A/cm3。
Preferably, the preparation method of module occurs for a kind of negative oxygen ion, which is characterized in that further includes:In electric heating
Reflective film layer (4) is set on film layer (5) adjacent position.
Preferably, the preparation method of module occurs for a kind of negative oxygen ion, which is characterized in that further includes:It is reflecting
Refractory heat-insulating cotton layer (3), thermal insulation board layer (2), film layer (1) are set gradually on film layer (4) adjacent position, are then existed
The identical interface (9) of power supply is set on negative oxygen ion coating (8).
It is further preferred that the thermal insulation board is XPS thermal insulation boards or polyurethane thermal insulation board.
Preferably, the reflective film layer is made of upper, middle and lower-ranking, and upper layer is also constituted by three layers, be arranged in order for
BOPP material layers (10), aluminium foil layer (11) and base fabric (12), middle level are EVA foamed cottons layer (13), and lower layer is also three-layer type
Structure is arranged in order as base fabric (12), aluminium foil layer (11) and BOPP material layers (10)
Preferably, the preparation of the negative oxygen ion powder Aloe Vera Gel mixture layer includes the following steps:By tourmaline powder and
It after rare earth powder is sieved respectively, is mixed in a certain ratio with Aloe Vera Gel, then wraps up heat-generating pipe and be made, wherein tourmaline powder, rare earth
Powder, Aloe Vera Gel proportions are 1:(50~500):(10~50);Preferably, wherein tourmaline powder, rare earth powder, Aloe Vera Gel three
Person's ratio is 1:(100~300):(10~30);It is further preferred that wherein, tourmaline powder, rare earth powder, Aloe Vera Gel three's ratio
Example is 1:250:20.
Preferably, the preparation of the negative oxygen ion brick includes the following steps:It is mixed by tourmaline powder, rare earth powder and adhesive
It closes, is fired at 1000~1500 DEG C;Wherein, tourmaline powder, rare earth powder, adhesive proportions are 1:(50~
1000):(10~100);Preferably, the tourmaline powder, rare earth powder, adhesive proportions are 1:(500~1000):
(10~60);It is further preferred that the tourmaline powder, rare earth powder, adhesive proportions be 1:600:30.
It is further preferred that firing temperature is 1250 DEG C.
It is further preferred that the adhesive is Aloe Vera Gel, clay or pulverized limestone.
Preferably, after the negative oxygen ion coating is sieved respectively by tourmaline powder and rare earth powder, with Aloe Vera Gel by certain
Ratio is mixed, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(50~500):(10~50);It is preferred that
, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(100~300):(10~30);It is further preferred that its
In, tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:250:20.
Preferably, the identical interface of the power supply is made of fine copper.
Preferably, module occurs for the negative oxygen ion, which is characterized in that a height of 100~200CM;It is further preferred that
A height of 120CM.
Preferably, module occurs for the negative oxygen ion, which is characterized in that width is 50~100CM;It is further preferred that
Width is 80CM.
A kind of negative oxygen ion generating device, which is characterized in that including a kind of keel installation structure, include aforementioned any
Module occurs for negative oxygen ion;
A kind of sweat steaming equipment, which is characterized in that including the heating equipment being located in a closing or hemi-closure space, Yi Jishe
Set the negative oxygen ion generating device in above-mentioned closing or hemi-closure space.
Advantageous effect
Compared with prior art, the present invention haing the following advantages:
The present invention is with simple in structure, cheap, easy for installation, purification efficiency is high, non-secondary pollution, energy conservation and environmental protection etc.
Advantage is capable of providing the negative oxygen ion for being beneficial to health.
Description of the drawings
Fig. 1 is the layer structure schematic diagram that module occurs for negative oxygen ion
Fig. 2 is that module side structure schematic view occurs for negative oxygen ion
Fig. 3 is the layer structure schematic diagram that inside modules reflective film layer occurs for negative oxygen ion
Fig. 4 is the side structure schematic view that inside modules reflective film layer occurs for negative oxygen ion
It is indicated in figure:1 is film layer, and 2 be thermal insulation board layer, and 3 be refractory heat-insulating cotton layer, and 4 be reflective film layer, 5
It is negative oxygen ion powder Aloe Vera Gel mixture layer for electric membranous layer, 6,7 be negative oxygen ion brick layer, and 8 be negative oxygen ion coating, and 9 be electricity
Source coincide interface, and 10 be BOPP material layers, and 11 be aluminium foil layer, and 12 be base fabric, and middle level 13 is EVA foamed cotton layers
Specific implementation mode
For a further understanding of the present invention, the present invention is further elaborated with below by embodiment combination attached drawing.
Embodiment 1
Referring to attached drawing 1, a kind of negative oxygen ion generation module, which is characterized in that its long 150CM, high 120CM, wide 80CM, tool
Body structure includes:Film layer (1), thermal insulation board layer (2), refractory heat-insulating cotton layer (3), reflective film layer (4), electric membranous layer
(5), negative oxygen ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8);The polyethylene
Film layer (1), thermal insulation board layer (2), refractory heat-insulating cotton layer (3), reflective film layer (4), electric membranous layer (5), negative oxygen ion powder reed
Luxuriant growth glue mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8) are arranged in order, and negative oxygen ion coating sets electricity on (8)
Source coincide interface (9);The thermal insulation board is XPS thermal insulation boards;The negative oxygen ion powder Aloe Vera Gel mixture layer stated is by tourmaline
It after powder and rare earth powder are sieved respectively, is mixed in a certain ratio with Aloe Vera Gel, then wraps up heat-generating pipe and be made, wherein tourmaline powder,
Rare earth powder, Aloe Vera Gel proportions are 1:250:20;The negative oxygen ion brick is mixed by tourmaline powder, rare earth with pulverized limestone,
It is fired at 1250 DEG C, wherein tourmaline powder, rare earth, pulverized limestone proportions are 1:600:30;The negative oxygen ion
It after coating is sieved respectively by tourmaline powder and rare earth powder, is mixed in a certain ratio and is made with Aloe Vera Gel, wherein is tourmaline powder, dilute
Native powder, Aloe Vera Gel proportions are 1:300:20;The identical interface of the power supply is made of fine copper.
Referring to attached drawing 2, the appearance that module occurs for the negative oxygen ion is illustrated, overlaying structure is arranged in order for multilayer material,
The identical interface (9) of power supply is set on negative oxygen ion coating (8).
Referring to attached drawing 3, the structural schematic diagram of reflective film layer.Reflective film layer is also and multilayer material is arranged in order superposition
It forms, is made of upper, middle and lower-ranking, upper layer is also constituted by three layers, is arranged in order as BOPP material layers (10), aluminium foil layer (11)
With base fabric (12), middle level is EVA foamed cottons layer (13), and lower layer is also three layers structure, is arranged in order as base fabric
(12), aluminium foil layer (11) and BOPP material layers (10).
After connecing electrical testing, inventing the negative oxygen ion module can be with releasing negative oxygen ion number:0.8×106~1.0 ×
106A/cm3。
Embodiment 2
Referring to attached drawing 1, a kind of negative oxygen ion generation module, which is characterized in that its long 100CM, high 120CM, wide 80CM, tool
Body structure includes:Film layer (1), thermal insulation board layer (2), refractory heat-insulating cotton layer (3), reflective film layer (4), electric membranous layer
(5), negative oxygen ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8);The polyethylene
Film layer (1), thermal insulation board layer (2), refractory heat-insulating cotton layer (3), reflective film layer (4), electric membranous layer (5), negative oxygen ion powder reed
Luxuriant growth glue mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8) are arranged in order, and negative oxygen ion coating sets electricity on (8)
Source coincide interface (9);The thermal insulation board is XPS thermal insulation boards;The negative oxygen ion powder Aloe Vera Gel mixture layer stated is by tourmaline
It after powder and rare earth powder are sieved respectively, is mixed in a certain ratio with Aloe Vera Gel, then wraps up heat-generating pipe and be made, wherein tourmaline powder,
Rare earth powder, Aloe Vera Gel proportions are 1:250:10;The negative oxygen ion brick is mixed by tourmaline powder, rare earth with Aloe Vera Gel,
It is fired at 1250 DEG C, wherein tourmaline powder, rare earth, Aloe Vera Gel proportions are 1:600:50;The negative oxygen ion
It after coating is sieved respectively by tourmaline powder and rare earth powder, is mixed in a certain ratio and is made with Aloe Vera Gel, wherein is tourmaline powder, dilute
Native powder, Aloe Vera Gel proportions are 1:300:30;The identical interface of the power supply is made of fine copper.
Referring to attached drawing 2, the appearance that module occurs for the negative oxygen ion is illustrated, overlaying structure is arranged in order for multilayer material,
The identical interface (9) of power supply is set on negative oxygen ion coating (8).
Referring to attached drawing 3, the structural schematic diagram of reflective film layer.Reflective film layer is also and multilayer material is arranged in order superposition
It forms, is made of upper, middle and lower-ranking, upper layer is also constituted by three layers, is arranged in order as BOPP material layers (10), aluminium foil layer (11)
With base fabric (12), middle level is EVA foamed cottons layer (13), and lower layer is also three layers structure, is arranged in order as base fabric
(12), aluminium foil layer (11) and BOPP material layers (10).
After connecing electrical testing, inventing the negative oxygen ion module can be with releasing negative oxygen ion number:0.6×106~0.8 ×
106A/cm3。
Embodiment 3
Referring to attached drawing 1, a kind of negative oxygen ion generation module, which is characterized in that its long 100CM, high 120CM, wide 80CM, tool
Body structure includes:Film layer (1), thermal insulation board layer (2), refractory heat-insulating cotton layer (3), reflective film layer (4), electric membranous layer
(5), negative oxygen ion powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8);The polyethylene
Film layer (1), thermal insulation board layer (2), refractory heat-insulating cotton layer (3), reflective film layer (4), electric membranous layer (5), negative oxygen ion powder reed
Luxuriant growth glue mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8) are arranged in order, and negative oxygen ion coating sets electricity on (8)
Source coincide interface (9);The thermal insulation board is XPS thermal insulation boards;The negative oxygen ion powder Aloe Vera Gel mixture layer stated is by tourmaline
It after powder and rare earth powder are sieved respectively, is mixed in a certain ratio with Aloe Vera Gel, then wraps up heat-generating pipe and be made, wherein tourmaline powder,
Rare earth powder, Aloe Vera Gel proportions are 1:250:20;The negative oxygen ion brick is mixed by tourmaline powder, rare earth with pulverized limestone,
It is fired at 1250 DEG C, wherein tourmaline powder, rare earth, pulverized limestone proportions are 1:600:20;The negative oxygen ion
It after coating is sieved respectively by tourmaline powder and rare earth powder, is mixed in a certain ratio and is made with Aloe Vera Gel, wherein is tourmaline powder, dilute
Native powder, Aloe Vera Gel proportions are 1:250:20;The identical interface of the power supply is made of fine copper.
Referring to attached drawing 2, the appearance that module occurs for the negative oxygen ion is illustrated, overlaying structure is arranged in order for multilayer material,
The identical interface (9) of power supply is set on negative oxygen ion coating (8).
Referring to attached drawing 3, the structural schematic diagram of reflective film layer.Reflective film layer is also and multilayer material is arranged in order superposition
It forms, is made of upper, middle and lower-ranking, upper layer is also constituted by three layers, is arranged in order as BOPP material layers (10), aluminium foil layer (11)
With base fabric (12), middle level is EVA foamed cottons layer (13), and lower layer is also three layers structure, is arranged in order as base fabric
(12), aluminium foil layer (11) and BOPP material layers (10).
After connecing electrical testing, inventing the negative oxygen ion module can be with releasing negative oxygen ion number:0.7×106~0.8 ×
106A/cm3。
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (10)
1. the preparation method of module occurs for a kind of negative oxygen ion, which is characterized in that step includes:Take electric membranous layer (5), negative oxygen from
Sub- powder Aloe Vera Gel mixture layer (6), negative oxygen ion brick layer (7), negative oxygen ion coating (8), be arranged in order bonding to get;
It is 4.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for the negative oxygen ion3~1.0 × 106A/cm3;Preferably, institute
It is 2.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for the negative oxygen ion stated5~1.0 × 106A/cm3;Further preferably
, it is 8.0 × 10 that the releasable negative oxygen ion number of module, which occurs, for the negative oxygen ion5~1.0 × 106A/cm3;Wherein,
The preparation of the negative oxygen ion powder Aloe Vera Gel mixture layer includes the following steps:It is sieved respectively by tourmaline powder and rare earth powder
Afterwards, it is mixed in a certain ratio and is made with Aloe Vera Gel, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(50~
500):(10~50);Preferably, in the negative oxygen ion powder Aloe Vera Gel mixture layer, tourmaline powder, rare earth powder, Aloe Vera Gel
Proportions are 1:(100~300):(10~30);It is further preferred that the negative oxygen ion powder Aloe Vera Gel mixture layer
In, tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:250:20;
The preparation of the negative oxygen ion brick includes the following steps:It is mixed with adhesive by tourmaline powder, rare earth powder, 1000~
It is fired at 1500 DEG C;Wherein, tourmaline powder, rare earth powder, adhesive proportions are 1:(50~1000):(10~100);
Preferably, in the negative oxygen ion powder Aloe Vera Gel mixture layer, tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:
(100~300):(10~30);It is tourmaline powder, dilute it is further preferred that in the negative oxygen ion powder Aloe Vera Gel mixture layer
Native powder, Aloe Vera Gel proportions are 1:250:20;
The preparation of the negative oxygen ion coating includes the following steps:After being sieved respectively by tourmaline powder and rare earth powder, with aloe
Glue, which is mixed in a certain ratio, to be made, wherein tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(50~500):(10~
50);Preferably, in the negative oxygen ion coating, tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:(100~300):
(10~30);It is further preferred that in the negative oxygen ion coating, tourmaline powder, rare earth powder, Aloe Vera Gel proportions are 1:
250:20.
2. preparation method according to claim 1, which is characterized in that step further includes:In electric membranous layer (5) adjacent position
Upper setting reflective film layer (4).
3. preparation method according to claim 2, which is characterized in that step further includes:In reflective film layer (4) adjacent bit
It sets and sets gradually refractory heat-insulating cotton layer (3), thermal insulation board layer (2), film layer (1), then in negative oxygen ion coating (8)
On set power supply coincide interface (9).
4. preparation method according to claim 1, which is characterized in that the firing temperature is 1250 DEG C.
5. preparation method according to claim 1, which is characterized in that the adhesive is Aloe Vera Gel, clay or lime
Powder.
6. preparation method according to claim 2, which is characterized in that the reflective film layer is by upper, middle and lower-ranking structure
At upper layer is also constituted by three layers, is arranged in order as bidirectional stretching polypropylene film material layer (10), aluminium foil layer (11) and woven cloth
Layer (12), middle level are ethene-vinyl acetate copolymer foamed cotton layer (13), and lower layer is also three layers structure, is arranged in order to compile
Nonwoven fabric layer (12), aluminium foil layer (11) and bidirectional stretching polypropylene film material layer (10).
7. preparation method according to claim 3, which is characterized in that the thermal insulation board is that extrusion moulding type polystyrene is heat-insulated
Thermal insulation board or polyurethane thermal insulation board.
8. preparation method according to claim 3, which is characterized in that the identical interface of the power supply is made of fine copper
's.
9. according to the preparation method described in claim 1~8 any one, which is characterized in that a height of the 100 of the module~
200CM;Preferably, a height of 120CM of the module.
10. according to the preparation method described in claim 1~8 any one, which is characterized in that the width of the module be 50~
100CM;Preferably, the width of the module is 80CM.