CN108677301A - A kind of cashmere flax complex yarn and preparation method thereof - Google Patents
A kind of cashmere flax complex yarn and preparation method thereof Download PDFInfo
- Publication number
- CN108677301A CN108677301A CN201810519658.1A CN201810519658A CN108677301A CN 108677301 A CN108677301 A CN 108677301A CN 201810519658 A CN201810519658 A CN 201810519658A CN 108677301 A CN108677301 A CN 108677301A
- Authority
- CN
- China
- Prior art keywords
- yarn
- cashmere
- flax
- single thread
- complex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of cashmere flax complex yarn of present invention offer and preparation method thereof, is related to textile technology field.A kind of production method of cashmere flax complex yarn, including：Cashmere single thread and flax single thread are subjected to doubling, using double twisting, yarn steaming, examine packet yarn.The production method carries out doubling, the texture of cashmere and the compound softness for remaining cashmere yarn of flax using cashmere single thread and flax single thread, while remaining the water suction water vapour permeability of linen thread and yarn again.The retractility of linen thread and yarn itself is poor, and cashmere yarn retractility is good, the compound resultant yarn of the two so that complex yarn has preferable telescopicing performance, expands the use scope of complex yarn.
Description
Technical field
The present invention relates to textile technology fields, and more particularly to a kind of cashmere flax complex yarn and preparation method thereof.
Background technology
Cashmere is a kind of fibrous material soft, warmth retention property is fabulous, but with the diversification of modern times dress, the production of summer cashmere
The lightweight of product；It is gradually decreased using cashmere in summer product；Therefore flax is this has absorbing sweat, good air permeability and to human body
The distinguishing features such as harmless, are increasingly paid attention to by the mankind.
There is flax recombination line at present, preparation method is by chemical fibre and flax be compound or chemical fibre and flax fiber
It is blended, do not include whole type of fibers merely with the few fibers in fiber in such product or method, and such product
Feel and pliability are poor, and wearability is poor.
Invention content
The purpose of the present invention is to provide a kind of production method of cashmere flax complex yarn, the production method technique letters
Single, controllability is strong, it can be achieved that large-scale processing produces.
Another object of the present invention is to provide above-mentioned cashmere flax complex yarn, which, which has, stretches
The characteristics of contracting is good, soft and moisture absorbing and sweat releasing.
The present invention solves its technical problem using following technical scheme to realize.
The present invention proposes a kind of production method of cashmere flax complex yarn, including：By cashmere single thread and flax single thread into
Row doubling using double twisting, yarn steaming, examines packet yarn.
The present invention proposes a kind of cashmere flax complex yarn, by the production method making of above-mentioned cashmere flax complex yarn
At.
The beneficial effects of the invention are as follows：
A kind of cashmere flax complex yarn provided by the invention and preparation method thereof, using cashmere single thread and flax single thread into
Row doubling, cashmere and the compound soft feel for remaining cashmere yarn of flax, while the moisture absorbing and sweat releasing of linen thread and yarn is remained again
Performance.The retractility of linen thread and yarn itself is poor, and cashmere yarn retractility is good, the compound resultant yarn of the two so that complex yarn has
There is preferable telescopicing performance, expands the use scope of complex yarn.Compared to stock yarn, resultant yarn is carried out after single thread is compound so that multiple
Yarns are more uniform, and various aspects of performance is more preferably.The production method controllability is strong, and complex yarn stability obtained is good, subsequently
Process on the performance of yarn without influence.
Specific implementation mode
It in order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below will be in the embodiment of the present invention
Technical solution be clearly and completely described.The person that is not specified actual conditions in embodiment, builds according to normal condition or manufacturer
The condition of view carries out.Reagents or instruments used without specified manufacturer is the conventional production that can be obtained by commercially available purchase
Product.
A kind of cashmere flax complex yarn of the embodiment of the present invention and preparation method thereof is specifically described below.
A kind of production method of cashmere flax complex yarn provided in an embodiment of the present invention, including：
Doubling is carried out using cashmere single thread and flax single thread, using double twisting, yarn steaming, examines packet yarn.
Further, in the preferred embodiment of the present invention, the doubling ratio of cashmere single thread and flax single thread is 1~2 strand：
1~2 strand.In existing complex yarn, the progress of generally use stock yarn is compound, compares stock yarn, carries out resultant yarn after single thread is compound, makes
Complex yarn it is more uniform, various aspects of performance is more preferably.Doubling is carried out using the number of share of stock so that cashmere yarn and linen thread and yarn are more
Stick on conjunction, remain the soft texture of cashmere yarn, while remaining the water suction water vapour permeability of linen thread and yarn again.Linen thread and yarn
The retractility of itself is poor, and cashmere yarn retractility is good, the compound resultant yarn of the two so that complex yarn has preferable retractility
Can, expand the use scope of complex yarn.It should be noted that the cashmere single thread that the present invention uses is 100% cashmere yarn
Or ratio containing suede is in 5~95% wool yarn.
Further, in the preferred embodiment of the present invention, the metric count N of cashmere single threadmIt is 14/1~80/1, flax
The metric count N of single threadmIt is 36/1~60/1.Under conditions of the number, the yarn retractility after doubling is preferable, more soft
Soft, moisture absorbing and sweat releasing property is more preferably.
Cashmere yarn and linen thread and yarn and and when, the tension of two kinds of yarns differs, cause and and effect it is bad, reduce and answer
The performance of yarns.The present invention uses the tension of the tension force yarn of 10~35cN so that the tension of two kinds of yarns more one
It causes.Preferably, tension when doubling is 10~25cN.When using Switzerland SSM doubling vehicles, tension force is used in 10~35cN
When Italian spinning doubling equipment, tension force is in 14~20cN.
After doubling, complete to twist by two-for-one twister.The metric count N of recombination line after double twistingmIt is 10/1~40/1, the twist
Be 120~600 twists/m, expansion and contraction be 3~20%, twist direction be " S " to.The recombination line has preferable stability.
After double twisting, yarn steaming is carried out using yarn steaming tank.
Complex yarn is put into yarn steaming tank, yarn steaming tank vacuum degree is then extracted into 210mbar, then be filled with into yarn steaming tank
90 DEG C of overheat saturated vapor makes the temperature in yarn steaming tank reach 85 DEG C, steams reciprocal of duty cycle and reaches 285mbar, then by slowly
Supplement steam achievees the effect that heat preservation 40 minutes, finally so that the steaming reciprocal of duty cycle of yarn steaming tank reaches 315mbar；Continuous saturation of taking out is steamed again
Vapour fills vacuum, achievees the effect that cooling 3 minutes, last yarn steaming terminates.
After yarn steaming, yarn defect is removed through examining, the yarn of 300~1000g is wound into using the machine of falling yarn.Further, at this
In the preferred embodiment of invention, when the yarn yarn count of cashmere single thread is in 26S/1 or less, by the molding Weight control of complex yarn
In every 800~900g of pipe, when the yarn yarn count of cashmere single thread is in 26S/1 or more, the molding Weight control of complex yarn is existed
Often 300~500g of pipe.
After resultant yarn, to cashmere flax complex yarn patch ticket packaging, so that later process uses.
The production method is compound using cashmere single thread and the progress of flax single thread, and simple for process, controllability is strong.Big rule can be achieved
Mould processes.
The present invention provides a kind of cashmere flax complex yarns, pass through the production method system of above-mentioned cashmere flax complex yarn
It is standby to form.Cashmere flax complex yarn function admirable, has the function of temperature adjustment, antibacterial, has soft texture, superior stretches
Malleability.Stability is good, and subsequent process is on the performance of yarn without influence.Using clothes made from cashmere flax complex yarn,
Profile docile body, while without constraint sense, body can be freely moved, and there is excellent dimensional stability and form to restore
Property, by repeatedly wearing or washing, dry, less deformation.With preferably moisture absorbing and sweat releasing performance so that skin is dry and comfortable, improves and relaxes
Appropriateness.
The feature and performance of the present invention are described in further detail with reference to embodiments.
Embodiment 1
A kind of cashmere flax complex yarn is present embodiments provided, is mainly made by following production method：
1 strand of cashmere single thread and 1 strand of flax single thread is used to carry out doubling under conditions of the tension of doubling vehicle is 26cN,
In, the metric count N of cashmere single threadmIt is 26/1, the metric count N of flax single threadmFor 48S/1.
After doubling, twisted by two-for-one twister then yarn steaming, examine packet yarn.The metric count of recombination line after double twisting
NmBe 17/1, the twist be 180 twists/m, expansion and contraction 12%, twist direction be " S " to.
After double twisting, yarn steaming is carried out using yarn steaming tank, examine and is wound into the yarn that every pipe molding weight is 800g.
Embodiment 2
A kind of cashmere flax complex yarn is present embodiments provided, is mainly made by following production method：
1 strand of cashmere single thread and 2 strands of flax single thread is used to carry out doubling under conditions of the tension of doubling vehicle is 28cN,
In, the metric count N of cashmere single threadmIt is 50/1, the metric count N of flax single threadmIt is 40/1.
After doubling, twisted by two-for-one twister then yarn steaming, examine packet yarn.The metric count of recombination line after double twisting
NmBe 14/1, the twist be 250 twists/m, expansion and contraction 15%, twist direction be " S " to.
After double twisting, yarn steaming is carried out using yarn steaming tank, examine and is wound into the yarn that every pipe molding weight is 300g.
Embodiment 3
A kind of cashmere flax complex yarn is present embodiments provided, is mainly made by following production method：
2 strands of cashmere single thread and 2 strands of flax single thread are used to carry out doubling under conditions of the tension of doubling vehicle is 30cN,
In, the metric count N of cashmere single threadmIt is 80/1, the metric count N of flax single threadmIt is 60/1.
After doubling, twisted by two-for-one twister then yarn steaming, examine packet yarn.The metric count of recombination line after double twisting
NmBe 17/1, the twist be 600 twists/m, expansion and contraction 14%, twist direction be " S " to.
After double twisting, yarn steaming is carried out using yarn steaming tank, examine and is wound into the yarn that every pipe molding weight is 500g.
Embodiment 4
A kind of cashmere flax complex yarn is present embodiments provided, is mainly made by following production method：
2 strands of cashmere single thread and 1 strand of flax single thread are used to carry out doubling under conditions of the tension of doubling vehicle is 20cN,
In, the metric count N of cashmere single threadmIt is 26/1, the metric count N of flax single threadmIt is 36/1.
After doubling, twisted by two-for-one twister then yarn steaming, examine packet yarn.The metric count of recombination line after double twisting
NmBe 10/1, the twist be 500 twists/m, expansion and contraction 20%, twist direction be " S " to.
After double twisting, yarn steaming is carried out using yarn steaming tank, examine and is wound into the yarn that every pipe molding weight is 1000g.
Comparative example 1
This comparative example provides a kind of cashmere flax complex yarn, is mainly made by following production method：
Cashmere stock yarn and flax stock yarn is used to carry out doubling under conditions of the tension of doubling vehicle is 35cN.
After doubling, complete to twist by two-for-one twister.
After double twisting, examines and be wound into the yarn that every pipe molding weight is 800g.
Comparative example 2
This comparative example provides a kind of cashmere flax complex yarn, is mainly made by following production method：
PPT fibers and flax stock yarn is used to carry out doubling under conditions of the tension of doubling vehicle is 30cN.
After doubling, complete to twist by two-for-one twister, the twist direction of the recombination line after double twisting be " S " to.
After double twisting, examines and be wound into yarn.
Comparative example 3
This comparative example provides a kind of cashmere flax complex yarn, is mainly made by following production method：
5 strands of cashmere single thread and 5 strands of flax single thread are used to carry out doubling under conditions of the tension of doubling vehicle is 55cN.
After doubling, complete to twist by two-for-one twister, the twist direction of the recombination line after double twisting be " S " to.
After double twisting, examines and be wound into yarn.
The cashmere flax complex yarn provided Examples 1 to 4 and comparative example 1~3 carries out performance detection, as a result such as table 1.
1 across comparison product effect of table
As shown in Table 1, Examples 1 to 4 provides the pliability of cashmere flax complex yarn, sucting wet air permeability and flexible
Property than comparative example 1, comparative example 2 and comparative example 3 provide cashmere flax complex yarn it is good, illustrate making side provided by the invention
Method is more scientific and reasonable, and the technique is compound using cashmere single thread and the progress of flax single thread, and obtained retractility is good, soft and moisture absorption is arranged
Cashmere flax complex yarn of sweat.
In conclusion the present invention carries out doubling using cashmere single thread and flax single thread, cashmere with flax is compound remains sheep
The soft texture of hair yarn, while the water suction water vapour permeability of linen thread and yarn is remained again.The retractility of linen thread and yarn itself compared with
Difference, and cashmere yarn retractility is good, the compound resultant yarn of the two so that complex yarn has preferable telescopicing performance, expands compound
The use scope of yarn.Compared to stock yarn, resultant yarn is carried out after single thread is compound so that complex yarn is more uniform, and various aspects of performance is more
It is good.The production method controllability is strong, and complex yarn stability obtained is good, and subsequent process is on the performance of yarn without influence.It should
Production method is simple for process, and controllability is strong, it can be achieved that large-scale processing produces.
Embodiments described above is a part of the embodiment of the present invention, instead of all the embodiments.The reality of the present invention
The detailed description for applying example is not intended to limit the range of claimed invention, but is merely representative of the selected implementation of the present invention
Example.Based on the embodiments of the present invention, those of ordinary skill in the art are obtained without creative efforts
Every other embodiment, shall fall within the protection scope of the present invention.
Claims (10)
1. a kind of production method of cashmere flax complex yarn, which is characterized in that including：Cashmere single thread and flax single thread are carried out
Doubling using double twisting, yarn steaming, examines packet yarn.
2. the production method of cashmere flax complex yarn according to claim 1, which is characterized in that the cashmere single thread with
The doubling ratio of flax single thread is 1~2 strand：1~2 strand.
3. the production method of cashmere flax complex yarn according to claim 1, which is characterized in that the cashmere single thread
Metric count NmIt is 14/1~80/1.
4. the production method of cashmere flax complex yarn according to claim 1 or 3, which is characterized in that described flax is single
The metric count N of yarnmIt is 36/1~60/1.
5. the production method of cashmere flax complex yarn according to claim 1, which is characterized in that cashmere list described in doubling
The tension of yarn and flax single thread is 10~35cN.
6. the production method of cashmere flax complex yarn according to claim 1, which is characterized in that the composite yarn after double twisting
The metric count N of linemBe 10/1~40/1, the twist be 120~600 twists/m, expansion and contraction be 3~20%, twist direction be " S " to.
7. the production method of cashmere flax complex yarn according to claim 1, which is characterized in that the method for the yarn steaming
Including：It will be put into yarn steaming tank by the complex yarn of double twisting, yarn steaming tank vacuum degree be extracted into 210mbar, is filled into yarn steaming tank
The overheat saturated vapor for entering 90 DEG C, make the temperature in yarn steaming tank reach 85 DEG C, steam reciprocal of duty cycle reach 285mbar, then by slow
Ground supplements steam insulation 40 minutes so that the steaming reciprocal of duty cycle of yarn steaming tank reaches 315mbar；Saturated vapor is continuously taken out again fills vacuum, it is cold
But 3 minutes, yarn steaming terminated.
8. the production method of cashmere flax complex yarn according to claim 1, which is characterized in that the inspection packet yarn
Method includes：Remove the complex yarn that yarn defect is wound into 300~1000g using the machine of falling yarn.
9. the production method of cashmere flax complex yarn according to claim 8, which is characterized in that when the cashmere single thread
Yarn yarn count in 26S/1 or less, by the molding Weight control of the complex yarn in every 800~900g of pipe, when the sheep
The yarn yarn count of suede single thread is in 26S/1 or more, by the molding Weight control of the complex yarn in every 300~500g of pipe.
10. a kind of cashmere flax complex yarn, which is characterized in that answered by cashmere flax as described in any one of claim 1 to 9
The production method of yarns is made.