CN108677044A - 一种高强度银饰品的加工方法 - Google Patents

一种高强度银饰品的加工方法 Download PDF

Info

Publication number
CN108677044A
CN108677044A CN201810458915.5A CN201810458915A CN108677044A CN 108677044 A CN108677044 A CN 108677044A CN 201810458915 A CN201810458915 A CN 201810458915A CN 108677044 A CN108677044 A CN 108677044A
Authority
CN
China
Prior art keywords
silver
alloy
high intensity
processing method
crucible
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810458915.5A
Other languages
English (en)
Inventor
侯彪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
In Leishan County Hong Yue Silver LLC
Original Assignee
In Leishan County Hong Yue Silver LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by In Leishan County Hong Yue Silver LLC filed Critical In Leishan County Hong Yue Silver LLC
Priority to CN201810458915.5A priority Critical patent/CN108677044A/zh
Publication of CN108677044A publication Critical patent/CN108677044A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度银饰品的加工方法，涉及银饰加工技术领域，主要是通过将银、镨、钇高温下熔化，再加入银继续熔化，制成金属条，再经激光雕刻而成，本发明方法加工的银饰品硬度高，耐硫化钠腐蚀。

Description

一种高强度银饰品的加工方法
技术领域
本发明涉及银饰加工技术领域，特别涉及一种高强度银饰品的加工方法。
背景技术
纯银以其优良的性能和较低价格优势，常用作饰品材料并受到消费者青睐。但纯银经过冷变形加工后，在常温存放数月，其机械强度和硬度均有明显下降，这种现象称作自然时效软化。经过试验发现这种软化程度，取决于纯银冷变形量和杂质的含量，为防止银饰品材料的自然时效软化人们研究了在银中添加铜、锆钛、镍及稀土元素以抑制银材的自然时效软化特性。
发明内容
为克服上述现有技术的缺陷，本发明提供一种高强度银饰品的加工方法，以提高银饰的硬度。
具体是通过以下技术方案得以实现的：
一种高强度银饰品的加工方法，包括如下步骤：
（1）以质量份计，取99.9份银、0.01份镨、0.01份钇配制稀土银合金在中频感应电路中用石墨坩埚于低温真空下融化，在炉膛内铸成 的圆柱形铸锭；
（2）将按质量比为1:1将上一步骤制得的圆柱形铸锭、银加入真空熔炼电磁搅拌合金连铸机的坩埚中，坩埚的材质为氮化硼，抽真空至4.0×10-1Pa以上，开始升温至1000-1100℃，待合金完全溶解，采用氮化硼搅拌棒搅拌8-10min，继续精炼20-30min，充入高纯Ar2至0.5MPa，开始采用间歇方式拉铸，形成宽度10-20mm、厚度3-5mm的银合金条；
（3）将银合金条按照饰品要求切割，然后在常规环境中采用功率为400-500W的激光在合金上雕刻出图案，打磨即得所述饰品；
进一步地，所述银的纯度为99.999%。
本发明的有益效果：
本发明中通过将银、镨、钇熔化成合金，再与银继续熔炼，提高合金分子间的均匀度，使得熔炼合金的强度和耐硫化钠腐蚀度提高。
具体实施方式
实施例1
一种高强度银饰品的加工方法，包括如下步骤：
（1）取99.9g银、0.01g镨、0.01g钇配制稀土银合金在中频感应电路中用石墨坩埚于低温真空下融化，在炉膛内铸成 的圆柱形铸锭；
（2）将上一步骤制得的圆柱形铸锭与99.92g银加入真空熔炼电磁搅拌合金连铸机的坩埚中，坩埚的材质为氮化硼，抽真空至4.0×10-1Pa以上，开始升温至1000℃，待合金完全溶解，采用氮化硼搅拌棒搅拌8min，继续精炼20min，充入高纯Ar2至0.5MPa，开始采用间歇方式拉铸，形成宽度10mm、厚度3mm的银合金条；
（3）将银合金条按照饰品要求切割，然后在常规环境中采用功率为400-的激光在合金上雕刻出图案，打磨即得所述饰品,所述银的纯度为99.999%。

Claims (2)

1.一种高强度银饰品的加工方法，其特征在于，包括如下步骤：
（1）以质量份计，取99.9份银、0.01份镨、0.01份钇配制稀土银合金在中频感应电路中用石墨坩埚于低温真空下融化，在炉膛内铸成 的圆柱形铸锭；
（2）将按质量比为1:1将上一步骤制得的圆柱形铸锭、银加入真空熔炼电磁搅拌合金连铸机的坩埚中，坩埚的材质为氮化硼，抽真空至4.0×10-1Pa以上，开始升温至1000-1100℃，待合金完全溶解，采用氮化硼搅拌棒搅拌8-10min，继续精炼20-30min，充入高纯Ar2至0.5MPa，开始采用间歇方式拉铸，形成宽度10-20mm、厚度3-5mm的银合金条；
（3）将银合金条按照饰品要求切割，然后在常规环境中采用功率为400-500W的激光在合金上雕刻出图案，打磨即得所述饰品。
2.根据权利要求1所述的高强度银饰品的加工方法，其特征在于，所述银的纯度为99.999%。
CN201810458915.5A 2018-05-15 2018-05-15 一种高强度银饰品的加工方法 Pending CN108677044A (zh)