CN108675757A - A kind of production method of immediately pottery craftwork - Google Patents

A kind of production method of immediately pottery craftwork Download PDF

Info

Publication number
CN108675757A
CN108675757A CN201810624379.1A CN201810624379A CN108675757A CN 108675757 A CN108675757 A CN 108675757A CN 201810624379 A CN201810624379 A CN 201810624379A CN 108675757 A CN108675757 A CN 108675757A
Authority
CN
China
Prior art keywords
parts
horse
head
craftwork
pottery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810624379.1A
Other languages
Chinese (zh)
Inventor
王现锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yuzhou City Is Jade Jun Co Ltd
Original Assignee
Yuzhou City Is Jade Jun Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yuzhou City Is Jade Jun Co Ltd filed Critical Yuzhou City Is Jade Jun Co Ltd
Priority to CN201810624379.1A priority Critical patent/CN108675757A/en
Publication of CN108675757A publication Critical patent/CN108675757A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of production methods of immediately pottery craftwork, include the following steps:Step 1, engraving model;Step 2 makes mold;Step 3 chooses clay;Step 4, slurrying;Step 5, injection forming;Step 6, dry;Step 7, biscuiting;Step 8, glazing;Step 9 is fired;The step 1, engraving model;Entire craftwork is divided into multiple portions to carve respectively, including head of the horse, Horse Neck, length, crupper, horse foreleg, horse back leg and horse hair, the Horse Neck are turned under, head of the horse is downward, and the mouth of head of the horse is in left front leg side;The clay includes following components:Kaolin 50 65,5 10 parts of alkaline earth, 35 parts of quartz, 8 12 parts of sandstone, 8 10 parts of lead powder, 8 10 parts of mullite, 12 parts of iron ore.Glaze-body bonding performance of the present invention is good, the high yield rate of pottery, and device shape and color can more embody the intention and artistic effect of works of the present invention.

Description

A kind of production method of immediately pottery craftwork
Technical field
The present invention relates to pottery technology field more particularly to a kind of production methods of immediately pottery craftwork.
Background technology
Pottery is known as first of Chinese " five big porcelain ", being the specialty of China Countermeasure In Yuzhou City of Henan Province, being mainly characterized by porcelain The color of device complicates, and changes the single colour glaze development grain of ancient times porcelain, has " of the same colour into kiln, kiln discharge ten thousand is color " etc. unique Characteristic is that other ceramics cannot achieve and compare.It is as shown in Figure 1 immediately, bow one's head to hang down neck, build be strong, tendon Grand reality, four limbs are slender effectively, it is contented to look perfectly relaxed, and are a technique value and the firing very high type of difficulty, glaze colours distribution Just right, horse gnaws forehoof and adhesion, the enamel formula of the prior art are difficult to reach artistic effect immediately, and kiln discharge cools down It easily cracks afterwards, yield rate is low.
Invention content
In view of this, the present invention provides a kind of production method of immediately pottery craftwork, glaze-body bonding performance is good, yield rate It is high.
To achieve the above object, the present invention uses following technical scheme:
A kind of production method of immediately pottery craftwork, includes the following steps:
Step 1, engraving model;Entire craftwork is divided into multiple portions to carve respectively, including head of the horse, Horse Neck, length, crupper, Horse foreleg, horse back leg and horse hair, the Horse Neck are turned under, and head of the horse is downward, and the mouth of head of the horse is in left front leg side;
Step 2 makes mold;Step 1 is carved into molding multiple portions and makes gypsum mold respectively;
Step 3 chooses clay;The clay includes following components:Kaolin 50-65,5-10 parts of alkaline earth, 3-5 parts of quartz, sand 8-12 parts of stone, 8-10 parts of lead powder, 8-10 parts of mullite, 1-2 parts of iron ore;
Step 4, slurrying;The clay of step 3 is carried out to coarse crushing first into sand shape or powdery, is then ground, is ground thin Degree is 230-250 mesh, and slurry is made in ball milling after adding water to mix;
Step 5, injection forming;Slurry is injected separately into each mold in step 2, and by multiple molds after slip casting The green body generated is solidified, is bonded together according to design requirement, by finishing, forms overall image;
Step 6, dry;The green body trimmed is dried at a temperature of 25-120 DEG C, the green body water content after drying is less than 3%;
Step 7, biscuiting;Green body is put into biscuit kiln, 5-6 hour is fired at a temperature of 900 DEG C -1000 DEG C;
Step 8, glazing;Surface first upper ground-coat enamel will be carried out after billet surface removal of impurities processing after biscuiting, be dried after glazing, Middle bottom not glazing;The ground-coat enamel includes:20-25 parts of melilite, white feldspar 8-12 parts, 10-15 parts of calcite, Copper Ores 3-5 Part, 3-5 parts of zinc chloride, 0.5-0.6 parts of barium carbonate, 1-2 parts of tin oxide, 5-7 parts of sodium silicate, 1-2 parts of sodium oxide molybdena, kieselguhr 3-5 Part;By brush finish glaze on the ground-coat enamel of the green body after drying, the overglaze includes 20-25 parts of quartz, 20-25 parts of dolomite, Fang Xie 5-6 parts of stone, 25-30 parts of manganese oxide, 1-2 parts of alkali stone, 1-2 parts of magnesia, 8-10 parts of aluminium oxide, 3-5 parts of iron oxide, cobalt oxide 5- 7 parts;The glaze of ground-coat enamel and overglaze is crushed respectively, is mixed, ball milling, it is 400-450 targeted fine powders to become fineness, is added Glaze slip is made after being stirred ball milling in water;When glazing, the moisture content of glaze slip is 50%;
Step 9 is fired;By after glazing and dry green body be put into kiln fired in 1320 DEG C -1350 DEG C of temperature it is 12-15 small When.
Beneficial effects of the present invention are:
The immediately pottery craftwork of the present invention bow one's head to hang down strong neck, build, the grand reality of tendon, four limbs it is slender it is strong, look perfectly relaxed from , glaze colours distribution is just right, is a technique value and the firing very high type of difficulty.The glaze-body bonding performance of the present invention It is good, while clay using the present invention, glaze and making step, the high yield rate of pottery, device shape and color can more embody this The intention and artistic effect of invention works.
Description of the drawings
Fig. 1 is a kind of structural schematic diagram of immediately pottery craftwork of the present invention.
In figure:1- head of the horses;2- Horse Necks;3- lengths;4- cruppers;5- horse hairs;6- horse back legs;7- horse forelegs.
Specific implementation mode
Technical solution in order to further illustrate the present invention illustrates the specific implementation mode of the present invention in conjunction with example;
Embodiment 1:
As shown in Figure 1, a kind of production method of immediately pottery craftwork, includes the following steps:
Step 1, engraving model;Entire craftwork is divided into multiple portions to carve respectively, including head of the horse 1, Horse Neck 2, length 3, horse Stern 4, horse foreleg 7, horse back leg 6 and horse hair 5, Horse Neck 2 are turned under, and head of the horse 1 is downward, the mouth of head of the horse 1 in left front leg side, not with Left front leg adhesion;
Step 2 makes mold;Step 1 is carved into molding multiple portions and makes gypsum mold respectively;
Step 3 chooses clay;The clay includes following components:Kaolin 50,5 parts of alkaline earth, 5 parts of quartz, 10 parts of sandstone, 10 parts of lead powder, 8 parts of mullite, 1 part of iron ore;
Step 4, slurrying;The clay of step 3 is carried out to coarse crushing first into sand shape or powdery, is then ground, is ground thin Degree is 230-250 mesh, and slurry is made in ball milling after adding water to mix;
Step 5, injection forming;Slurry is injected separately into each mold in step 2, and by multiple molds after slip casting The green body generated is solidified, is bonded together according to design requirement, by finishing, forms overall image;
Step 6, dry;The green body trimmed is dried at a temperature of 25 DEG C, the green body water content after drying is less than 3%;
Step 7, biscuiting;Green body is put into biscuit kiln, 5-6 hour is fired at a temperature of 900 DEG C;
Step 8, glazing;Surface first upper ground-coat enamel will be carried out after billet surface removal of impurities processing after biscuiting, be dried after glazing, Middle bottom not glazing;The ground-coat enamel includes:20 parts of melilite, 8 parts of white feldspar, 10 parts of calcite, 5 parts of Copper Ores, zinc chloride 5 Part, 0.5 part of barium carbonate, 1 part of tin oxide, 5 parts of sodium silicate, 1 part of sodium oxide molybdena, 3 parts of kieselguhr;It will be on the ground-coat enamel of the green body after drying Brush finish glaze, the overglaze include 20 parts of quartz, 20 parts of dolomite, 5 parts of calcite, 25 parts of manganese oxide, 2 parts of alkali stone, magnesia 1 Part, 10 parts of aluminium oxide, 5 parts of iron oxide, 5 parts of cobalt oxide;The glaze of ground-coat enamel and overglaze is crushed respectively, is mixed, ball milling makes It is 400-450 targeted fine powders that it, which becomes fineness, and glaze slip is made after adding water to be stirred ball milling;When glazing, the moisture content of glaze slip is 50%;
Step 9 is fired;It will be after glazing and temperature that dry green body is put into kiln at 1320 DEG C fires 12-15 hour.
Potassium oxide and sodium oxide molybdena are added in the glaze of invention, reduces the melting temperature and high temperature viscosity of glaze, improves glaze Chemical stability and thermal stability make glaze have good transparency and glossiness, and glaze-body bonding performance is good, while using this hair Bright clay, glaze and making step, the high yield rate of pottery, device shape and color can more embody works of the present invention intention and Artistic effect.In the above embodiment it should be noted that in main part glazing, it shall be guaranteed that the glazed thickness of glazing is little In 1 millimeter, to ensure to reduce the cracking of glaze layer, the artistic effect of this works is influenced.The present invention burnt out pulls up a horse color as blueness Coppery.
Embodiment 2:
As shown in Figure 1, a kind of production method of immediately pottery craftwork, includes the following steps:
Step 1, engraving model;Entire craftwork is divided into multiple portions to carve respectively, including head of the horse, Horse Neck, length, crupper, Horse foreleg, horse back leg and horse hair, the Horse Neck are turned under, and head of the horse is downward, and the mouth of head of the horse is in left front leg side;
Step 2 makes mold;Step 1 is carved into molding multiple portions and makes gypsum mold respectively;
Step 3 chooses clay;The clay includes following components:Kaolin 65,10 parts of alkaline earth, 5 parts of quartz, 8 parts of sandstone, 10 parts of lead powder, 8 parts of mullite, 2 parts of iron ore;
Step 4, slurrying;The clay of step 3 is carried out to coarse crushing first into sand shape or powdery, is then ground, is ground thin Degree is 230-250 mesh, and slurry is made in ball milling after adding water to mix;
Step 5, injection forming;Slurry is injected separately into each mold in step 2, and by multiple molds after slip casting The green body generated is solidified, is bonded together according to design requirement, by finishing, forms overall image;
Step 6, dry;The green body trimmed is dried at a temperature of 60 DEG C, the green body water content after drying is less than 3%;
Step 7, biscuiting;Green body is put into biscuit kiln, 5-6 hour is fired at a temperature of 900 DEG C -1000 DEG C;
Step 8, glazing;Surface first upper ground-coat enamel will be carried out after billet surface removal of impurities processing after biscuiting, be dried after glazing, Middle bottom not glazing;The ground-coat enamel includes:25 parts of melilite, 12 parts of white feldspar, 10 parts of calcite, 4 parts of Copper Ores, zinc chloride 3 Part, 0.5 part of barium carbonate, 2 parts of tin oxide, 6 parts of sodium silicate, 1 part of sodium oxide molybdena, 3 parts of kieselguhr;It will be on the ground-coat enamel of the green body after drying Brush finish glaze, the overglaze include 25 parts of quartz, 25 parts of dolomite, 5 parts of calcite, 25 parts of manganese oxide, 2 parts of alkali stone, magnesia 2 Part, 9 parts of aluminium oxide, 4 parts of iron oxide, 6 parts of cobalt oxide;The glaze of ground-coat enamel and overglaze is crushed respectively, is mixed, ball milling makes It is 400-450 targeted fine powders that it, which becomes fineness, and glaze slip is made after adding water to be stirred ball milling;When glazing, the moisture content of glaze slip is 50%;
Step 9 is fired;It will be after glazing and temperature that dry green body is put into kiln at 1350 DEG C fires 12-15 hour.
In the above embodiment it should be noted that in main part glazing, it shall be guaranteed that the glazed thickness of glazing is little In 1 millimeter, to ensure to reduce the cracking of glaze layer, the artistic effect of this works is influenced.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all the present invention spirit and Within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention.

Claims (1)

1. a kind of production method of immediately pottery craftwork, it is characterised in that:Include the following steps:Step 1, engraving model;Step Rapid 2, mold is made;Step 3 chooses clay;Step 4, slurrying;Step 5, injection forming;Step 6, dry;Step 7, biscuiting; Step 8, glazing;Step 9 is fired;Entire craftwork is divided into multiple portions and carved respectively by the step 1, including head of the horse, horse Neck, length, crupper, horse foreleg, horse back leg and horse hair, the Horse Neck are turned under, and head of the horse is downward, and the mouth of head of the horse is in left front leg one Side;The clay includes following components:Kaolin 50-65,5-10 parts of alkaline earth, 3-5 parts of quartz, 8-12 parts of sandstone, lead powder 8- 10 parts, 8-10 parts of mullite, 1-2 parts of iron ore.
CN201810624379.1A 2018-06-16 2018-06-16 A kind of production method of immediately pottery craftwork Withdrawn CN108675757A (en)