CN108659735A - A kind of low grammes per square metre adhesive for corrugated paperboard and its compounding method - Google Patents
A kind of low grammes per square metre adhesive for corrugated paperboard and its compounding method Download PDFInfo
- Publication number
- CN108659735A CN108659735A CN201710187747.6A CN201710187747A CN108659735A CN 108659735 A CN108659735 A CN 108659735A CN 201710187747 A CN201710187747 A CN 201710187747A CN 108659735 A CN108659735 A CN 108659735A
- Authority
- CN
- China
- Prior art keywords
- per square
- square metre
- grammes per
- adhesive
- corrugated paperboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of low grammes per square metre adhesive for corrugated paperboard and its compounding methods, it is with tapioca 250kg, borax 2.3kg, caustic soda 4.5kg, water 700kg, adhesive 4kg, bleeding agent 3kg, aluminum sulfate 2kg are assembled, and are made up of carrier tank, main body tank stirring copolymerization dissolving, time control.This product is especially bonded securely the high grammes per square metre watt paper of low grammes per square metre or grammes per square metre ＞ 400g/ ㎡, and cementability is superior, and another new product, new selection are provided for carton composite caking agent market.
Description
Technical field
The present invention relates to a kind of natural polymer adhesive, especially a kind of low grammes per square metre adhesive for corrugated paperboard and its prepare
Method.
Background technology
Currently, with the production of industrial products high speed and environmental protection requirement, with the glue that natural polymer is the polymerization of main base material
Stick is widely used, and has become the mainstream in food, drug and agricultural and sideline product packing case compound sticking.
Natural polymer adhesive applications, mostly use one-component at present or one-component polymerization is made.And based on tapioca starch
Raw material is wanted, the adhesive object grain size generated by auxiliary material polymerization is small, is evenly distributed, and has excellent quick-drying, tack, adapts to
Low grammes per square metre corrugated board bonding production needs.
For low grammes per square metre adhesive for corrugated paperboard compared with other natural one-components or one-component polymerization adhesive for paper box, prescription is skilful
It is wonderful, safe and simple to operation, especially the high grammes per square metre watt paper of low grammes per square metre or grammes per square metre ＞ 400g/ ㎡ is bonded securely, cementability is excellent
More, another new product, new selection are provided for carton composite caking agent market.
Invention content
The present invention uses tapioca 250kg, borax 2.3kg, caustic soda 4.5kg, water 700kg, adhesive 4kg, bleeding agent
3kg, aluminum sulfate 2kg are assembled, and are made up of carrier tank, main body tank stirring copolymerization dissolving, time control.
A kind of low grammes per square metre adhesive for corrugated paperboard and its compounding method of the present invention, it is characterised in that first by pure caustic soda
4.5/kg is pressed with water：10/kg prepares into aqueous slkali, then adds water 310/kg, rotation blender that 25/kg wood is added in carrier tank
Sweet potato starch stirs, then the aqueous slkali prepared is poured slowly into, and clinker is made in 15 minutes in stirring.
A kind of low grammes per square metre adhesive for corrugated paperboard and its compounding method of the present invention, it is characterised in that in main body tank
Add water 370/kg, rotation blender that 225/kg tapiocas are added and stir, adds adhesive 4/kg, stir 15 points
Carrier tank clinker is put into after clock, time control is put into and was completed at 10 minutes.
A kind of low grammes per square metre adhesive for corrugated paperboard and its compounding method of the present invention, it is characterised in that first by aluminum sulfate
2/kg is pressed with water：10/kg prepares into aluminum sulfate solution, and after carrier tank clinker is all put into main body tank, 3/kg bleeding agents are added
It is sufficiently stirred, then the aluminum sulfate solution prepared is poured into main body tank, 2.3/kg solids borax is slowly sprinkled by stirring after 2 minutes
In body barrel, stirring is made for 15 minutes.
The invention has the advantages that：
1, it uses using tapioca starch as primary raw material, the adhesive object grain size generated by auxiliary material polymerization is small, is evenly distributed, and has excellent
Different quick-drying, tack adapt to low grammes per square metre corrugated board bonding production needs；
2, it is widely used, low grammes per square metre adhesive for corrugated paperboard and its compounding method will provide a kind of completely new thinking, height for market
The product of effect；
3, prescription is ingenious, and compatibility is good and safe and reliable, is the low compound optimal bonding agent of grammes per square metre corrugated board, market application
Well, it has a extensive future.
Specific implementation mode
Pure caustic soda and water are first pressed 4.5/kg by embodiment by component：10/kg prepares into aqueous slkali, then in carrier tank
Add water 310/kg, rotation blender is added 25/kg tapiocas and stirs, then the aqueous slkali prepared is slowly fallen
Enter, clinker is made in 15 minutes in stirring.In main body tank plus water 370/kg, rotation blender are added 225/kg tapiocas and fully stir
It mixes uniformly, adds adhesive 4/kg, carrier tank clinker is put by stirring after 15 minutes, and it is complete at 10 minutes to be put into time control
At.Aluminum sulfate and water press 2/kg：10/kg prepares into aluminum sulfate solution, after carrier tank clinker is all put into main body tank, is added 3/
Kg bleeding agents are sufficiently stirred, then the aluminum sulfate solution prepared is poured into main body tank, by 2.3/kg solid boraxs after stirring 2 minutes
It is slowly sprinkled into body barrel, stirring is made for 15 minutes.
Claims (4)
1. a kind of low grammes per square metre adhesive for corrugated paperboard and its compounding method, it is characterised in that with tapioca 250kg, borax
2.3kg, caustic soda 4.5kg, water 700kg, adhesive 4kg, bleeding agent 3kg, aluminum sulfate 2kg are assembled, and are stirred by carrier tank, main body tank
Mix copolymerization dissolving, time control is made.
2. a kind of low grammes per square metre adhesive for corrugated paperboard according to claim 1 and its compounding method, it is characterised in that first will
Pure caustic soda and water press 4.5/kg：10/kg prepares into aqueous slkali, and water 310/kg, rotation blender is then added to be added in carrier tank
25/kg tapiocas stir, then the aqueous slkali prepared is poured slowly into, and clinker is made in 15 minutes in stirring.
3. a kind of low grammes per square metre adhesive for corrugated paperboard according to claim 1 and its compounding method, it is characterised in that in master
In body tank plus water 370/kg, rotation blender are added 225/kg tapiocas and stir, add adhesive 4/kg, stir
Carrier tank clinker is put into after mixing 15 minutes, time control is put into and was completed at 10 minutes.
4. a kind of low grammes per square metre adhesive for corrugated paperboard according to claim 1 and its compounding method, it is characterised in that first will
Aluminum sulfate and water press 2/kg：10/kg prepares into aluminum sulfate solution, and after carrier tank clinker is all put into main body tank, 3/kg is added
Bleeding agent is sufficiently stirred, then the aluminum sulfate solution prepared is poured into main body tank, after stirring 2 minutes that 2.3/kg solid boraxs is slow
Slowly it is sprinkled into body barrel, stirring is made for 15 minutes.