CN108658535A - Permeable pavement brick is mated formation with the permeable mortar of polymer - Google Patents
Permeable pavement brick is mated formation with the permeable mortar of polymer Download PDFInfo
- Publication number
- CN108658535A CN108658535A CN201810481582.8A CN201810481582A CN108658535A CN 108658535 A CN108658535 A CN 108658535A CN 201810481582 A CN201810481582 A CN 201810481582A CN 108658535 A CN108658535 A CN 108658535A
- Authority
- CN
- China
- Prior art keywords
- permeable
- mortar
- cement
- slurry
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of permeable pavement bricks to mat formation with the permeable mortar of polymer, is made of the raw material of following parts by weight：The high molecular polymer compound powder of 1 part of cement, 5 parts of aggregate and cement consumption 1 3%；Cement is 42.5 Portland cements of P.O；Aggregate is the basalt particle or quartz sand of 3 5mm of grain size；It is coated on the permeable mortar and dips in slurry, dipped in slurry and the modulation of 0.1% methylcellulose is mixed by 42.5 Portland cements of P.O.The present invention is with five parts of aggregates of a cement proportion, and the high molecular polymer compound powder for being doped with cement amount 1 3% is mixed evenly, so that the permeable mortar strength reaches M15 or more, and also there is the coefficient of permeability of 0.05cm/s or more, and carry out topical application in water-permeable brick bottom and dip in slurry, improve the caking property of permeable mortar and water-permeable brick；The modulation of 0.1% methylcellulose is mixed by 42.5 Portland cements of P.O by dipping in slurry, ensure that adhesive property is good and will not excessively reduce water permeability.
Description
Technical field
The present invention relates to technical field of building construction, more specifically, it relates to which a kind of permeable pavement brick is mated formation with polymerization
The permeable mortar of object.
Background technology
According to CJJ/T188-2012《Water-permeable brick pavement technique regulation》During screed-coat can be used in water-permeable brick pavement construction
Sand, coarse sand and dry cement mortar, but above-mentioned material is used in practice of construction, the water-permeable brick after mating formation is easy loosening or saturating
Water effect is undesirable.
Brick bottom is added completely to dip in sizing process using C15 pea gravel concretens in Beijing olympic park water-permeable brick pavement construction.Though
So make screed-coat than traditional middle sand, coarse sand and dry cement mortar and solves the problems, such as that water-permeable brick loosens to a certain extent, but
It is to considerably reduce the water permeability of water-permeable brick, overall effect is bad since cement mortar is completely dipped at brick bottom.
Accordingly, the present invention proposes a kind of permeable pavement brick and mats formation with the permeable mortar of polymer.
Invention content
It is an object of the invention to overcome above-mentioned deficiency in the prior art, a kind of permeable pavement brick is provided and is mated formation with polymerization
The permeable mortar of object, the permeable mortar use the permeable mortar of polymer, so that conventional cement mortar is modified, substantially increase caking property,
Water-retaining property and toughness form inierpeneirating network structure, strengthen bonding since two kinds of polymer and cement generate crosslinking copolymerization reaction
Ability.
In order to solve the above technical problems, the object of the present invention is achieved like this：A kind of permeable road according to the present invention
The permeable mortar of facing brick paving polymer, is made of the raw material of following parts by weight：1 part of cement, 5 parts of aggregate and cement consumption 1-3%
High molecular polymer compound powder.
The present invention is further arranged to：The cement is 42.5 Portland cements of P.O.
The present invention is further arranged to：The aggregate is the basalt particle or quartz sand of grain size 3-5mm.
The present invention is further arranged to：The high molecular polymer compound powder is ethylene-vinyl acetate copolymer, gathers
One or more compounds of vinyl alcohol, polyacrylamide.
The present invention is further arranged to：The permeable mortar, which is configured with, dips in slurry, dips in slurry by 42.5 Portland cements of P.O
Mix the modulation of 0.1% methylcellulose.
In conclusion the invention has the advantages that：Permeable pavement brick according to the present invention, which is mated formation, uses polymer
Permeable mortar with five parts of aggregates of a cement proportion, and is doped with cement by the mixing of cement and aggregate according to a certain percentage
The high molecular polymer compound powder of amount 1-3% is mixed evenly so that and the permeable mortar strength reaches M15 or more,
And also there is the coefficient of permeability of 0.05cm/s or more, and carry out part in water-permeable brick bottom and dip in slurry, keep it close with permeable mortar
Bonding, improves the caking property of permeable mortar and water-permeable brick；It dips in slurry and 0.1% methyl is mixed by 42.5 Portland cements of P.O
Cellulose is modulated, and ensure that adhesive property is good and will not excessively reduce water permeability, allomeric function is perfect, highly practical.
Specific implementation mode
With reference to preferred embodiment, the present invention is further described.
A kind of permeable pavement brick involved by the present embodiment is mated formation with the permeable mortar of polymer, by the raw material of following parts by weight
It is made：The high molecular polymer compound powder of 1 part of cement, 5 parts of aggregate and cement consumption 1-3%；The cement is that P.O 42.5 is general
Logical portland cement；The aggregate is the basalt particle or quartz sand of grain size 3-5mm；The high molecular polymer compound powder
For ethylene-vinyl acetate copolymer, one or more compounds of polyvinyl alcohol, polyacrylamide.
The permeable mortar of polymer has high viscosity compared with common dry cement mortar or pea gravel concreten and has preferably
Water-retaining property, due to polymer itself hydrophilic colloid characteristic and be formed by filling and the blocking effect of polymer film, formed
Mixture have and higher intensity and keep good workability in a longer period of time；Polymer mortar is than dry water
Cement mortar or pea gravel concreten, which are compared, preferable water penetration, and common dry cement mortar or pea gravel concreten are using continuous
The mixture of grading, preparation is more closely knit, it is difficult to ensure water penetration, and the aggregate that the permeable mortar of polymer uses is shaping aggregate,
Grain size is the basalt particle of 3-5m, and shaping aggregate shape is regular, and slurry package is more uniform, and the two is firmly bonded, and is interruption
The mix of grading, formation has good workability and generates continuous porosity, to ensure preferable water permeability and mat formation smooth
Degree.
Further, water-permeable brick bottom carries out part and dips in slurry, dips in slurry and is mixed by 42.5 Portland cements of P.O
0.1% methylcellulose is modulated, and the slurry that dips in of this method modulation has higher caking property, even if the area of slurry 15% is dipped in part,
Water-permeable brick can also be met the requirements with permeable mortar adhesive property, and will not be loosened.
By by a cement（42.5 Portland cements of P.O）Match five parts of aggregates（The basalt of grain size 3-5mm
Particle or quartz sand）, and the high molecular polymer compound powder for being doped with cement amount 1-3% is mixed evenly, and is matched in this way
The permeable mortar of polymer than going out, suitable depth control design effective drainage porosity 12%, not only ensure that intensity but also met in 3cm
Water permeability, water-permeable brick bottom carry out part and dip in slurry, water-permeable brick is bonded on permeable mortar screed-coat, both ensure that caking property
Can water permeability not be reduced excessively again.
The present invention with five parts of aggregates of a cement proportion, and is mixed by the mixing of cement and aggregate according to a certain percentage
It is mixed evenly with the high molecular polymer compound powder of cement amount 1-3% so that the permeable mortar strength reaches M15
Or more, and the also coefficient of permeability with 0.05cm/s or more, and carry out part in water-permeable brick bottom and dip in slurry so that with permeable sand
Close adhesion is starched, the caking property of permeable mortar and water-permeable brick is improved；Slurry is dipped in be mixed by 42.5 Portland cements of P.O
0.1% methylcellulose is modulated, and ensure that adhesive property is good and will not excessively reduce water permeability, allomeric function is perfect, practical
Property is strong.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be in the protection domain being defined in the patent claims.
Claims (5)
1. permeable pavement brick is mated formation with the permeable mortar of polymer, which is characterized in that be made of the raw material of following parts by weight：Cement 1
Part, the high molecular polymer compound powder of 5 parts of aggregate and cement consumption 1-3%.
2. permeable pavement brick according to claim 1 is mated formation with the permeable mortar of polymer, which is characterized in that the cement is
42.5 Portland cements of P.O.
3. permeable pavement brick according to claim 1 or 2 is mated formation with the permeable mortar of polymer, which is characterized in that the bone
Material is the basalt particle or quartz sand of grain size 3-5mm.
4. permeable pavement brick according to claim 3 is mated formation with the permeable mortar of polymer, which is characterized in that the macromolecule
Polymer compound powder agent is one or more compounds of ethylene-vinyl acetate copolymer, polyvinyl alcohol, polyacrylamide.
5. permeable pavement brick according to claim 1 is mated formation with the permeable mortar of polymer, which is characterized in that the permeable mortar
Upper be coated with dips in slurry, dips in slurry and mixes the modulation of 0.1% methylcellulose by 42.5 Portland cements of P.O.