CN108642411A - 一种铝合金板的制造方法 - Google Patents
一种铝合金板的制造方法 Download PDFInfo
- Publication number
- CN108642411A CN108642411A CN201810616772.6A CN201810616772A CN108642411A CN 108642411 A CN108642411 A CN 108642411A CN 201810616772 A CN201810616772 A CN 201810616772A CN 108642411 A CN108642411 A CN 108642411A
- Authority
- CN
- China
- Prior art keywords
- alloy plate
- aluminium alloy
- heat treatment
- manufacturing
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝合金板的制造方法，包括步骤：熔炼、铸造、均热化热处理、轧制和固溶处理，在所述固溶处理步骤中：加热到350‑400℃，加热时间为75分钟，然后冷却到20℃，冷却时间10分钟。本发明通过冷轧步骤得到的冷轧板可以通过连续气垫式热处理炉进行固溶处理，从而使得冷轧板中的作为金属间化合物尽可能多地固溶，以确保成形后的烘烤硬化性。
Description
技术领域
本发明涉及一种铝合金板材，尤其涉及一种铝合金板材的制造方法。
背景技术
汽车轻量化是当前汽车发展方向之一，尤其是汽车车身铝合金板材的应用正在快速发展，已经成为国际上汽车行业热切关注的重点。众所周知，汽车的外板如引擎盖、车门、车顶或后备箱盖等对材料的要求较高。一方面，在引擎盖和车门等大型覆盖件的成形加工中，必须确保零件的形状尺寸精度，还有良好的包边性和表面无皱痕等影响外观的缺陷。另一方面,汽车板材需要具有优异的烘烤硬化能力，即通过成形后的覆盖件在涂装烘烤处理时发生人工时效硬化导致屈服强度明显提高，从而确保具备较好的抗凹性。
目前，用于冲压成形的汽车用铝合金外板材主要两个牌号AA6016和AA6111，其主要通过在铝中添加镁元素和硅元素来实现强化。其中，AA6111铝合金中还添加了铜元素来增大合金的强度。通常，这些铝合金通过熔铸、热轧、冷轧和热处理工序制备成铝板卷，在汽车厂经冲压成形并喷漆后烘烤处理。因此，汽车用铝板不仅要求易于成形，而且烘烤后的强度需要大幅度提升以获得良好的抗凹性能。
发明内容
本发明的目的在于提供一种铝合金板的制造方法，包括步骤：熔炼、铸造、均热化热处理、轧制和固溶处理，其特征在于，在所述固溶处理步骤中：加热到350-400℃，加热时间为75分钟，然后冷却到20℃，冷却时间10分钟。
优选的，在所述均热化热处理步骤中：热处理温度为450-550℃，热处理时间为55分钟。
进一步的所述固溶的冷却方式为水冷加风冷。
固溶处理是本技术方案中的核心步骤，通过冷轧步骤得到的冷轧板可以通过连续气垫式热处理炉进行固溶处理，从而使得冷轧板中的作为金属间化合物尽可能多地固溶，以确保成形后的烘烤硬化性。
具体实施方式
下面将通过具体的实施例对本发明铝合金板材的其制造方法做进一步的解释和说明，然而，该解释和说明并不对本发明的技术方案构成不当限定。
实施例
步骤如下：
(1)熔炼；
(2)铸造；
(3)铣面；
(4)在加热炉中进行均热化热处理：热处理温度为450-550℃，热处理时间为55分周公；
(5)热轧；
(6)冷轧；
(7)固溶处理：加热到350-400℃，加热时间为75分钟，然后冷却到20℃，冷却时间10分钟，水冷加风冷。
通过冷轧步骤得到的冷轧板可以通过连续气垫式热处理炉进行固溶处理，从而使得冷轧板中的作为金属间化合物尽可能多地固溶，以确保成形后的烘烤硬化性。
需要注意的是，以上列举的仅为本发明的具体实施例，显然本发明不限于以上实施例，随之有着许多的类似变化。本领域的技术人员如果从本发明公开的内容直接导出或联想到的所有变形，均应属于本发明的保护范围。
Claims (3)
1.一种铝合金板的制造方法，包括步骤：熔炼、铸造、均热化热处理、轧制和固溶处理，其特征在于，在所述固溶处理步骤中：加热到350-400℃，加热时间为75分钟，然后冷却到20℃，冷却时间10分钟。
2.如权利要求1所述的铝合金板的制造方法，其特征在于，在所述均热化热处理步骤中：热处理温度为450-550℃，热处理时间为55分钟。
3.如权利要求1所述的铝合金板的制造方法，其特征在于，所述固溶的冷却方式为水冷加风冷。