CN108638732B - Method for manufacturing shell powder decorative picture - Google Patents
Method for manufacturing shell powder decorative picture Download PDFInfo
- Publication number
- CN108638732B CN108638732B CN201810525177.1A CN201810525177A CN108638732B CN 108638732 B CN108638732 B CN 108638732B CN 201810525177 A CN201810525177 A CN 201810525177A CN 108638732 B CN108638732 B CN 108638732B
- Authority
- CN
- China
- Prior art keywords
- shell powder
- decorative picture
- decorative
- manufacturing
- making
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a method for manufacturing a shell powder decorative picture, which belongs to the technical field of decorative engineering and comprises the steps of manufacturing a decorative picture paster, manufacturing a background surface and pasting the decorative picture paster to the background surface. The invention can use shell powder material to make multilayer decorative pictures with different styles, and solves the problem that the prior art can only brush and brush a single layer of decorative pictures and has monotonous decorative style; the shell powder can be used as a main material of the decorative picture, so that the decorative picture is high in environmental friendliness; the shell powder material is coated with the shell powder material by the shell powder coating process, so that the contact surface of the shell powder material and air is greatly increased, and toxic and harmful gases in the air can be more effectively adsorbed; meanwhile, because the shell powder material has air permeability, moisture in the wall can escape, and the shell powder material is not easy to peel off or damage; in addition, the invention has simple manufacturing steps, single material, convenient manufacture, short manufacturing period, dirt resistance and wear resistance of the manufactured decorative picture, can save a large amount of cost in the manufacturing and using processes, and has strong economical efficiency and convenient popularization and use.
Description
Technical Field
The invention belongs to the technical field of decoration engineering, and particularly relates to a method for manufacturing a shell powder decorative picture.
Background
Shell powder is a crushed powder of shell, 95% of which is calcium carbonate as a main component and a small amount of amino acids and polysaccharide substances. Can be used as high-grade materials for food, cosmetics and interior decoration, and is widely suitable for livestock and poultry feed, food calcium source additives, ornament processing, drying agents and the like. The shell powder biological coating is a new home decoration inner wall coating in recent years, is one of new applications of the shell powder, and is the most important advantage of natural environmental protection. In the existing decoration engineering, the shell powder material is adopted to decorate the wall, generally, the wall is coated with a single layer (namely, a decorative layer is coated and brushed), the coloring is single, and the decoration style is monotonous; some users can adopt wallpaper decoration outside the shell powder decoration layer, and as the wallpaper is made of organic materials, toxic and harmful gases can be released all the time in the using process, thus affecting the health of the users; meanwhile, the existing wall paint or wallpaper is easy to be wetted and peeled off, and the maintenance cost is high.
Disclosure of Invention
The invention aims to provide a method for manufacturing a shell powder decorative picture, which aims to solve the technical problem that the shell powder material in the prior art can only be coated in a single layer, so that the decorative style is monotonous.
In order to achieve the purpose, the invention adopts the technical scheme that: the shell powder decorative picture manufacturing method comprises the steps of manufacturing a decorative picture paster, manufacturing a background surface and pasting the decorative picture paster to the background surface; the step of manufacturing the decorative picture comprises the steps of S11, manufacturing a decorative picture sheet by adopting a shell powder material, and S12, engraving the decorative picture sheet to form a decorative picture patch; the step of manufacturing the background surface comprises the step of S21, priming, wherein a substrate material is uniformly coated on the backboard to form a priming layer; step S22, elastic coating, namely spraying the elastic coating material to the bottom layer by using a spraying device to form semisolid particles; s23, leveling, namely leveling the semi-solid particles after the elastic coating according to the required height, and drying to form an elastic coating; and step S24, polishing, namely polishing the smoothed back plate by using a polishing tool to form a background surface.
Further, in the method for manufacturing the shell powder decorative picture, the decorative picture patch comprises an auxiliary film and a base layer, and the step of manufacturing the decorative picture patch comprises: paving the auxiliary film, mixing the pigment in the base material, coating the base material on the auxiliary film base material to form a base layer, and drying for 0.5-1.5 h.
Further, in the method for manufacturing the shell powder decorative painting, the decorative painting sheet includes an auxiliary film, a color layer and a base layer, and the step of manufacturing the decorative painting sheet includes: spreading the auxiliary film, coating a color layer material on the auxiliary film to form a color layer, drying for 0.5-1.5 h, coating a base layer material on the color layer to form a base layer, and drying for 0.5-1.5 h.
Further, in the method for manufacturing the shell powder decorative picture, the color layer comprises 1 part by mass of shell powder, 0.6-1 part by mass of water and 0.01-0.1 part by mass of pigment.
Further, in the method for manufacturing the shell powder decorative picture, the material of the base layer comprises 1 part of shell powder and 0.6-1 part of water by mass.
Further, in the method for manufacturing the shell powder decorative picture, in the step of manufacturing the background surface, the substrate material comprises 1 part by mass of shell powder and 0.8-1.2 parts by mass of water.
Further, in the method for manufacturing the shell powder decorative picture, in the step of manufacturing the background surface, the elastic coating material comprises 1 part by mass of shell powder and 0.6-1 part by mass of water.
Further, in the method for manufacturing the shell powder decorative picture, in the step of manufacturing the background surface, the semisolid particles on the back plate after the elastic coating are leveled according to a preset height, and the semisolid particles are dried for 0.5 to 1.5 hours to form the elastic coating.
Further, in the method for manufacturing the shell powder decorative picture, the step of adhering the decorative picture to the background surface is to adhere the decorative picture patch to the background surface, and after the decorative picture patch is firmly adhered, the auxiliary film is removed.
Further, in the method for manufacturing the shell powder decorative picture, the step of adhering the decorative picture patch to the background surface includes coating an adhesive material on the outer side of the base layer of the decorative picture patch to form an adhesive layer, and adhering the decorative picture patch to the background surface; the bonding material comprises, by mass, 1 part of shell powder and 0.6-1 part of water.
The shell powder decorative picture manufacturing method provided by the invention has the beneficial effects that: compared with the prior art, the invention can use shell powder material to make multilayer decorative pictures with different styles, and solves the problem that the prior art can only brush single layer and has monotonous decorative style; the invention has simple manufacturing steps, single material, convenient manufacturing, short manufacturing period, dirt resistance and wear resistance of the manufactured decorative picture, saving a large amount of cost in the manufacturing and using processes, strong economy and convenient popularization and use.
Drawings
In order to more clearly illustrate the technical solutions in the embodiments of the present invention, the drawings needed to be used in the embodiments or the prior art descriptions will be briefly described below, and it is obvious that the drawings in the following description are only some embodiments of the present invention, and it is obvious for those skilled in the art to obtain other drawings based on these drawings without inventive exercise.
Fig. 1 is a schematic view of a method for making a shell powder decorative picture according to an embodiment of the present invention;
fig. 2 is a schematic cross-sectional structure view of a decorative picture manufactured by the method for manufacturing a shell powder decorative picture according to another embodiment of the present invention.
Wherein, in the figures, the respective reference numerals:
10-decorating the picture paster; 20-an adhesive layer; 30-an elastic coating; 40-priming coat; 50-a back plate.
Detailed Description
In order to make the technical problems, technical solutions and advantageous effects to be solved by the present invention more clearly apparent, the present invention is further described in detail below with reference to the accompanying drawings and embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
It will be understood that when an element is referred to as being "secured to" or "disposed on" another element, it can be directly on the other element or be indirectly on the other element. When an element is referred to as being "connected to" another element, it can be directly connected to the other element or be indirectly connected to the other element.
It will be understood that the terms "length," "width," "upper," "lower," "front," "rear," "left," "right," "vertical," "horizontal," "top," "bottom," "inner," "outer," and the like, as used herein, refer to an orientation or positional relationship indicated in the drawings that is solely for the purpose of facilitating the description and simplifying the description, and do not indicate or imply that the device or element being referred to must have a particular orientation, be constructed and operated in a particular orientation, and is therefore not to be construed as limiting the invention.
Furthermore, the terms "first", "second" and "first" are used for descriptive purposes only and are not to be construed as indicating or implying relative importance or implicitly indicating the number of technical features indicated. Thus, a feature defined as "first" or "second" may explicitly or implicitly include one or more of that feature. In the description of the present invention, "a plurality" means two or more unless specifically defined otherwise.
Referring to fig. 1 and fig. 2, a method for making a shell powder decorative painting according to the present invention will now be described. The manufacturing method of the shell powder decorative picture comprises the following steps: the method comprises the steps of manufacturing the decorative picture paster 10, manufacturing the background surface and pasting the decorative picture paster 10 on the background surface.
The steps of making the decorative picture comprise:
step S11, manufacturing decorative drawing sheets by using shell powder materials, wherein the sheets are whole materials, and a plurality of or a plurality of decorative drawing sheets can be manufactured according to different color and size requirements;
step S12, engraving the decorative painting sheet to form the decorative painting patch 10, wherein the engraving is to engrave the decorative painting sheet into a specific shape.
The method for manufacturing the background surface comprises the following steps:
step S21, priming, namely, uniformly coating the substrate material on the back plate 50 to form a priming layer 40, wherein the priming layer 40 can be used for changing the flatness and smoothness of the priming layer by using tools such as a trowel and the like according to requirements, and the back plate 50 refers to boards such as a wood board and a plywood and structural surfaces such as a wall surface and a roof;
step S22, performing elastic coating, namely spraying the elastic coating material onto the base layer 40 by using a spraying device to form semisolid particles, wherein the elastic coating material is taken out by air in the spraying device or extruded by the pressure of the spraying device to form pasty liquid drops, and the pasty semisolid particles are formed after the elastic coating material falls on the base layer 40;
step S23, leveling, namely leveling the semi-solid particles after the elastic coating according to the required height, and drying to form an elastic coating 30, wherein the required height refers to the distance between the top surface of the semi-solid particles and the bottom layer 40, the elastic coating 30 can be a layered structure formed by arranging the particles instead of a layered structure which can completely cover the bottom layer 40, and the drying refers to the process of drying and hardening in the air after the shell powder material is mixed with water;
step S24, polishing the smoothed back plate 50 with a polishing tool to form a background surface. The polishing function is to make the surface of the elastic coating 30 smoother and finer, so that the decorative painting paster 10 can be pasted more smoothly, and the decorative painting appearance is more attractive.
When the decorative picture is actually used, the decorative picture sheet can be manufactured in advance, engraving is carried out on the spot according to the actual situation, and at the moment, because a large engraving tool is inconvenient to use, manual engraving can be adopted, so that the spot manufacturing is favorable for reasonable layout, and the layout effect is good; in addition, the decorative drawing sheet can be manufactured in advance, a large engraving tool is adopted for engraving, and the next step is carried out on site, so that the engraved pattern is smooth in line and good in effect of the detail part. The decorative picture patches may be fabricated on site, but they are preferably fabricated in advance because the environment of the construction site is complicated and the decorative picture patches are easily damaged.
Compared with the prior art, the shell powder material can be used for manufacturing multi-layer decorative pictures with different styles, so that the problem that the shell powder material in the prior art can only be coated in a single layer and has a monotonous decorative style is solved; the decorative picture can adopt shell powder as a main material, organic materials and other non-environment-friendly materials can be completely omitted in the manufacturing process, or the number of the used non-environment-friendly materials is very small, and the finished decorative picture basically does not contain toxic and harmful substances and is strong in environment friendliness; moreover, the shell powder material can adsorb toxic and harmful gases in the air, and the contact surface between the shell powder material and the air is greatly increased by the elastic coating process, so that the toxic and harmful gases in the air can be more effectively adsorbed; meanwhile, because the shell powder material has air permeability, moisture in the wall can escape, and the shell powder material is not easy to peel off or damage; in addition, the invention has simple manufacturing steps, single material, convenient manufacture, short manufacturing period, dirt resistance and wear resistance of the manufactured decorative picture, can save a large amount of cost in the manufacturing and using processes, and has strong economical efficiency and convenient popularization and use.
Further, referring to fig. 1 and fig. 2, as a specific embodiment of the method for manufacturing the shell powder decorative painting provided by the present invention, the decorative painting patch includes an auxiliary film and a base layer, and the step of manufacturing the decorative painting patch includes: paving the auxiliary film, mixing the pigment in the base material, coating the base material on the auxiliary film base material to form a base layer, and drying for 0.5-1.5 h. The pigment used in this embodiment is preferably a low diffusivity pigment. The auxiliary film is preferably a smooth-surface inelastic film, can be a plastic film, can also be leather, and can also be a rubber lining cloth, the smooth surface is used for preventing the decorative painting patch from being adhered to the auxiliary film, and the inelastic surface is used for preventing the decorative painting patch from being torn.
Further, referring to fig. 1 and fig. 2, as an embodiment of the method for manufacturing the shell powder decorative painting provided by the present invention, the decorative painting sheet includes an auxiliary film, a color layer and a base layer, and the step of manufacturing the decorative painting sheet includes: spreading the auxiliary film, coating a color layer material on the auxiliary film to form a color layer, drying for 0.5-1.5 h, coating a base layer material on the color layer to form a base layer, and drying for 0.5-1.5 h. The base layer is arranged independently mainly for preventing the pigment in the color layer from diffusing to the background surface, which causes the aesthetic property of the decorative picture to be reduced and the quality to be poor.
Further, as a specific implementation mode of the manufacturing method of the shell powder decorative painting provided by the invention, in order to achieve the effect that the material of the color layer is convenient to coat and can be dried quickly, the material of the color layer comprises, by mass, 1 part of shell powder, 0.6-1 part of water and 0.01-0.1 part of pigment. The specific parts by mass referred to herein are parts by mass that are proportioned under common construction conditions, and the proportioning can be appropriately changed under the conditions of large changes in ambient humidity, temperature, carbon dioxide concentration in air, and the like. The mass part of the pigment may be appropriately adjusted depending on the nature of the pigment and the desired color effect, and is not necessarily strictly added in the above mass part.
Further, as a specific implementation mode of the manufacturing method of the shell powder decorative painting provided by the invention, in order to achieve the effects that the material of the base layer is convenient to coat and can be quickly dried, the material of the base layer comprises 1 part of shell powder and 0.6-1 part of water by mass.
Further, as a specific implementation manner of the method for manufacturing the shell powder decorative picture provided by the invention, in the step of manufacturing the background surface, in order to achieve the effects that the substrate material is convenient to coat and can be quickly dried, the substrate material comprises 1 part by mass of shell powder and 0.8-1.2 parts by mass of water.
Further, as a specific implementation manner of the method for manufacturing the shell powder decorative picture provided by the invention, in the step of manufacturing the background surface, the elastic coating material comprises 1 part by mass of the shell powder and 0.6-1 part by mass of water, and the viscosity of the elastic coating material is higher than that of the substrate material, so that the strength of the elastic coating material is ensured, and a better effect is achieved during leveling.
Further, as a specific embodiment of the method for making the shell powder decorative painting provided by the present invention, in the step of making the background surface, the semisolid particles on the back plate 50 after the elastic coating are leveled according to a preset height, and the elastic coating 30 is formed after the semisolid particles are dried for 0.5h to 1.5 h.
Further, as a specific implementation manner of the manufacturing method of the shell powder decorative painting provided by the invention, the step of adhering the decorative painting to the background surface is to adhere the decorative painting patch 10 to the background surface, and after the decorative painting patch 10 is firmly adhered, the auxiliary film is removed.
Further, as a specific implementation manner of the manufacturing method of the shell powder decorative painting provided by the invention, the step of adhering the decorative painting patch 10 to the background surface includes coating an adhesive material on the outer side of the base layer of the decorative painting patch 10 to form an adhesive layer 20, and then adhering the decorative painting patch 10 to the background surface; the bonding material comprises, by mass, 1 part of shell powder and 0.6-1 part of water.
In one embodiment of the present invention, the specific steps are as follows.
Manufacturing a decorative picture paster 10: spreading an auxiliary film, mixing 1 part of shell powder, 0.8 part of water and 0.02 part of pigment, coating the mixture on the auxiliary film until the mixture is dried for 1 hour, wherein the color layer is slightly dry and hard, mixing 1 part of shell powder and 0.8 part of water, coating the mixture on the color layer until the mixture is dried for 1 hour, wherein the base layer is basically dry and hard, and forming the decorative drawing sheet. And engraving the decorative picture sheet to form a piece of decorative picture patch 10.
Preparing a background surface: when the color layer is to be dried, 1 part of shell powder and 1 part of water are mixed and coated on the wall surface to form the priming layer 40, and at the moment, the priming layer can be dried or dried within 1h, namely, the priming layer 40 ensures that the priming layer is not dried and hard. Then mixing 1 part of shell powder and 0.8 part of water into an elastic coating material, filling the elastic coating material into a spraying device such as a pneumatic spraying pot and spraying the elastic coating material onto the primed wall surface, then troweling semisolid particles which are elastically coated on the wall surface according to the required height by using a trowel, drying the trowel for 1 hour to form an elastic coating layer 30, and then polishing the elastic coating layer 30 by using a polishing tool such as sand paper and the like according to the requirement to form a background surface.
Finally, 1 part of shell powder and 0.7 part of water are mixed and coated on the outer side of the base layer of the decorative picture patch 10 to form an adhesive layer. Or the shell powder can be pasted on the outer side of the base layer by using the non-setting adhesive to form a bonding layer. And then, pasting the decorative picture paster 10 on the background surface, after drying for 0.5h, basically and firmly bonding the bonding layer, and tearing off the auxiliary film of the decorative picture paster 10.
The shell powder decorative picture manufactured by the method is detected in a formaldehyde adsorption experiment box, so that the concentration of formaldehyde in the experiment box can be controlled from 0.2mg/m3To 0.07mg/m3The adsorption effect is obvious.
The invention mainly introduces a method for manufacturing shell powder decorative pictures on wall surfaces, but the protection scope of the invention is not limited to the method, the shell powder decorative pictures can be manufactured on some back plates 50, such as gypsum plates, wood plates and cement plates, the shell powder decorative pictures manufactured on the back plates 50 can be directly fixed on the wall surfaces to be used as part of the wall bodies, and can also be used as wall hanging decoration after being mounted.
The present invention is not limited to the above preferred embodiments, and any modifications, equivalent substitutions and improvements made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (8)
1. A method for making shell powder decorative picture is characterized by comprising
A step of manufacturing a decorative picture paster,
a step of manufacturing a background surface, wherein,
pasting the decorative picture paster to a background surface;
the step of making the decorative picture comprises
Step S11, manufacturing a decorative drawing sheet by adopting shell powder material,
step S12, engraving the decorative picture sheet to form a decorative picture patch;
the step of making the background surface comprises
Step S21, priming, namely uniformly coating a substrate material on a backboard to form a priming layer, wherein the substrate material comprises 1 part by mass of shell powder and 0.8-1.2 parts by mass of water;
step S22, performing elastic coating, namely spraying an elastic coating material onto the bottom layer by using a spraying device to form semisolid particles, wherein the elastic coating material comprises 1 part by mass of shell powder and 0.6-1 part by mass of water;
s23, leveling, namely leveling the semi-solid particles after the elastic coating according to the required height, and drying to form an elastic coating;
and step S24, polishing, namely polishing the smoothed back plate by using a polishing tool to form a background surface.
2. The method for making the shell powder decorative picture according to claim 1, wherein the decorative picture patch comprises an auxiliary film and a base layer, and the step of making the decorative picture patch comprises: paving the auxiliary film, mixing the pigment in the base material, coating the base material on the auxiliary film base material to form a base layer, and drying for 0.5-1.5 h.
3. The method for making the shell powder decorative picture according to claim 1, wherein the decorative picture sheet comprises an auxiliary film, a color layer and a base layer, and the step of making the decorative picture sheet comprises: spreading the auxiliary film, coating a color layer material on the auxiliary film to form a color layer, drying for 0.5-1.5 h, coating a base layer material on the color layer to form a base layer, and drying for 0.5-1.5 h.
4. The method for making the shell powder decorative picture according to claim 3, wherein the color layer comprises 1 part of shell powder, 0.6-1 part of water and 0.01-0.1 part of pigment in parts by mass.
5. The method for making the shell powder decorative picture as claimed in claim 2 or 3, wherein the material of the base layer comprises 1 part of shell powder and 0.6-1 part of water by mass.
6. The method for making the shell powder decorative picture according to claim 1, wherein in the step of making the background surface, the semisolid particles on the back plate after the elastic coating are leveled according to a preset height and dried for 0.5h to 1.5h to form the elastic coating.
7. The method for making the shell powder decorative picture according to claim 2 or 3, wherein the step of adhering the decorative picture to the background surface is to adhere the decorative picture patch to the background surface, and remove the auxiliary film after the decorative picture patch is firmly adhered.
8. The method for making the shell powder decorative picture as claimed in claim 7, wherein the step of pasting the decorative picture patch on the background surface comprises
Coating the adhesive material on the outer side of the base layer of the decorative picture paster to form an adhesive layer, and then adhering the decorative picture paster to the background surface;
the bonding material comprises, by mass, 1 part of shell powder and 0.6-1 part of water.