CN108610009A - 一种达摩哺雀钧瓷工艺品的制作方法 - Google Patents
一种达摩哺雀钧瓷工艺品的制作方法 Download PDFInfo
- Publication number
- CN108610009A CN108610009A CN201810624405.0A CN201810624405A CN108610009A CN 108610009 A CN108610009 A CN 108610009A CN 201810624405 A CN201810624405 A CN 201810624405A CN 108610009 A CN108610009 A CN 108610009A
- Authority
- CN
- China
- Prior art keywords
- sparrow
- alms bowl
- hands
- clay
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种达摩哺雀钧瓷工艺品的制作方法,包括以下步骤,步骤1、雕刻模型;将整个工艺品分为多个部分分别雕刻,包括头部、双手部、主体部、麻雀、钵盂、底座、眉毛和胡子,其中主体部站立着,双手部平抬,右手半握左手,双手部捧着钵盂,钵盂上站着一只麻雀,右臂上散落着两只麻雀;步骤2、制作模具;步骤3、选取陶土;步骤4、制浆;步骤5、注浆成型;步骤6、干燥;步骤7、素烧;步骤8、施釉;步骤9、烧制;所述的步骤4是将步骤3的陶土首先进行粗碎成沙粒状或粉状,然后进行磨碎,其磨碎为230‑250目,加水混合后球磨,制成浆料,本发明坯釉结合性能好,钧瓷的成品率高,其器形及颜色更能体现本发明作品的创意和艺术效果。
Description
技术领域
本发明涉及钧瓷工艺领域,具体涉及一种达摩哺雀钧瓷工艺品的制作方法。
背景技术
陶瓷是中华文化的重要组成部分之一,而钧瓷又是中华陶瓷文化中的一颗璀璨明珠。钧瓷发源于东汉,是宋代五大名窑瓷器之一,是传统制瓷工艺中的珍品,以独特的窑变艺术而著称于世,素有“黄金有价钧无价”和“家有万贯,不如钧瓷一片”的美誉。钧瓷被誉为中国“五大名瓷”之首,为我国河南省禹州市的特产,其主要特征为瓷器的颜色复杂化,改变了古代瓷器的单色釉发展脉络,具有“进窑一色,出窑万彩”等独特的特色,本作品的设计思想是以大雪封山鸟儿难以觅食,达摩双手捧盛满谷粒的钵端立在雪中,须眉皆白,两只雀儿饱餐后与达摩嬉语,另一只还在啄食。达摩的大慈大悲、善良智慧以及万物有灵的和谐之美,通过钧瓷被表现得淋漓尽致。由于钧瓷制作工艺方法步骤多,在制作过程中稍微有点瑕疵就造成报废。
发明内容
有鉴于此,本发明提供一种达摩哺雀钧瓷工艺品的制作方法,坯釉结合性能好,成品率高。
一种达摩哺雀钧瓷工艺品的制作方法,包括以下步骤:
步骤1、雕刻模型;将整个工艺品分为多个部分分别雕刻,包括头部、双手部、主体部、麻雀、钵盂、底座、眉毛和胡子,其中主体部站立着,双手部平抬,右手半握左手,双手部捧着钵盂,钵盂上站着一只麻雀,右臂上散落着两只麻雀,眉毛和胡子为白色。
步骤2、制作模具;将步骤1雕刻成型的多个部分分别制作石膏模具。
步骤3、选取陶土;主体陶土包括以下部分组成:高岭土70-75%,砂石6-10%,铅粉8-12%,莫来石8-12%,铁矿石1-2%,氧化钴0.2-0.4%,食用碱0.3-0.5%,眉毛和胡子陶土组成:苏州土30%;黑毛土30%;白长石20%;石英20%。
步骤4、制浆;将步骤3的陶土首先进行粗碎成沙粒状或粉状,然后进行磨碎,其磨碎为230-250目,加水混合后球磨,制成浆料。
步骤5、注浆成型;将浆料分别注入步骤2中的各个模具中,并将多个模具内经过注浆后凝固生产的坯体,按照设计要求粘接在一起,经过修整,形成整体形象。
步骤6、干燥;将修整好的坯体在25-120℃温度下进行干燥,干燥后的坯体含水量低于3%。
步骤7、素烧;将坯体放入素烧窑中,在900℃-1000℃的温度下烧制5-6个小时。
步骤8、施釉;将素烧后的坯体表面除杂处理后进行表面涂釉材,其中面部、双手部不施釉,主体部分采用刷釉或者喷釉或者蘸釉的方法进行施釉;釉料是将包括黄长石55-60%,白长石8-12%,方解石8-11%,铜矿石3-5%,氯化锌3-5%,碳酸钡0.1-0.4%,氧化锡0.1-0.8%,三氧化二铁3-6%,氧化钾1-5%,氧化钠0.5-1%,木节土3-8%的釉料进行粉碎,混合,球磨,使其成为细度为400-450目的细粉,加水搅拌混合球磨后制成釉浆。
步骤9、烧制;将施釉后并干燥的坯体放入窑中在1280℃-1300℃的温度烧制12-15个小时。
本发明的有益效果为:
1、本发明的釉料中加入氧化钾和氧化钠,降低了釉的熔融温度和高温粘度,改善釉的化学稳定性和热稳定性,使釉具有良好的透明度和光泽度,坯釉结合性能好,同时采用本发明的陶土、釉料及制作步骤,钧瓷的成品率高,其器形及颜色更能体现本发明作品的创意和艺术效果。
2、本发明的胡子和眉毛所用的陶土为:苏州土30%;黑毛土30%;白长石20%;石英20%,烧制后眉毛和胡子为白色,突出表现达摩哺雀的慈悲胸怀。
附图说明
图1为本发明的结构示意图;
头部1;眉毛2;胡子3;麻雀4;双手部5;钵盂6;主体7;底座8。
具体实施方式
下面结合附图及实施例对本发明作进一步的详细说明。
实施例1
如图1所示,一种大漠哺雀钧瓷工艺品的制作方法,包括以下步骤:
步骤1、雕刻模型;将整个工艺品分为多个部分分别雕刻,包括头部、双手部5、主体7部、麻雀4、钵盂6、底座8、眉毛2和胡子3,其中主体7部站立着,双手部5平抬,右手半握左手,双手部5捧着钵盂6,钵盂6上站着一只麻雀4,右臂上散落着两只麻雀4,眉毛2和胡子3为白色。
步骤2、制作磨具;将步骤1雕刻成型的多个部分分别制作石膏模具。
步骤3、选取陶土;主体7陶土包括以下部分组成:高岭土70-75%,砂石6-10%,铅粉8-12%,莫来石8-12%,铁矿石1-2%,氧化钴0.2-0.4%,食用碱0.3-0.5%,眉毛2和胡子3陶土组成:苏州土30%;黑毛土30%;白长石20%;石英20%。
步骤4、制浆;将步骤3的陶土首先进行粗碎成沙粒状或粉状,然后进行磨碎,其磨碎为230-250目,加水混合后球磨,制成浆料。
步骤5、注浆成型;将浆料分别注入步骤2中的各个模具中,并将多个模具内经过注浆后凝固生产的坯体,按照设计要求粘接在一起,经过修整,形成整体形象。
步骤6、干燥;将修整好的坯体在25-120℃温度下进行干燥,干燥后的坯体含水量低于3%。
步骤7、素烧;将坯体放入素烧窑中,在900℃-1000℃的温度下烧制5-6个小时。
步骤8、施釉;将素烧后的坯体表面除杂处理后进行表面涂釉材,其中面部、双手部5及底座8不施釉,主体7部分采用刷釉或者喷釉或者蘸釉的方法进行施釉;釉料是将包括黄长石55-60%,白长石8-12%,方解石8-11%,铜矿石3-5%,氯化锌3-5%,碳酸钡0.1-0.4%,氧化锡0.1-0.8%,三氧化二铁3-6%,氧化钾1-5%,氧化钠0.5-1%,木节土3-8%的釉料进行粉碎,混合,球磨,使其成为细度为400-450目的细粉,加水搅拌混合球磨后制成釉浆。
步骤9、烧制;将施釉后并干燥的坯体放入窑中在1280℃-1300℃的温度烧制12-15个小时。本发明的釉料中加入氧化钾和氧化钠,降低了釉的熔融温度和高温粘度,改善釉的化学稳定性和热稳定性,使釉具有良好的透明度和光泽度,坯釉结合性能好,同时采用本发明的陶土、釉料及制作步骤,钧瓷的成品率高,其器形及颜色更能体现本发明作品的创意和艺术效果。本发明的胡子3和眉毛2所用的陶土为:苏州土30%;黑毛土30%;白长石20%;石英20%。能够明确表现出达摩哺雀的慈悲胸怀。
实施例2
如图1所示,一种达摩哺雀钧瓷工艺品的制作方法,包括以下步骤:
步骤1、雕刻模型;将整个工艺品分为多个部分分别雕刻,包括头部、双手部5、主体7部、麻雀4、钵盂6、底座8、眉毛2和胡子3,其中主体7部站立,右手半捧着左手,双手部5平抬捧着钵盂6,钵盂6上站着一只麻雀4,右臂上散落着两只麻雀4,眉毛2和胡子3为白色。
步骤2、制作磨具;将步骤1雕刻成型的多个部分分别制作石膏模具。
步骤3、选取陶土;主体7陶土包括以下部分组成:高岭土70%,砂石6%,铅粉10%,莫来石10%,铁矿石3%,氧化钴0.5%,食用碱0.5%,眉毛2和胡子3陶土组成:苏州土30%;黑毛土30%;白长石20%;石英20%。
步骤4、制浆;将步骤3的陶土首先进行粗碎成沙粒状或粉状,然后进行磨碎,其磨碎为230-250目,加水混合后球磨,制成浆料。
步骤5、注浆成型;将浆料分别注入步骤2中的各个模具中,并将多个模具内经过注浆后凝固生产的坯体,按照设计要求粘接在一起,经过修整,形成整体形象。
步骤6、干燥;将修整好的坯体在25-120℃温度下进行干燥,干燥后的坯体含水量低于3%。
步骤7、素烧;将坯体放入素烧窑中,在900℃-1000℃的温度下烧制5-6个小时。
步骤8、施釉;将素烧后的坯体表面除杂处理后进行表面涂釉材,其中面部、双手部5及底座8不施釉,主体7部分采用刷釉或者喷釉或者蘸釉的方法进行施釉;釉料是将包括黄长石55%,白长石12%,方解石11%,铜矿石3%,氯化锌5%,碳酸钡0.4%,氧化锡0.6%,三氧化二铁6%,氧化钾3%,氧化钠1%,木节土3%的釉料进行粉碎,混合,球磨,使其成为细度为400-450目的细粉,加水搅拌混合球磨后制成釉浆。
步骤9、烧制;将施釉后并干燥的坯体放入窑中在1280℃-1300℃的温度烧制12-15个小时。
在以上的实施例中应当注意,在主体7部分施釉时,应当保证施釉的釉层厚度不大于1毫米,以保证减少釉层的开裂,影响本作品的视感。
Claims (1)
1.一种达摩哺雀钧瓷工艺品的制作方法,其特征在于:包括以下步骤,步骤1、雕刻模型;将整个工艺品分为多个部分分别雕刻,包括头部、双手部、主体部、麻雀、钵盂、底座、眉毛和胡子,其中主体部站立着,双手部平抬,右手半握左手,双手部捧着钵盂,钵盂上站着一只麻雀,右臂上散落着两只麻雀,眉毛和胡子为白色;步骤2、制作模具;步骤3、选取陶土;步骤4、制浆;步骤5、注浆成型; 步骤6、干燥;步骤7、素烧;步骤8、施釉;步骤9、烧制;所述的步骤4是将步骤3的陶土首先进行粗碎成沙粒状或粉状,然后进行磨碎,其磨碎为230-250目,加水混合后球磨,制成浆料。