CN108546432A - A kind of underwater anticorrosive paint of water dam - Google Patents
A kind of underwater anticorrosive paint of water dam Download PDFInfo
- Publication number
- CN108546432A CN108546432A CN201810364356.1A CN201810364356A CN108546432A CN 108546432 A CN108546432 A CN 108546432A CN 201810364356 A CN201810364356 A CN 201810364356A CN 108546432 A CN108546432 A CN 108546432A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- water
- anticorrosive paint
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to metal rust preventing technical fields, specifically disclose a kind of underwater anticorrosive paint of water dam, are made from the following raw materials in parts by weight：400~500 parts of aqueous acrylic emulsion, 100 parts of micaceous iron oxide, 4~5 parts of auxiliary rheological agents LT, 2~7 parts of dispersant, 1~3 part of wetting agent, 1.5~2 parts of powdered whiting, 4~9 parts of ethylene glycol, 10~30 parts of blanc fixe, 5~10 parts of mould inhibitor, 0.5~1.8 part of modifying agent, 2~4 parts of aluminium triphosphate, 180 parts of deionized water, 20~30 parts of antifoaming agent, 15~18 parts of cosolvent, 30~50 parts of anti-flash rusting auxiliary agent.The advantages that the present invention overcomes the deficiencies in the prior art, are screened by the depth to lotion, rust resisting pigment and auxiliary agent, is reasonably combined, aqueous quick-drying anti-rust paint has been made, having fast drying, and water resistance and salt fog resistance are excellent, and storage stability is good.
Description
Technical field
The present invention relates to metal rust preventing technical fields, particularly belong to a kind of underwater anticorrosive paint of water dam.
Background technology
Water dam is the main security facility of underground waterproof, and all floods threaten serious mine, is designed in underworkings
In arrangement, just the position of waterproof lock room and floodgate wall should be reserved in appropriate place, mine formation is made to divide the wing, point level or divide
Exploiting field isolation exploitation.When flood occurs, mine subregion can be made to be isolated, reduce the condition of a disaster coverage, the control flow of water endangers, really
Protect mine safety.
As the more and more water dams of development of society use metal material, but existing metal water dam encounters
Maximum problem is exactly surface anticorrosion.
Invention content
The object of the present invention is to provide a kind of underwater anticorrosive paints of water dam, overcome the deficiencies in the prior art,
It is screened by the depth to lotion, rust resisting pigment and auxiliary agent, is reasonably combined, aqueous quick-drying anti-rust paint has been made, there is fast drying,
The advantages that water resistance and salt fog resistance are excellent, and storage stability is good.
To solve the above problems, the technical solution used in the present invention is as follows：
A kind of underwater anticorrosive paint of water dam, is made from the following raw materials in parts by weight：Aqueous acrylic emulsion 400~500
Part, 100 parts of micaceous iron oxide, 4~5 parts of auxiliary rheological agents LT, 2~7 parts of dispersant, 1~3 part of wetting agent, powdered whiting 1.5
~2 parts, 4~9 parts of ethylene glycol, 10~30 parts of blanc fixe, 5~10 parts of mould inhibitor, 0.5~1.8 part of modifying agent, tripolyphosphate
2~4 parts of aluminium, 180 parts of deionized water, 20~30 parts of antifoaming agent, 15~18 parts of cosolvent, 30~50 parts of anti-flash rusting auxiliary agent.
Further, it is made from the following raw materials in parts by weight：450 parts of aqueous acrylic emulsion, 100 parts of micaceous iron oxide, stream
Become 4.5 parts of auxiliary agent LT, 4 parts of dispersant, 2 parts of wetting agent, 1.8 parts of powdered whiting, 6 parts of ethylene glycol, 18 parts of blanc fixe,
7.5 parts of mould inhibitor, 3 parts of aluminium triphosphate, 180 parts of deionized water, 25 parts of antifoaming agent, 16 parts of cosolvent, is prevented 1.6 parts of modifying agent
40 parts of flash rusting auxiliary agent.
Further, the sluice gate is with the preparation method of underwater anticorrosive paint：The deionized water weighed is added first
Enter into dispersion cylinder, then adjust mixing speed to 600r/min, sequentially adds micaceous iron oxide, auxiliary rheological agents LT, dispersion
Agent, wetting agent, powdered whiting, blanc fixe, mould inhibitor, modifying agent, aluminium triphosphate, deionized water, antifoaming agent, stirring
Then 5~10min adjusts mixing speed to 1000r/min, sequentially add aqueous acrylic emulsion, cosolvent, anti-flash rusting and help
Agent, ethylene glycol stir 30~40min.
Compared with prior art, implementation result of the invention is as follows by the present invention：
A kind of underwater anticorrosive paint of water dam of the present invention, screened by the depth to lotion, rust resisting pigment and auxiliary agent,
It is reasonably combined, aqueous quick-drying anti-rust paint has been made, there is fast drying, water resistance and salt fog resistance are excellent, and storage stability is good etc.
Advantage.
Specific implementation mode
With reference to embodiment, the invention will be further described, but the present invention is not limited to these instances, and is being de-
Under the premise of from present inventive concept, carried out by it is any improvement be within the scope of the present invention.
Embodiment 1
A kind of underwater anticorrosive paint of water dam of the present invention, is made from the following raw materials in parts by weight：Water soluble acrylic acid
400~500 parts of lotion, 100 parts of micaceous iron oxide, 4~5 parts of auxiliary rheological agents LT, 2~7 parts of dispersant, 1~3 part of wetting agent, again
1.5~2 parts of matter calcium carbonate, 4~9 parts of ethylene glycol, 10~30 parts of blanc fixe, 5~10 parts of mould inhibitor, modifying agent 0.5~1.8
Part, 2~4 parts of aluminium triphosphate, 180 parts of deionized water, 20~30 parts of antifoaming agent, 15~18 parts of cosolvent, anti-flash rusting auxiliary agent 30
~50 parts.
Embodiment 2
A kind of underwater anticorrosive paint of water dam of the present invention, is made from the following raw materials in parts by weight：Water soluble acrylic acid
450 parts of lotion, 100 parts of micaceous iron oxide, 4.5 parts of auxiliary rheological agents LT, 4 parts of dispersant, 2 parts of wetting agent, powdered whiting 1.8
Part, 6 parts of ethylene glycol, 18 parts of blanc fixe, 7.5 parts of mould inhibitor, 1.6 parts of modifying agent, 3 parts of aluminium triphosphate, deionized water 180
Part, 25 parts of antifoaming agent, 16 parts of cosolvent, 40 parts of anti-flash rusting auxiliary agent.
Embodiment 3
A kind of underwater anticorrosive paint of water dam of the present invention, the preparation method of the underwater anticorrosive paint of the sluice gate
For：The deionized water weighed is added in dispersion cylinder first, then mixing speed is adjusted to 600r/min, is sequentially added
Micaceous iron oxide, auxiliary rheological agents LT, dispersant, wetting agent, powdered whiting, blanc fixe, mould inhibitor, modifying agent, trimerization
Aluminum phosphate, deionized water, antifoaming agent stir 5~10min, then adjust mixing speed to 1000r/min, sequentially add water
Property acrylic emulsion, cosolvent, anti-flash rusting auxiliary agent, ethylene glycol, stir 30~40min.
Above content is only to present inventive concept example and explanation, affiliated those skilled in the art couple
Described specific embodiment does various modifications or additions or substitutes by a similar method, without departing from invention
Conceive or beyond the scope defined by this claim, is within the scope of protection of the invention.
Claims (3)
1. a kind of underwater anticorrosive paint of water dam, it is characterised in that：It is made from the following raw materials in parts by weight：Water soluble acrylic acid
400~500 parts of lotion, 100 parts of micaceous iron oxide, 4~5 parts of auxiliary rheological agents LT, 2~7 parts of dispersant, 1~3 part of wetting agent, again
1.5~2 parts of matter calcium carbonate, 4~9 parts of ethylene glycol, 10~30 parts of blanc fixe, 5~10 parts of mould inhibitor, modifying agent 0.5~1.8
Part, 2~4 parts of aluminium triphosphate, 180 parts of deionized water, 20~30 parts of antifoaming agent, 15~18 parts of cosolvent, anti-flash rusting auxiliary agent 30
~50 parts.
2. a kind of underwater anticorrosive paint of water dam according to claim 1, it is characterised in that：By following parts by weight
Raw material is made：450 parts of aqueous acrylic emulsion, 100 parts of micaceous iron oxide, 4.5 parts of auxiliary rheological agents LT, 4 parts of dispersant, moistening
2 parts of agent, 1.8 parts of powdered whiting, 6 parts of ethylene glycol, 18 parts of blanc fixe, 7.5 parts of mould inhibitor, 1.6 parts of modifying agent, trimerization phosphorus
3 parts of sour aluminium, 180 parts of deionized water, 25 parts of antifoaming agent, 16 parts of cosolvent, 40 parts of anti-flash rusting auxiliary agent.
3. according to a kind of underwater anticorrosive paint of water dam of claims 1 or 2 any one of them, it is characterised in that：It is described
Sluice gate is with the preparation method of underwater anticorrosive paint：The deionized water weighed is added in dispersion cylinder first, then will
Mixing speed is adjusted to 600r/min, sequentially adds micaceous iron oxide, auxiliary rheological agents LT, dispersant, wetting agent, heavy carbonic acid
Calcium, blanc fixe, mould inhibitor, modifying agent, aluminium triphosphate, deionized water, antifoaming agent stir 5~10min, then will stir
It mixes speed to adjust to 1000r/min, sequentially adds aqueous acrylic emulsion, cosolvent, anti-flash rusting auxiliary agent, ethylene glycol, stirring 30
~40min.