CN103396720A - Waterproof building pigment - Google Patents
Waterproof building pigment Download PDFInfo
- Publication number
- CN103396720A CN103396720A CN2013103682347A CN201310368234A CN103396720A CN 103396720 A CN103396720 A CN 103396720A CN 2013103682347 A CN2013103682347 A CN 2013103682347A CN 201310368234 A CN201310368234 A CN 201310368234A CN 103396720 A CN103396720 A CN 103396720A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof
- mixture
- filler
- buildings waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to a waterproof building pigment which comprises the following components in parts by weight: 20-27 parts of epoxy, 14-17 parts of phenolic neoprene, 11-16 parts of rubber, 4-9 parts of potassium tripolyphosphate, 2-5 parts of melamine polyphosphate, 6-11 parts of double melamine polyphosphate, 16-21 parts of waterproof heat-preservation powder, 6-8 parts of stabilizer, 5-7 parts of enhancer and 11-16 parts of filler. The waterproof building pigment has excellent waterproof performance and a high/low temperature resisting effect, can bear various corrosion of strong acid, salt and alkali, is low in cost and has no gasification pollution.
Description
Technical field
The present invention relates to waterproof paint, particularly buildings waterproof pigment.
Background technology
At present, domestic widely used coating type is various, and is used for building surface, as still using three oily two felt water-proof materials in roof, exterior wall etc., and time-consuming taking a lot of work during construction, and also use range is subject to great limitation.This method no-reflection temperature reduction performance particularly,, because three oily two felts obtain heat-absorbing action, make the temperature of attic or freezer, grain depot raise every summer, keep temperature suitable, consumes energy larger.
Summary of the invention
The purpose of this invention is to provide a kind of pigment, it is low that the present invention aims to provide a kind of cost, without the buildings waterproof pigment of gasification pollution.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of buildings waterproof pigment, and the parts by weight of its component are:
Epoxy: 20 ~ 27 parts;
Phenolic aldehyde neoprene: 14 ~ 17 parts;
Rubber: 11 ~ 16 parts;
Potassium tripolyphosphate: 4 ~ 9 parts;
Melamine phosphate: 2 ~ 5 parts;
The two trimeric cyanamides of phosphoric acid: 6 ~ 11 parts;
Waterproof thermal-insulated powder: 16 ~ 21 parts;
Stablizer: 6 ~ 8 parts;
Toughener: 5 ~ 7 parts;
Filler: 11 ~ 16 parts.
Further, described waterproof thermal-insulated powder is the mixture of a kind of in ashes, paraffin, light calcium carbonate and stearic acid or stearate or at least two kinds.
Further, described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
Further, described toughener is or slag or gypsum or aluminum oxide.
Further, described filler is the mixture of a kind of in trimeric cyanamide, clorafin, urea or at least two kinds.
The invention has the beneficial effects as follows: a kind of buildings waterproof pigment of the present invention, have excellent water resistance and anti-high and low-temp effect, can bear the saline and alkaline various corrosion of strong acid and with low cost, nothing gasification pollution.
Embodiment
For understanding better the present invention; below by two embodiment, the present invention is done further concrete elaboration; but unintelligible is limitation of the invention; some nonessential improvement and adjustment for those skilled in the art does according to the foregoing invention content, also be considered as dropping in protection scope of the present invention.
Embodiment 1
A kind of buildings waterproof pigment of the present embodiment, the parts by weight of its component are:
Epoxy: 27 parts;
Phenolic aldehyde neoprene: 17 parts;
Rubber: 16 parts;
Potassium tripolyphosphate: 9 parts;
Melamine phosphate: 5 parts;
The two trimeric cyanamides of phosphoric acid: 11 parts;
Waterproof thermal-insulated powder: 21 parts;
Stablizer: 8 parts;
Toughener: 7 parts;
Filler: 16 parts.
Described waterproof thermal-insulated powder is the mixture of a kind of in ashes, paraffin, light calcium carbonate and stearic acid or stearate or at least two kinds.
Described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
Described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
Described filler is the mixture of a kind of in trimeric cyanamide, clorafin, urea or at least two kinds.
Embodiment 2
A kind of buildings waterproof pigment of the present embodiment, the parts by weight of its component are:
Epoxy: 20 parts;
Phenolic aldehyde neoprene: 14 parts;
Rubber: 11 parts;
Potassium tripolyphosphate: 4 parts;
Melamine phosphate: 2 parts;
The two trimeric cyanamides of phosphoric acid: 6 parts;
Waterproof thermal-insulated powder: 16 parts;
Stablizer: 6 parts;
Toughener: 5 parts;
Filler: 11 ~ part.
Described waterproof thermal-insulated powder is the mixture of a kind of in ashes, paraffin, light calcium carbonate and stearic acid or stearate or at least two kinds.
Described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
Described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
Described filler is the mixture of a kind of in trimeric cyanamide, clorafin, urea or at least two kinds.
Embodiment 3
A kind of buildings waterproof pigment of the present embodiment, the parts by weight of its component are:
Epoxy: 22 parts;
Phenolic aldehyde neoprene: 15 parts;
Rubber: 14 parts;
Potassium tripolyphosphate: 5 parts;
Melamine phosphate: 3 parts;
The two trimeric cyanamides of phosphoric acid: 8 parts;
Waterproof thermal-insulated powder: 18 parts;
Stablizer: 7 parts;
Toughener: 6 parts;
Filler: 14 parts.
Described waterproof thermal-insulated powder is the mixture of a kind of in ashes, paraffin, light calcium carbonate and stearic acid or stearate or at least two kinds.
Described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
Described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
Described filler is the mixture of a kind of in trimeric cyanamide, clorafin, urea or at least two kinds.
Claims (5)
1. a buildings waterproof pigment, is characterized in that, the parts by weight of its component are:
Epoxy: 20 ~ 27 parts;
Phenolic aldehyde neoprene: 14 ~ 17 parts;
Rubber: 11 ~ 16 parts;
Potassium tripolyphosphate: 4 ~ 9 parts;
Melamine phosphate: 2 ~ 5 parts;
The two trimeric cyanamides of phosphoric acid: 6 ~ 11 parts;
Waterproof thermal-insulated powder: 16 ~ 21 parts;
Stablizer: 6 ~ 8 parts;
Toughener: 5 ~ 7 parts;
Filler: 11 ~ 16 parts.
2. a kind of buildings waterproof pigment according to claim 1, is characterized in that, described waterproof thermal-insulated powder is the mixture of a kind of in ashes, paraffin, light calcium carbonate and stearic acid or stearate or at least two kinds.
3. a kind of buildings waterproof pigment according to claim 1, is characterized in that, described stablizer is the mixture that polypropylene, polyethylene, polyvinyl chloride mix according to 1:1:1.
4. a kind of buildings waterproof pigment according to claim 1, is characterized in that, described toughener is or slag or gypsum or aluminum oxide.
5. a kind of buildings waterproof pigment according to claim 1, is characterized in that, described filler is the mixture of a kind of in trimeric cyanamide, clorafin, urea or at least two kinds.