CN104231501A - Synthesized resin tile and preparing method thereof - Google Patents
Synthesized resin tile and preparing method thereof Download PDFInfo
- Publication number
- CN104231501A CN104231501A CN201410519436.1A CN201410519436A CN104231501A CN 104231501 A CN104231501 A CN 104231501A CN 201410519436 A CN201410519436 A CN 201410519436A CN 104231501 A CN104231501 A CN 104231501A
- Authority
- CN
- China
- Prior art keywords
- parts
- synthetic resins
- resin
- watt
- tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a synthesized resin tile. The synthesized resin tile comprises 30-40 parts of modified polyacrylic acid resin, 20-25 parts of PVC (Polyvinyl Chloride) resin, 10-20 parts of coal ash, 5-8 parts of calcium charbonate, 2-5 parts of antioxidant, 1-3 parts of flame retardant and 3-5 parts of dispersant. The invention further discloses a preparing method thereof. The tile is prepared from composites, the defect that the traditional clay tile wastes resources is overcome, and the tile self has excellent performance in the aspects of energy conservation, sound isolation, low temperature resistance, corrosion resistance, fire retardancy, impact resistance, load resistance, water proofness, light weight, insulation and the like and has remarkable economic benefit and social benefit.
Description
Technical field
The present invention relates to a kind of synthetic resins watt and preparation method thereof, belong to a watt manufacture technology field.
Background technology
For a long time, people mostly concentrate in the understanding to watt material the understanding of roof cladding.As waterproof, insulation, heat insulation roof cladding; clay shingle is that we use one of more, that history is longer roof cladding; but; this kind watt needs to consume a large amount of clay, and in order to protect farmland, protection of the environment, save energy, China's restriction or even prohibit the use clay shingle gradually.And based on above-mentioned situation, research and develop and a kind of there is efficient, energy-conservation, joint soil, the lightweight of environmental protection, high-strength, insulation, the focus that heat insulation, fp roof cladding becomes concern.
Summary of the invention
For solving the deficiencies in the prior art, the object of the present invention is to provide a kind of energy-conservation, sound insulation, shock resistance, heatproof, corrosion resistant synthetic resins watt and preparation method thereof.
For achieving the above object, the present invention is achieved by the following technical solutions:
A kind of synthetic resins watt, it is characterized in that, comprise following component, and the parts by weight of each component is respectively:
Modified polypropene acid resin: 30-40 part;
Polyvinyl chloride resin: 20-25 part;
Flyash: 10-20 part;
Calcium carbonate: 5-8 part;
Oxidation inhibitor: 2-5 part;
Fire retardant: 1-3 part;
Dispersion agent: 3-5 part.
Preferably, described a kind of synthetic resins watt, comprises following component, and the parts by weight of each component are respectively:
Modified polypropene acid resin: 30 parts;
Polyvinyl chloride resin: 20 parts;
Flyash: 10 parts;
Calcium carbonate: 5 parts;
Oxidation inhibitor: 2 parts;
Fire retardant: 3 parts;
Dispersion agent: 5 parts.
Further, described acrylic resin modified in be epoxy organosilicon oil for carrying out the properties-correcting agent of modification to polyacrylic resin.
Described oxidation inhibitor is antioxidant 1010.
Described fire retardant is silicone based flame retardant.
Described dispersion agent is hexenyl bis-stearamides.
Further, the preparation method of a kind of above-mentioned synthetic resins watt, it is characterized in that, concrete steps are: according to weight fraction ratio: after modified polypropene acid resin, polyvinyl chloride resin, flyash, calcium carbonate, oxidation inhibitor, fire retardant, dispersant, then be added in twin screw extruder extrude, granulation, then, carry out hot-forming after being heated to plastics molten state, after cooling and demolding, obtain synthetic resins watt.
The invention has the beneficial effects as follows: the present invention to be prepared watt by adopting matrix material, overcome the defect of traditional clay tile waste resource, and from the aspect such as energy-conservation, sound insulation, low temperature resistant, corrosion-resistant, fire-resistant, shock resistance, anti-load, waterproof, light weight, insulation, all there is outstanding performance, there is considerable economic benefit and social benefit.
Embodiment
Below in conjunction with embodiment, concrete introduction is carried out to the present invention.
In following examples, described acrylic resin modified in be epoxy organosilicon oil for carrying out the properties-correcting agent of modification to polyacrylic resin.
embodiment 1
By modified polypropene acid resin: 30 parts; Polyvinyl chloride resin: 20 parts; Flyash: 10 parts; Calcium carbonate: 5 parts; Antioxidant 1010: 5 parts; Silicone based flame retardant: 1 part; Hexenyl bis-stearamides: after 3 parts of mixing, be added in twin screw extruder carry out extruding, granulation, carry out hot-forming after being then heated to plastics molten state, then obtain synthetic resins watt after cooling and demolding.
embodiment 2
By modified polypropene acid resin: 40 parts; Polyvinyl chloride resin: 25 parts; Flyash: 20 parts; Calcium carbonate: 8 parts; Antioxidant 1010: 2 parts; Silicone based flame retardant: 3 parts; Hexenyl bis-stearamides: after 5 parts of mixing, be added in twin screw extruder carry out extruding, granulation, carry out hot-forming after being then heated to plastics molten state, then obtain synthetic resins watt after cooling and demolding.
embodiment 3
By modified polypropene acid resin: 35 parts; Polyvinyl chloride resin: 22 parts; Flyash: 15 parts; Calcium carbonate: 6 parts; Antioxidant 1010: 4 parts; Silicone based flame retardant: 2 parts; Hexenyl bis-stearamides: after 4 parts of mixing, be added in twin screw extruder carry out extruding, granulation, carry out hot-forming after being then heated to plastics molten state, then obtain synthetic resins watt after cooling and demolding.
embodiment 4
By modified polypropene acid resin: 30 parts; Polyvinyl chloride resin: 20 parts; Flyash: 10 parts; Calcium carbonate: 5 parts; Antioxidant 1010: 2 parts; Silicone based flame retardant: 3 parts; Hexenyl bis-stearamides: after 5 parts of mixing, be added in twin screw extruder carry out extruding, granulation, carry out hot-forming after being then heated to plastics molten state, then obtain synthetic resins watt after cooling and demolding.
The thermal conductivity of synthetic resins that above-described embodiment 1-4 prepares watt can reach 0.325w/mk, is 1/3 of clay, and when suffering the ectocines such as heavy rain, hail, strong wind, all can good absorption noise.
And tested known by physical testing, 1kg steel ball highly freely drops on the tiling of synthetic resins watt at 1.5m and does not crack, under low temperature ball falling impact maximum 12 times without destroying, through 10 freeze cycle, resin tile bubble-free, stripping, crackle and hollowing phenomenon.
Fire resistance rating reaches B1 level, and corrosion resistance nature, water resistance, good insulation preformance.
The present invention is illustrated according to above-described embodiment, should be appreciated that above-described embodiment does not limit the present invention in any form, and all employings are equal to replacement or the technical scheme that obtains of equivalent transformation mode, all drop within protection scope of the present invention.
Claims (7)
1. a synthetic resins watt, is characterized in that, comprises following component, and the parts by weight of each component are respectively:
Modified polypropene acid resin: 30-40 part;
Polyvinyl chloride resin: 20-25 part;
Flyash: 10-20 part;
Calcium carbonate: 5-8 part;
Oxidation inhibitor: 2-5 part;
Fire retardant: 1-3 part;
Dispersion agent: 3-5 part.
2. a kind of synthetic resins watt according to claim 1, is characterized in that, comprises following component, and the parts by weight of each component are respectively:
Modified polypropene acid resin: 30 parts;
Polyvinyl chloride resin: 20 parts;
Flyash: 10 parts;
Calcium carbonate: 5 parts;
Oxidation inhibitor: 2 parts;
Fire retardant: 3 parts;
Dispersion agent: 5 parts.
3. a kind of synthetic resins watt according to claim 1, is characterized in that, described acrylic resin modified in be epoxy organosilicon oil for carrying out the properties-correcting agent of modification to polyacrylic resin.
4. a kind of synthetic resins watt according to claim 1, is characterized in that, described oxidation inhibitor is antioxidant 1010.
5. a kind of synthetic resins watt according to claim 1, is characterized in that, described fire retardant is silicone based flame retardant.
6. a kind of synthetic resins watt according to claim 1, is characterized in that, described dispersion agent is hexenyl bis-stearamides.
7. the preparation method of synthetic resins described in any one of a claim 1-6 claim watt, it is characterized in that, concrete steps are: according to weight fraction ratio: after modified polypropene acid resin, polyvinyl chloride resin, flyash, calcium carbonate, oxidation inhibitor, fire retardant, dispersant, then be added in twin screw extruder extrude, granulation, then, carry out hot-forming after being heated to plastics molten state, after cooling and demolding, obtain synthetic resins watt.