CN108532087A - Tatting wash-and-wear fabrics and preparation method thereof - Google Patents
Tatting wash-and-wear fabrics and preparation method thereof Download PDFInfo
- Publication number
- CN108532087A CN108532087A CN201810210642.2A CN201810210642A CN108532087A CN 108532087 A CN108532087 A CN 108532087A CN 201810210642 A CN201810210642 A CN 201810210642A CN 108532087 A CN108532087 A CN 108532087A
- Authority
- CN
- China
- Prior art keywords
- water repellent
- wash
- yarn
- wear
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of tatting wash-and-wear fabrics and preparation method thereof, include the following steps：Yarn is carried out to yarn dyeing, warping and sizing operation processing successively, then carries out tatting weaving and finishing process processing successively, obtains woven fabric；The yarn includes warp thread and weft yarn, and the warp thread or weft yarn add water repellent finishing agent to be carried out at the same time water repellent finish in yarn dyeing in carrying out yarn dyeing process processing；The woven fabric is subjected to noniron finish process processing using wash and wear finisher aqueous solution, obtains tatting wash-and-wear fabrics.The preparation method of the present invention can adsorb enough wash and wear finisher aqueous solutions by the yarn without water repellent effect to ensure the flatness of fabric, to meet appearance requirement, less wash and wear finisher aqueous solution is adsorbed to improve its strength by the yarn with water repellent effect simultaneously, it is made to meet the requirement of Tear strength.Tatting wash-and-wear fabrics obtained can meet appearance and Tear strength requirement simultaneously.
Description
Technical field
The present invention relates to textile technology fields, more particularly to a kind of tatting wash-and-wear fabrics and preparation method thereof.
Background technology
The noniron finish of textile industry, General Principle are resin and fibre under the action of certain temperature condition and catalyst
Dimension crosslinks reaction, and the performances such as fabrics for shrinkage, wrinkle resistant can be improved in such arrangement.Through the processed fabric of noniron finish, often
Reflect non-ironing effect by its crosslinking degree.And the flatness and Tear strength of fabric can then reflect fabric noniron finish
Crosslinking degree, i.e., non-ironing effect.It finds in actual production, under normal circumstances in a certain range, resin and fibrogenic
Cross-linking reaction is more, and fabric appearance can be better, and it is higher to be mainly manifested in flatness；However the strength damage suffered by fabric also can be just
It is bigger.For tatting wash-and-wear fabrics, with yarn quality other than the Tear strength of fabric to be considered, it is also necessary to consider fabric
Fabric appearance.What is brought therewith is the increase with yarn cost and quality risk.Therefore it is based on current textile industry technology, tatting is exempted from
Boiling hot fabric is often faced with the case where strength is less than Customer Standard less than standard or fabric appearance.
Invention content
Based on this, it is necessary to provide a kind of tatting wash-and-wear fabrics that can meet appearance and Tear strength requirement simultaneously and its
Preparation method.
A kind of preparation method of tatting wash-and-wear fabrics, includes the following steps：
Yarn is carried out to yarn dyeing, warping and sizing operation processing successively, then carries out tatting weaving and finishing process successively
Processing, obtains woven fabric；The woven fabric includes warp thread and weft yarn, and the warp thread or weft yarn are carrying out yarn dyeing process processing
Middle addition water repellent finishing agent in yarn dyeing to be carried out at the same time water repellent finish；
The woven fabric is subjected to noniron finish process processing using wash and wear finisher aqueous solution, obtains that tatting is non-ironing to knit
Object.
The preparation method of above-mentioned tatting wash-and-wear fabrics, when the warp thread or weft yarn of woven fabric carry out yarn dyeing, addition water repellent is whole
It manages agent and carries out water repellent finish, make the yarn that there is water repellent effect；And another yarn does not have water repellent effect.There should be water repellent effect
The ability that the yarn of fruit adsorbs wash and wear finisher aqueous solution in noniron finish process reduces, without the yarn of water repellent effect
The ability for adsorbing wash and wear finisher aqueous solution is unaffected.Traditional preparation method for not adding water repellent finishing agent is so compared,
The preparation method of the present invention can adsorb enough wash and wear finisher aqueous solutions by the yarn without water repellent effect to ensure to knit
The flatness of object, to meet appearance requirement, while it is water-soluble by the yarn with water repellent effect to adsorb less wash and wear finisher
Liquid improves its strength, so that it is met the requirement of Tear strength.Tatting wash-and-wear fabrics obtained can meet appearance and tear simultaneously
Strength is split to require.
Keep the yarn without water repellent finish in the warp thread and weft yarn whole in addition water repellent in one of the embodiments,
Wash and wear finisher adsorbance before and after managing agent is constant, reduces another yarn through water repellent finish in addition water repellent finishing agent
Wash and wear finisher adsorbance later.
The yarn without water repellent finish is before and after adding water repellent finishing agent in one of the embodiments,
Wash and wear finisher adsorbance is respectively CX1And C ' X1’；And C '=C, X1'=X1；
Wash and wear finisher adsorbance difference of the yarn through water repellent finish before and after adding water repellent finishing agent
For CX2And C ' X2’；And X2’<X2；
Wherein,
C, C ' is respectively the mass percentage concentration of wash and wear finisher aqueous solution before and after adding water repellent finishing agent, unit
For %；
X1、X1' it is respectively liquid carrying rate of the yarn without water repellent finish before and after adding water repellent finishing agent, unit
For %；
X2、X2' it is respectively liquid carrying rate of the yarn through water repellent finish before and after adding water repellent finishing agent, unit
For %.
The yarn through water repellent finish in the warp thread and weft yarn is kept to add water repellent finish in one of the embodiments,
Wash and wear finisher adsorbance before and after agent is constant, increases another yarn without water repellent finish in addition water repellent finishing agent
Wash and wear finisher adsorbance later.
The yarn without water repellent finish is before and after adding water repellent finishing agent in one of the embodiments,
Wash and wear finisher adsorbance is respectively CX1And C ' X1’；And C ' ＞ C, X1'=X1；
Wash and wear finisher adsorbance difference of the yarn through water repellent finish before and after adding water repellent finishing agent
For CX2And C ' X2’；And X2’<X2, C ' X2'=CX2；
Wherein,
C, C ' is respectively the mass percentage concentration of wash and wear finisher aqueous solution before and after adding water repellent finishing agent, unit
For %；
X1、X1' it is respectively liquid carrying rate of the yarn without water repellent finish before and after adding water repellent finishing agent, unit
For %；
X2、X2' it is respectively liquid carrying rate of the yarn through water repellent finish before and after adding water repellent finishing agent, unit
For %.
The wash and wear finisher in the wash and wear finisher aqueous solution is mainly by dihydroxymethyl two in one of the embodiments,
Hydroxyalkyl vinyl urea forms.
The mode of the noniron finish process, which is tatting ready-made non-ironing garment, in one of the embodiments, shuttle-woven fabric is dry hands over
It is non-ironing to join the damp crosslinking of non-ironing or shuttle-woven fabric.
The yarn dyeing includes the pre-treatment carried out successively, dyeing and excessively soft arrangement step in one of the embodiments,；Institute
Water repellent finishing agent is stated to be added in the finishing agent of the excessively soft arrangement in the excessively soft arrangement step.
In one of the embodiments, the water repellent finishing agent be fluorinated water repellent finishing agent, the water repellent finishing agent with
The mass volume ratio of the finishing agent of the excessively soft arrangement is (0.1g~30g):1L.
Tatting wash-and-wear fabrics made from the preparation method of any of the above-described tatting wash-and-wear fabrics.
Specific implementation mode
To facilitate the understanding of the present invention, below will to invention is more fully described, and give the present invention compared with
Good embodiment.But the present invention can realize in many different forms, however it is not limited to embodiment described herein.Phase
Instead, purpose of providing these embodiments is makes the disclosure of the present invention more thorough and comprehensive.
Unless otherwise defined, all of technologies and scientific terms used here by the article and belong to the technical field of the present invention
The normally understood meaning of technical staff is identical.Used term is intended merely to description tool in the description of the invention herein
The purpose of the embodiment of body, it is not intended that in the limitation present invention.Term as used herein "and/or" includes one or more phases
Any and all combinations of the Listed Items of pass.
The preparation method of the tatting wash-and-wear fabrics of an embodiment of the present invention, includes the following steps S1~S2.
Step S1：Yarn is carried out successively yarn dyeing, warping and sizing operation processing, then successively carry out tatting weaving and it is rear whole
The processing of science and engineering sequence, obtains woven fabric；Woven fabric includes warp thread and weft yarn, and warp thread or weft yarn are in carrying out yarn dyeing process processing
Water repellent finishing agent is added to be carried out at the same time water repellent finish in yarn dyeing.
Yarn dyeing includes the pre-treatment carried out successively, dyeing and excessively soft arrangement step in one of the embodiments,.And water repellent
Finishing agent was added in excessively soft arrangement step in the finishing agent of soft arrangement.
Further, water repellent finishing agent is fluorinated water repellent finishing agent.Water repellent finishing agent and the finishing agent of excessively soft arrangement
Mass volume ratio is (0.1g~30g):1L.Specifically, using trade nameN1811liq. water repellent finishing agent,
For the fluorine chemical based on six carbon alkyl.Specifically in one embodiment, the finishing agent of excessively soft arrangement is water.Preferably, water repellent is whole
The mass volume ratio for managing agent and the finishing agent of excessively soft arrangement is (5g~15g):1L.
It is understood that water repellent finishing agent is not limited to fluorinated water repellent finishing agent.
Further, the temperature of excessively soft arrangement is 55 DEG C, time 15min.
Specifically, the dyeing the step of after and the step of in soft arrangement excessively before, further include fixation step.It is especially right
In the deeper situation of the color of dyeing, need to increase fixation step.
Step S2：Woven fabric is subjected to noniron finish process processing using wash and wear finisher aqueous solution, tatting is obtained and exempts from
Scald fabric.
Further, the wash and wear finisher in wash and wear finisher aqueous solution is mainly made of dihydroxymethyl dihydroxy ethylene urea.
Specifically, the mass percentage concentration of wash and wear finisher aqueous solution can adjust according to actual needs.Specifically in one embodiment, exempting from
It scalds in aqueous finish solution, the mass volume ratio of dihydroxymethyl dihydroxy ethylene urea and water is (250g~300g):1L.
The mode of noniron finish process is tatting ready-made non-ironing garment in one of the embodiments, shuttle-woven fabric dry crosslinking is exempted from
It scalds or the crosslinking of shuttle-woven fabric tide is non-ironing.
Further, tatting ready-made non-ironing garment include the clothing manufacturing carried out successively, it is wash and wear finisher aqueous solution feeding, pre-
Baking, pressing and wash water step.Specifically, the condition of preliminary drying is to dry 1min at 100 DEG C.Preliminary drying is dried using baker open width.
Pressing step is to carry out pressing again prior to getting damp again in moisture regain case.Specifically, the time of moisture regain is 10min, and the temperature of pressing is 150
DEG C, time 20s.
Further, shuttle-woven fabric dry crosslinking it is non-ironing including carry out successively wash and wear finisher aqueous solution feeding, drying, roasting
Baking and wash water step.
Further, shuttle-woven fabric tide is crosslinked non-ironing wash and wear finisher aqueous solution feeding, drying, heap including carrying out successively
It sets and wash water step.
Further, wash and wear finisher aqueous solution feeding, which uses, pads mode feeding.Specifically, in such a way that two leachings two are rolled
By padding machine.Specifically, the pressure of padding machine is 2.5bar.Specifically, the speed of padding machine is 60m/min.
The preparation method of above-mentioned tatting wash-and-wear fabrics, when the warp thread or weft yarn of woven fabric carry out yarn dyeing, addition water repellent is whole
It manages agent and carries out water repellent finish, make the yarn that there is water repellent effect；And another yarn does not have water repellent effect.The present invention is by grinding
Study carefully discovery, should adsorb the ability of wash and wear finisher aqueous solution in noniron finish process with the yarn of water repellent effect reduces, and
The ability of yarn absorption wash and wear finisher aqueous solution without water repellent effect is unaffected.So refused compared to traditional not adding
The preparation method of the wash-and-wear fabrics of water finishing agent, preparation method of the invention can adsorb foot by the yarn without water repellent effect
Enough wash and wear finisher aqueous solutions ensure the flatness of fabric, to meet appearance requirement, while by with water repellent effect
Yarn adsorbs less wash and wear finisher aqueous solution to improve its strength, it is made to meet the requirement of Tear strength.Tatting obtained
Wash-and-wear fabrics can meet appearance and Tear strength requirement simultaneously.
Compared with the preparation process of traditional wash-and-wear fabrics, the preparation method of tatting wash-and-wear fabrics of the present invention can be according to fabric
Specific performance require the characteristics of carry out corresponding technique adjustment, to be met the tatting of appearance and Tear strength requirement simultaneously
Wash-and-wear fabrics.
As noted previously, as wash and wear finisher aqueous solution should be adsorbed in noniron finish process with the yarn of water repellent effect
Ability reduce, without water repellent effect yarn adsorb wash and wear finisher aqueous solution ability it is unaffected.So even
It is identical in the conditions such as the pressure that the vehicle of wash and wear finisher aqueous solution feeding time control weaving object entirety rolls and speed, but warp thread and weft yarn
Practical liquid carrying rate because the adsorption capacity of wash and wear finisher aqueous solution has difference can difference.The liquid carrying rate of yarn can be adopted
The fabric made of yarn of the same race controls the same terms and measures.
So if needing the Tear strength of promotion fabric in the case of keeping appearance to be basically unchanged, only it need to keep non-ironing whole
The mass concentration for managing agent aqueous solution is constant before and after adding water repellent finishing agent, and warp thread or weft yarn are being carried out yarn dyeing process
Water repellent finishing agent is added in processing to carry out water repellent finish, you can keep the yarn without water repellent finish in the warp thread and weft yarn
Wash and wear finisher adsorbance before and after adding water repellent finishing agent is constant, and another yarn through water repellent finish is adding
Wash and wear finisher adsorbance after water repellent finishing agent is reduced.It is equal that water repellent finishing agent is added in the yarn dyeing process of warp thread or weft yarn
It can.
For example, weft yarn is added into water repellent finishing agent to carry out water repellent finish in carrying out yarn dyeing process processing, and it is non-ironing whole
The conditions such as the mass percentage concentration of agent aqueous solution are managed to remain unchanged, therefore, wash and wear finisher absorption of the warp thread in noniron finish
Measure it is unaffected, to ensure the appearance of fabric entirety；And weft yarn is due to water repellent effect, in the situation that other conditions are constant
Under, wash and wear finisher adsorbance of the weft yarn in noniron finish is reduced, to improve the Tear strength of fabric.
Further, at this point, noniron finish of the yarn without water repellent finish before and after adding water repellent finishing agent
Agent adsorbance is respectively CX1And C ' X1’；And C '=C, X1'=X1；
Wash and wear finisher adsorbance of the yarn through water repellent finish before and after adding water repellent finishing agent is respectively C
X2And C ' X2’；And X2’<X2；
Wherein,
C, C ' is respectively the mass percentage concentration of wash and wear finisher aqueous solution before and after adding water repellent finishing agent, unit
For %；
X1、X1' it is respectively liquid carrying rate of the yarn without water repellent finish before and after adding water repellent finishing agent, unit
For %；
X2、X2' it is respectively liquid carrying rate of the yarn through water repellent finish before and after adding water repellent finishing agent, unit
For %.
Due to C '=C and X1'=X1, therefore C ' X1'=CX1.Due to C '=C and X2’<X2, therefore C ' X2’<C·
X2。
Above-mentioned wash and wear finisher adsorbance refers to the quality of the wash and wear finisher of the yarn absorption of unit mass.
The strength if necessary to holding wash-and-wear fabrics is promoted non-ironing in the case of being basically unchanged in one of the embodiments,
The appearance of fabric, appearance are mainly manifested in flatness performance；Warp thread or weft yarn need to only be added in carrying out yarn dyeing process processing
Water repellent finishing agent properly increases the mass percentage concentration of wash and wear finisher aqueous solution to carry out water repellent finish, so that through water repellent
Wash and wear finisher adsorbance of the yarn of arrangement before and after adding water repellent finishing agent is constant, and another without water repellent finish
Wash and wear finisher adsorbance of the yarn after adding water repellent finishing agent increase, you can.
For example, weft yarn is added water repellent finishing agent to carry out water repellent finish, and except non-ironing in carrying out yarn dyeing process processing
The quality percentage that the mass percentage concentration of aqueous finish solution is higher than wash and wear finisher aqueous solution when being not added with water repellent finishing agent is dense
Degree, other conditions remain unchanged, and the mass percentage concentration of wash and wear finisher aqueous solution changes the noniron finish so that weft yarn
The practical adsorbance of agent, which is held essentially constant, to be advisable, to ensure that the strength of wash-and-wear fabrics is basically unchanged.And at the same time, due to exempting from
The raising of the mass percentage concentration of aqueous finish solution is scalded, the practical adsorbance of wash and wear finisher of warp thread improves, to improve
The appearance property of wash-and-wear fabrics.
Further, at this point, noniron finish of the yarn without water repellent finish before and after adding water repellent finishing agent
Agent adsorbance is respectively CX1And C ' X1’；And C ' ＞ C, X1'=X1；
Wash and wear finisher adsorbance of the yarn through water repellent finish before and after adding water repellent finishing agent is respectively C
X2And C ' X2’；And X2’<X2, C ' X2'=CX2；
Wherein,
C, C ' is respectively the mass percentage concentration of wash and wear finisher aqueous solution before and after adding water repellent finishing agent, unit
For %；
X1、X1' it is respectively liquid carrying rate of the yarn without water repellent finish before and after adding water repellent finishing agent, unit
For %；
X2、X2' it is respectively liquid carrying rate of the yarn through water repellent finish before and after adding water repellent finishing agent, unit
For %.
Due to C ' ＞ C and X1'=X1, therefore C ' X1' ＞ CX1.Due to C ' ＞ C and X2’<X2, therefore concentration is adjusted, it can
Make C ' X2'=CX2。
The present invention also provides the tatting wash-and-wear fabrics of an embodiment, using the preparation method of above-mentioned tatting wash-and-wear fabrics
It is made.The tatting wash-and-wear fabrics can meet appearance and Tear strength requirement simultaneously.
It is specific embodiment below.
Comparative example 1
Yarn is handled according to dyeing, warping, sizing, tatting weaving, final finishing flow, woven fabric is made.It should
Woven fabric be weft density be 120*80, the calico of yarn count 40S*80S/2.Wherein, yarn dyeing includes the preceding place carried out successively
Reason, dyeing and excessively soft arrangement step, wherein the finishing agent of excessively soft arrangement is water.The condition for crossing soft arrangement is to be handled at 55 DEG C
15min。
The noniron finish for being 250g/1L with the mass volume ratio of dihydroxymethyl dihydroxy ethylene urea and water by above-mentioned woven fabric
Agent aqueous solution is impregnated with, the padding machine in such a way that two leachings two are rolled through excess pressure for 2.5bar, speed 60m/min.It is used after crossing padding machine
Baker open width is dried, and drying condition is to dry 1min at 100 DEG C.Woven fabric after baking is put into moisture regain case and is got damp again
It is taken out after 10min and pressing, fusing condition is pressing 20s at 150 DEG C.It finally removes the woven fabric after pressing and carries out wash water,
Wash water condition is 40 DEG C of washing 10min；Tatting wash-and-wear fabrics are made.
Embodiment 1
Embodiment 1 and comparative example 1 the difference is that, in the finishing agent of the excessively soft arrangement in the yarn dyeing step of weft yarn
Water repellent finishing agent is added, warp thread does not change.The mass volume ratio of wherein water repellent finishing agent and the finishing agent of excessively soft arrangement is
10g:1L.Specifically, using trade nameN1811liq. water repellent finishing agent is the fluorination based on six carbon alkyl
Product.
Embodiment 2
Embodiment 2 difference from example 1 is that, except the finishing agent of excessively soft arrangement in the yarn dyeing step of weft yarn
Except middle addition water repellent finishing agent, the mass volume ratio of dihydroxymethyl dihydroxy ethylene urea and water in wash and wear finisher aqueous solution is adjusted
For 270g:1L so that wash and wear finisher adsorbance of weft yarn before and after adding water repellent finishing agent is basically unchanged, i.e., with it is right
The wash and wear finisher adsorbance of ratio 1 is essentially identical, and the wash and wear finisher adsorbance of corresponding warp thread should can increase, also with exempt from
The concentration for scalding finishing agent is related, but is more than weft yarn, the increase of wash and wear finisher concentration of aqueous solution by warp-wise density under normal circumstances
Influence to warp-wise Tear strength is smaller.
Embodiment 3~4
Embodiment 3~4 difference from example 1 is that, the quality of the finishing agent of water repellent finishing agent and excessively soft arrangement
Volume ratio adjusts separately as 0.1g:1L and 30g:1L.
By physical testing mechanism, the fabric physics of tatting wash-and-wear fabrics made from test comparison example 1, Examples 1 to 4 refers to
Mark, as a result such as table 1.Wherein, the grade scale of flat appearance degree is tested according to AATCC 143.
Table 1
| Classification | Comparative example 1 | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
| Flatness | 3 grades | 3 grades | 3.5 grade | 3 grades | ≤ 3 grades |
| Warp-wise Tear strength | 2.1 pound | 2.1 pound | 2.0 pound | 2.1 pound | 2.1 pound |
| Broadwise Tear strength | 1.4 pound | 1.9 pound | 1.5 pound | 1.6 pound | 2.5 pound |
Each technical characteristic of embodiment described above can be combined arbitrarily, to keep description succinct, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, it is all considered to be the range of this specification record.
Several embodiments of the invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection of the present invention
Range.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. a kind of preparation method of tatting wash-and-wear fabrics, which is characterized in that include the following steps：
Yarn is carried out to yarn dyeing, warping and sizing operation processing successively, then carries out tatting weaving and finishing process processing successively,
Obtain woven fabric；The woven fabric includes warp thread and weft yarn, and the warp thread or weft yarn add in carrying out yarn dyeing process processing
Add water repellent finishing agent to be carried out at the same time water repellent finish in yarn dyeing；
The woven fabric is subjected to noniron finish process processing using wash and wear finisher aqueous solution, obtains tatting wash-and-wear fabrics.
2. the preparation method of tatting wash-and-wear fabrics as described in claim 1, which is characterized in that keep in the warp thread and weft yarn
Wash and wear finisher adsorbance of the yarn without water repellent finish before and after adding water repellent finishing agent is constant, reduces another warp
Wash and wear finisher adsorbance of the yarn of water repellent finish after adding water repellent finishing agent.
3. the preparation method of tatting wash-and-wear fabrics as claimed in claim 2, which is characterized in that
Wash and wear finisher adsorbance of the yarn without water repellent finish before and after adding water repellent finishing agent be respectively
C·X1And C ' X1’；And C '=C, X1'=X1；
Wash and wear finisher adsorbance of the yarn through water repellent finish before and after adding water repellent finishing agent is respectively C
X2And C ' X2’；And C '=C, X2’<X2；
Wherein,
C, C ' is respectively the mass percentage concentration of the wash and wear finisher aqueous solution before and after adding water repellent finishing agent, unit
For %；
X1、X1' it is respectively liquid carrying rate of the yarn without water repellent finish before and after adding water repellent finishing agent, unit %；
X2、X2' it is respectively liquid carrying rate of the yarn through water repellent finish before and after adding water repellent finishing agent, unit %.
4. the preparation method of tatting wash-and-wear fabrics as described in claim 1, which is characterized in that keep in the warp thread and weft yarn
Wash and wear finisher adsorbance of the yarn through water repellent finish before and after adding water repellent finishing agent is constant, increase it is another without
Wash and wear finisher adsorbance of the yarn of water repellent finish after adding water repellent finishing agent.
5. the preparation method of tatting wash-and-wear fabrics as claimed in claim 4, which is characterized in that
Wash and wear finisher adsorbance of the yarn without water repellent finish before and after adding water repellent finishing agent be respectively
C·X1And C ' X1’；And C ' ＞ C, X1'=X1；
Wash and wear finisher adsorbance of the yarn through water repellent finish before and after adding water repellent finishing agent is respectively C
X2And C ' X2’；And X2’<X2, C ' X2'=CX2；
Wherein,
C, C ' is respectively the mass percentage concentration of wash and wear finisher aqueous solution before and after adding water repellent finishing agent, unit
For %；
X1、X1' it is respectively liquid carrying rate of the yarn without water repellent finish before and after adding water repellent finishing agent, unit %；
X2、X2' it is respectively liquid carrying rate of the yarn through water repellent finish before and after adding water repellent finishing agent, unit %.
6. such as the preparation method of Claims 1 to 5 any one of them tatting wash-and-wear fabrics, which is characterized in that described non-ironing whole
Wash and wear finisher in reason agent aqueous solution is mainly made of dihydroxymethyl dihydroxy ethylene urea.
7. such as the preparation method of Claims 1 to 5 any one of them tatting wash-and-wear fabrics, which is characterized in that described non-ironing whole
The mode of science and engineering sequence is tatting ready-made non-ironing garment, shuttle-woven fabric dry crosslinking is non-ironing or the damp crosslinking of shuttle-woven fabric is non-ironing.
8. such as the preparation method of Claims 1 to 5 any one of them tatting wash-and-wear fabrics, which is characterized in that the yarn dyeing packet
Include the pre-treatment carried out successively, dyeing and excessively soft arrangement step；The water repellent finishing agent is added in the excessively soft arrangement step
In the finishing agent of the excessively soft arrangement.
9. the preparation method of tatting wash-and-wear fabrics as claimed in claim 8, which is characterized in that the water repellent finishing agent is fluorine-containing
The mass volume ratio of class water repellent finishing agent, the water repellent finishing agent and the finishing agent of the excessively soft arrangement is (0.1g~30g):
1L。
10. the tatting wash-and-wear fabrics as made from the preparation method of claim 1~9 any one of them tatting wash-and-wear fabrics.