CN108530948A - Iron oxide brown coloring powder - Google Patents
Iron oxide brown coloring powder Download PDFInfo
- Publication number
- CN108530948A CN108530948A CN201810367802.4A CN201810367802A CN108530948A CN 108530948 A CN108530948 A CN 108530948A CN 201810367802 A CN201810367802 A CN 201810367802A CN 108530948 A CN108530948 A CN 108530948A
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- powder
- brown coloring
- coloring powder
- brown
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of iron oxide brown coloring powders, by percentage to the quality, including following component：Iron oxide red：30% 50%, iron oxide yellow 15% 35%, iron oxide black：35%‑55%.The obtained iron oxide brown coloring powder of the present invention has the characteristics that：Chocolate brown powder, more than 320 mesh of powder particle size, Bu Rong Yu Shui ﹑ alcohol is dissolved in acid.Powder is fine and smooth, is the iron oxide compound of crystal, tinting strength, tinting power, covering power, light resistance, acid resistance, alkali resistance are good, nontoxic non-hazardous.With the preparation method, the iron oxide brown ceramic powder for making gained is applied in pigment, and heatproof degree is up to 200 DEG C or more, it is ensured that 3 years colour-fast.This iron oxide brown coloring powder can be widely used in all kinds of building ground floors simultaneously（Marble terrace, terrazzo terrace）Coloring, have good improvement result to cement works and exterior coating, market prospects are very wide, also can reach the diversified demand of client's color.
Description
Technical field
The present invention relates to a kind of raw material made for pigment, especially a kind of iron oxide brown coloring powders.
Background technology
Iron oxide brown is mainly used in pigment production field, and iron oxide brown pigment is made in all kinds of precast concretes and building
It is used as pigment or colorant in product material, directly calls in cement and applies.The color concrete surface of various indoor and outdoors, such as wall
Face, terrace, ceiling, pillar, porch, road surface, parking lot, ladder, station etc.；Various architectural potteries and coloured glaze ceramics, such as face
Brick, floor tile, roofing tile, panel, terrazzo, mosaic ornamental slab for paving the floor, artificial marble etc..Simultaneously its be also applied for various pigment colorations and
Protective substances, including aqueous coating for internal and external wall, powdery paints etc.；It includes going back oxygen, alkyd, amino etc. respectively to be equally applicable to oil paint
Kind priming paint and finishing coat；It can also be used for toy lacquer, decorative paint, furniture lacquer, electrophoretic paint and enamel paint.
Existing iron oxide brown powder has following problem：Poor heat resistance, fugitive color are especially making applied to room
When the pigment on outer color concrete surface, summer outdoor temperature is higher, and easily there is a phenomenon where fall paint, fade.This and wherein oxygen
The component of change cologne earth powder is constituted, manufacture craft has and its close association.
Invention content
To solve the above problems, the present invention proposes, performance is good, and coloration time is short, iron oxide brown pigment not easy to fade
End.
A kind of iron oxide brown coloring powder that the present invention designs, by percentage to the quality, including following component：Iron oxide
It is red：30%-50%, iron oxide yellow 15%-35%, iron oxide black：35%-55%.
Preferably, iron oxide brown coloring powder, by percentage to the quality, including following component：Iron oxide red：30%, oxygen
Change iron oxide yellow：15%, iron oxide black：55%.
Preferably, iron oxide brown coloring powder, by percentage to the quality, including following component：Iron oxide red：50%, oxygen
Change iron oxide yellow：15%, iron oxide black：35%.
Preferably, iron oxide brown coloring powder, by percentage to the quality, including following component：Iron oxide red：40%, oxygen
Change iron oxide yellow：35%, iron oxide black：25%.
Preferably, the powder is in sepia.The powder particle size is 320 mesh or more.Its major technique is joined
Number：Moisture≤1.0%, the hydrotrope≤0.3%, residue on sieve≤0.1%, pH value 6.5, oil absorption 19.5.
A kind of preparation method of iron oxide brown coloring powder, includes the following steps：By iron oxide red, iron oxide yellow, oxidation
Iron oxide black is according to iron oxide red：30%-50%, iron oxide yellow 15%-35%, iron oxide black：35%-55%.Mass ratio be added to height
In fast blender；The mixture of above-mentioned material is at the uniform velocity stirred 1 hour or more in homogenizer；By above-mentioned material
Mixture crushes uniformly in pulverizer.
Compared with prior art, the obtained iron oxide brown coloring powder of the present invention has the characteristics that：Chocolate brown powder,
More than 320 mesh of powder particle size, Bu Rong Yu Shui ﹑ alcohol is dissolved in acid.Powder is fine and smooth, is the iron oxide compound of crystal, coloring
Power, covering power, light resistance, acid resistance, alkali resistance are good, nontoxic non-hazardous.With the preparation method, the iron oxide of gained is made
Brown ceramic powder is applied in pigment, and heatproof degree is up to 200 DEG C or more, it is ensured that 3 years colour-fast.This iron oxide brown simultaneously
Color powder can be widely used in all kinds of building ground floors（Marble terrace terrazzo terrace）Coloring, to cement works and exterior wall
Coating has good improvement result, and market prospects are very wide, also can reach the diversified demand of client's color.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below.
Embodiment 1
The iron oxide brown coloring powder of the present embodiment description, by percentage to the quality, including following component：Iron oxide red：30%,
Iron oxide yellow：15%, iron oxide black：55%.The present invention is the powder of sepia.The powder particle size is 320 mesh.It is main
It is moisture≤1.0%, the hydrotrope≤0.3%, residue on sieve≤0.3%, pH value 4-7, oil absorption 20-30 to want technical parameter.
A kind of preparation method of iron oxide brown coloring powder, includes the following steps：（1）By iron oxide red, iron oxide yellow, oxygen
Change iron oxide black according to iron oxide red：30%, iron oxide yellow：15%, iron oxide black：55% mass ratio is added in homogenizer；
（2）The mixture of above-mentioned material is at the uniform velocity stirred 1 hour or more in homogenizer；（3）By the mixing of above-mentioned material
Object crushes uniformly in pulverizer.
Embodiment 2
As different from Example 1, the iron oxide brown coloring powder of the present embodiment description, by percentage to the quality, including as follows
Component：Iron oxide red：50%, iron oxide yellow：15%, iron oxide black：35%.Other technologies parameter and specific preparation method with reality
It is identical to apply example 1.
Embodiment 3
As different from Example 1, the iron oxide brown coloring powder of the present embodiment description, by percentage to the quality, including as follows
Component：Iron oxide red：40%, iron oxide yellow：35%, iron oxide black：25%.Other technologies parameter and specific preparation method with reality
It is identical to apply example 1.
Claims (7)
1. a kind of iron oxide brown coloring powder, it is characterised in that：By percentage to the quality, including following component：Iron oxide red：
30%-50%, iron oxide yellow 15%-35%, iron oxide black：35%-55%.
2. iron oxide brown coloring powder according to claim 1, it is characterised in that：By percentage to the quality, including it is as follows
Component：Iron oxide red：30%, iron oxide yellow：15%, iron oxide black：55%.
3. iron oxide brown coloring powder according to claim 1, it is characterised in that：By percentage to the quality, including it is as follows
Component：Iron oxide red：50%, iron oxide yellow：15%, iron oxide black：35%.
4. iron oxide brown coloring powder according to claim 1, it is characterised in that：By percentage to the quality, including it is as follows
Component：Iron oxide red：40%, iron oxide yellow：35%, iron oxide black：25%.
5. iron oxide brown coloring powder according to claim 1, it is characterized in that the powder is in sepia.
6. iron oxide brown coloring powder according to claim 1, it is characterized in that the powder particle size be 320 mesh with
On.
7. a kind of preparation method of iron oxide brown coloring powder as described in claim 1, it is characterised in that include the following steps：
（1）Iron oxide red, iron oxide yellow, iron oxide black are added to high-speed stirring according to mass ratio as described in claim 1
It mixes in machine；
（2）The mixture of above-mentioned material is at the uniform velocity stirred 1 hour or more in homogenizer；
（3）The mixture of above-mentioned material is crushed uniformly in pulverizer.