CN108525010A - 一种材质轻盈强度高的合成骨材料 - Google Patents

一种材质轻盈强度高的合成骨材料 Download PDF

Info

Publication number
CN108525010A
CN108525010A CN201810733698.6A CN201810733698A CN108525010A CN 108525010 A CN108525010 A CN 108525010A CN 201810733698 A CN201810733698 A CN 201810733698A CN 108525010 A CN108525010 A CN 108525010A
Authority
CN
China
Prior art keywords
bone
parts
slim
graceful
synthesis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810733698.6A
Other languages
English (en)
Inventor
张培英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuancheng South Patrol Intelligent Technology Co Ltd
Original Assignee
Xuancheng South Patrol Intelligent Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuancheng South Patrol Intelligent Technology Co Ltd filed Critical Xuancheng South Patrol Intelligent Technology Co Ltd
Priority to CN201810733698.6A priority Critical patent/CN108525010A/zh
Publication of CN108525010A publication Critical patent/CN108525010A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种材质轻盈强度高的合成骨材料，按照质量组份计，所述合成骨材料的配方如下：袋鼠骨骼50‑70份，海螵蛸5‑10份，纳米二氧化钛6‑8份，硅灰石粉4‑6份，骨形成蛋白6‑18份，致孔剂6‑10份，稳定剂3‑5份，偶联剂3‑5份。本发明以袋鼠骨骼为主料，袋鼠骨骼是坚韧且轻质的材料，制成的合成骨材料材质轻盈且机械强度高，再辅以海螵蛸、纳米二氧化钛和硅灰石粉，可进一步增加其机械强度和韧性；本发明提供的一种材质轻盈强度高的合成骨材料的制备方法，通过煅烧、研磨、球磨、密炼和挤出等工艺，使得制备的合成骨材料，其材质压实轻盈且机械强度高，本发明步骤简单合理，操作方便，制备时间短，有利于推广和普及，可适用于鼻部美容。

Description

一种材质轻盈强度高的合成骨材料
技术领域
本发明属于合成骨技术领域，更具体地说，尤其涉及一种材质轻盈强度高的合成骨材料。同时，本发明还涉及一种材质轻盈强度高的合成骨材料的制备方法。
背景技术
在骨科领域,由于严重创伤、骨肿瘤、骨髓炎等多种原因所致的骨缺损十分常见。目前常用的骨修复材料包括自体骨和金属假体。自体骨增加了患者的创伤和痛苦；金属假体存在松动、断裂等问题。因此,合成骨替代材料移植修复骨缺损成为医学重点。合成骨是指可以替代人体骨或者修复骨组织缺损的人工生物材料。当需替换关节或治疗骨断裂时，最理想的方式是通过组织再生功能实现骨的自身修复。然而在许多情形下，人体骨并不能实现自身修复，例如骨组织坏死，骨关节创伤，这时就需要合成骨的帮助。
合成骨是一类高技术材料，可以是天然的，也可以是合成的，或是它们的复合。近年来已经制造出各类合成骨，并取得了一定的效果。然而其在机械强度方面和材质轻盈度方面还存在一定的缺陷。
发明内容
本发明的目的是为了解决现有技术中由于在机械强度方面和材质轻盈度方面存在一定的缺陷，而提出的一种材质轻盈强度高的合成骨材料。
为实现上述目的，本发明提供如下技术方案：一种材质轻盈强度高的合成骨材料，按照质量组份计，所述合成骨材料的配方如下：袋鼠骨骼50-70份，海螵蛸5-10份，纳米二氧化钛6-8份，硅灰石粉4-6份，骨形成蛋白6-18份，致孔剂6-10份，稳定剂3-5份，偶联剂3-5份。
优选的，所述袋鼠骨骼为成年袋鼠的股骨。
优选的，所述纳米二氧化钛的粒径为21nm。
优选的，所述稳定剂为氧化钙、硬脂酸钙和硬脂酸锌中的一种或几种。
优选的，所述偶联剂为钛酸酯偶联剂、硅烷偶联剂和铝锆酸酯偶联剂中的一种或几种。
本发明还提供一种材质轻盈强度高的合成骨材料的制备方法，包括如下步骤：
S1、将袋鼠骨骼用清水洗净后，先用盐酸溶液浸泡2-3 h，取出用清水洗净后在100℃的沸水中煮4-6 h，取出用清水洗净后，再放入100℃的干燥箱中24-30 h；
S2、将经S1处理后的袋鼠骨骼放入煅烧机中进行煅烧2-4 h，然后置于常温下冷却3-4h；
S3、将S2中得到的袋鼠骨骼和海螵蛸放入研钵机中进行研磨30-50 min，得到混合粉末A；
S4、将S3得到的混合粉末A、纳米二氧化钛、硅石灰粉和骨形成蛋白加入球磨机中，加入等质量的乙醇溶液进行湿法球磨，球磨时间为2-4 h，再放入80℃的干燥箱中进行烘干2-3h，得到混合粉末B；
S5、将混合粉末B注入密炼炉中，再加入致孔剂、稳定剂和偶联剂，边搅拌边加热至300-400℃，反应时间为40-60 min，反应结束后注入喷雾干燥塔进行干燥处理，得到颗粒状物料；
S6、将S5得到的颗粒状物料加入挤出机中熔融共混8-15分钟，在温度为200-250℃下挤出，即得合成骨材料。
优选的，所述S2中的煅烧机的煅烧温度为60-80℃，升温速度为15℃/min。
优选的，所述S3中的研钵机的研磨棒的转速为120 rpm，研钵转速为10 rpm。
本发明的技术效果和优点：本发明提供的一种材质轻盈强度高的合成骨材料，与传统技术相比，本发明以袋鼠骨骼为主料，袋鼠骨骼是坚韧且轻质的材料，制成的合成骨材料材质轻盈且机械强度高，再辅以海螵蛸、纳米二氧化钛和硅灰石粉，可进一步增加其机械强度和韧性；本发明提供的一种材质轻盈强度高的合成骨材料的制备方法，通过煅烧、研磨、球磨、密炼和挤出等工艺，使得制备的合成骨材料，其材质压实轻盈且机械强度高，本发明步骤简单合理，操作方便，制备时间短，有利于推广和普及。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合具体实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种材质轻盈强度高的合成骨材料，按照质量组份计，所述合成骨材料的配方如下：袋鼠骨骼50份，海螵蛸6份，纳米二氧化钛6份，硅灰石粉4份，骨形成蛋白8份，致孔剂6份，稳定剂3份，偶联剂3份。
本发明还提供一种材质轻盈强度高的合成骨材料的制备方法，包括如下步骤：
S1、将袋鼠骨骼用清水洗净后，先用盐酸溶液浸泡2 h，取出用清水洗净后在100℃的沸水中煮4 h，取出用清水洗净后，再放入100℃的干燥箱中24 h；
S2、将经S1处理后的袋鼠骨骼放入煅烧机中进行煅烧2 h，然后置于常温下冷却3 h，煅烧机的煅烧温度为60℃，升温速度为15℃/min；
S3、将S2中得到的袋鼠骨骼和海螵蛸放入研钵机中进行研磨30 min，得到混合粉末A，研钵机的研磨棒的转速为120 rpm，研钵转速为10 rpm；
S4、将S3得到的混合粉末A、纳米二氧化钛、硅石灰粉和骨形成蛋白加入球磨机中，加入等质量的乙醇溶液进行湿法球磨，球磨时间为2 h，再放入80℃的干燥箱中进行烘干2 h，得到混合粉末B；
S5、将混合粉末B注入密炼炉中，再加入致孔剂、稳定剂和偶联剂，边搅拌边加热至300℃，反应时间为40 min，反应结束后注入喷雾干燥塔进行干燥处理，得到颗粒状物料；
S6、将S5得到的颗粒状物料加入挤出机中熔融共混9分钟，在温度为220℃下挤出，即得合成骨材料。
实施例2
一种材质轻盈强度高的合成骨材料，按照质量组份计，所述合成骨材料的配方如下：袋鼠骨骼60份，海螵蛸8份，纳米二氧化钛7份，硅灰石粉5份，骨形成蛋白12份，致孔剂8份，稳定剂4份，偶联剂4份。
本发明还提供一种材质轻盈强度高的合成骨材料的制备方法，包括如下步骤：
S1、将袋鼠骨骼用清水洗净后，先用盐酸溶液浸泡2.5 h，取出用清水洗净后在100℃的沸水中煮5 h，取出用清水洗净后，再放入100℃的干燥箱中26 h；
S2、将经S1处理后的袋鼠骨骼放入煅烧机中进行煅烧3h，然后置于常温下冷却3.5 h，煅烧机的煅烧温度为70℃，升温速度为15℃/min；
S3、将S2中得到的袋鼠骨骼和海螵蛸放入研钵机中进行研磨40 min，得到混合粉末A，研钵机的研磨棒的转速为120 rpm，研钵转速为10 rpm；
S4、将S3得到的混合粉末A、纳米二氧化钛、硅石灰粉和骨形成蛋白加入球磨机中，加入等质量的乙醇溶液进行湿法球磨，球磨时间为3 h，再放入80℃的干燥箱中进行烘干2.5h，得到混合粉末B；
S5、将混合粉末B注入密炼炉中，再加入致孔剂、稳定剂和偶联剂，边搅拌边加热至350℃，反应时间为50 min，反应结束后注入喷雾干燥塔进行干燥处理，得到颗粒状物料；
S6、将S5得到的颗粒状物料加入挤出机中熔融共混8-15分钟，在温度为240℃下挤出，即得合成骨材料。
实施例3
一种材质轻盈强度高的合成骨材料，按照质量组份计，所述合成骨材料的配方如下：袋鼠骨骼70份，海螵蛸10份，纳米二氧化钛8份，硅灰石粉6份，骨形成蛋白18份，致孔剂10份，稳定剂5份，偶联剂5份。
本发明还提供一种材质轻盈强度高的合成骨材料的制备方法，包括如下步骤：
S1、将袋鼠骨骼用清水洗净后，先用盐酸溶液浸泡3 h，取出用清水洗净后在100℃的沸水中煮6 h，取出用清水洗净后，再放入100℃的干燥箱中30 h；
S2、将经S1处理后的袋鼠骨骼放入煅烧机中进行煅烧4 h，然后置于常温下冷却4 h，煅烧机的煅烧温度为80℃，升温速度为15℃/min；
S3、将S2中得到的袋鼠骨骼和海螵蛸放入研钵机中进行研磨50 min，得到混合粉末A，研钵机的研磨棒的转速为120 rpm，研钵转速为10 rpm；
S4、将S3得到的混合粉末A、纳米二氧化钛、硅石灰粉和骨形成蛋白加入球磨机中，加入等质量的乙醇溶液进行湿法球磨，球磨时间为4 h，再放入80℃的干燥箱中进行烘干3 h，得到混合粉末B；
S5、将混合粉末B注入密炼炉中，再加入致孔剂、稳定剂和偶联剂，边搅拌边加热至400℃，反应时间为60 min，反应结束后注入喷雾干燥塔进行干燥处理，得到颗粒状物料；
S6、将S5得到的颗粒状物料加入挤出机中熔融共混15分钟，在温度为250℃下挤出，即得合成骨材料。
综上所述：本发明提供的一种材质轻盈强度高的合成骨材料，与传统技术相比，本发明以袋鼠骨骼为主料，袋鼠骨骼是坚韧且轻质的材料，制成的合成骨材料材质轻盈且机械强度高，再辅以海螵蛸、纳米二氧化钛和硅灰石粉，可进一步增加其机械强度和韧性；本发明提供的一种材质轻盈强度高的合成骨材料的制备方法，通过煅烧、研磨、球磨、密炼和挤出等工艺，使得制备的合成骨材料，其材质压实轻盈且机械强度高，本发明步骤简单合理，操作方便，制备时间短，有利于推广和普及。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种材质轻盈强度高的合成骨材料，其特征在于：按照质量组份计，所述合成骨材料的配方如下：袋鼠骨骼50-70份，海螵蛸5-10份，纳米二氧化钛6-8份，硅灰石粉4-6份，骨形成蛋白6-18份，致孔剂6-10份，稳定剂3-5份，偶联剂3-5份。
2.根据权利要求1所述的一种材质轻盈强度高的合成骨材料，其特征在于：所述袋鼠骨骼为成年袋鼠的股骨。
3.根据权利要求1所述的一种材质轻盈强度高的合成骨材料，其特征在于：所述纳米二氧化钛的粒径为21nm。
4.根据权利要求1所述的一种材质轻盈强度高的合成骨材料，其特征在于：所述稳定剂为氧化钙、硬脂酸钙和硬脂酸锌中的一种或几种。
5.根据权利要求1所述的一种材质轻盈强度高的合成骨材料，其特征在于：所述偶联剂为钛酸酯偶联剂、硅烷偶联剂和铝锆酸酯偶联剂中的一种或几种。
6.一种权利要求1所述的材质轻盈强度高的合成骨材料的制备方法，其特征在于：包括如下步骤：
S1、将袋鼠骨骼用清水洗净后，先用盐酸溶液浸泡2-3 h，取出用清水洗净后在100℃的沸水中煮4-6 h，取出用清水洗净后，再放入100℃的干燥箱中24-30 h；
S2、将经S1处理后的袋鼠骨骼放入煅烧机中进行煅烧2-4 h，然后置于常温下冷却3-4h；
S3、将S2中得到的袋鼠骨骼和海螵蛸放入研钵机中进行研磨30-50 min，得到混合粉末A；
S4、将S3得到的混合粉末A、纳米二氧化钛、硅石灰粉和骨形成蛋白加入球磨机中，加入等质量的乙醇溶液进行湿法球磨，球磨时间为2-4 h，再放入80℃的干燥箱中进行烘干2-3h，得到混合粉末B；
S5、将混合粉末B注入密炼炉中，再加入致孔剂、稳定剂和偶联剂，边搅拌边加热至300-400℃，反应时间为40-60 min，反应结束后注入喷雾干燥塔进行干燥处理，得到颗粒状物料；
S6、将S5得到的颗粒状物料加入挤出机中熔融共混8-15分钟，在温度为200-250℃下挤出，即得合成骨材料。
7.根据权利要求6所述的一种材质轻盈强度高的合成骨材料的制备方法，其特征在于：所述S2中的煅烧机的煅烧温度为60-80℃，升温速度为15℃/min。
8.根据权利要求6所述的一种材质轻盈强度高的合成骨材料的制备方法，其特征在于：所述S3中的研钵机的研磨棒的转速为120 rpm，研钵转速为10 rpm。
CN201810733698.6A 2018-07-06 2018-07-06 一种材质轻盈强度高的合成骨材料 Pending CN108525010A (zh)