CN108516798A - 一种鼓钉洗钧瓷工艺品的制作方法 - Google Patents

一种鼓钉洗钧瓷工艺品的制作方法 Download PDF

Info

Publication number
CN108516798A
CN108516798A CN201810624394.6A CN201810624394A CN108516798A CN 108516798 A CN108516798 A CN 108516798A CN 201810624394 A CN201810624394 A CN 201810624394A CN 108516798 A CN108516798 A CN 108516798A
Authority
CN
China
Prior art keywords
blank
glaze
clay
pottery
drawing machine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810624394.6A
Other languages
English (en)
Inventor
杨俊峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810624394.6A priority Critical patent/CN108516798A/zh
Publication of CN108516798A publication Critical patent/CN108516798A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种鼓钉洗钧瓷工艺品的制作方法，其特征在于：包括以下步骤，步骤1、选取陶土；步骤2、制浆练泥；步骤3、成型；将步骤2的泥块放在拉坯机上，根据预先的设计，用手拉出器型，即为毛坯，在拉坯机上把毛坯旋成厚度合适、造型美观的壳体，旋坯后在坯体上粘接足、鼓钉附件；步骤4、素烧；步骤5、实釉；步骤6、烧制；所述的陶土包括以下组分：高岭土65‑75%，砂石8‑15%，铅粉8‑12%，莫来石8‑10%，铁矿石3‑5%，氧化钴0.2‑0.4%，食用碱0.3‑0.5%；采用本发明的陶土，钧瓷成品率高。

Description

一种鼓钉洗钧瓷工艺品的制作方法
技术领域
本发明涉及钧瓷工艺领域，尤其涉及一种鼓钉洗钧瓷工艺品的制作方法。
背景技术
陶瓷是中华文化的重要组成部分之一，而钧瓷又是中华陶瓷文化中的一颗璀璨明珠。钧瓷发源于东汉，是宋代五大名窑瓷器之一，是传统制瓷工艺中的珍品，以独特的窑变艺术而著称于世，素有“黄金有价钧无价”和“家有万贯，不如钧瓷一片”的美誉。钧瓷被誉为中国“五大名瓷”之首，为我国河南省禹州市的特产，其主要特征为瓷器的颜色复杂化，改变了古代瓷器的单色釉发展脉络，具有“进窑一色，出窑万彩”等独特的特色，是其他陶瓷工艺品无法实现和比拟的。本发明根据"钧官窑鼓钉神洗"为发明依据，结合仿青铜制作出，壳体周身凸起鼓钉装饰，壳体下部有三足，钧瓷的关键在于瓷釉，瓷釉在进行釉烧后变彩决定着钧瓷的价值，在烧制时，钧瓷在出窑冷却后极易开裂，从而导致珍品率低。
发明内容
有鉴于此，本发明提供一种鼓钉洗钧瓷工艺品的制作方法，坯釉结合性能好，成品率高。
一种鼓钉洗钧瓷工艺品的制作方法，包括以下步骤：
步骤1、选取陶土；所述的陶土包括以下组分：高岭土65-75%，砂石8-15%，铅粉8-12%，莫来石8-10%，铁矿石3-5%，氧化钴0.2-0.4%，食用碱0.3-0.5%。
步骤2、制浆练泥；将步骤1的陶土首先进行粗碎成沙粒状或粉状，然后进行磨碎，其磨碎为230-250目，加水混合后球磨，制成浆料，将制成的浆料练成泥块。
步骤3、成型；将步骤2的泥块放在拉坯机上，根据预先的设计，用手拉出器型，即为毛坯，在拉坯机上把毛坯旋成厚度合适、造型美观的壳体，旋坯后在坯体上粘接足、鼓钉附件。
步骤4、素烧；将步骤3所制的坯体放入素烧窑中，在900℃-950℃的温度下烧制5-6个小时。
步骤5、施釉；将素烧后的坯体表面除杂处理后进行表面涂釉材，主体部分采用刷釉或者喷釉或者蘸釉的方法进行施釉；釉料是将包括黄长石35-40%，白长石15-25%，方解石10-20%，氧化铜0.3-0.5%，石英7-10%，滑石2.5-5%，氧化锌3-5%，熔块17-20%，氧化铁0.2-0.5% 的釉料进行粉碎，混合，球磨，使其成为细度为400-450目的细粉，加水搅拌混合球磨后制成釉浆。
步骤6、烧制；将施釉后并干燥的坯体放入窑中在1280℃-1300℃的温度烧制12-15个小时。
本发明的有益效果为：
1、本发明的釉料中加入氧化锌和氧化铁，降低了釉的熔融温度和高温粘度，改善釉的化学稳定性和热稳定性，使釉具有良好的透明度和光泽度，坯釉结合性能好，同时采用本发明的陶土、釉料及制作步骤，钧瓷的成品率高，鼓钉洗在烧制时外部与内部温度不一，其色变效果丰富，其器形及颜色更能体现本发明作品的创意和艺术效果。
附图说明
图1为本发明的结构示意图；
壳体1；足2；鼓钉3。
具体实施方式
下面结合附图及实施例对本发明作进一步的详细说明。
实施例1
如图1所示，一种鼓钉洗钧瓷工艺品的制作方法，包括以下步骤：
步骤1、选取陶土；所述的陶土包括以下组分：高岭土72.5%，砂石8%，铅粉8%，莫来石8%，铁矿石3%，氧化钴0.2%，食用碱0.3%。
步骤2、制浆练泥；将步骤1的陶土首先进行粗碎成沙粒状或粉状，然后进行磨碎，其磨碎为230-250目，加水混合后球磨，制成浆料，将制成的浆料练成泥块。
步骤3、成型；将步骤2的泥块放在拉坯机上，根据预先的设计，用手拉出器型，即为毛坯，在拉坯机上把毛坯旋成厚度合适、造型美观的壳体1，旋坯后在坯体上粘接足2、鼓钉3附件。
步骤4、素烧；将步骤3所制的坯体放入素烧窑中，在900℃-950℃的温度下烧制5-6个小时。
步骤5、施釉；将素烧后的坯体表面除杂处理后进行表面涂釉材，主体部分采用刷釉或者喷釉或者蘸釉的方法进行施釉；釉料是将包括黄长石35%，白长石20%，方解石15%，氧化铜0.3%，石英7%，滑石2.5%，氧化锌3%，熔块17%，氧化铁0.2% 的釉料进行粉碎，混合，球磨，使其成为细度为400-450目的细粉，加水搅拌混合球磨后制成釉浆；
步骤6、烧制；将施釉后并干燥的坯体放入窑中在1280℃-1300℃的温度烧制12-15个小时。在以上的实施例中应当注意，在主体部分施釉时，应当保证施釉的釉层厚度不大于1毫米，以保证减少釉层的开裂，影响本作品的视感。
实施例2
如图1所示，一种鼓钉洗钧瓷工艺品的制作方法，包括以下步骤：
步骤1、选取陶土；所述的陶土包括以下组分：高岭土65%，砂石10%，铅粉12%，莫来石8%，铁矿石4%，氧化钴0.5%，食用碱0.5%。
步骤2、制浆练泥；将步骤1的陶土首先进行粗碎成沙粒状或粉状，然后进行磨碎，其磨碎为230-250目，加水混合后球磨，制成浆料，将制成的浆料练成泥块。
步骤3、成型；将步骤2的泥块放在拉坯机上，根据预先的设计，用手拉出器型，即为毛坯，在拉坯机把毛坯旋成厚度合适、造型美观的壳体1，旋坯后在坯体上粘接足2、鼓钉3附件。
步骤4、素烧；将步骤3所制的坯体放入素烧窑中，在900℃-950℃的温度下烧制5-6个小时。
步骤5、施釉；将素烧后的坯体表面除杂处理后进行表面涂釉材，主体部分采用刷釉或者喷釉或者蘸釉的方法进行施釉；釉料是将包括黄长石38%，白长石15%，方解石10%，氧化铜0.5%，石英8%，滑石3%，氧化锌5%，熔块20%，氧化铁0.5% 的釉料进行粉碎，混合，球磨，使其成为细度为400-450目的细粉，加水搅拌混合球磨后制成釉浆。
步骤6、烧制；将施釉后并干燥的坯体放入窑中在1280℃-1300℃的温度烧制12-15个小时。
在以上的实施例中应当注意，在主体部分施釉时，应当保证施釉的釉层厚度不大于1毫米，以保证减少釉层的开裂，影响本作品的视感。

Claims (1)

1.一种鼓钉洗钧瓷工艺品的制作方法，其特征在于：包括以下步骤，步骤1、选取陶土；步骤2、制浆练泥；步骤3、成型；将步骤2的泥块放在拉坯机上，根据预先的设计，用手拉出器型，即为毛坯，在拉坯机上把毛坯旋成厚度合适、造型美观的壳体，旋坯后在坯体上粘接足、鼓钉附件；步骤4、素烧；步骤5、施釉；步骤6、烧制；所述的陶土包括以下组分：高岭土65-75%，砂石8-15%，铅粉8-12%，莫来石8-10%，铁矿石3-5%，氧化钴0.2-0.4%，食用碱0.3-0.5%。
CN201810624394.6A 2018-06-16 2018-06-16 一种鼓钉洗钧瓷工艺品的制作方法 Pending CN108516798A (zh)