CN108504242A - A kind of environment-friendly type high transparency coating - Google Patents
A kind of environment-friendly type high transparency coating Download PDFInfo
- Publication number
- CN108504242A CN108504242A CN201710358898.3A CN201710358898A CN108504242A CN 108504242 A CN108504242 A CN 108504242A CN 201710358898 A CN201710358898 A CN 201710358898A CN 108504242 A CN108504242 A CN 108504242A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- agent
- friendly type
- type high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the raw material compositions of a kind of environment-friendly type high transparency coating, including following parts by weight：80 100 parts of epoxy resin；50 60 parts of polyester；24 parts of levelling agent；0.2 1 parts of styrax；45 60 parts of delustering agent；5 10 parts of curing agent.The present invention passes through the reasonable compounding of component and accurately controlling for dosage so that coating obtained has the high grade of transparency, substantially increases the aesthetics of product appearance, decorative appearance field is can be widely used for, and raw material sources are extensive, it is environmentally protective, industrialization is at low cost, conducive to increasing economic efficiency.
Description
Technical field
The present invention relates to decorative paint technical fields, more particularly to a kind of environment-friendly type high transparency coating.
Background technology
Pursuit with people to life, the decoration of electronic product appearance increasingly become the important means for attracting consumer
One of, but with the raising of people's material and cultural life, the requirement to product appearance is no longer limited to decorate for the moment
Property and aesthetic effect, and to the dicoration of product appearance, more stringent requirements are proposed with the persistence of aesthetic effect, especially produces
The transparency of product decorative appearance coating.
Invention content
The object of the present invention is to provide a kind of environment-friendly type high transparency coating, are decorated for product appearance.
The technical solution that the present invention is proposed in view of the above technical defects is：
A kind of environment-friendly type high transparency coating includes the raw material composition of following parts by weight：
80-100 parts of epoxy resin；
50-60 parts of polyester；
2-4 parts of levelling agent；
0.2-1 parts of styrax；
45-60 parts of delustering agent；
5-10 parts of curing agent.
Further, including the raw material of following weight forms：
80 parts of epoxy resin；
50 parts of polyester；
2 parts of levelling agent；
0.2 part of styrax；
45 parts of delustering agent；
5 parts of curing agent.
Further, including the raw material of following weight forms：
100 parts of epoxy resin；
60 parts of polyester；
4 parts of levelling agent；
1 part of styrax；
60 parts of delustering agent；
10 parts of curing agent.
Further, the levelling agent is polyether siloxane copolymer.
Further, the delustering agent is organosilicon.
The beneficial effects of the invention are as follows：The present invention passes through the reasonable compounding of component and accurately controlling for dosage so that system
The coating obtained has the high grade of transparency, substantially increases the aesthetics of product appearance, can be widely used for decorative appearance field, Er Qieyuan
Material derives from a wealth of sources, environmentally protective, and industrialization is at low cost, conducive to increasing economic efficiency.
Specific implementation mode
Present invention is further described in detail With reference to embodiment.
Embodiment 1
A kind of environment-friendly type high transparency coating includes the raw material composition of following parts by weight：
80 parts of epoxy resin；
50 parts of polyester；
2 parts of levelling agent；
0.2 part of styrax；
45 parts of delustering agent；
5 parts of curing agent.
Embodiment 2
A kind of environment-friendly type high transparency coating includes the raw material composition of following parts by weight：
90 parts of epoxy resin；
55 parts of polyester；
3 parts of levelling agent；
0.6 part of styrax；
55 parts of delustering agent；
8 parts of curing agent.
Embodiment 3
A kind of environment-friendly type high transparency coating includes the raw material composition of following parts by weight：
100 parts of epoxy resin；
60 parts of polyester；
4 parts of levelling agent；
1 part of styrax；
60 parts of delustering agent；
10 parts of curing agent.
The beneficial effects of the invention are as follows：The present invention passes through the reasonable compounding of component and accurately controlling for dosage so that system
The coating obtained has the high grade of transparency, substantially increases the aesthetics of product appearance, can be widely used for decorative appearance field, Er Qieyuan
Material derives from a wealth of sources, environmentally protective, and industrialization is at low cost, conducive to increasing economic efficiency.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, any made by repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (5)
1. a kind of environment-friendly type high transparency coating, it is characterised in that：Raw material composition including following parts by weight：
80-100 parts of epoxy resin；
50-60 parts of polyester；
2-4 parts of levelling agent；
0.2-1 parts of styrax；
45-60 parts of delustering agent；
5-10 parts of curing agent.
2. a kind of environment-friendly type high transparency coating according to claim 1, it is characterised in that：Raw material group including following weight
At：
80 parts of epoxy resin；
50 parts of polyester；
2 parts of levelling agent；
0.2 part of styrax；
45 parts of delustering agent；
5 parts of curing agent.
3. a kind of environment-friendly type high transparency coating according to claim 1, it is characterised in that：Raw material group including following weight
At：
100 parts of epoxy resin；
60 parts of polyester；
4 parts of levelling agent；
1 part of styrax；
60 parts of delustering agent；
10 parts of curing agent.
4. a kind of environment-friendly type high transparency coating according to claim 1, it is characterised in that：The levelling agent is polyethers silica
Alkyl copolymer.
5. a kind of environment-friendly type high transparency coating according to claim 1, it is characterised in that：The delustering agent is organosilicon.