CN106221561A - A kind of anticorrosion aging resistance exterior coating - Google Patents

A kind of anticorrosion aging resistance exterior coating Download PDF

Info

Publication number
CN106221561A
CN106221561A CN201610618354.1A CN201610618354A CN106221561A CN 106221561 A CN106221561 A CN 106221561A CN 201610618354 A CN201610618354 A CN 201610618354A CN 106221561 A CN106221561 A CN 106221561A
Authority
CN
China
Prior art keywords
parts
aging resistance
exterior coating
coating
anticorrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610618354.1A
Other languages
Chinese (zh)
Inventor
赵文刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAICANG SHUNRUCHENG BUILDING MATERIALS Co Ltd
Original Assignee
TAICANG SHUNRUCHENG BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAICANG SHUNRUCHENG BUILDING MATERIALS Co Ltd filed Critical TAICANG SHUNRUCHENG BUILDING MATERIALS Co Ltd
Priority to CN201610618354.1A priority Critical patent/CN106221561A/en
Publication of CN106221561A publication Critical patent/CN106221561A/en
Pending legal-status Critical Current

Abstract

The present invention proposes a kind of anticorrosion aging resistance exterior coating, and the raw material including following parts by weight forms: emulsion binder 40 ~ 65 parts；Filler 8 ~ 20 parts；Fiber 3 ~ 6 parts；Coalescents 1 ~ 6 part；Thickening agent 0.3 ~ 2.5 part；Levelling agent 0.3 ~ 1.2 part；Defoamer 0.2 ~ 0.6 part；Dispersant 0.5 ~ 1.5 part；Pigment 1 ~ 5 part；Deionized water 5 ~ 20 parts.Formulation for coating material proposed by the invention is reasonable, preparation method is simple, be not easy dry linting, come off, the long algae of mildew, weatherability and mildew-resistant algae property are good, reduce the aging of exterior wall, thus improve its service life, simultaneously, this coating also has certain heat-insulating property, and aesthetics is high, meets the artificial use requirement to coating.

Description

A kind of anticorrosion aging resistance exterior coating
Technical field
The present invention relates to building material technical field, be specifically related to a kind of anticorrosion aging resistance exterior coating.
Background technology
Paint finishing can bond and be formed the material of complete and tough and tensile protecting film very well in body surface with matrix material, claims For coating.Coating and paint are the identicals concept.Paint is people's custom used for a long time titles, after introducing China, and profit the most always It is used in building trade.The effect of coating may be summarized to be three aspects: protective effect, decoration function, specific function effect.It is coated with The general composition of material: comprise film forming matter, color stuffing, solvent, auxiliary agent.
Building external paint has decoration functions, defencive function and livability and improves function.Proportion shared by various functions It is not quite similar because application target is different.Decoration functions is the function beautifying the appearance value improving it by building. Mainly include the concept of the concept in terms of plane color, pattern and gloss and three-dimensional pattern.But will with building originally The size and shape of the moulding of body and base material itself matches, and just can fully play out.Defencive function refers to protection building The thing function with destruction the most protected from environmental.Different types of content defencive function required by protective also each not phase With.Building external paint is directly exposed in external environment condition, protected from environmental very big, the most directly exacerbate coating aging, Corruption so that the service life of coating reduces.
Therefore, for the problems referred to above, the present invention proposes a kind of new technical scheme.
Summary of the invention
It is an object of the invention to provide a kind of formula reasonable, improve weatherability, mildew-resistant algae property is good, improves making of coating With the anticorrosion aging resistance exterior coating in life-span.
The present invention is achieved through the following technical solutions:
A kind of anticorrosion aging resistance exterior coating, the raw material including following parts by weight forms:
Emulsion binder 40 ~ 65 parts；
Filler 8 ~ 20 parts；
Fiber 3 ~ 6 parts；
Coalescents 1 ~ 6 part；
Thickening agent 0.3 ~ 2.5 part；
Levelling agent 0.3 ~ 1.2 part；
Defoamer 0.2 ~ 0.6 part；
Dispersant 0.5 ~ 1.5 part；
Pigment 1 ~ 5 part；
Deionized water 5 ~ 20 parts.
Further, described emulsion binder is organosilan and organosiloxane mixed emulsion.
Further, described filler includes hollow glass micropearl 2 ~ 8 parts, 2 ~ 6 parts of rutile titanium white lead, silicon dioxide powder 1 ~ 3 parts, heavy calcium carbonate 2 ~ 5 parts and calcite in powder 1 ~ 4 part.
Further, described fiber is aluminium silicate chopped strand.
Further, described coalescents is COASOL or ten diester alcohol.
Further, described defoamer is alkali resistant mineral oil type antifoaming agent.
The invention has the beneficial effects as follows: formulation for coating material proposed by the invention is reasonable, and preparation method is simple, it is not easy to fall Powder, come off, the long algae of mildew, weatherability and mildew-resistant algae property are good, reduce the aging of exterior wall, thus improve its service life, with Time, this coating also has certain heat-insulating property, and aesthetics is high, meets the artificial use requirement to coating.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
A kind of anticorrosion aging resistance exterior coating, the raw material including following parts by weight forms:
Emulsion binder 40 parts；
Filler 8 parts；
Aluminium silicate chopped strand 3 parts；
Ten diester alcohol 1 part；
Thickening agent 0.3 part；
Levelling agent 0.3 part；
Defoamer 0.2 part；
Dispersant 0.5 part；
Pigment 1 part；
Deionized water 5 parts.
In the present embodiment, emulsion binder is organosilan and organosiloxane mixed emulsion, and filler includes hollow glass Microballon 2 parts, 2 parts of rutile titanium white lead, silicon dioxide powder 1 part, heavy calcium carbonate 2 parts and calcite in powder 1 part, coalescents Being alternatively COASOL, defoamer is alkali resistant mineral oil type antifoaming agent.
Embodiment 2
A kind of anticorrosion aging resistance exterior coating, the raw material including following parts by weight forms:
Emulsion binder 50 parts；
Filler 15 parts；
Aluminium silicate chopped strand 4 parts；
Ten diester alcohol 3 parts；
Thickening agent 1.2 parts；
Levelling agent 0.8 part；
Defoamer 0.4 part；
Dispersant 1.2 parts；
Pigment 3 parts；
Deionized water 12 parts.
In the present embodiment, emulsion binder is organosilan and organosiloxane mixed emulsion, and filler includes hollow glass Microballon 4 parts, 3 parts of rutile titanium white lead, silicon dioxide powder 2 parts, heavy calcium carbonate 3 parts and calcite in powder 3 parts, coalescents Being alternatively COASOL, defoamer is alkali resistant mineral oil type antifoaming agent.
Embodiment 3
A kind of anticorrosion aging resistance exterior coating, the raw material including following parts by weight forms:
Emulsion binder 65 parts；
Filler 20 parts；
Aluminium silicate chopped strand 6 parts；
Ten diester alcohol 6 parts；
Thickening agent 2.5 parts；
Levelling agent 1.2 parts；
Defoamer 0.6 part；
Dispersant 1.5 parts；
Pigment 5 parts；
Deionized water 20 parts.
In the present embodiment, emulsion binder is organosilan and organosiloxane mixed emulsion, and filler includes hollow glass Microballon 6 parts, 4 parts of rutile titanium white lead, silicon dioxide powder 3 parts, heavy calcium carbonate 4 parts and calcite in powder 3 parts, coalescents Being alternatively COASOL, defoamer is alkali resistant mineral oil type antifoaming agent.
Formulation for coating material proposed by the invention is reasonable, and preparation method is simple, it is not easy to dry linting, come off, the long algae of mildew, weather-proof Property and mildew-resistant algae property are good, reduce the aging of exterior wall, thus improve its service life, and meanwhile, this coating also has certain Heat-insulating property, aesthetics is high, meets the artificial use requirement to coating.
The above, be only embodiments of the invention, is not the restriction that the present invention makees any other form, and Any amendment made according to the technical spirit of the present invention or equivalent variations, still fall within scope of the present invention.

Claims (6)

1. an anticorrosion aging resistance exterior coating, it is characterised in that: include that the raw material of following parts by weight forms:
Emulsion binder 40 ~ 65 parts；
Filler 8 ~ 20 parts；
Fiber 3 ~ 6 parts；
Coalescents 1 ~ 6 part；
Thickening agent 0.3 ~ 2.5 part；
Levelling agent 0.3 ~ 1.2 part；
Defoamer 0.2 ~ 0.6 part；
Dispersant 0.5 ~ 1.5 part；
Pigment 1 ~ 5 part；
Deionized water 5 ~ 20 parts.
A kind of anticorrosion aging resistance exterior coating, it is characterised in that: described emulsion binder is organosilicon Alkane and organosiloxane mixed emulsion.
A kind of anticorrosion aging resistance exterior coating, it is characterised in that: described filler includes hollow glass Microballon 2 ~ 8 parts, 2 ~ 6 parts of rutile titanium white lead, silicon dioxide powder 1 ~ 3 part, heavy calcium carbonate 2 ~ 5 parts and calcite in powder 1 ~ 4 Part.
A kind of anticorrosion aging resistance exterior coating, it is characterised in that: described fiber is aluminium silicate chopped Fiber.
A kind of anticorrosion aging resistance exterior coating, it is characterised in that: described coalescents is COASOL Or ten diester alcohol.
A kind of anticorrosion aging resistance exterior coating, it is characterised in that: described defoamer is alkali resistant ore deposit Thing oil type defoamer.
CN201610618354.1A 2016-08-01 2016-08-01 A kind of anticorrosion aging resistance exterior coating Pending CN106221561A (en)