CN104448977A - Anti-ultraviolet wear-resistant curable coating - Google Patents
Anti-ultraviolet wear-resistant curable coating Download PDFInfo
- Publication number
- CN104448977A CN104448977A CN201310435848.2A CN201310435848A CN104448977A CN 104448977 A CN104448977 A CN 104448977A CN 201310435848 A CN201310435848 A CN 201310435848A CN 104448977 A CN104448977 A CN 104448977A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- curable coating
- coating
- resistant curable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-ultraviolet wear-resistant curable coating which is prepared from the following raw materials in parts by weight: 2.5-4 parts of a photosensitive initiator, 2-3 parts of nano-zirconium oxide, 0.8-1.5 parts of acrylic polyol, 5.6-7.2 parts of carbamate, 4.5-6.6 parts of vinyl acetate maleate, 1.2-1.5 parts of itaconic acid, 0.35-0.78 part of a filler, 0.3-0.5 part of a dispersant and 0.1-0.2 part of a mildew-proof agent. The anti-ultraviolet wear-resistant curable coating disclosed by the invention can obtain an aesthetic and high-performance coated film by performing spraying construction once; in comparison with a traditional way of coating twice or three times, the anti-ultraviolet wear-resistant curable coating has the advantages of high production efficiency, low energy consumption, low cost and the like, the obtained coated film has the characteristics of great appearance, excellent resistance to scratching, wear resistance and solvent resistance and the like; and in addition, a water-based colored coating composition has the advantages of no or a relatively low content of volatile organic compounds and little environmental pollution, and can be used as an environment-friendly material.
Description
Technical field
The present invention relates to a kind of coating, especially relate to a kind of can antiultraviolet wear-resisting coating material solidified, belong to paint field.
Background technology
Past is used for the coating of base material and is mostly solvent based coating, however solvent based coating be discharged into volatile organic solvent in air, but can make a very bad impression to environment.In recent years, because the mankind are to the attention of environmental protection and the energy, countries in the world strictly control the content of VOC in coating in succession, impel the research of coating to be gradually transferred to water-borne coatings by the solvent based coating commonly used.Compared with solvent based coating, water-borne coatings has not lower containing VOC or VOC content advantage, and environmental pollution is low.Traditional coating at plastic part surface, generally needs roasting through two paintings two or that three paintings three are roasting programs.Be coated with for two and two bake, first spray-applied primer, priming paint, still can sealing substrate the finish paint of spraying and the sticking power etc. of substrate after strengthening except providing color required on plastic part surface.Priming paint is after overbaking, and then, then spray paint, finish paint and priming paint are arranged in pairs or groups and made Bulk coat show gloss and color sense, and make coating have the characteristics such as high abrasion.The operation of multiple working procedure, not only the consumption of coating is large, also during unusual work consuming, and then adds cost.Therefore, industry is all devoted to develop and can be reached the wear-resisting coating material solidified of the coating had concurrently with performance attractive in appearance by an application.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, provide a kind of can antiultraviolet wear-resisting coating material solidified, improve ultraviolet resistance and the stability of coating, asepsis environment-protecting, improves production efficiency, reduces production cost.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of can antiultraviolet wear-resisting coating material solidified, it is made up of the raw material of following parts by weight:
Photoinitiator 2.5-4 part, nano zircite 2-3 part, acrylic polyol 0.8-1.5 part, carbamate 5.6-7.2 part, vinyl-acetic ester maleic acid ester 4.5-6.6 part, methylene-succinic acid 1.2-1.5 part, filler 0.35-0.78 part, dispersion agent 0.3-0.5 part; Mould inhibitor 0.1-0.2 part.
Optimize, above-mentioned can antiultraviolet wear-resisting coating material solidified, it is made up of the raw material of following parts by weight:
Photoinitiator 2.5 parts, nano zircite 2 parts, acrylic polyol 0.8 part, carbamate 5.6 parts, vinyl-acetic ester maleic acid ester 4.5 parts, methylene-succinic acid 1.2 parts, filler 0.35 part, dispersion agent 0.3 part; Mould inhibitor 0.1 part.
Optimize, above-mentioned can antiultraviolet wear-resisting coating material solidified, its filler is process white.
Antiultraviolet of the present invention wear-resisting coating material solidified when can obtain the film had concurrently with high-performance attractive in appearance with a spraying application, compared to the application mode of traditional secondary or three times; The present invention has the advantages such as high efficiency, low power consuming and low cost, and the paint film of acquisition has that outward appearance is good, resistance to scratches good, wear resistance and the good feature of solvent resistance; Aqueous pigmented coating composition has not containing volatile organic compounds or the lower advantage of its content in addition, and environmental pollution is low, can be used as environment-friendly materials.
Embodiment
Below in conjunction with embodiment, invention is further described.
Embodiment 1
The present invention be a kind of can antiultraviolet wear-resisting coating material solidified, it is made up of the raw material of following parts by weight: photoinitiator 2.5 parts, nano zircite 2 parts, acrylic polyol 0.8 part, carbamate 5.6 parts, vinyl-acetic ester maleic acid ester 4.5 parts, methylene-succinic acid 1.2 parts, filler and process white 0.35 part, dispersion agent 0.3 part; Mould inhibitor 0.1 part.
Embodiment 2
The present invention be a kind of can antiultraviolet wear-resisting coating material solidified, it is made up of the raw material of following parts by weight: photoinitiator 4 parts, nano zircite 3 parts, acrylic polyol 1.5 parts, carbamate 7.2 parts, vinyl-acetic ester maleic acid ester 6.6 parts, methylene-succinic acid 1.5 parts, filler and process white 0.78 part, dispersion agent 0.5 part; Mould inhibitor 0.2 part.
Embodiment 3
The present invention be a kind of can antiultraviolet wear-resisting coating material solidified, it is made up of the raw material of following parts by weight: photoinitiator 3.2 parts, nano zircite 2.5 parts, acrylic polyol 1.2 parts, carbamate 6.2 parts, vinyl-acetic ester maleic acid ester 5.4 parts, methylene-succinic acid 1.4 parts, filler and process white 0.55 part, dispersion agent 0.4 part; Mould inhibitor 0.15 part.Antiultraviolet of the present invention wear-resisting coating material solidified when can obtain the film had concurrently with high-performance attractive in appearance with a spraying application, compared to the application mode of traditional secondary or three times; The present invention has the advantages such as high efficiency, low power consuming and low cost, and the paint film of acquisition has that outward appearance is good, resistance to scratches good, wear resistance and the good feature of solvent resistance; Aqueous pigmented coating composition has not containing volatile organic compounds or the lower advantage of its content in addition, and environmental pollution is low, can be used as environment-friendly materials.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned citing; those skilled in the art; in essential scope of the present invention, the change made, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned citing; those skilled in the art; in essential scope of the present invention, the change made, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (3)
1. one kind can antiultraviolet wear-resisting coating material solidified, it is characterized in that:
Be made up of the raw material of following parts by weight:
Photoinitiator 2.5-4 part, nano zircite 2-3 part, acrylic polyol 0.8-1.5 part, carbamate 5.6-7.2 part, vinyl-acetic ester maleic acid ester 4.5-6.6 part, methylene-succinic acid 1.2-1.5 part, filler 0.35-0.78 part, dispersion agent 0.3-0.5 part; Mould inhibitor 0.1-0.2 part.
2. according to claim 1 can antiultraviolet wear-resisting coating material solidified, it is characterized in that:
Be made up of the raw material of following parts by weight:
Photoinitiator 2.5 parts, nano zircite 2 parts, acrylic polyol 0.8 part, carbamate 5.6 parts, vinyl-acetic ester maleic acid ester 4.5 parts, methylene-succinic acid 1.2 parts, filler 0.35 part, dispersion agent 0.3 part; Mould inhibitor 0.1 part.
3. according to claim 1 can antiultraviolet wear-resisting coating material solidified, it is characterized in that: described filler is process white.