CN108486889B - 一种府绸类紧密织物上浆用浆料的制备方法 - Google Patents

一种府绸类紧密织物上浆用浆料的制备方法 Download PDF

Info

Publication number
CN108486889B
CN108486889B CN201810234491.4A CN201810234491A CN108486889B CN 108486889 B CN108486889 B CN 108486889B CN 201810234491 A CN201810234491 A CN 201810234491A CN 108486889 B CN108486889 B CN 108486889B
Authority
CN
China
Prior art keywords
sizing agent
fiber
sizing
poplin
paste
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201810234491.4A
Other languages
English (en)
Other versions
CN108486889A (zh
Inventor
叶澄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Fuyang he chemical fiber auxiliary Co.,Ltd.
Original Assignee
Hangzhou Fuyang He Chemical Fiber Auxiliary Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Fuyang He Chemical Fiber Auxiliary Co ltd filed Critical Hangzhou Fuyang He Chemical Fiber Auxiliary Co ltd
Priority to CN201810234491.4A priority Critical patent/CN108486889B/zh
Publication of CN108486889A publication Critical patent/CN108486889A/zh
Application granted granted Critical
Publication of CN108486889B publication Critical patent/CN108486889B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种府绸类紧密织物纤维上浆用浆料的制备方法，将聚氧乙烯、聚氧丙烯醚、聚丙烯酰胺、双鼠李糖脂和浆纱膏投加入装有搅拌器、温度计和回流冷凝管的烧瓶中，加入去离子水和牛磺酸钠，升温至85℃，通入氮气保护，搅拌40‑50min，然后缓慢滴入柠檬酸，约2h滴加完毕，保温2h后加入PMA浆料、月桂醇聚氧乙烯醚、乙醇，再反应9‑12h，冷却至室温，即得到府绸类紧密织物上浆用浆料。用该方法制备得到的浆料上浆后纤维粘着力强，抱合力大，在纤维外表形成的皮膜能防止纤维起毛；并且不因摩擦而掉浆或使纤维强力下降，能增加纤维的强度，同时保持纤维的弹性、柔软性和延伸度。

Description

一种府绸类紧密织物上浆用浆料的制备方法
技术领域
本发明涉及一种纺织品上浆剂的制备方法，特别涉及一种府绸类紧密织物上浆用浆料的制备方法。
背景技术
纺织工业中，上浆剂是一种重要的纺织用助剂。目前，基本上都是用淀粉或变性淀粉添加定量的聚乙烯醇（PVA）进行混合后，熬制上浆。上述上浆剂在聚乙烯醇PVA退浆时起泡很大，且不易降解，会对环境污染严重。而目前如果纯用变性淀粉或淀粉进行上浆，无论从对线的粘着力，还是浆膜的断裂强度、浆膜断裂伸长率、耐磨性等都不能达到标准要求。
上浆剂在国外的研究已经比较成熟，国内发展相对有一定的差距。现有的公开资料多 集中于碳纤维的上浆剂。例如，衫浦直树等人的发明专利“碳纤维用上浆剂、其水分散液、 上浆处理过的碳纤维、使用该碳纤维的片状物、以及碳纤维强化复合材料（CN1701148A）” 对上浆剂组分做了详尽的权利要求；李春刚等人的发明专利“自乳化型碳纤维用聚氨酯类 环氧上浆剂及其制备方法（CN101845755A）”通过异氰酸酯改性，环氧改性，制备了具有自乳化功能的聚氨酯上浆剂；刘芝兰等人的发明专利“一种用于碳纤维的水溶性上浆剂及 其制备方法（CN102691211A）”通过魔芋低聚糖和氧化淀粉复配，制备了一种对碳纤维有 较好粘附性的上浆剂。但关于府绸类紧密织物的表面上浆剂则没有报道。
发明内容
本发明的目的在于克服上述问题，提供一种府绸类紧密织物纤维上浆用浆料的制备方法，该浆料上浆后纤维粘着力强，抱合力大，在纤维外表形成的皮膜能防止纤维起毛；并且不因摩擦而掉浆或使纤维强力下降，能增加纤维的强度，同时保持纤维的弹性、柔软性和延伸度， 使其在织布过程中能经受剧烈摩擦而减少断头等特点。
为了实现上述目的，本发明采用如下技术方案：一种府绸类紧密织物上浆用浆料的制备方法，将聚氧乙烯、聚氧丙烯醚、聚丙烯酰胺、双鼠李糖脂和浆纱膏投加入装有搅拌器、温度计和回流冷凝管的烧瓶中，加入去离子水和牛磺酸钠，升温至85℃，通入氮气保护，搅拌40-50min，然后缓慢滴入柠檬酸，约2h滴加完毕，保温2h后加入PMA浆料、月桂醇聚氧乙烯醚、乙醇，再反应9-12h，冷却至室温，即得到府绸类紧密织物上浆用浆料；
所得上浆用浆料的具体组分含量以重量份计如下：
聚氧乙烯 20-30
聚氧丙烯醚 15-18
浆纱膏 12-16
PMA浆料 3-7
聚丙烯酰胺 2-8
牛磺酸钠 0.5-3
柠檬酸 4-8
双鼠李糖脂 10-20
月桂醇聚氧乙烯醚 2-5
乙醇 30-50
去离子水 80-100；
所述浆纱膏由软脂酸、动物油和弱碱按照质量比63:20:15的比例混合乳化而成；所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照一定配比聚合而成的。
进一步地，所述上浆用浆料还包括以重量份计15-20份的聚乙二醇600。
进一步地，所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照质量比20:15:10:6:30:18:40:20聚合而成的。
府绸类紧密织物上浆用浆料适量加入印花浆中，调节印花色浆的厚度，以使花纹轮廓清晰，不渗化。
与现有技术相比，本发明具有如下显著效果：
（1）粘着力强，抱合力大，在纤维外表形成的皮膜能防止纤维起毛；并且不因摩擦而掉浆或使纤维强力下降；
（2）能增加纤维的强度，同时保持纤维的弹性、柔软性和延伸度， 使其在织布过程中能经受剧烈摩擦而减少断头；
（3）易于练洗除去，不会影响织物的漂白、染色和后整理。
具体实施方式
下面通过实施例，对本发明的技术方案作进一步具体的说明。
实施例一：
一种府绸类紧密织物上浆用浆料的制备方法，将聚氧乙烯、聚氧丙烯醚、聚丙烯酰胺、双鼠李糖脂和浆纱膏投加入装有搅拌器、温度计和回流冷凝管的烧瓶中，加入去离子水和牛磺酸钠，升温至85℃，通入氮气保护，搅拌40-50min，然后缓慢滴入柠檬酸，约2h滴加完毕，保温2h后加入PMA浆料、月桂醇聚氧乙烯醚、乙醇，再反应9-12h，冷却至室温，即得到府绸类紧密织物上浆用浆料；
所得上浆用浆料的具体组分含量以重量份计如下：
聚氧乙烯 20
聚氧丙烯醚 15
浆纱膏 12
PMA浆料 3
聚丙烯酰胺 2
牛磺酸钠 0.5
柠檬酸 4
双鼠李糖脂 10
月桂醇聚氧乙烯醚 2
乙醇 30
去离子水 80；
所述浆纱膏由软脂酸、动物油和弱碱按照质量比63:20:15的比例混合乳化而成；所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照一定配比聚合而成的。所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照质量比20:15:10:6:30:18:40:20聚合而成的。
实施例二：
一种府绸类紧密织物上浆用浆料的制备方法，将聚氧乙烯、聚氧丙烯醚、聚丙烯酰胺、双鼠李糖脂和浆纱膏投加入装有搅拌器、温度计和回流冷凝管的烧瓶中，加入去离子水和牛磺酸钠，升温至85℃，通入氮气保护，搅拌40-50min，然后缓慢滴入柠檬酸，约2h滴加完毕，保温2h后加入PMA浆料、月桂醇聚氧乙烯醚、乙醇，再反应9-12h，冷却至室温，即得到府绸类紧密织物上浆用浆料；
所得上浆用浆料的具体组分含量以重量份计如下：
聚氧乙烯 30
聚氧丙烯醚 18
浆纱膏 16
PMA浆料 7
聚丙烯酰胺 8
牛磺酸钠 3
柠檬酸 8
双鼠李糖脂 20
月桂醇聚氧乙烯醚 5
乙醇 50
去离子水 100；
所述浆纱膏由软脂酸、动物油和弱碱按照质量比63:20:15的比例混合乳化而成；所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照一定配比聚合而成的。所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照质量比20:15:10:6:30:18:40:20聚合而成的。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (2)

1.一种府绸类紧密织物上浆用浆料的制备方法，其特征在于，将聚氧乙烯、聚氧丙烯醚、聚丙烯酰胺、双鼠李糖脂和浆纱膏投加入装有搅拌器、温度计和回流冷凝管的烧瓶中，加入去离子水和牛磺酸钠，升温至85℃，通入氮气保护，搅拌40-50min，然后缓慢滴入柠檬酸，2h滴加完毕，保温2h后加入PMA浆料、月桂醇聚氧乙烯醚、乙醇，再反应9-12h，冷却至室温，即得到府绸类紧密织物上浆用浆料；
所得上浆用浆料的具体组分含量以重量份计如下：
聚氧乙烯 20
聚氧丙烯醚 15
浆纱膏 12
PMA浆料 3
聚丙烯酰胺 2
牛磺酸钠 0.5
柠檬酸 4
双鼠李糖脂 10
月桂醇聚氧乙烯醚 2
乙醇 30
去离子水 80；
所述浆纱膏由软脂酸、动物油和弱碱按照质量比63:20:15的比例混合乳化而成；所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照一定配比聚合而成的。
2.根据权利要求1所述的制备方法，其特征在于，所述PMA浆料是由丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸盐、丙烯腈、丙烯酰胺、苯乙烯和乙酸乙烯单体按照质量比20:15:10:6:30:18:40:20聚合而成的。
CN201810234491.4A 2015-11-01 2015-11-01 一种府绸类紧密织物上浆用浆料的制备方法 Active CN108486889B (zh)