CN108486629A - 表面调整剂及其制备方法 - Google Patents
表面调整剂及其制备方法 Download PDFInfo
- Publication number
- CN108486629A CN108486629A CN201810132065.XA CN201810132065A CN108486629A CN 108486629 A CN108486629 A CN 108486629A CN 201810132065 A CN201810132065 A CN 201810132065A CN 108486629 A CN108486629 A CN 108486629A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- surface conditioner
- added
- carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种表面调整剂及其制备方法,表面调整剂包括如下质量份的各组分:碳酸盐20份~45份;硝酸5份~10份;氨基磺酸15份~30份;有机酸10份~20份;异丙醇2份~8份;去离子水17份~63份。上述表面调整剂采用碳酸盐作为除酸主体,能够对硫酸形成的多孔氧化膜进行活化整形,溶解掉阳极氧化膜孔内夹携的部分松散的水合物等阳极副产物和间隙残酸,使得膜孔腔体贯穿性得以强化,基本形貌趋于规整一致,便于随后染色时染料的物理吸附及化学吸附,提高染色的稳定性和均染性。采用该表面调整剂后,间隙处染色露白率大大降低。
Description
技术领域
本发明涉及表面调整技术领域,具体涉及一种表面调整剂及其制备方法。
背景技术
手机已逐渐成为人们日常生活中的必备电子产品,人们对手机性能和外形的要求也越来越高。手机外壳是衡量手机手感的重要指标之一,金属机身所带来的华丽光泽和冰凉的手感,和它所带来的高强度机身颇受用户欢迎。
纳米注塑成型技术的发展,在解决了金属外壳对信号屏蔽问题的同时,也使得外观视觉丰富,层次感增强,让产品更轻、薄、短、小,且较数控加工更具成本效益。纳米注塑成型技术(NMT)即金属与塑料以纳米技术结合的工艺。先对金属表面进行纳米化处理,再将塑料注射在金属表面,可将铝、镁、不锈钢、钛等金属与硬质树脂结合,实现一体化成型。
但在实际生产中,金属壳纳米注塑后微观层面都存在不可避免的铝塑结合缝隙。在阳极氧化过程中的化抛工序中,由于热胀冷缩原理,金属和塑料在温度变化时,收缩程度不同,导致产生裂缝。少量化抛剂如高浓度硝酸、硫酸和磷酸混合物会渗进微缝中,不易清洗出来;在硫酸阳极电解液中,由于长时间的电解反应也会有少量酸渗入;即使经过清洗,在后工序的染色和封孔工序还是会有残酸流出,染色剂遇见酸变成白色,也就是露白现象。特别是封孔工序也是高温,热胀冷缩原理导致酸渗出,破坏染料形成露白,尤其是黑色或其他深色系产品,稍有露白就很明显。
发明内容
基于此,有必要提供一种将裂缝中的酸反应掉,以降低露白率的表面调整剂。
一种表面调整剂,包括如下质量份的各组分:
在其中一个实施例中,所述碳酸盐为碳酸钠和碳酸氢钠中的至少一种。
在其中一个实施例中,所述有机酸为冰乙酸和柠檬酸中的至少一种。
在其中一个实施例中,所述表面调整剂的使用温度为3℃~5℃。
一种表面调整剂的制备方法,包括如下步骤:
提供碳酸盐、硝酸、氨基磺酸、有机酸、异丙醇和去离子水;
将所述碳酸盐、所述硝酸、所述氨基磺酸、所述有机酸、所述异丙醇和所述去离子水进行混合,得到表面调整剂,其中,所述碳酸盐、所述硝酸、所述氨基磺酸、所述有机酸、所述异丙醇和所述去离子水的质量比例为(20~45):(5~10):(15~30):(10~20):(2~8):(17~63)。
上述表面调整剂采用碳酸盐作为除酸主体,能够对硫酸形成的多孔氧化膜进行活化整形,溶解掉阳极氧化膜孔内夹携的部分松散的水合物等阳极副产物和间隙残酸,使得膜孔腔体贯穿性得以强化,基本形貌趋于规整一致,便于随后染色时染料的物理吸附及化学吸附,提高染色的稳定性和均染性。采用该表面调整剂后,间隙处染色露白率大大降低。
附图说明
图1为本发明一实施方式的表面调整剂的制备方法的步骤流程图。
具体实施方式
为使本发明的上述目的、特征和优点能够更加明显易懂,下面结合附图对本发明的具体实施方式做详细的说明。在下面的描述中阐述了很多具体细节以便于充分理解本发明。但是本发明能够以很多不同于在此描述的其它方式来实施,本领域技术人员可以在不违背本发明内涵的情况下做类似改进,因此本发明不受下面公开的具体实施例的限制。
一实施方式中的表面调整剂,包括如下质量份的各组分:
上述表面调整剂采用碳酸盐作为除酸主体,能够对硫酸形成的多孔氧化膜进行活化整形,溶解掉阳极氧化膜孔内夹携的部分松散的水合物等阳极副产物和间隙残酸,使得膜孔腔体贯穿性得以强化,基本形貌趋于规整一致,便于随后染色时染料的物理吸附及化学吸附,提高染色的稳定性和均染性。采用该表面调整剂后,间隙处染色露白率大大降低。
又一实施方式中,表面调整剂,包括如下质量份的各组分:
又一实施方式中,表面调整剂,包括如下质量份的各组分:
为了进一步降低染色露白率,例如,所述碳酸盐为碳酸钠和碳酸氢钠中的至少一种,又如,所述碳酸盐为碳酸钠,又如,所述有机酸为冰乙酸和柠檬酸中的至少一种,如此,能够进一步降低染色露白率。
为了进一步降低染色露白率,所述表面调整剂的使用温度为3℃~5℃,如此,能够进一步降低染色露白率。
请参阅图1,一实施方式的表面调整剂的制备方法,包括如下步骤:
S110、提供碳酸盐、硝酸、氨基磺酸、有机酸、异丙醇和去离子水;
S120、将所述碳酸盐、所述硝酸、所述氨基磺酸、所述有机酸、所述异丙醇和所述去离子水进行混合,得到表面调整剂,其中,所述碳酸盐、所述硝酸、所述氨基磺酸、所述有机酸、所述异丙醇和所述去离子水的质量比例为(20~45):(5~10):(15~30):(10~20):(2~8):(17~63)。
通过步骤S110和步骤S120能够制备得到表面调整剂。上述表面调整剂采用碳酸盐作为除酸主体,能够对硫酸形成的多孔氧化膜进行活化整形,溶解掉阳极氧化膜孔内夹携的部分松散的水合物等阳极副产物和间隙残酸,使得膜孔腔体贯穿性得以强化,基本形貌趋于规整一致,便于随后染色时染料的物理吸附及化学吸附,提高染色的稳定性和均染性。采用该表面调整剂后,间隙处染色露白率大大降低。
具体实施例如下:
实施例1
在烧杯中加入20g碳酸钠,加入5g硝酸,加入15g氨基磺酸,加入10g冰乙酸,加入2g异丙醇和40g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例1的表面调整剂。
实施例2
在烧杯中加入20g碳酸钠,加入5g硝酸,加入15g氨基磺酸,加入10g柠檬酸,加入2g异丙醇和40g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例2的表面调整剂。
实施例3
在烧杯中加入20g碳酸氢钠,加入5g硝酸,加入15g氨基磺酸,加入10g冰乙酸,加入2g异丙醇和40g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例3的表面调整剂。
实施例4
在烧杯中加入25g碳酸钠,加入5g硝酸,加入18g氨基磺酸,加入10g冰乙酸,加入2g异丙醇和50g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例4的表面调整剂。
实施例5
在烧杯中加入27g碳酸钠,加入6g硝酸,加入17g氨基磺酸,加入11g冰乙酸,加入2g异丙醇和50g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例5的表面调整剂。
实施例6
在烧杯中加入30g碳酸氢钠,加入6g硝酸,加入17g氨基磺酸,加入12g冰乙酸,加入1g异丙醇和60g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例6的表面调整剂。
实施例7
在烧杯中加入15g碳酸钠,17g碳酸氢钠,加入5g硝酸,加入15g氨基磺酸,加入12g柠檬酸,加入1g异丙醇和60g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例7的表面调整剂。
实施例8
在烧杯中加入20g碳酸钠,12g碳酸氢钠,加入8g硝酸,加入17g氨基磺酸,加入12g柠檬酸,加入2g异丙醇和60g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例8的表面调整剂。
实施例9
在烧杯中加入20g碳酸氢钠,加入7g硝酸,加入18g氨基磺酸,加入10g冰乙酸,加入10g柠檬酸,加入1g异丙醇和60g去离子水,搅拌5分钟,待加入的物质溶解完全,制备得到实施例9的表面调整剂。
实施例10
在烧杯中加入20g碳酸钠,加入5g硝酸,加入10g冰乙酸、2g异丙醇和63g去离子水,0.04g钛白粉、0.003g偏铝酸钠、0.2g硫酸氧钛、0.05g三聚磷酸盐、0.1g磷酸氢二钠、0.5g焦磷酸钠、0.01g硼砂、0.05g纳米级的二氧化钛、0.04g纳米级的二氧化硅、2.3g聚乙二醇、1g过氧化氢、0.1g硫酸铬、0.1g氯化高锰、0.001g亚硫酸钾,搅拌5分钟,制备得到实施例10的表面调整剂。
下面将实施例1至10制备得到的表面调整剂,在3℃~5℃,对手机壳注塑产品进行除酸,实施例1-10能够达到吐酸的作用,露白率也大大降低,实施例1-9在经过检测后,依然存在缝隙侧壁存在微小损伤的问题,尤其需要指出的是,实施例10通过一些填充粉体、填充成分以及更加适合的弱酸强碱盐,能够使得缝隙侧壁的裸露程度不会太高,在后续氧化漂白时,能够起到一定修复或阻挡过氧化的作用,使得手机壳注塑产品整体颜色同一,且缝隙处内侧壁比较平整,结合度较高,杂质残余量更少,且引入温和的氧化剂,还能够弥补硝酸氧化缺陷,使得在吐酸过程中,能够更加温和地除去在后续氧化过程中起到还原作用的杂质,且不会损坏手机壳注塑产品的表面和缝隙品质。
以上所述实施例的各技术特征可以进行任意的组合,为使描述简洁,未对上述实施例中的各块技术特征所有可能的组合都进行描述,然而,只要这些技术特征的组合不存在矛盾,都应当认为是本说明书记载的范围。
以上所述实施方式仅表达了本发明的几种实施方式,其描述较为具体和详细,但并不能因此而理解为对本发明专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。因此,本发明专利的保护范围应以所附权利要求为准。
Claims (5)
1.一种表面调整剂,其特征在于,包括如下质量份的各组分:
2.根据权利要求1所述的表面调整剂,其特征在于,所述碳酸盐为碳酸钠和碳酸氢钠中的至少一种。
3.根据权利要求1所述的表面调整剂,其特征在于,所述有机酸为冰乙酸、柠檬酸中的至少一种。
4.根据权利要求1所述的表面调整剂,其特征在于,所述表面调整剂的使用温度为3℃~5℃。
5.一种表面调整剂的制备方法,其特征在于,包括如下步骤:
提供碳酸盐、硝酸、氨基磺酸、有机酸、异丙醇和去离子水;
将所述碳酸盐、所述硝酸、所述氨基磺酸、所述有机酸、所述异丙醇和所述去离子水进行混合,得到表面调整剂,其中,所述碳酸盐、所述硝酸、所述氨基磺酸、所述有机酸、所述异丙醇和所述去离子水的质量比例为(20~45):(5~10):(15~30):(10~20):(2~8):(17~63)。