CN108480424A - A kind of restorative procedure for surface of vehicle recess - Google Patents
A kind of restorative procedure for surface of vehicle recess Download PDFInfo
- Publication number
- CN108480424A CN108480424A CN201810229366.4A CN201810229366A CN108480424A CN 108480424 A CN108480424 A CN 108480424A CN 201810229366 A CN201810229366 A CN 201810229366A CN 108480424 A CN108480424 A CN 108480424A
- Authority
- CN
- China
- Prior art keywords
- recess
- crystal slab
- processing
- vehicle
- sucker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of restorative procedures for surface of vehicle recess, include the following steps：Preposition processing, based process one, based process two, transition processing one, transition processing two, transition processing three, transition processing four, transition processing five, reply processing one, reply processing two, reply processing three, reply processing four, reply processing five, head and the tail are handled, the restorative procedure for surface of vehicle recess of the present invention, it is integrally exerted a force to recess by crystal slab, so that concave face entirety stress is replied, so that entire concave face replys uniform, promotion reply effect.
Description
Technical field
The present invention relates to a kind of restorative procedures for surface of vehicle recess.
Background technology
Existing vehicle depression treatment, more conventional is exactly to do metal plate in Auto repair shop, is then painted, this
Processing mode not only spends higher, but also the progress handled is also slow, it is also desirable to injured component is dismantled, it is cumbersome.
And relatively easy processing method is exerted a force at the implements alignment recess by external tool, such as sucker etc
It is pulled outwardly, although this processing mode can also play certain effect, since position is relatively simple, operates very
Expection is also not achieved in trouble, repairing effect, it is more likely that only part is responded, and other positions are in etat lacunaire.
Invention content
The technical problem to be solved by the present invention is to：For overcome the deficiencies in the prior art, the present invention provides a kind of for vehicle
The restorative procedure of surface indentation.
The technical solution adopted by the present invention to solve the technical problems is：A kind of reparation side for surface of vehicle recess
Method includes the following steps：
A, preposition processing：The recess of vehicle is cleaned up, is dried, vehicle, which is placed on the dustless of room temperature >=20 DEG C, to be added
Work workshop；
B, based process one：Take one piece of area that can cover the soft transparent PVC crystal slabs of whole recess, by the crystal
Plate is attached to the surface of recess；
C, based process two：Remove the bubble between crystal slab and sunk surface so that crystal slab is seamless with sunk surface
Gap is bonded；
D, transition processing one：Uniform smearing thickness is the alumina silicate salt deposit of 2-3mm on the surface of crystal slab, then with wet
Gauze is compacted into so that alumina silicate salt deposit is attached on crystal slab, then removes gauze；
E, transition processing two：Uniform smearing thickness is the clay after being impregnated by alcohol of 5-8mm on alumina silicate salt deposit
Layer；
F, transition processing three：Clay layer is heated 15-20 minutes using 150-200 DEG C of cold flame；
G, transition processing four：Clay layer surface is evenly heated using 400-600 DEG C of high temperature, continues 40-60 minutes so that
Crystal slab is heated micro- molten, and crystal slab is attached to sunk surface completely；
H, transition processing five：With the time of 10-15s, the alumina silicate salt deposit of crystal plate surface will be quickly attached to tool
It scrapes；
I, reply processing one：Three circular metal plates are arranged on crystal slab, the thickness of metallic plate is 5-7mm, three gold
Belong to the edge that plate is pressed respectively against recess, three metallic plates are located on three vertex of the same equilateral triangle, and recess is most
A sucker is arranged at big collapsed position, presses sucker so that merged with crystal slab at the edges Pan Kou of sucker；
J：Reply processing two：Crystal slab and surface of vehicle are cooled down；
K：Reply processing three：By external force, it is pulled outwardly positioned at the maximum collapsed position of recess along the opposite direction that is recessed
Sucker, while three metallic plates are withstood by external force, it is lasting to exert a force, until recess is returned to original state position；
L, reply processing four：Sucker is cut down from crystal slab with cutter, is then blown against crystal slab with hair-dryer
Hot wind continues 5-8 minutes so that crystal slab falls off from sunk surface；
M, ending is handled：With alcohol wipe recess surface.
Preferably, in one step of based process, by cutting, the shape of crystal slab is cut into the shape phase with recess
Seemingly, the area of crystal slab is more than the area of recess.
Preferably, in two step of based process, using soft scraper plate, bubble is struck off.
Preferably, in one step of reply processing, sucker is located at the center of the triangle where three metallic plates.
Preferably, in two step of reply processing, the temperature of crystal slab and surface of vehicle is down to room temperature.
Preferably, in three step of reply processing, the three times for withstanding the power of single metal plate are more than the work for being pulled outwardly sucker
Size firmly.
Preferably, in two step of transition processing, the concentration of alcohol is more than 80%.
The invention has the advantages that the restorative procedure for surface of vehicle recess of the present invention, passes through crystal slab entirety
It exerts a force to recess so that concave face entirety stress is replied, so that entire concave face is replied uniformly, is promoted and is replied effect
Fruit.
Specific implementation mode
Embodiment 1
A kind of restorative procedure for surface of vehicle recess includes the following steps：
A, preposition processing：The recess of vehicle is cleaned up, is dried, vehicle, which is placed on the dustless of room temperature >=20 DEG C, to be added
Work workshop；
B, based process one：Take one piece of area that can cover the soft transparent PVC crystal slabs of whole recess, by the crystal
Plate is attached to the surface of recess；
C, based process two：Remove the bubble between crystal slab and sunk surface so that crystal slab is seamless with sunk surface
Gap is bonded；
D, transition processing one：Uniform smearing thickness is the alumina silicate salt deposit of 2mm on the surface of crystal slab, then with wet yarn
Cloth is compacted into so that alumina silicate salt deposit is attached on crystal slab, then removes gauze；
E, transition processing two：Uniform smearing thickness is the clay layer after being impregnated by alcohol of 5mm on alumina silicate salt deposit；
F, transition processing three：Clay layer is heated using 150 DEG C of cold flames 15-20 minutes；
G, transition processing four：Clay layer surface is evenly heated using 400 DEG C of high temperature, continues 40 minutes so that crystal slab
Heated micro- molten, crystal slab is attached to sunk surface completely；
H, transition processing five：With the time of 10-15s, the alumina silicate salt deposit of crystal plate surface will be quickly attached to tool
It scrapes；
I, reply processing one：Three circular metal plates are arranged on crystal slab, the thickness of metallic plate is 5mm, three metals
Plate is pressed respectively against the edge of recess, and three metallic plates are located on three vertex of the same equilateral triangle, the maximum of recess
A sucker is arranged at collapsed position, presses sucker so that merged with crystal slab at the edges Pan Kou of sucker；
J：Reply processing two：Crystal slab and surface of vehicle are cooled down；
K：Reply processing three：By external force, it is pulled outwardly positioned at the maximum collapsed position of recess along the opposite direction that is recessed
Sucker, while three metallic plates are withstood by external force, it is lasting to exert a force, until recess is returned to original state position；
L, reply processing four：Sucker is cut down from crystal slab with cutter, is then blown against crystal slab with hair-dryer
Hot wind continues 5 minutes so that crystal slab falls off from sunk surface；
M, ending is handled：With alcohol wipe recess surface.
Preferably, in one step of based process, by cutting, the shape of crystal slab is cut into the shape phase with recess
Seemingly, the area of crystal slab is more than the area of recess.
Preferably, in two step of based process, using soft scraper plate, bubble is struck off.
Preferably, in one step of reply processing, sucker is located at the center of the triangle where three metallic plates.
Preferably, in two step of reply processing, the temperature of crystal slab and surface of vehicle is down to room temperature.
Preferably, in three step of reply processing, the three times for withstanding the power of single metal plate are more than the work for being pulled outwardly sucker
Size firmly.
Preferably, in two step of transition processing, the concentration of alcohol is more than 80%.
Embodiment 2
A kind of restorative procedure for surface of vehicle recess includes the following steps：
A, preposition processing：The recess of vehicle is cleaned up, is dried, vehicle, which is placed on the dustless of room temperature >=20 DEG C, to be added
Work workshop；
B, based process one：Take one piece of area that can cover the soft transparent PVC crystal slabs of whole recess, by the crystal
Plate is attached to the surface of recess；
C, based process two：Remove the bubble between crystal slab and sunk surface so that crystal slab is seamless with sunk surface
Gap is bonded；
D, transition processing one：Uniform smearing thickness is the alumina silicate salt deposit of 3mm on the surface of crystal slab, then with wet yarn
Cloth is compacted into so that alumina silicate salt deposit is attached on crystal slab, then removes gauze；
E, transition processing two：Uniform smearing thickness is the clay layer after being impregnated by alcohol of 8mm on alumina silicate salt deposit；
F, transition processing three：Clay layer is heated using 200 DEG C of cold flames 20 minutes；
G, transition processing four：Clay layer surface is evenly heated using 600 DEG C of high temperature, continues 60 minutes so that crystal slab
Heated micro- molten, crystal slab is attached to sunk surface completely；
H, transition processing five：With the time of 10-15s, the alumina silicate salt deposit of crystal plate surface will be quickly attached to tool
It scrapes；
I, reply processing one：Three circular metal plates are arranged on crystal slab, the thickness of metallic plate is 7mm, three metals
Plate is pressed respectively against the edge of recess, and three metallic plates are located on three vertex of the same equilateral triangle, the maximum of recess
A sucker is arranged at collapsed position, presses sucker so that merged with crystal slab at the edges Pan Kou of sucker；
J：Reply processing two：Crystal slab and surface of vehicle are cooled down；
K：Reply processing three：By external force, it is pulled outwardly positioned at the maximum collapsed position of recess along the opposite direction that is recessed
Sucker, while three metallic plates are withstood by external force, it is lasting to exert a force, until recess is returned to original state position；
L, reply processing four：Sucker is cut down from crystal slab with cutter, is then blown against crystal slab with hair-dryer
Hot wind continues 8 minutes so that crystal slab falls off from sunk surface；
M, ending is handled：With alcohol wipe recess surface.
Preferably, in one step of based process, by cutting, the shape of crystal slab is cut into the shape phase with recess
Seemingly, the area of crystal slab is more than the area of recess.
Preferably, in two step of based process, using soft scraper plate, bubble is struck off.
Preferably, in one step of reply processing, sucker is located at the center of the triangle where three metallic plates.
Preferably, in two step of reply processing, the temperature of crystal slab and surface of vehicle is down to room temperature.
Preferably, in three step of reply processing, the three times for withstanding the power of single metal plate are more than the work for being pulled outwardly sucker
Size firmly.
Preferably, in two step of transition processing, the concentration of alcohol is more than 80%.
It is in preprocessing steps, the recess of vehicle is clearly clean, primarily to the impurity at removal concave face, this
Being bonded between sample concave face and crystal slab just will appear bubble, influence subsequent reply effect.
In one step of based process, by cutting, crystal slab is cut into shape similar with concave face, in fact, water
The area of brilliant plate is slightly larger than the area of concave face, and effect is preferable, otherwise can be impacted to the normal face in periphery,
When subsequent step exerts a force, it is possible to can make normal face that slight deformation occur.
Crystal slab is attached to sunk surface, accomplished as possible not by two step of based process, the process of actually one pad pasting
Bubble is stayed, and in practical operation, since the deformation degree of recess differs, can also there be a small amount of bubble, but in controlled range
Interior bubbles volume will not reply recess and cause substantive influence.
In one step of excess processes, in the surface smear alumina silicate salt deposit of crystal slab, actually this is a kind of clay layer, is sticked
Soil particle is thinner, and high temperature resistant, and such a layer of based structures are arranged herein, primarily to preventing in operation transition position
When reason three and transition processing four steps, the alcohol burn in clay layer directly heats crystal slab, causes crystal slab fusing excessive,
It is possible that the phenomenon that crystal slab being caused locally to be fused.
And adhere to clay layer on alumina silicate salt deposit, mainly play the role of heat transmission, when operation, directly to clay layer
It is heated, then even heat is transferred on crystal slab by alumina silicate salt deposit, because clay layer high temperature resistant, and heat
Afterwards, it may appear that sintering phenomenon can thus keep the globality of clay layer, such heating effect will be more preferable, then by alumina silicate
The uniform heat of salt deposit transmits, can avoid well crystal slab due to local temperature is excessively high and the phenomenon that generate local burn through.
In one step of reply processing, actually arrange that the point of application, three metallic plates are for withstanding crystal slab, leading to
It crosses external force and draws sucker, and in fact, sucker acts on crystal slab, crystal slab is fitted in again on concave face, is applied in this way
Power on sucker will be transferred on entire crystal slab, i.e., entire concave face all can under tension effect, when concave face send out
When raw reply, since crystal slab is originally soft and has tensile properties, so the crystal that the deformation band of concave face comes
The stretching variation of plate also can be by crystal slab autodigestion.
It after completing return phase, is heated, can easily be removed crystal slab from concave face very much by hair-dryer.
Compared with prior art, the restorative procedure for surface of vehicle recess of the invention, by crystal slab integrally to recessed
Sunken place exerts a force so that concave face entirety stress is replied, so that entire concave face is replied uniformly, is promoted and is replied effect.
It is enlightenment with above-mentioned desirable embodiment according to the present invention, through the above description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention' entirely.The technology of this invention
Property range is not limited to the contents of the specification, it is necessary to determine its technical scope according to right.
Claims (7)
1. a kind of restorative procedure for surface of vehicle recess, which is characterized in that include the following steps：
A, preposition processing：The recess of vehicle is cleaned up, is dried, vehicle is placed on to the dustless processing cart of room temperature >=20 DEG C
Between；
B, based process one：It takes one piece of area that can cover the soft transparent PVC crystal slabs of whole recess, which is pasted
It is attached to the surface of recess；
C, based process two：Remove the bubble between crystal slab and sunk surface so that crystal slab and the seamless patch of sunk surface
It closes；
D, transition processing one：Uniform smearing thickness is the alumina silicate salt deposit of 2-3mm on the surface of crystal slab, then uses wet gauze
It is compacted into so that alumina silicate salt deposit is attached on crystal slab, then removes gauze；
E, transition processing two：Uniform smearing thickness is the clay layer after being impregnated by alcohol of 5-8mm on alumina silicate salt deposit；
F, transition processing three：Clay layer is heated 15-20 minutes using 150-200 DEG C of cold flame；
G, transition processing four：Clay layer surface is evenly heated using 400-600 DEG C of high temperature, continues 40-60 minutes so that crystal
Plate is heated micro- molten, and crystal slab is attached to sunk surface completely；
H, transition processing five：With the time of 10-15s, quickly the alumina silicate salt deposit for being attached to crystal plate surface is scraped with tool；
I, reply processing one：Three circular metal plates are arranged on crystal slab, the thickness of metallic plate is 5-7mm, three metallic plates
It is pressed respectively against the edge of recess, three metallic plates are located on three vertex of the same equilateral triangle, under the maximum of recess
It falls into and arranges a sucker at position, press sucker so that merged with crystal slab at the edges Pan Kou of sucker；
J：Reply processing two：Crystal slab and surface of vehicle are cooled down；
K：Reply processing three：By external force, it is pulled outwardly the sucker positioned at the maximum collapsed position of recess along the opposite direction that is recessed,
Three metallic plates are withstood by external force simultaneously, it is lasting to exert a force, until recess is returned to original state position；
L, reply processing four：Sucker is cut down from crystal slab with cutter, then uses hair-dryer against crystal slab blowing hot-air,
Continue 5-8 minutes so that crystal slab falls off from sunk surface；
M, ending is handled：With alcohol wipe recess surface.
2. a kind of restorative procedure for surface of vehicle recess as described in claim 1, it is characterised in that：One step of based process
In rapid, by cutting, the shape of crystal slab is cut into similar with the shape being recessed, the area of crystal slab is more than the area being recessed.
3. a kind of restorative procedure for surface of vehicle recess as described in claim 1, it is characterised in that：Two step of based process
In rapid, using soft scraper plate, bubble is struck off.
4. a kind of restorative procedure for surface of vehicle recess as described in claim 1, it is characterised in that：One step of reply processing
In rapid, sucker is located at the center of the triangle where three metallic plates.
5. a kind of restorative procedure for surface of vehicle recess as described in claim 1, it is characterised in that：Two step of reply processing
In rapid, the temperature of crystal slab and surface of vehicle is down to room temperature.
6. a kind of restorative procedure for surface of vehicle recess as described in claim 1, it is characterised in that：Three step of reply processing
In rapid, the three times for withstanding the power of single metal plate are more than the size for the active force for being pulled outwardly sucker.
7. a kind of restorative procedure for surface of vehicle recess as described in claim 1, it is characterised in that：Two step of transition processing
In rapid, the concentration of alcohol is more than 80%.