CN101623964A - Production method for electric aluminum material heat printing on non-woven fabric - Google Patents
Production method for electric aluminum material heat printing on non-woven fabric Download PDFInfo
- Publication number
- CN101623964A CN101623964A CN200910183712A CN200910183712A CN101623964A CN 101623964 A CN101623964 A CN 101623964A CN 200910183712 A CN200910183712 A CN 200910183712A CN 200910183712 A CN200910183712 A CN 200910183712A CN 101623964 A CN101623964 A CN 101623964A
- Authority
- CN
- China
- Prior art keywords
- electrochemical aluminium
- nonwoven
- aluminum material
- roller
- material heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a production method for electric aluminum material heat printing on a non-woven fabric, relating to the technical field of processing of non-woven fabrics. The production method comprises the following technical steps: carving concave patterns on the surface of a roll; dipping the roll in glue; scraping redundant rubber stock on the surface of the roll except the concave patterns; transferring the rubber stock in the concave patterns on the roll onto one surface of an electric aluminum material heat printing film through a press roll; baking the rubber stock on the rubberized electric aluminum material heat printing film to be semi-dry through an oven; compounding a non-woven base fabric on the electric aluminum material heat printing film with a rubber layer; carrying out heat insulation and solidification on a semifinished product; and separating the electric aluminum material heat printing film from the compounded non-woven fabric. The invention has simple process, is easy to produce and control, can form regular golden, silver and metal laser letters and patterns which are not easy to fall off on a conventional non-woven fabric.
Description
Technical field
The present invention relates to a kind of processing technique field of nonwoven, particularly have the processing technology of the nonwoven of electrochemical aluminium thermoprinting pattern.
Background technology
On now a lot of nonwoven are applied to decorating in large quantities, as pack gift, flowers, but present non-woven fabrics craft is shredding, preparing, lapping, main comb, lapping, dipping slurries, dipping pressure roller pressure removal part slurries, oven dry, rolling, mostly be single color greatly, it is single that kind also shows, and can not satisfy the needs in market.
Summary of the invention
The present invention seeks in order to improve product specification, to increase product variety and the production method of the nonwoven that designs with electrochemical aluminium thermoprinting pattern.
The present invention includes following processing step:
1) scribes the spill decorative pattern on the surface of flower roller;
2) will spend roller to cross glue;
3) scrape off the redundant rubber stock on the colored roller surface beyond the spill decorative pattern;
4) will spend the sizing material in the spill decorative pattern on the roller to be transferred to the one side of electrochemical aluminium thermoprinting film by pressure roller;
5) sizing material on the electrochemical aluminium thermoprinting film of gluing is baked and banked up with earth to half-dried through baking oven;
6) under the roller surface temperature is 110～120 ℃ condition, non-woven base cloth is compounded on the electrochemical aluminium thermoprinting film with glue-line, rolling forms semi-finished product;
7) with semi-finished product heat preservation solidification 12 ± 0.5 hours under 60～70 ℃ of conditions of drying room temperature;
8) after the heat preservation solidification, the electrochemical aluminium thermoprinting film is separated the rolling respectively of electrochemical aluminium thermoprinting film and nonwoven from compound nonwoven.
Technology of the present invention is simple, be easy to production control, can on conventional nonwoven, form the gold, silver of rule of difficult drop-off and metal laser letters, pattern by above processing step, can be decorative pattern or font, the nonwoven product variety is increased, and improve product specification.And conventional nonwoven can be grey cloth or bleaching or stained clot-h, also can be random decorative pattern cloth, also can be not limited to above several.
The grammes per square metre of described non-woven base cloth is 25g～100g/m before compound
2, the grammes per square metre of electrochemical aluminium thermoprinting film is 20～40g/m
2The selection of the electrochemical aluminium thermoprinting film grammes per square metre of suitable base cloth grammes per square metre and appropriate amount, the effect of formation can demonstrate fully the effect of metal film on base cloth, also can make the pattern on the product more firm.
Control for convenience, improve product quality and production efficiency, in the step 5) of the present invention, it is in 50～70 ℃ the baking oven that the electrochemical aluminium thermoprinting film of gluing is placed temperature.
The specific embodiment
1, produce conventional non-woven base cloth:
Fiber mixing shredding, preparing, lapping, main comb, lapping, dipping slurries, dipping pressure roller are pressed except that part slurries, oven dry, rolling, form the nonwoven finished product.Also can form bleaching or stained clot-h by conventional method, also can be random decorative pattern cloth.
Make non-woven base cloth of the present invention with above-mentioned technology, can select grammes per square metre is 25g～100g/m
2Non-woven base cloth, stand-by.
2, prepare the flower roller:
Outer surface at cylindrical rigidity roll body adopts laser engraving, makes the colored roller with spill decorative pattern or literal, and is stand-by.
3, formulate sizes:
Adhesive, butanone and curing agent are prepared the formation sizing material according to a conventional method, and sizing material is inserted in the glue cylinder.
4, selecting the grammes per square metre of rolling is 20～40g/m
2Electrochemical aluminium thermoprinting film (being electrochemical aluminium thermoprinting gold or silver foil film), stand-by.
5, the formation that has electrochemical aluminium thermoprinting film figure nonwoven:
Below the flower roller, establish plastic tank, rotate the flower roller, make the outer surface gluing of colored roller, scrape off the redundant rubber stock on the colored roller surface except that the spill decorative pattern again by scraper, and make the interior sizing material that keeps of concave panel of spill decorative pattern.
To spend roller and an elasticity pressure roller to be arranged on the frame in pairs, and make colored roller be arranged in the pressure roller below.To spend the sizing material in the spill decorative pattern on the roller to be transferred to the one side of electrochemical aluminium thermoprinting film by pressure roller.
Is 50～70 ℃ baking oven with the electrochemical aluminium thermoprinting film of gluing through excess temperature, will make sizing material baking on the electrochemical aluminium thermoprinting film of gluing to half-dried.
Under 110～120 ℃ of temperature conditions, use a pair of pressure roller of rubber rollers under the steel rider, non-woven base cloth is compounded on the electrochemical aluminium thermoprinting film with glue-line, and is heat preservation solidification 12 ± 0.5 hours in 60～70 ℃ the baking oven in temperature.
Treat after the heat preservation solidification electrochemical aluminium thermoprinting film to be separated from compound nonwoven rolling respectively.
Claims (3)
1, a kind of production method of carrying out electrochemical aluminium hot stamping on nonwoven is characterized in that may further comprise the steps:
1) scribes the spill decorative pattern on the surface of flower roller;
2) will spend roller to cross glue;
3) scrape off the redundant rubber stock on the colored roller surface beyond the spill decorative pattern;
4) will spend the sizing material in the spill decorative pattern on the roller to be transferred to the one side of electrochemical aluminium thermoprinting film by pressure roller;
5) sizing material on the electrochemical aluminium thermoprinting film of gluing is baked and banked up with earth to half-dried through baking oven;
6) under the roller surface temperature is 110～120 ℃ condition, non-woven base cloth is compounded on the electrochemical aluminium thermoprinting film with glue-line, rolling forms semi-finished product;
7) with semi-finished product heat preservation solidification 12 ± 0.5 hours under 60～70 ℃ of conditions of drying room temperature;
8) after the heat preservation solidification, the electrochemical aluminium thermoprinting film is separated the rolling respectively of electrochemical aluminium thermoprinting film and nonwoven from compound nonwoven.
2,, it is characterized in that the grammes per square metre of compound preceding described non-woven base cloth is 25g～100g/m according to the described production method of on nonwoven, carrying out electrochemical aluminium hot stamping of claim 1
2, the grammes per square metre of electrochemical aluminium thermoprinting film is 20～40g/m
2
3, according to claim 1 or 2 described production methods of on nonwoven, carrying out electrochemical aluminium hot stamping, it is characterized in that in the described step 5) that described temperature of oven is 50～70 ℃.