CN108467250A - A kind of type composite flooring bricks and preparation method thereof of breathing freely that absorb water - Google Patents
A kind of type composite flooring bricks and preparation method thereof of breathing freely that absorb water Download PDFInfo
- Publication number
- CN108467250A CN108467250A CN201810330684.XA CN201810330684A CN108467250A CN 108467250 A CN108467250 A CN 108467250A CN 201810330684 A CN201810330684 A CN 201810330684A CN 108467250 A CN108467250 A CN 108467250A
- Authority
- CN
- China
- Prior art keywords
- parts
- type composite
- mesh
- water suction
- composite flooring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses ventilative type composite flooring bricks of a kind of water suction and preparation method thereof, are related to brick brick material field, include the raw material of following parts by weight meter：50 60 parts of clay, 20 30 parts of diatomite, 13 20 parts of cinder, 15 22 parts of sepiolite fibre, 8 15 parts of lignocellulosic, 9 16 parts of feldspar powder, 5 10 parts of quartz glass slag, 6 12 parts of glass fibre, 13 parts of magnesia, 48 parts of nano-titanium dioxide, 15 20 parts of waterglass, 12 17 parts of polyacrylate dispersion；The present invention provides ventilative type composite flooring bricks of a kind of water suction and preparation method thereof, and floor tile property of the present invention is stablized, and resistance to compression, weathering resistance and corrosion resistance are superior, have good water imbibition and gas permeability, can adjust pavement humidity, reduce the dry and cracked phenomenon on road surface.
Description
Technical field
The present invention relates to brick material fields, and in particular to a kind of type composite flooring bricks and preparation method thereof of breathing freely that absorb water.
Background technology
Pavement refers to specializing in walk with what kerbstone or guardrail and other similar facilities were separated in road
Part.Pavement is very universal in city, has pavement by general street.Most people trade is cement system
, also there is part pavement to be laid with the material that pitch etc. is softer than cement, in addition there are specializing in for the other materials such as rubble, wood
The type in the channel that pedestrian uses, common sidewalk ground tile has cement flower floor tile and granite ground to lay bricks.
The shared feature of traditional floor tile is hardness height, and resistance to mechanical superior performance is existing to improve the water proofing property on road surface
Floor tile do not have any water imbibition, when there is ponding on rainy day or road surface, floor tile water imbibition is poor, surface area water reduce road surface
Frictional force is easy to slide into, and when rainwater is few, pavior brick does not have ventilative adjusting humidity function, is cracked with arid.
Invention content
For problems of the prior art, the present invention provides a kind of ventilative type composite flooring bricks of water suction and its preparation sides
Method, floor tile property of the present invention are stablized, and resistance to compression, weathering resistance and corrosion resistance are superior, have good water imbibition and gas permeability,
Pavement humidity can be adjusted, the dry and cracked phenomenon on road surface is reduced.
In order to achieve the above object, the present invention is achieved through the following technical solutions：
A kind of ventilative type composite flooring bricks of water suction, include the raw material of following parts by weight meter：
50-60 parts of clay, 20-30 parts of diatomite, 13-20 parts of cinder, 15-22 parts of sepiolite fibre, lignocellulosic 8-
15 parts, 9-16 parts of feldspar powder, 5-10 parts of quartz glass slag, 6-12 parts of glass fibre, 1-3 parts of magnesia, nano-titanium dioxide 4-8
Part, 15-20 parts of waterglass, 12-17 parts of polyacrylate dispersion.
Preferably, include the raw material of following parts by weight meter：54-58 parts of clay, 23-27 parts of diatomite, 15-18 parts of cinder,
17-20 parts of sepiolite fibre, 10-14 parts of lignocellulosic, 12-14 parts of feldspar powder, 6-8 parts of quartz glass slag, glass fibre 8-
11 parts, 1.5-2.5 parts of magnesia, 5-7 parts of nano-titanium dioxide, 16-18 parts of waterglass, 13-15 parts of polyacrylate dispersion.
Preferably, include the raw material of following parts by weight meter：56 parts of clay, 25 parts of diatomite, 17 parts of cinder, sepiolite fibre
19 parts, 12 parts of lignocellulosic, 13 parts of feldspar powder, 7 parts of quartz glass slag, 9 parts of glass fibre, 2 parts of magnesia, nanometer titanium dioxide
6 parts of titanium, 17 parts of waterglass, 14 parts of polyacrylate dispersion.
Preferably, the ventilative type composite flooring bricks of the water suction further include 3-5 parts of nano-silicon nitride, 2-4 parts of aluminium oxide and two sulphur
Change 1-3 parts of molybdenum.
Preferably, the clay is 100-300 mesh clays；Diatomite is 100-300 mesh diatomite；Cinder is 80-150 mesh
Cinder；Sepiolite fibre length is 200-800 microns；Lignocellulosic length is 200-800 microns；Feldspar powder is 200-300
Mesh feldspar powder, quartz glass slag are 50-100 mesh quartz glass slags；Glass fibre length is 500-800 microns, and magnesia is
300-500 mesh magnesia.
Preferably, the aluminium oxide is 300-500 mesh aluminium oxide, and molybdenum disulfide is 300-500 mesh molybdenum disulfide.
Preferably, the waterglass is sodium silicate and potassium water glass according to mass ratio 4:1 mixing composition.
A kind of preparation method of the ventilative type composite flooring bricks of above-mentioned water suction is also disclosed in the present invention, specifically, including it is following
Step：
(1) above-mentioned raw materials are added in high-speed mixer with 2000-3000 revs/min of speed, are uniformly mixed.
(2) harder, compression moulding is used to stand 15-30 minutes mixed material made from step (1)；
(3) floor tile after air-drying is placed into anaerobic in firing kiln to heat, the heating is divided into pre-heat phase, forges
Burning stage and holding stage；110-140 degrees Celsius of the pre-heat phase heating temperature, heating time are 30-50 minutes；Institute
300-400 degrees Celsius of the calcination stage heating temperature stated, heating time are 13-15 hours；The holding stage heating temperature
160-200 degrees Celsius, heating time is 3-4 hours.
Preferably, the holding stage be temperature control to 160-200 degrees Celsius, heating 3-4 hour after, pass hull closure, naturally
After being cooled to room temperature, finished product is taken out.
The present invention has following advantageous effect：
(1) the present invention provides ventilative type composite flooring bricks of a kind of water suction and preparation method thereof, floor tile property of the present invention is steady
Fixed, resistance to compression, weathering resistance and corrosion resistance are superior, have good water imbibition and gas permeability, can adjust pavement humidity, reduce
The dry and cracked phenomenon on road surface.
(2) present invention addition diatomite is primary raw material, and diatomite has fine and smooth, light, porous, water imbibition and permeability
Strong property, surface have countless pores, peculiar smell adsorbable, in decomposition air to have damping, deodorization functions, diatomite fine and closely woven
Porous, large specific surface area can absorb moisture if ambient humidity is big, if ambient enviroment is dried, releasable moisture.
(3) sepiolite fibre is added in raw material of the present invention, sepiolite fibre is a kind of natural mineral fiber, structure two
One layer of magnesia octahedron is pressed from both sides among layer oxygen-octahedron, forms the pore structure of the layered structure unit of 2: 1 types, is had good
Adsorptivity can increase the compactness and structural stability of material with inorganic molecule in sorbing material, while can adsorb road surface
Moisture.
(4) lignocellulosic is added in raw material of the present invention, lignocellulosic is the capillarity of fibre structure, will be
Moisture inside system is promptly transferred to surface and interface of materials so that the uniform moisture distribution inside material material significantly reduces knot
Skin phenomenon.And adhesion strength and surface strength are significantly improved, reduce the dry and cracked phenomenon of material.
Specific implementation mode
The specific implementation mode of the present invention is further described with reference to embodiment, following embodiment is only used for more
Technical scheme of the present invention is clearly demonstrated, and not intended to limit the protection scope of the present invention.
Embodiment 1
A kind of ventilative type composite flooring bricks of water suction, include the raw material of following parts by weight meter：
50 parts of clay, 20 parts of diatomite, 13 parts of cinder, 15 parts of sepiolite fibre, 8 parts of lignocellulosic, 9 parts of feldspar powder,
5 parts of quartz glass slag, 6 parts of glass fibre, 1 part of magnesia, 4 parts of nano-titanium dioxide, 15 parts of waterglass, polyacrylate dispersion
12 parts.
Wherein, clay is 100 mesh clays；Diatomite is 100 mesh diatomite；Cinder is 80 mesh cinders；Sepiolite fibre is long
Degree is 200 microns；Lignocellulosic length is 200 microns；Feldspar powder is 200 mesh feldspar powders, and quartz glass slag is 50 mesh quartz
Glass dregs；Glass fibre length is 500 microns, and magnesia is 300 mesh magnesia.
Waterglass is sodium silicate and potassium water glass according to mass ratio 4:1 mixing composition.
The preparation method of the ventilative type composite flooring bricks of water suction specifically includes the following steps：
(1) above-mentioned raw materials are added in high-speed mixer with 2000 revs/min of speed, are uniformly mixed.
(2) harder, compression moulding is used to stand 15 minutes mixed material made from step (1)；
(3) floor tile after air-drying is placed into and fires anaerobic heating in kiln, heating is divided into pre-heat phase, calcination stage
And holding stage；
110 degrees Celsius of pre-heat phase heating temperature, heating time are 30 minutes；
300 degrees Celsius of calcination stage heating temperature, heating time are 13 hours；
160 degrees Celsius of holding stage heating temperature, heating time are 3 hours, pass hull closure, after cooled to room temperature,
Take out finished product.
Embodiment 2
A kind of ventilative type composite flooring bricks of water suction, include the raw material of following parts by weight meter：
60 parts of clay, 30 parts of diatomite, 20 parts of cinder, 22 parts of sepiolite fibre, 15 parts of lignocellulosic, feldspar powder 16
Part, 10 parts of quartz glass slag, 12 parts of glass fibre, 3 parts of magnesia, 8 parts of nano-titanium dioxide, 20 parts of waterglass, polyacrylic acid
17 parts of ester lotion.
Wherein, clay is 300 mesh clays；Diatomite is 300 mesh diatomite；Cinder is 150 mesh cinders；Sepiolite fibre is long
Degree is 800 microns；Lignocellulosic length is 800 microns；Feldspar powder is 300 mesh feldspar powders, and quartz glass slag is 100 mesh quartz
Glass dregs；Glass fibre length is 800 microns, and magnesia is 500 mesh magnesia.
Waterglass is sodium silicate and potassium water glass according to mass ratio 4:1 mixing composition.
The preparation method of the ventilative type composite flooring bricks of water suction specifically includes the following steps：
(1) above-mentioned raw materials are added in high-speed mixer with 3000 revs/min of speed, are uniformly mixed.
(2) harder, compression moulding is used to stand 30 minutes mixed material made from step (1)；
(3) floor tile after air-drying is placed into anaerobic in firing kiln to heat, the heating is divided into pre-heat phase, forges
Burning stage and holding stage；
140 degrees Celsius of pre-heat phase heating temperature, heating time are 50 minutes；
400 degrees Celsius of calcination stage heating temperature, heating time are 15 hours；
200 degrees Celsius of holding stage heating temperature, heating time are 4 hours, pass hull closure, after cooled to room temperature,
Take out finished product.
Embodiment 3
A kind of ventilative type composite flooring bricks of water suction, include the raw material of following parts by weight meter：
54 parts of clay, 23 parts of diatomite, 15 parts of cinder, 17 parts of sepiolite fibre, 10 parts of lignocellulosic, feldspar powder 12
Part, 6 parts of quartz glass slag, 8 parts of glass fibre, 1.5 parts of magnesia, 5 parts of nano-titanium dioxide, 16 parts of waterglass, polyacrylic acid
1 part of 13 parts of ester lotion, 3 parts of nano-silicon nitride, 2 parts of aluminium oxide and molybdenum disulfide.
Wherein, clay is 200 mesh clays；Diatomite is 200 mesh diatomite；Cinder is 100 mesh cinders；Sepiolite fibre is long
Degree is 500 microns；Lignocellulosic length is 300 microns；Feldspar powder is 200 mesh feldspar powders, and quartz glass slag is 80 mesh quartz
Glass dregs；Glass fibre length is 600 microns；Magnesia is 400 mesh magnesia, aluminium oxide is 300 mesh aluminium oxide, molybdenum disulfide
For 300 mesh molybdenum disulfide.
Waterglass is sodium silicate and potassium water glass according to mass ratio 4:1 mixing composition.
The preparation method of the ventilative type composite flooring bricks of water suction specifically includes the following steps：
(1) above-mentioned raw materials are added in high-speed mixer with 2500 revs/min of speed, are uniformly mixed.
(2) harder, compression moulding is used to stand 18 minutes mixed material made from step (1)；
(3) floor tile after air-drying is placed into and fires anaerobic heating in kiln, heating is divided into pre-heat phase, calcination stage
And holding stage；
130 degrees Celsius of pre-heat phase heating temperature, heating time are 40 minutes；
350 degrees Celsius of calcination stage heating temperature, heating time are 14 hours；
180 degrees Celsius of holding stage heating temperature, heating time are 3.5 hours.
Holding stage is temperature control to 180 degrees Celsius, and after heating 3.5 hours, pass hull closure after cooled to room temperature, takes
Go out finished product.
Embodiment 4
A kind of ventilative type composite flooring bricks of water suction, include the raw material of following parts by weight meter：
58 parts of clay, 27 parts of diatomite, 18 parts of cinder, 20 parts of sepiolite fibre, 14 parts of lignocellulosic, feldspar powder 14
Part, 8 parts of quartz glass slag, 11 parts of glass fibre, 2.5 parts of magnesia, 7 parts of nano-titanium dioxide, 18 parts of waterglass, polyacrylic acid
3 parts of 15 parts of ester lotion, 5 parts of nano-silicon nitride, 4 parts of aluminium oxide and molybdenum disulfide.
Wherein, clay is 180 mesh clays；Diatomite is 200 mesh diatomite；Cinder is 120 mesh cinders；Sepiolite fibre is long
Degree is 400 microns；Lignocellulosic length is 600 microns；Feldspar powder is 250 mesh feldspar powders, and quartz glass slag is 60 mesh quartz
Glass dregs；Glass fibre length is 550 microns, and magnesia is 350 mesh magnesia, aluminium oxide is 400 mesh aluminium oxide, molybdenum disulfide
For 450 mesh molybdenum disulfide.
Waterglass is sodium silicate and potassium water glass according to mass ratio 4:1 mixing composition.
The preparation method of the ventilative type composite flooring bricks of water suction specifically includes the following steps：
(1) above-mentioned raw materials are added in high-speed mixer with 2200 revs/min of speed, are uniformly mixed.
(2) harder, compression moulding is used to stand 25 minutes mixed material made from step (1)；
(3) floor tile after air-drying is placed into and fires anaerobic heating in kiln, heating is divided into pre-heat phase, calcination stage
And holding stage；
130 degrees Celsius of pre-heat phase heating temperature, heating time are 35 minutes；
360 degrees Celsius of calcination stage heating temperature, heating time are 13 hours；
180 degrees Celsius of holding stage heating temperature, heating time are 3.5 hours.Pass hull closure, cooled to room temperature
Afterwards, finished product is taken out.
Embodiment 5
A kind of ventilative type composite flooring bricks of water suction, include the raw material of following parts by weight meter：
56 parts of clay, 25 parts of diatomite, 17 parts of cinder, 19 parts of sepiolite fibre, 12 parts of lignocellulosic, feldspar powder 13
Part, 7 parts of quartz glass slag, 9 parts of glass fibre, 2 parts of magnesia, 6 parts of nano-titanium dioxide, 17 parts of waterglass, polyacrylate
2 parts of 14 parts of lotion, 4 parts of nano-silicon nitride, 3 parts of aluminium oxide and molybdenum disulfide.
Wherein, clay is 100 mesh clays；Diatomite is 100 mesh diatomite；Cinder is 80 mesh cinders；Sepiolite fibre is long
Degree is 200 microns；Lignocellulosic length is 200 microns；Feldspar powder is 200 mesh feldspar powders, and quartz glass slag is 50 mesh quartz
Glass dregs；Glass fibre length is 500 microns, and magnesia is 300 mesh magnesia；Aluminium oxide is 300 mesh aluminium oxide；Molybdenum disulfide
For 300 mesh molybdenum disulfide.
Waterglass is sodium silicate and potassium water glass according to mass ratio 4:1 mixing composition.
A kind of preparation method of the ventilative type composite flooring bricks of above-mentioned water suction is also disclosed in the present invention, specifically, including it is following
Step：
(1) above-mentioned raw materials are added in high-speed mixer with 2800 revs/min of speed, are uniformly mixed.
(2) harder, compression moulding is used to stand 25 minutes mixed material made from step (1)；
(3) floor tile after air-drying is placed into and fires anaerobic heating in kiln, heating is divided into pre-heat phase, calcination stage
And holding stage；
130 degrees Celsius of the pre-heat phase heating temperature, heating time are 50 minutes；
360 degrees Celsius of the calcination stage heating temperature, heating time are 14 hours；
180 degrees Celsius of the holding stage heating temperature, heating time are 4 hours, and pass hull closure naturally cools to room
Wen Hou takes out finished product.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution recorded in example is modified or equivalent replacement of some of the technical features.All essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (9)
- The type composite flooring bricks 1. a kind of water suction is breathed freely, which is characterized in that include the raw material of following parts by weight meter：50-60 parts of clay, silicon 20-30 parts of diatomaceous earth, 13-20 parts of cinder, 15-22 parts of sepiolite fibre, 8-15 parts of lignocellulosic, 9-16 parts of feldspar powder, quartz 5-10 parts of glass dregs, 6-12 parts of glass fibre, 1-3 parts of magnesia, 4-8 parts of nano-titanium dioxide, 15-20 parts of waterglass, poly- third 12-17 parts of olefin(e) acid ester lotion.
- The type composite flooring bricks 2. water suction according to claim 1 is breathed freely, which is characterized in that include the original of following parts by weight meter Material：54-58 parts of clay, 23-27 parts of diatomite, 15-18 parts of cinder, 17-20 parts of sepiolite fibre, 10-14 parts of lignocellulosic, 12-14 parts of feldspar powder, 6-8 parts of quartz glass slag, 8-11 parts of glass fibre, 1.5-2.5 parts of magnesia, nano-titanium dioxide 5-7 Part, 16-18 parts of waterglass, 13-15 parts of polyacrylate dispersion.
- The type composite flooring bricks 3. water suction according to claim 1 is breathed freely, which is characterized in that include the original of following parts by weight meter Material：56 parts of clay, 25 parts of diatomite, 17 parts of cinder, 19 parts of sepiolite fibre, 12 parts of lignocellulosic, 13 parts of feldspar powder, quartz 7 parts of glass dregs, 9 parts of glass fibre, 2 parts of magnesia, 6 parts of nano-titanium dioxide, 17 parts of waterglass, polyacrylate dispersion 14 Part.
- The type composite flooring bricks 4. water suction according to claim 1 is breathed freely, which is characterized in that the ventilative type composite flooring bricks of water suction Further include 1-3 parts of 3-5 parts of nano-silicon nitride, 2-4 parts of aluminium oxide and molybdenum disulfide.
- The type composite flooring bricks 5. water suction according to claim 1 is breathed freely, which is characterized in that the clay is viscous for 100-300 mesh Soil；Diatomite is 100-300 mesh diatomite；Cinder is 80-150 mesh cinders；Sepiolite fibre length is 200-800 microns；Wood Matter fiber length is 200-800 microns；Feldspar powder is 200-300 mesh feldspar powders, and quartz glass slag is 50-100 mesh quartz glass Glass slag；Glass fibre length is 500-800 microns, and magnesia is 300-500 mesh magnesia.
- The type composite flooring bricks 6. water suction according to claim 4 is breathed freely, which is characterized in that the aluminium oxide is 300-500 mesh Aluminium oxide；Molybdenum disulfide is 300-500 mesh molybdenum disulfide.
- 7. it is according to claim 1 water suction breathe freely type composite flooring bricks, which is characterized in that the waterglass be sodium silicate and Potassium water glass is according to mass ratio 4:1 mixing composition.
- The preparation method of type composite flooring bricks 8. a kind of water suction as described in claim 1 is breathed freely, which is characterized in that including following step Suddenly：(1) above-mentioned raw materials are added in high-speed mixer with 2000-3000 revs/min of speed, are uniformly mixed.(2) harder, compression moulding is used to stand 15-30 minutes mixed material made from step (1)；(3) floor tile after air-drying is placed into and fires anaerobic heating in kiln, the heating is divided into pre-heat phase, calcining rank Section and holding stage；110-140 degrees Celsius of the pre-heat phase heating temperature, heating time are 30-50 minutes；Described 300-400 degrees Celsius of calcination stage heating temperature, heating time are 13-15 hours；The holding stage heating temperature 160- 200 degrees Celsius, heating time is 3-4 hours.
- The preparation method of type composite flooring bricks 9. water suction according to claim 8 is breathed freely, which is characterized in that the holding stage It is temperature control to 160-200 degrees Celsius, after heating 3-4 hour, pass hull closure, after cooled to room temperature, taking-up finished product.