CN108414721A - 一种铝板带箔表面清洁度检验方法 - Google Patents
一种铝板带箔表面清洁度检验方法 Download PDFInfo
- Publication number
- CN108414721A CN108414721A CN201810107199.6A CN201810107199A CN108414721A CN 108414721 A CN108414721 A CN 108414721A CN 201810107199 A CN201810107199 A CN 201810107199A CN 108414721 A CN108414721 A CN 108414721A
- Authority
- CN
- China
- Prior art keywords
- briquetting
- aluminium sheet
- foil
- sheet strip
- strip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种铝板带箔表面清洁度检验方法,检测所使用的擦拭溶液为NaOH:2—8%,STPP:0.1—0.5%,TSP:0.1—0.5%,纯水:92—97%;以上各组分重量百分比之和为100%;检测所使用的擦试器包括压块、外罩,压块为长方体,压块的两侧对称设有螺孔,外罩的两侧对称设有条形孔,两螺栓通过外罩的条形孔并经压块上的螺孔将压块固定。所述擦试器压块的压靠面为32mm*32mm且为R100±5mm的圆弧面,压块重量900g。本发明巧妙地设计带有圆弧面的擦拭器,并针对铝板带箔的加工特性重新选择了擦拭溶液,它的优点是能将脏物一次擦干净,提高了检验结果的准确性。
Description
技术领域
本发明涉及一种铝板带箔表面清洁度检验方法。
背景技术
铝板带箔表面清洁度在产品质量上是一项非常重要的指标,主要表现为铝板坯料表面不清洁直接关系后续轧制后成品的表面质量,如出现孔洞、针孔、线状或片状划伤;铝箔(特别是食品箔)表面不清洁,所含的污物直接关系到人体健康。
目前,在铝板带箔表面清洁度的检验方法上还存在一些技术上的难题,即按常规的检验方法无法科学有效地评估表面的清洁度,主要原因是常规方法以植物油为溶液,擦拭不易干净,常规擦拭工具由涂抹块、限位圈、限位方框组成,无法将表面污物均匀分布于擦拭纸面,辨识困难且不便于比对。即便擦拭工具设计足够巧妙能够满足要求,擦拭溶液不加以选择的话,擦拭时还是会有部分污物无法被湿润、乳化、皂化、分散和悬浮而残留于板面,而无法全部让纸擦拭掉,这样的话,检验结果还是不准确。
显然,现有的铝板带箔表面清洁度检验方法明显不适用,随着电池箔等新兴产品的出现且发展趋势猛烈,以及国人对于食品包装物中残留的污物影响人体健康的重视,这些新兴行业和社会健康意识增强都促进了对铝板带箔表面清洁度的检验提出更高的要求,在此背景下,攻克此检验方法成为不可回避的课题。
发明内容
本发明的目的在于提供一种铝板带箔表面清洁度的检验方法,从而解决无法科学有效检验铝板带箔表面清洁度的难题。本发明检验过程精简,同时提高了检验结果准确性和检验效率。
本发明是这样实现的,所述一种铝板带箔表面清洁度检验方法,其步骤如下:
1、试验准备
a)检测所使用的设备与器具:喷壶、柯达灰阶卡、白色纸巾纸、擦拭器、钢卷尺和工具刀;
b)检测所使用的试剂:擦拭溶液为NaOH:2—8%,STPP:0.1—0.5%,TSP:0.1—0.5%,纯水:92—97%;以上各组分重量百分比之和为100%;
c)检测试验要求在环境温度和充足光线下进行;
d)取样:整幅铝板带箔要求平整,不得折皱,不得用手触摸铝板带箔表面;
2、组织检验
a)将待测铝板带箔试样置于平整、洁净的水平面;
b)检测部位:铝板带箔试样表面中部和距两边部各100mm的位置;
c)将铝板带箔试样水平放置后,使用喷壶将擦试溶液水平喷出一层细密的喷雾并覆盖于试样检测部位表面;
d)橡皮筋将擦拭纸包住擦拭器压块的弧面,并确保压块弧面的擦拭纸平整无褶皱;以压块的圆弧面为接触面,手握擦拭器外罩,靠压块自重在检测位置沿轧制方向移动0.6m;
e)从压块上取下擦拭纸,以擦拭纸上灰度最深的部位与柯达灰阶卡的灰度值对比,取最接近的灰度值为试样的清洁度等级;
f)铝板带箔试样表面每次清洁度检测时更换新的擦拭纸;试样表面3-7个位置检测所得的最高灰阶卡值判定为该料卷的清洁度最终等级。
本发明所述擦试液最佳为NaOH:4.5%,STPP:0.25%,TSP:0.25%,纯水:95%。
本发明所述白色纸巾的表面不压花纹。
本发明所述擦试器包括压块、外罩,压块为长方体,压块的两侧对称设有螺孔,外罩的两侧对称设有条形孔,两螺栓通过外罩的条形孔并经压块上的螺孔将压块固定。
本发明所述擦试器压块的压靠面为32mm*32mm且为R100±5mm的圆弧面,压块重量900g。
本发明的有益效果是,攻克常规方式所带来的辨识度不高的问题,且巧妙地将常规方式中的涂抹块、限位圈、限位方框等工具整合设计为擦拭器,既提高了辨识度也简化检验过程,提高工作效率。另外,针对铝板带箔的加工特性重新选择了擦拭溶液,提高了检验结果的准确性。本方法简单、实用、可操作性强,具有比常规方法减少操作时间、易辨识和更准确的特点。
附图说明
图1为本发明所述擦试器示意图。
图2为图1局部剖示图。
图3为本发明所述擦试器的外罩示意图。
图4为本发明所述擦试器的压块示意图。
图5为本发明所述铝板带箔检测部位示意图。
图中:1.压块,2.外罩,3.螺孔,4.条形孔,5.螺栓,6.六角螺母。
具体实施方式
所述一种铝板带箔表面清洁度检验方法,如图1-5所示,其步骤如下:
1、试验准备
a)检测所使用的设备与器具:喷壶、柯达灰阶卡、白色纸巾纸(表面不压花纹)、擦拭器、橡皮筋、钢卷尺和工具刀;
b)检测所使用的试剂:擦拭溶液为NaOH:4.5%,STPP:0.25%,TSP:0.25%,纯水:95%;
c)检测试验要求在环境温度和充足光线下进行;
d)取样:整幅铝板带箔要求平整,不得折皱,不得用手触摸铝板带箔表面;
2、组织检验
a)将待测铝板带箔试样置于平整、洁净的水平面;
b)检测部位:铝板带箔试样表面中部和距两边部各100mm的位置;
c)将铝板带箔试样水平放置后,使用喷壶将擦试溶液水平喷出一层细密的喷雾并覆盖于试样检测部位表面;
d)橡皮筋将擦拭纸包住擦拭器压块的弧面,并确保压块弧面的擦拭纸平整无褶皱;以压块的圆弧面为接触面,手握擦拭器外罩,靠压块自重在检测位置沿轧制方向移动0.6m;
e)从压块上取下擦拭纸,以擦拭纸上灰度最深的部位与柯达灰阶卡的灰度值对比,取最接近的灰度值为试样的清洁度等级;
f)铝板带箔试样表面每次清洁度检测时更换新的擦拭纸;试样表面3个位置检测所得的最高灰阶卡值判定为该料卷的清洁度最终等级。
本发明所述擦试器包括压块1、外罩2,压块1为长方体,压块1的两侧对称设有螺孔3,外罩2的两侧对称设有条形孔4,两螺栓5通过外罩2的条形孔4并经压块1上的螺孔3将压块1固定。本发明所述擦试器压块的压靠面为32mm*32mm且为R100±5mm的圆弧面,压块重量900g。图1中还标有六角螺母6。
3、表面清洁度检测注意事项:
a)擦拭器沿着压块弧面方向保持匀速移动,使其受力均匀地与铝板带箔试样表面摩擦。
b)安全注意事项:使用工具刀取样和搬运铝板材时,注意避免被板带材和利器割伤。
本发明巧妙地设计带有圆弧面的擦拭器,并针对铝板带箔的加工特性重新选择了擦拭溶液,它的优点是能将脏物一次擦干净,提高了检验结果的准确性。
STPP:为三聚磷酸钠,清洗的作用,可以络合Ca、Mg及其他金属。
TSP:为磷酸钠,清洗的作用,有效去除矿物油,表现为对杂质的软化、络合、乳化、分散和悬浮。
本发明整体优于现有的常规方法主要体现在以下几个方面:
1.准确性:本发明通过多次试验摸索,探寻出的擦拭溶液可通过将铝板带箔表面的污物湿润、乳化、皂化、分散和悬浮于板面,从而用擦拭纸可以把污物全部擦拭到纸面。而现有的常规方法的擦拭溶液(植物油)会使擦拭过后的铝板带箔表面仍然残留部分污物。所以采用现有的常规检验方法无法真实地全面地体现出铝板带箔表面的清洁程度,以现有的常规方法所得的检测结果作为判定铝板带箔表面质量合格与否的依据易导致质量等级的错判或漏判。
2.辨识度:现有的常规方法用擦拭纸包裹圆柱块进行擦拭作业时,纸张形成的几处褶皱部位聚集大部分的污物;另外,由于擦拭面为平面,大量的污物也会聚集在圆柱面的边沿,试验后发现擦拭纸上的污物都聚集在上述两个部位,导致擦拭纸与柯达灰阶卡比对时不易辨识清洁程度等级。本发明的擦拭器压块为方形,擦拭纸剪裁为压块尺寸大小,作业时纸张无褶皱;擦拭器的擦拭面为圆弧面,作业时擦拭压块能小角度地摆动,使污物均匀地分布于擦拭纸上,与柯达灰阶卡比对时非常容易辨识。
3.便捷性:现有的常规方法需要涂抹块、限位圈、限位方框等多个工具配合使用,整个过程操作繁琐易出错。本发明采用的擦拭器,试验作业时一气呵成,快速而简捷,整个试验时间约为现有的常规方法的四分之一,大大提高了工作效率。
Claims (5)
1.一种铝板带箔表面清洁度检验方法,其步骤如下:
1)试验准备
检测所使用的设备与器具:喷壶、柯达灰阶卡、白色纸巾纸、擦拭器、钢卷尺和工具刀;
检测所使用的试剂:擦拭溶液为NaOH:2—8%,STPP:0.1—0.5%,TSP:0.1—0.5%,纯水:92—97%;以上各组分重量百分比之和为100%;
检测试验要求在环境温度和充足光线下进行;
取样:整幅铝板带箔要求平整,不得折皱,不得用手触摸铝板带箔表面;
2)组织检验
将待测铝板带箔试样置于平整、洁净的水平面;
检测部位:铝板带箔试样表面中部和距两边部各100mm的位置;
将铝板带箔试样水平放置后,使用喷壶将擦试溶液水平喷出一层细密的喷雾并覆盖于试样检测部位表面;
橡皮筋将擦拭纸包住擦拭器压块的弧面,并确保压块弧面的擦拭纸平整无褶皱;以压块的圆弧面为接触面,手握擦拭器外罩,靠压块自重在检测位置沿轧制方向移动0.6m;
从压块上取下擦拭纸,以擦拭纸上灰度最深的部位与柯达灰阶卡的灰度值对比,取最接近的灰度值为试样的清洁度等级;
铝板带箔试样表面每次清洁度检测时更换新的擦拭纸;试样表面3-7个位置检测所得的最高灰阶卡值判定为该料卷的清洁度最终等级。
2.根据权利要求1所述一种铝板带箔表面清洁度检验方法,其特征是:所述擦试液(重量百分比)为NaOH:4.5%,STPP:0.25%,TSP:0.25%,纯水:95%。
3.根据权利要求1所述一种铝板带箔表面清洁度检验方法,其特征是:所述白色纸巾的表面不压花纹。
4.根据权利要求1所述一种铝板带箔表面清洁度检验方法,其特征是:所述擦试器包括压块、外罩,压块为长方体,压块的两侧对称设有螺孔,外罩的两侧对称设有条形孔,两螺栓通过外罩的条形孔并经压块上的螺孔将压块固定。
5.根据权利要求1所述一种铝板带箔表面清洁度检验方法,其特征是:所述擦试器压块的压靠面为32mm*32mm且为R100±5mm的圆弧面,压块重量900g。