CN108411635A - A kind of silk shirt - Google Patents
A kind of silk shirt Download PDFInfo
- Publication number
- CN108411635A CN108411635A CN201810106808.6A CN201810106808A CN108411635A CN 108411635 A CN108411635 A CN 108411635A CN 201810106808 A CN201810106808 A CN 201810106808A CN 108411635 A CN108411635 A CN 108411635A
- Authority
- CN
- China
- Prior art keywords
- silk
- shirt
- impregnated
- minutes
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of silk shirts, belong to garment industry.This silk shirt is cut out by silk to be made, and the silk is by 90 95% silk fibers, 3 5% rabbit suedes and 2 5% camel's hairs composition, and the fineness of the silk fiber is 15 18 μm, and length is 40 50mm；The fineness of rabbit suede is 13 15 μm, long 30 40mm；The fineness of camel's hair is 20 28 μm, long 35 40mm.The silk be will silk fiber, rabbit suede, camel's hair carry out and hair, spinning, weaving after, impregnated by clear water, fulling agent and there is softening agent the maintenances processing such as to impregnate simultaneously and be cut out again to make silk shirt.The silk shirt of the present invention can solve traditional silk shirt and easily wrinkle, hardness, the twist and the poor problem of elastic force, this silk shirt soft comfortable, and moisture absorption is ventilative, extremely efficient in preserving heat, resilience is good, not fugitive color, and with anti-ultraviolet function, moreover it is possible to reduce cost.
Description
Technical field
The present invention relates to garment industries, and in particular to a kind of silk shirt.
Background technology
Shirt is a kind of dress ornament that men and women, old and young like, and common shirt fabric mainly has：Cotton, burlap, mixes chemical fibre
Spinning, silk etc..Various fabrics have respective advantage and disadvantage, specific as follows：1, the advantages of cotton shirt, cotton easy shirt is light
Pine it is warming, soft and close-fitting, hygroscopicity, gas permeability are favourable, its advantage is that easily contracting, easily wrinkle, in appearance less well-pressed beauty,
It must often be pressed when wearing, and be easy to wear, deform, fade；2, chemical fibre shirt, advantage be bright in luster, soft texture,
It dangles well-pressed, smooth comfortable, disadvantage is then that abrasion resistance, heat resistance, hygroscopicity, gas permeability are poor, and heat is easily deformed, and is held
Easy to produce static electricity, though can be used to make all kinds of clothes, overall class is not high；3, burlap shirt, advantage are that intensity is high, inhale
Wet, heat conduction, gas permeability are favourable, and disadvantage is then that dress is not comfortable, and appearance is more coarse, stiff, uncomfortable；4, blended shirt,
Blended shirt be by natural fiber and chemical fibre according to a certain percentage, shirt made of mixed textile, its strong point is both
The shortcomings that absorbing the advantage of cotton, fiber crops, silk, hair and chemical fibre respectively, and being avoided as much as each, and in value
It is comparatively cheap, thus it is popular, but processing and making process is complex；5, silk shirt, frivolous, soft, smooth,
Ventilative, elegant, wear are comfortable, insufficient then be easy raw wrinkle, be easy to inhale body, it is not sufficiently strong, fade it is very fast, elastic not good enough.
Silk is natural animal protein fiber, is rich in the amino acid of 18 kinds of needed by human body, mainly by fibroin albumen and
Sericin forms, and is that silk weaves most important raw material.Silk has many advantages, such as moisture absorption, warming, ventilative, sense of touch is smooth,
It is soft, cool in summer and warm in winter, there are good extensibility, preferable heat resistance.
Silk fiber has following characteristic：First, moisture adsorption and releasing are good.Fibroin fiber be enriched many amidos (-
CHNH), the hydrophilic radicals such as amino (- NH2), and due to its porosity, it is easy to water diffusion, so it can be inhaled in air
It receives moisture or distributes moisture, keep its internal moisture certain.Under normal temperature, it can help skin to possess certain water
Point, do not make skin excessively dry；It wears, and the sweat and heat that human body is discharged can be distributed rapidly in summer, make one to feel cool
It is refreshing incomparable.Just because of this performance, make silk fabric more suitable for being in direct contact with human skin.Silk not only has preferable
Heat dissipation performance, also good warmth retention property.Its heat insulating ability revels in its multi-void fiber structure.In a silk fiber
In there are many superfine small fiber, and these tiny fibers are made of more tiny fiber.Therefore, seem solid
It is hollow that silk, which actually has 38% or more, and there is a large amount of air, these air to prevent heat in these gaps
Distribute, make silk have good warmth retention property.Second, sound-absorbing, dust suction, heat resistance.Real silk fabric has higher voidage, because
And with good sound absorption properties with it is inspiratory.Third has good comfort.Silk broadcloth is made of azelon, with
Human body has fabulous biocompatibility, and surface is smooth in addition, and the friction stimulation coefficient to human body is minimum in each fiber
, only 7.4%.But silk fiber self character is crisp, hardness, the twist and elastic force are poor.
Invention content
The object of the present invention is to provide a kind of silk shirt, this silk shirt is by a certain proportion of silk fiber, rabbit suede
It is made with camel's hair, traditional silk shirt can be solved and easily wrinkled, hardness, the twist and the poor problem of elastic force, this silk shirt softness are relaxed
Suitable, moisture absorption is ventilative, extremely efficient in preserving heat, resilience is good, not fugitive color, and with anti-ultraviolet function, moreover it is possible to reduce cost.
In order to achieve the above object, the technical solution adopted by the present invention is as follows：
A kind of silk shirt, is cut out by silk and is made, and the silk is by 90-95% silk fibers, 3-5% rabbits suede and 2-
5% camel's hair forms.
Above-mentioned technical proposal, preferably, the fineness of the silk fiber is 15-18 μm, length 40-50mm；Rabbit suede
Fineness be 13-15 μm, long 30-40mm；The fineness of camel's hair is 20-28 μm, long 35-40mm.
Above-mentioned technical proposal, preferably, the silk be by silk fiber, rabbit suede, camel's hair carries out and hair, spins, knits
It after making, is cut out again by maintenance processing and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 20-40 in bath raio, temperature is impregnated 5-10 minutes under conditions of being 20-25 DEG C；
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 30-40,35-40 DEG C of temperature, impregnates 15-30 points
Clock, Stirring 5-10 minutes, the fulling agent, softening agent, silk weight ratio be 2：0.8-1.5：70-90；
S3, dehydration, it is 45-50% to make the dewatered water content of silk；
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 30-40 minutes dry.
Above-mentioned technical proposal, preferably, the fulling agent is neutral soap powder.
Above-mentioned technical proposal, preferably, the softening agent is in hydroxy-terminated polysiloxane lotion, turkey red oil, sulfonated oil
One or more.
Above-mentioned technical proposal, preferably, maintenance processing further includes following steps：S5, the silk after drying is put
Enter and impregnated in antiultraviolet solution, the antiultraviolet solution is that anti-ultraviolet finishing agent is deployed into mass concentration with water is 2-
4% solution, soaking time are 20-30 minutes.
Above-mentioned technical proposal, preferably, the anti-ultraviolet finishing agent is prepared from the following raw materials in parts by weight：Nanometer
10-20 parts of titanium dioxide, 2-3 parts of anhydrous sodium sulphate, 15-20 parts of polybutylene terephthalate, 5-10 parts of lauryl sodium sulfate.
Above-mentioned technical proposal, preferably, maintenance processing further includes following steps：S6, antiultraviolet will have been impregnated
It is 70-90 DEG C that the silk of solution, which is placed in temperature, and decatize is carried out in the water vapour that humidity is 50-60%, and steaming time is 8-15 points
Clock.
Advantageous effect：
This silk shirt have it is frivolous, smooth bright and clean, soft and have certain hardness, it is drapability, gas permeability, warming
Property is preferable.Using silk made of silk fiber, rabbit suede, camel's hair after maintenance is handled, silk can be effectively maintained and be rich in
Amino acid and keep fibroin bioactivity, to human body have certain health-care effect；And silk lining can be improved
The moisture retention of clothing, moisturizing rate can improve the elasticity of silk shirt up to 65% or more, and the elasticity of compression makes it not up to 85% or more
It is yielding.In addition, this silk shirt compares traditional silk shirt, the day light fastness in addition to that can promote shirt also has very
Good anti-ultraviolet function, extends the service life of shirt.This silk shirt can solve traditional silk shirt and easily wrinkle, fugitive color,
Hardness, the twist and the poor problem of elastic force are made by adding rabbit suede and camel's hair with silk fiber, moreover it is possible to reduce cost.
Specific implementation mode
With reference to specific embodiment, the invention will be further described.
A kind of silk shirt, is cut out by silk and is made, and the silk is by 90-95% silk fibers, 3-5% rabbits suede and 2-
5% camel's hair forms；The fineness of the silk fiber is 15-18 μm, length 40-50mm；The fineness of rabbit suede is 13-15 μm, long
30-40mm；The fineness of camel's hair is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 20-40 in bath raio, temperature is impregnated 5-10 minutes under conditions of being 20-25 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 30-40,35-40 DEG C of temperature, impregnates 15-30 points
Clock, Stirring 5-10 minutes, the fulling agent, softening agent, silk weight ratio be 2：0.8-1.5：70-90；The fulling milling
Agent is neutral soap powder；The softening agent is one or more of hydroxy-terminated polysiloxane lotion, turkey red oil, sulfonated oil.
S3, dehydration, it is 45-50% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 30-40 minutes dry.
S5, the silk after drying is put into antiultraviolet solution and is impregnated, the antiultraviolet solution is with water by anti-purple
Outside line finishing agent is deployed into the solution that mass concentration is 2-4%, and soaking time is 20-30 minutes.The anti-ultraviolet finishing agent
It is prepared from the following raw materials in parts by weight：10-20 parts of nano-titanium dioxide, 2-3 parts of anhydrous sodium sulphate, polybutylene terephthalate
15-20 parts, 5-10 parts of lauryl sodium sulfate.
S6, the silk for having impregnated antiultraviolet solution is placed in temperature be 70-90 DEG C, humidity be 50-60% water vapour
Middle carry out decatize, steaming time are 8-15 minutes.
Embodiment 1
A kind of silk shirt, is cut out by silk and is made, and the silk is by 92% silk fiber, 4% rabbit suede and 4% camel's hair group
At；The fineness of the silk fiber is 15-18 μm, length 40-45mm；The fineness of rabbit suede is 13-15 μm, long 30-45mm；Camel
The fineness of suede is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 35 in bath raio, temperature is impregnated 8 minutes under conditions of being 24 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 35,37 DEG C of temperature, is impregnated 20 minutes, rotation is stirred
Mix 6 minutes, the fulling agent, softening agent, silk weight ratio be 2：0.9：80；The fulling agent is neutral soap powder；It is described soft
Soft dose is the hydroxy-terminated polysiloxane lotion of arbitrary proportion, turkey red oil, sulfonated oil.
S3, dehydration, it is 50% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 35 minutes dry.
S5, the silk after drying is put into antiultraviolet solution and is impregnated, the antiultraviolet solution is with water by anti-purple
Outside line finishing agent is deployed into the solution that mass concentration is 3%, and soaking time is 20-30 minutes.The anti-ultraviolet finishing agent by
The raw material of following parts by weight is made：15 parts of nano-titanium dioxide, 2.5 parts of anhydrous sodium sulphate, 17 parts of polybutylene terephthalate, ten
8 parts of sodium dialkyl sulfate.
S6, the silk for having impregnated antiultraviolet solution is placed in temperature be 80 DEG C, humidity be 55% water vapour in carry out
Decatize, steaming time are 10 minutes.
Embodiment 2
A kind of silk shirt, is cut out by silk and is made, and the silk is by 95% silk fiber, 3% rabbit suede and 2% camel's hair group
At；The fineness of the silk fiber is 15-18 μm, length 45-50mm；The fineness of rabbit suede is 13-15 μm, long 35-40mm；Camel
The fineness of suede is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 20 in bath raio, temperature is impregnated 10 minutes under conditions of being 25 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 30,35 DEG C of temperature, is impregnated 30 minutes, rotation is stirred
Mix 5 minutes, the fulling agent, softening agent, silk weight ratio be 2：0.8：70；The fulling agent is neutral soap powder；It is described soft
Soft dose is turkey red oil.
S3, dehydration, it is 45% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 30 minutes dry.
S5, the silk after drying is put into antiultraviolet solution and is impregnated, the antiultraviolet solution is with water by anti-purple
Outside line finishing agent is deployed into the solution that mass concentration is 2%, and soaking time is 30 minutes.The anti-ultraviolet finishing agent is by following
The raw material of parts by weight is made：10 parts of nano-titanium dioxide, 2 parts of anhydrous sodium sulphate, 15 parts of polybutylene terephthalate, dodecyl
5 parts of sodium sulphate.
S6, the silk for having impregnated antiultraviolet solution is placed in temperature be 70 DEG C, humidity be 60% water vapour in carry out
Decatize, steaming time are 15 minutes.
Embodiment 3
A kind of silk shirt, is cut out by silk and is made, and the silk is by 90% silk fiber, 5% rabbit suede and 5% camel's hair group
At；The fineness of the silk fiber is 15-18 μm, length 40-50mm；The fineness of rabbit suede is 13-15 μm, long 30-40mm；Camel
The fineness of suede is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 40 in bath raio, temperature is impregnated 5 minutes under conditions of being 20 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 40,40 DEG C of temperature, is impregnated 15 minutes, rotation is stirred
Mix 10 minutes, the fulling agent, softening agent, silk weight ratio be 2：1.5：90；The fulling agent is neutral soap powder；It is described soft
Soft dose is one or more of hydroxy-terminated polysiloxane lotion, turkey red oil, sulfonated oil.
S3, dehydration, it is 50% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 40 minutes dry.
S5, the silk after drying is put into antiultraviolet solution and is impregnated, the antiultraviolet solution is with water by anti-purple
Outside line finishing agent is deployed into the solution that mass concentration is 4%, and soaking time is 20 minutes.The anti-ultraviolet finishing agent is by following
The raw material of parts by weight is made：20 parts of nano-titanium dioxide, 3 parts of anhydrous sodium sulphate, 20 parts of polybutylene terephthalate, dodecyl
10 parts of sodium sulphate.
S6, the silk for having impregnated antiultraviolet solution is placed in temperature be 90 DEG C, humidity be 50% water vapour in carry out
Decatize, steaming time are 8 minutes.
Embodiment 4
A kind of silk shirt, is cut out by silk and is made, and the silk is by 93% silk fiber, 4% rabbit suede and 3% camel's hair group
At；The fineness of the silk fiber is 15-18 μm, length 40-50mm；The fineness of rabbit suede is 13-15 μm, long 30-40mm；Camel
The fineness of suede is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 25 in bath raio, temperature is impregnated 9 minutes under conditions of being 22 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 36,38 DEG C of temperature, is impregnated 25 minutes, rotation is stirred
Mix 7 minutes, the fulling agent, softening agent, silk weight ratio be 2：1.3：82；The fulling agent is neutral soap powder；It is described soft
Soft dose is sulfonated oil.
S3, dehydration, it is 48% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 37 minutes dry.
S5, the silk after drying is put into antiultraviolet solution and is impregnated, the antiultraviolet solution is with water by anti-purple
Outside line finishing agent is deployed into the solution that mass concentration is 2.5%, and soaking time is 26 minutes.The anti-ultraviolet finishing agent by with
The raw material of lower parts by weight is made：13 parts of nano-titanium dioxide, 2 parts of anhydrous sodium sulphate, 16 parts of polybutylene terephthalate, dodecane
7 parts of base sodium sulphate.
S6, the silk for having impregnated antiultraviolet solution is placed in temperature be 85 DEG C, humidity be 55% water vapour in carry out
Decatize, steaming time are 11 minutes.
Embodiment 5
A kind of silk shirt, is cut out by silk and is made, and the silk is by 94% silk fiber, 4% rabbit suede and 2% camel's hair group
At；The fineness of the silk fiber is 15-18 μm, length 40-50mm；The fineness of rabbit suede is 13-15 μm, long 30-40mm；Camel
The fineness of suede is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 35 in bath raio, temperature is impregnated 6 minutes under conditions of being 24 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 38,37 DEG C of temperature, is impregnated 22 minutes, rotation is stirred
Mix 9 minutes, the fulling agent, softening agent, silk weight ratio be 2：1.1：79；The fulling agent is neutral soap powder；It is described soft
Soft dose is that mass ratio is 1：1 turkey red oil and sulfonated oil.
S3, dehydration, it is 50% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 35 minutes dry.
S5, the silk after drying is put into antiultraviolet solution and is impregnated, the antiultraviolet solution is with water by anti-purple
Outside line finishing agent is deployed into the solution that mass concentration is 3.5%, and soaking time is 21 minutes.The anti-ultraviolet finishing agent by with
The raw material of lower parts by weight is made：18 parts of nano-titanium dioxide, 2.6 parts of anhydrous sodium sulphate, 19 parts of polybutylene terephthalate, 12
8 parts of sodium alkyl sulfate.
S6, the silk for having impregnated antiultraviolet solution is placed in temperature be 82 DEG C, humidity be 55% water vapour in carry out
Decatize, steaming time are 12 minutes.
Embodiment 6
A kind of silk shirt, is cut out by silk and is made, and the silk is by 91% silk fiber, 5% rabbit suede and 4% camel's hair group
At；The fineness of the silk fiber is 15-18 μm, length 40-50mm；The fineness of rabbit suede is 13-15 μm, long 30-40mm；Camel
The fineness of suede is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 30 in bath raio, temperature is impregnated 8 minutes under conditions of being 25 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 35,36 DEG C of temperature, is impregnated 25 minutes, rotation is stirred
Mix 8 minutes, the fulling agent, softening agent, silk weight ratio be 2：1.2：83；The fulling agent is neutral soap powder；It is described soft
Soft dose is that mass ratio is 1：1：1 hydroxy-terminated polysiloxane lotion, turkey red oil and sulfonated oil.
S3, dehydration, it is 45% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 32 minutes dry.
S5, the silk after drying is put into antiultraviolet solution and is impregnated, the antiultraviolet solution is with water by anti-purple
Outside line finishing agent is deployed into the solution that mass concentration is 3.2%, and soaking time is 24 minutes.The anti-ultraviolet finishing agent by with
The raw material of lower parts by weight is made：14 parts of nano-titanium dioxide, 2.3 parts of anhydrous sodium sulphate, 17 parts of polybutylene terephthalate, 12
6 parts of sodium alkyl sulfate.
Embodiment 7
A kind of silk shirt, is cut out by silk and is made, and the silk is by 93% silk fiber, 5% rabbit suede and 2% camel's hair group
At；The fineness of the silk fiber is 15-18 μm, length 40-50mm；The fineness of rabbit suede is 13-15 μm, long 30-40mm；Camel
The fineness of suede is 20-28 μm, long 35-40mm.
The silk is carried out after silk fiber, rabbit suede, camel's hair progress and hair, spinning, weaving again by maintenance processing
It cuts out and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 25 in bath raio, temperature is impregnated 10 minutes under conditions of being 20 DEG C.
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 36,38 DEG C of temperature, is impregnated 20 minutes, rotation is stirred
Mix 10 minutes, the fulling agent, softening agent, silk weight ratio be 2：1：81；The fulling agent is neutral soap powder；The softness
Agent is hydroxy-terminated polysiloxane lotion.
S3, dehydration, it is 45-50% to make the dewatered water content of silk.
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 37 minutes dry.
Although the present invention is disclosed as above with preferred embodiment, so it is not intended to limiting the invention, any this field skill
Art personnel, without departing from the spirit and scope of the present invention, when a little modification and perfect, therefore the protection model of the present invention can be made
It encloses to work as and is subject to what claims were defined.
Claims (8)
1. a kind of silk shirt, which is characterized in that cut out and be made by silk, the silk is by 90-95% silk fibers, 3-5%
Rabbit suede and 2-5% camel's hairs composition.
2. silk shirt as described in claim 1, it is characterised in that：The fineness of the silk fiber is 15-18 μm, and length is
40-50mm；The fineness of rabbit suede is 13-15 μm, long 30-40mm；The fineness of camel's hair is 20-28 μm, long 35-40mm.
3. silk shirt as described in claim 1, it is characterised in that：The silk is to carry out silk fiber, rabbit suede, camel's hair
It after hair, spinning, weaving, is cut out again by maintenance processing and makes silk shirt, the maintenance processing includes the following steps：
S1, it is impregnated with clear water, is 1: 20-40 in bath raio, temperature is impregnated 5-10 minutes under conditions of being 20-25 DEG C；
S2, it is impregnated with fulling agent and softening agent, under conditions of bath raio 1: 30-40,35-40 DEG C of temperature, is impregnated 15-30 minutes,
Stirring 5-10 minutes, the fulling agent, softening agent, silk weight ratio be 2：0.8-1.5：70-90；
S3, dehydration, it is 45-50% to make the dewatered water content of silk；
S4, dewatered silk is placed under 85 DEG C of temperature condition, it is 30-40 minutes dry.
4. silk shirt as claimed in claim 3, it is characterised in that：The fulling agent is neutral soap powder.
5. silk shirt as claimed in claim 3, it is characterised in that：The softening agent is hydroxy-terminated polysiloxane lotion, too
One or more of ancient oil, sulfonated oil.
6. silk shirt as claimed in claim 3, it is characterised in that：The maintenance processing further includes following steps：S5, it will do
Silk after dry, which is put into antiultraviolet solution, to be impregnated, and the antiultraviolet solution is to be deployed into anti-ultraviolet finishing agent with water
Mass concentration is the solution of 2-4%, and soaking time is 20-30 minutes.
7. silk shirt as claimed in claim 6, it is characterised in that：The anti-ultraviolet finishing agent is by following parts by weight
Raw material is made：10-20 parts of nano-titanium dioxide, 2-3 parts of anhydrous sodium sulphate, 15-20 parts of polybutylene terephthalate, dodecyl sulphur
Sour sodium 5-10 parts.
8. silk shirt as claimed in claim 6, which is characterized in that the maintenance processing further includes following steps：S6, it will soak
Steeped antiultraviolet solution silk be placed in temperature be 70-90 DEG C, humidity be 50-60% water vapour in carry out decatize, decatize
Time is 8-15 minutes.