CN106723417A - A kind of high-grade winter underwear fabric and preparation method thereof - Google Patents
A kind of high-grade winter underwear fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106723417A CN106723417A CN201611123075.4A CN201611123075A CN106723417A CN 106723417 A CN106723417 A CN 106723417A CN 201611123075 A CN201611123075 A CN 201611123075A CN 106723417 A CN106723417 A CN 106723417A
- Authority
- CN
- China
- Prior art keywords
- fiber
- fabric
- pearl
- preparation
- underwear fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-grade winter underwear fabric, blending is carried out using multiple fiber, pearl fiber possesses extraordinary healthcare function, and add a small amount of acrylic fiber can just to make blended yarn weaved fabric thermal property good；The existing good thermal property of fabric of the invention, while having pliability, permeability and environmental-protecting performance concurrently；In preparation process, the addition of hydrogen peroxide is reduced, while adding alkaline pectase, control the injury of basicity and temperature to fiber；Sodium Polyacrylate and organic acid are added, and using the processing mode for gradually heating up, not only Color is good, and small to the injury of fiber；Temperature is finally risen to 85 90 DEG C, enzyme is inactivated, preparation method of the invention, the pliability of fiber is very good, without adding softening agent to the further treatment of fiber；Processed using single bath process, met process requirements of the country to textile industry water-saving efficient.
Description
Technical field
The present invention relates to a kind of fabric, belong to field of textile, more particularly to a kind of high-grade winter underwear fabric and its
Preparation method.
Background technology
Traditional winter underwear fabric be conceived to it is warming, but with the continuous improvement of people's quality of the life, people couple
The requirement more and more higher of winter underwear, the winter underwear of high-quality not only requires that thermal property is good, also to winter underwear fabric
Pliability, health-care efficacy and environmental-protecting performance have certain requirement, therefore are necessary to research and develop a kind of high-grade winter underwear fabric.
The content of the invention
Based on the technical problem that background technology is present, the present invention proposes a kind of high-grade winter underwear fabric and its preparation side
Method.
Technical scheme is as follows：
A kind of high-grade winter underwear fabric, is formed by following fiber blend：Pearl fiber, acrylic fiber, cotton fiber and
Coolplus fibers.
Preferably, the composition of described high-grade winter underwear fabric, including following percentage by weight：
Pearl fiber 35-45%
Acrylic fiber 8-15%
Cotton fiber 20-30%
Coolplus fiber surpluses.
A kind of preparation method of high-grade winter underwear fabric, comprises the following steps：
A, with pearl fiber and acrylic fiber as warp thread, with cotton fiber and Coolplus fibers as weft yarn, knitted using water spray
Cloth machine, is made into blended yarn weaved fabric；
B, blended yarn weaved fabric is put into pre-configured integrated treatment liquid is processed, treatment conditions are：Regulation pH
It is 5.5-6.0 to be worth, and process time is 45-60min, and bath raio is 1：(40-50), 85-90 DEG C is gradually heating to by temperature from normal temperature,
And keeping the temperature at 85-90 DEG C, soaking time is 5-8min；Described integrated treatment liquid, including following main component：It is double
Oxygen water, chelating agent, organic acid, Sodium Polyacrylate, coloring agent and alkaline pectase；
C, fabric is taken out after, rinse 3-5min repeatedly with 90 DEG C of warm water, drain；
D, in 120-140 DEG C of rapid dehydration high-temperature shaping, you can.
Preferably, in described step B, described integrated treatment liquid, including following percentage by weight composition：
Hydrogen peroxide 0.5-1%
Chelating agent 0.4-0.8%
Organic acid 0.2-0.5%
Sodium Polyacrylate 1-3%
Coloring agent 2-8%
Alkaline pectase 1-2%
Water surplus.
Preferably, described chelating agent is EDTA.
Preferably, described coloring agent is vegetable dyeing agent.
Preferably, described organic acid is citric acid.
Pearl fiber is that nano-glass pearl powder is added in fiber in viscose rayon spinning using high-tech means, makes fibre
Dimension is in vivo and appearance is uniform-distribution with nano-pearl particulate.Specially pearl protein function master batch and fibre resin section structure
Into, the inner and outer table of corpus fibrosum is uniform-distribution with nano-pearl particulate, individual fibers are just as a string pearl necklace, abnormal light
It is bright smooth.It is a kind of tencel for cooperating common research and development with Shanghai novel spinning center by Donghua University, category is pioneering both at home and abroad
High-grade functional fiber.
The existing pearl face skin-care effect of pearl fiber, there is that viscose rayon moisture absorption is ventilative, characteristic comfortable and easy to wear again.Pearl
Fiber surface is uniform-distribution with pearl micro-particle, for a long time in skin contact, with pearl face skin care, Toxin-Vanquishing of relieving inflammation or internal heat, tender white muscle skin,
Anti-ultraviolet effect.Pearl fiber contains several amino acids and trace element, and fiber surface is smooth nice and cool, there is light as pearl
Pool.
After pearl powder is absorbed by the body, by participating in body metabolism, reaches the overall conditioning of whole body skin and maintain.Its energy
Promote neonatal cell synthesis, and constantly add to skin surface, make skin smooth, exquisiteness, flexible.Scientifically take pearl powder
Play the role of significantly to mitigate serum lipid peroxidation, and this lipid is combined into protein and can generate lipofuscin (age mark), this
The secret place that exactly the Empress Dowager is held with the kind beauty treatment of pearl.
After with pearl powder painting face, the activity of human skin superoxide dismutase (SOD) can be promoted, suppress melanin
Synthesis, keeps whitening skin.Further, since SOD has the effect for removing free radical, skin senescence, corrugation can be prevented.
(1) beauty care, tender pale skin
Human body wears pearl fiber underwear, the pearl nano particle on fiber and skin intimate contact, the lactic acid in sweat
Meeting dissolution fiber middles point pearl nutritional composition, is absorbed by skin, promotes human skin superoxide dismutase (SOD)
Activity, the synthesis for suppressing melanin keeps whitening skin.Further, since SOD has the effect for removing free radical, skin can be prevented
Aging wrinkles.The traditional Chinese medical science thinks：Pearl sweet-salty cold in nature, thoughts of returning home Liver Channel, function appearance skin makeup, moisturizing myogenic, clear spot subtracts wrinkle, delays
Aging；It is mainly used in the weary pool of facial freckle, chloasma, senile plaque, wrinkle, of flaccid muscles, pachylosis, has an old and weathered face and Cuo
Sore, burn and scald, sore, wound are not received, dermatitis etc..Pearl growth is cold in nature in water, with Toxin-Vanquishing effect of relieving inflammation or internal heat, long-term dress
Pearl fiber underwear can remove skin surface hot acne poison, have functions that nti-freckle, except acne, maintenance skin.
(2) uvioresistant
The main component of pearl is calcium carbonate, and itself has anti-ultraviolet function, is added when it is ground into nm regime
During fiber, its function is greatly reinforced.There is pearl fiber the anti-skin aging of antiultraviolet to act on.According to recent studies have shown that：Nanometer
Pearl powder also has the function of transmitting infrared waves, and it can improve microcirculation in human body, have health-care effect to human body.
(3) moisture absorption is breathed freely, takes comfortable
The carrier of nano-pearl fiber is viscose rayon, and its moisture absorption air permeable dress uses comfortable, after the resistance to pearl powder of addition in fiber
Portion and surface are uniform-distribution with pearl nano particle, and fabric hand is smooth nice and cool, and outward appearance is beautiful.
(4) All Pure Nature
Nano pearl powder is processed through pure physical method by high-quality fresh water pearl, and prezenta is carried by cotton linter
Take, therefore harmful substance of the pearl fiber without any chemically product, there is natural compatibility with skin.
(5) it is durable in use
Pearl nano particle is intimately combined with fiber in pearl fiber, with permanent, dress washed for a long time and be will not fall off.
Pearl is not alkaline-resisting acidproof, and alkaline washing does not hinder the slightest, and only pearl nano particle can just produce part under acidic sweat effect
Separate out, pearl underwear is in fact to turn the perfect adaptation with washing.
Existing pearl fiber has an extraordinary health-care efficacy, but present consumer, especially female consumer
Underwear demand to environmental protection, antibacterial, health is more and more stronger, therefore is necessary while health-care efficacy is taken into account, further lifting
The antibiotic effect of fabric.
Coolplus fiber surfaces carry numerous micropores and micro-grooves, can produce capillary effect, can be by human body flesh
The sweat and moisture on skin top layer, are absorbed to outer fabric layer, Quick diffusing moisture and sweat quickly, make human body surface keep it is dry and comfortable,
It is refrigerant, comfortable, the effect with regulation body temperature.Fibre section is "+" type, and surface is micro-grooves, while addition is special gathering
Zoarium utilizes the deliquescent difference of the material, assigns fiber countless trickle cavities.The capillary produced by these micro-grooves is showed
As with sweat via effects such as wicking diffusion, transmission, moment excretes the moisture for discharging skin surface.Coolplus is fine
Dimension is widely used, can pure spinning, also can be with cotton, hair, silk, numb and all kinds of chemical fibre blending or intertexture, can tatting, also knitting.Both gathered around
Just like the sense of touch of the natural fibers such as cotton, fiber crops, silk, wool, and surmounted natural fiber, Coolplus fabrics no matter rapid-drying properties,
Natural cotton is superior in gas permeability, preventing sheding tintability, shrink resistance and wrinkle resistance.
The beneficial effects of the present invention are：
1st, blending is carried out using multiple fiber, cotton fiber, Coolplus fibers and pearl fiber be all snugness of fit it is high,
The fiber of good air permeability；Pearl fiber possesses extraordinary healthcare function and adds a small amount of acrylic fiber just can be with simultaneously
Make blended yarn weaved fabric thermal property good；The existing good thermal property of fabric of the invention, while having pliability, permeability concurrently
And environmental-protecting performance；
2nd, in preparation process, processed using single bath process, meeting country will to the flow of textile industry water-saving efficient
Ask；
3rd, using single bath process process mainly needs to overcome two difficulties, and one is the even dyeing of various blend fibres
Property, especially acrylic fibers are relatively difficult to coloring；Two is to prevent preparation process from being destroyed to the structure of Coolplus fibers and pearl fiber,
So as to the Coolplus fibers and the performance of the pearl fiber of good health care effect that influence comfortableness strong；In the present invention, reduce double
The addition of oxygen water, while adding alkaline pectase, controls the injury of basicity and temperature to fiber；Add polyacrylic acid
Sodium and organic acid, and using the processing mode for gradually heating up, not only Color is good, and small to the injury of fiber；Finally will
Temperature rises to 85-90 DEG C, inactivates enzyme, preparation method of the invention, and the pliability of fiber is very good, without adding softening agent pair
Fiber is further processed.
Specific embodiment
Embodiment 1
A kind of high-grade winter underwear fabric, including following percentage by weight composition：
Pearl fiber 42%
Acrylic fiber 12%
Cotton fiber 25%
Coolplus fiber surpluses.
A kind of preparation method of high-grade winter underwear fabric, comprises the following steps：
A, with pearl fiber and acrylic fiber as warp thread, with cotton fiber and Coolplus fibers as weft yarn, knitted using water spray
Cloth machine, is made into blended yarn weaved fabric；
B, blended yarn weaved fabric is put into pre-configured integrated treatment liquid is processed, treatment conditions are：Regulation pH
It is 5.5-6.0 to be worth, and process time is 55min, and bath raio is 1：45, temperature is gradually heating to 88 DEG C from normal temperature, and temperature is protected
Hold at 88 DEG C, soaking time is 7min；
C, fabric is taken out after, rinse 4min repeatedly with 90 DEG C of warm water, drain；
D, in 125 DEG C of rapid dehydration high-temperature shapings, you can.
In described step B, described integrated treatment liquid, including following percentage by weight composition：
Hydrogen peroxide 0.8%
EDTA 0.8%
Citric acid 0.3%
Sodium Polyacrylate 2.5%
Vegetable dyeing agent 5%
Alkaline pectase 1.5%
Water surplus.
Embodiment 2
A kind of high-grade winter underwear fabric, including following percentage by weight composition：
Pearl fiber 35%
Acrylic fiber 15%
Cotton fiber 20%
Coolplus fiber surpluses.
A kind of preparation method of high-grade winter underwear fabric, comprises the following steps：
A, with pearl fiber and acrylic fiber as warp thread, with cotton fiber and Coolplus fibers as weft yarn, knitted using water spray
Cloth machine, is made into blended yarn weaved fabric；
B, blended yarn weaved fabric is put into pre-configured integrated treatment liquid is processed, treatment conditions are：Regulation pH
It is 5.5-6.0 to be worth, and process time is 60min, and bath raio is 1：40, temperature is gradually heating to 90 DEG C from normal temperature, and temperature is protected
Hold at 90 DEG C, soaking time is 5min；
C, fabric is taken out after, rinse 3min repeatedly with 90 DEG C of warm water, drain；
D, in 140 DEG C of rapid dehydration high-temperature shapings, you can.
In described step B, described integrated treatment liquid, including following percentage by weight composition：
Hydrogen peroxide 0.5%
EDTA 0.8%
Citric acid 0.2%
Sodium Polyacrylate 3%
Vegetable dyeing agent 2%
Alkaline pectase 2%
Water surplus.
Embodiment 3
A kind of high-grade winter underwear fabric, including following percentage by weight composition：
Pearl fiber 45%
Acrylic fiber 8%
Cotton fiber 30%
Coolplus fiber surpluses.
A kind of preparation method of high-grade winter underwear fabric, comprises the following steps：
A, with pearl fiber and acrylic fiber as warp thread, with cotton fiber and Coolplus fibers as weft yarn, knitted using water spray
Cloth machine, is made into blended yarn weaved fabric；
B, blended yarn weaved fabric is put into pre-configured integrated treatment liquid is processed, treatment conditions are：Regulation pH
It is 5.5-6.0 to be worth, and process time is 45min, and bath raio is 1：50, temperature is gradually heating to 85 DEG C from normal temperature, and temperature is protected
Hold at 85 DEG C, soaking time is 8min；
C, fabric is taken out after, rinse 5min repeatedly with 90 DEG C of warm water, drain；
D, in 120 DEG C of rapid dehydration high-temperature shapings, you can.
In described step B, described integrated treatment liquid, including following percentage by weight composition：
Hydrogen peroxide 1%
EDTA 0.4%
Citric acid 0.5%
Sodium Polyacrylate 1%
Vegetable dyeing agent 8%
Alkaline pectase 1%
Water surplus.
Embodiment 1-3 is detected：
This detection data is just for above-mentioned detection sample.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technology according to the present invention scheme and its
Inventive concept is subject to equivalent or change, should all be included within the scope of the present invention.
Claims (7)
1. a kind of high-grade winter underwear fabric, it is characterised in that formed by following fiber blend：Pearl fiber, acrylic fiber, cotton
Fiber and Coolplus fibers.
2. top grade winter underwear fabric as claimed in claim 1, it is characterised in that the composition including following percentage by weight：
Pearl fiber 35-45%
Acrylic fiber 8-15%
Cotton fiber 20-30%
Coolplus fiber surpluses.
3. a kind of preparation method of high-grade winter underwear fabric, it is characterised in that comprise the following steps：
A, with pearl fiber and acrylic fiber as warp thread, with cotton fiber and Coolplus fibers as weft yarn, using weaving machine with water spraying,
It is made into blended yarn weaved fabric；
B, blended yarn weaved fabric is put into pre-configured integrated treatment liquid is processed, treatment conditions are：Adjusting pH value is
5.5-6.0, process time is 45-60min, and bath raio is 1：（40-50）, temperature is gradually heating to 85-90 DEG C from normal temperature, and will
Temperature is maintained at 85-90 DEG C, and soaking time is 5-8min；Described integrated treatment liquid, including following main component：Dioxygen
Water, chelating agent, organic acid, Sodium Polyacrylate, coloring agent and alkaline pectase；
C, fabric is taken out after, rinse 3-5min repeatedly with 90 DEG C of warm water, drain；
D, in 120-140 DEG C of rapid dehydration high-temperature shaping, you can.
4. the preparation method of top grade winter underwear fabric as claimed in claim 1, it is characterised in that in described step B, institute
The integrated treatment liquid stated, including following percentage by weight composition：
Hydrogen peroxide 0.5-1%
Chelating agent 0.4-0.8%
Organic acid 0.2-0.5%
Sodium Polyacrylate 1-3%
Coloring agent 2-8%
Alkaline pectase 1-2%
Water surplus.
5. the preparation method of top grade winter underwear fabric as claimed in claim 1, it is characterised in that described chelating agent is
EDTA。
6. the preparation method of top grade winter underwear fabric as claimed in claim 1, it is characterised in that described coloring agent is to plant
Thing coloring agent.
7. the preparation method of top grade winter underwear fabric as claimed in claim 1, it is characterised in that described organic acid is lemon
Lemon acid.