CN108409211B - 一种干粉砂浆及其制备方法和用途 - Google Patents
一种干粉砂浆及其制备方法和用途 Download PDFInfo
- Publication number
- CN108409211B CN108409211B CN201810214282.3A CN201810214282A CN108409211B CN 108409211 B CN108409211 B CN 108409211B CN 201810214282 A CN201810214282 A CN 201810214282A CN 108409211 B CN108409211 B CN 108409211B
- Authority
- CN
- China
- Prior art keywords
- component
- mortar
- bag
- meshes
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
样品 | 凝结时间/h | 28d抗压强度/MPa | 14d拉伸粘结强度/MPa |
实施例1 | 3.3 | 10.2 | 0.7 |
实施例2 | 3.2 | 10.8 | 0.8 |
实施例3 | 3.5 | 13.8 | 1.0 |
实施例4 | 3.8 | 12.1 | 1.2 |
实施例5 | 4.3 | 14.2 | 1.2 |
对比例1 | 3.3 | 8.2 | 0.4 |
对比例2 | 3.2 | 8.8 | 0.4 |
对比例3 | 3.5 | 9.2 | 0.5 |
对比例4 | 3.1 | 9.9 | 0.6 |
对比例5 | 3.2 | 9.7 | 0.6 |
Claims (9)