CN108396438A - A kind of preparation method of woven carpet without gum operating process - Google Patents
A kind of preparation method of woven carpet without gum operating process Download PDFInfo
- Publication number
- CN108396438A CN108396438A CN201810137351.5A CN201810137351A CN108396438A CN 108396438 A CN108396438 A CN 108396438A CN 201810137351 A CN201810137351 A CN 201810137351A CN 108396438 A CN108396438 A CN 108396438A
- Authority
- CN
- China
- Prior art keywords
- yarn
- ethylene
- clad
- carpet
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of the woven carpet without gum operating process, use the second clad for meldable fibre long filament or spun yarn, first clad is polypropylene fiber long filament or spun yarn, second clad accounts for 20% the 50% of composite yarn gross mass, first clad accounts for 10% the 15% of composite yarn gross mass, and surplus is that the mode of heart yarn is made and hangs pile filling.When producing non-adhesive carpet as adhesives using hot melt ethylene-vinyl acetate co-polymer fiber, and cooperation cotton fiber, pile yams made of viscose rayon, when hot melt ethylene-vinyl acetate co-polymer fiber is melted when hot pressing process is heated to its fusing point or more, fiber Macromolecular chain configuration changes, pass through the transition of segment, entire macromolecular chain is set to slide, VISCOUS FLOW occurs, pile and weft yarn and weft yarn and warp thread carry out effectively solid after solidification, enhance the extraction strength and the conformality of carpet and the stability of size of pile, to which the gum process in carpet preparation process be omitted, keep carpet obtained more environmentally friendly.
Description
Technical field
The present invention relates to field of sanitary equipment more particularly to a kind of preparation sides of woven carpet without gum operating process
Method.
Background technology
With the raising of modern life level, to the comfort of part public place and house fitting-up, fashion, environmental protection
The requirements such as property are also higher and higher.The utilization rate of carpet accounts for greatly in part public place and house ornamentation.Carpet has
The function of warming adjusting, in large area place mat carpet can reduce indoor by ground dispersed heat, block ground cold air
Invasion make one to bask comfortable.There is sound absorption function simultaneously, the surface that the abundant quality of carpet is stood with lint cluster has well
Sound-absorbing effect, and can suitably reduce influence of noise, due to the fabric that carpet is high resilience fiber, have plentiful, thick and solid, soft
Quality, so above walk when will produce preferable screen resilience, be comfortable on softness.Carpet has both aesthetic function simultaneously,
Quality is plentiful, and ground can seem dignified gorgeous after the magnificent laying carpet of appearance, obtain fabulous decorative effect.
Carpet is had by type point:Wool carpet, chemical fibre carpet, cortex carpet, rubber carpet, natural fiber carpet etc..
Respectively there are the characteristics and advantages of oneself.
Carpet can be divided into woven carpet and hand-made carpet by production method difference.Woven carpet includes tufted carpet and machine again
Knit Wilden carpet, woven Axminster carpet.Woven Wilden carpet is interweaved by warp thread, weft yarn, pile yams, through upper
The later process such as glue, shorn velvet are arranged and are made, and warp thread, weft yarn, pile yams mechanical adhesion, woven Axminster carpet is made to be also
Interweaved by warp thread, weft yarn, pile yams, arranged by processes such as gluing, shorn velvets, wherein being needed using organic in gluing program
Solvent has the following problems by glue dissolved dilution, therefore in upper glue process:(1) during gluing, volatilization pernicious gas pollution
Environment influences worker's health;(2) gluing and dry solidification technological process are long, of long duration, limit speed of production, equipment accounts for
Big with space, glue consumption is big, high energy consumption, and then increases the production cost of carpet;(3) traditional carpet uses embryo blanket backsizing
Mode, glue need to infiltrate to pile yams by embryo blanket base cloth, due to the presence of embryo blanket base cloth, are easy to make pile yams by seldom glue
It is deadlocked, cause pile yams to extract strength insufficient, poor dimensional stability, it is yielding the problems such as.Meanwhile to reduce cost and raising
The problem of stiffness of carpet generally uses glue bond layer with during gluing together with calcium carbonate, and this method is brought is not
Easy reuse, and, when burning waste, fire retardant filler material is contained in waste.
Therefore, the prior art needs further improvement and develops.
Invention content
In view of above-mentioned deficiencies of the prior art, the purpose of the present invention is to provide a kind of without the woven of gum operating process
The preparation method of carpet, ensure pile extract strength and omit coating process under the premise of, enhance carpet conformality and
Dimensional stability, and reduce the lower machine broadwise crimp after braiding carpet.
In order to solve the above technical problems, the present invention program includes:
A kind of preparation method of woven carpet without gum operating process, the carpet include base fabric, pile yams, weft yarn and
Warp thread, wherein the weft yarn includes hanging pile filling and not hanging pile filling, and extension pile filling is with the ratio for not hanging pile filling
1:1-1:4, naturally it is also possible to suitably be adjusted according to needs of production to hanging pile filling and not hanging the ratio of pile filling
It is whole, for example can also cancel all using the above-mentioned weft yarn of pile filling composition is hung and do not hang pile filling, to further increase ground
The properties of blanket.Pile yams be Quality Pure Cotton Yarn Production, cotton fiber mixed yarn, viscose fiber filament yarn, viscose rayon staple yarns yarn,
One kind in viscose rayon staple blended yarn, the extension pile filling are composite yarn, and composite yarn is made of heart yarn and clad, the core
Yarn is the normal weft for meeting carpet requirement, which includes the first clad and the second clad, and the second clad is heat
Molten fiber filament or spun yarn, the first clad are polypropylene fiber long filament or spun yarn, and the second clad accounts for composite yarn gross mass
20%-50%, the first clad accounts for the 10%-15% of composite yarn gross mass, and surplus is heart yarn;
Above-mentioned meldable fibre is hot melt ethylene-vinyl acetate co-polymer fiber, which heats ethylene-vinyl acetate
Ester copolymer fiber is composite fibre, which includes ethylene-vinyl acetate co-polymer material, bonding additives and inorganic
Nano material, wherein the mass ratio of ethylene-vinyl acetate co-polymer material, bonding additives and inorganic nano material is (85-
98.5):(1-10):(0.5-5);
Using silane coupling agent, titanate coupling agent, aluminate coupling agent or phosphate coupling agent to inorganic nano material
Surface modification is carried out, then ethylene-vinyl acetate co-polymer material with fusing point for 60 DEG C -70 DEG C and surface-modified nothing
Machine nano material is (60-70) in mass ratio:The ratio melt blending of (30-40) is granulated, and the first master batch is made;With fusing point for 60
DEG C -70 DEG C of ethylene-vinyl acetate co-polymer material is (50-60) in mass ratio with bonding additives:The ratio of (40-50) is molten
Melt blending to be granulated, the second master batch is made, it is 80 DEG C -110 DEG C then to press design requirement by the first master batch, the second master batch and fusing point
Above-mentioned hot melt ethylene-vinyl acetate co-polymer fiber is made in ethylene-vinyl acetate co-polymer material molten spinning.
The preparation method, wherein above-mentioned bonding additives be ethene-vinyl acetate-glycidyl methacrylate,
Ethylene-maleic acid-methacrylic dehydrated glyceride, ethylene-methyl acrylate-glyceryl methacrylate, ethylene-
Ethyl acrylate-glycidyl methacrylate, ethylene/n-butyl acrylate-glycidyl methacrylate, polypropylene
Graft glycidyl methacrylate, polyethylene to graft glycidyl methacrylate, ethylene/butylene copolymers are grafted first
Base glycidyl acrylate, ethylene/octene graft glycidyl methacrylate, styrene/ethylene/butadiene
Block copolymer graft glycidyl methacrylate, ethylene-methyl acrylate-maleic anhydride terpolymer, ethylene-the third
Olefin(e) acid acrylate-co-maleic anhydride terpolymer, ethylene/n-butyl acrylate-maleic anhydride terpolymer, maleic anhydride grafting
Ethylene-vinyl acetate co-polymer, maleic anhydride grafted polyethylene, ethylene/octene grafted maleic anhydride, ethylene/fourth
Alkene copolymer connects one or more in school maleic anhydride, ethylene-acrylic acid copolymer;Above-mentioned inorganic nano material is titanium dioxide
One or more in silicon, calcium carbonate, montmorillonite, titanium dioxide, inorganic nano material grain size is 15 nanometers -20 nanometers, compares table
Area is 150 ± l0m2/g。
The preparation method, wherein press the advance structure design of carpet, be made after pile yams, weft yarn and warp thread are interweaved
Embryo blanket makes the fusing flowing of the second clad to embryo blanket hot-pressing processing, through cooling and solidifying, bonding pile yams and weft yarn and weft yarn with
Warp thread, then above-mentioned carpet is obtained after subsequent processing.
The preparation method, wherein above-mentioned hot using being carried out after far infrared or hot-air preheating to embryo blanket hot-pressing processing
Roller pressurizes;Before embryo blanket enters heat roller tube surface, first far infrared or hot-air is used to preheat embryo blanket, on heat roller tube surface
It is provided with 1-3 pressure roller, heat roller tube is dynamic for main turn, and pressure roller is driven rotation, and embryo blanket is slave drive, hot-rolling drum surface temperature
It it is 120 DEG C -160 DEG C, embryo blanket carries out hot pressurization by different pressure rollers successively;Embryo blanket leaves to enter in heat preservation zone after hot-rolling and carry out etc.
Temperature crystallization.
The preparation method, wherein the composite yarn of above-mentioned extension pile filling is to be added using coating machine or Novelty twisters
Composite yarn made of work.
The preparation method, wherein with polypropylene fiber long filament or spun yarn for the first clad, to heat ethylene-vinegar
Vinyl acetate copolymer fiber filament or spun yarn are the second clad, coating machine or fancy twist yarn when coating the first clad
It is 10 centimetres -20 centimetres that the seal wire of machine, which hooks distance, when coat the second clad the seal wire of coating machine or Novelty twisters hook away from
From being 1 centimetre -15 centimetres, and when the distance that seal wire hooks when the second layer coats coat than first layer seal wire hook distance it is 5 centimetres low
More than;
First clad is wrapped in compact state on heart yarn, and the second clad is wrapped in the first clad in soft fluffy state
On surface, above-mentioned extension pile filling is made after carrying out first layer cladding and second layer cladding to the heart yarn for hanging pile filling.
The preparation method, wherein above-mentioned carpet is woven Wilden carpet or woven Axminster carpet.
A kind of preparation method of woven carpet without gum operating process provided by the invention heats ethylene-acetic acid second
There is enoate copolymer fiber amorphous-crystalline state structure, the presence of crystal region fiber to be made to have certain strength;And it is amorphous
The presence in area makes the macromolecular chain of fiber can move freely, and to make the property of fiber close to amorphous high polymer, has
Some physical state features possessed by Amorphous Polymers, thus it is heated when have glassy state, elastomeric state, viscous state, therefore heat
Molten ethylene-vinyl acetate co-polymer fiber can carry out melt-processed, and have after cooling and solidifying again certain strength and
Flexibility, when producing non-adhesive carpet as adhesives using hot melt ethylene-vinyl acetate co-polymer fiber, and cooperation
Pile yams made of cotton fiber, viscose rayon, when hot melt ethylene-vinyl acetate co-polymer fiber is heated to it in hot pressing process
It is melted when more than fusing point, fiber Macromolecular chain configuration changes, and by the transition of segment, entire macromolecular chain is made to slide
It moves, VISCOUS FLOW occurs and is flowed by the capillarity of glued Inter-fiber voids and the surface tension effects of fiber
Melt sprawl infiltration in fiber surface, again cool and solidify after, pass through mechanical adhesion power and diffusion interfacial molecular active force
Pile yams and weft yarn are bonded, while weft yarn and warp thread are effectively consolidated after curing, enhances the conformality and size of carpet
Stability keeps carpet obtained more environmentally friendly to which the gum process in carpet preparation process be omitted.
And weft yarn is divided into the normal weft for not hanging pile and hangs the composite yarn of pile, due to meldable fibre phase in composite yarn
To higher price, therefore selectivity uses composite yarn as weft yarn, can reduce meldable fibre dosage, is ensureing tuft withdrawal force
Under the premise of, the production cost of carpet is reduced, and the stiffness and conformality of carpet can be improved in the addition of inorganic nano material.With silicon
Alkane coupling agent, titanate coupling agent, aluminate coupling agent, phosphate coupling agent etc. carry out surface modification to inorganic nano material,
One layer of organic matter, enhancing inorganic nano material and ethylene-vinyl acetate co-polymer material are covered on inorganic nano material surface
Compatibility and bonding force, and dispersibility of the enhancing inorganic nano material in ethylene-vinyl acetate co-polymer material;With
Ethylene-vinyl acetate co-polymer material that fusing point is 60 DEG C -70 DEG C and surface-modified inorganic nano material melt blending
It is granulated, the first master batch is made, viscosity is low when due to fusing point being 60 DEG C -70 DEG C of ethylene-vinyl acetate co-polymer material molten
Good fluidity can make inorganic nano material have preferable dispersibility, profit in heating ethylene-vinyl acetate co-polymer fiber
It is processed in follow-up spinning.
Meldable fibre is directly placed in embryo blanket using during carpet weaving, can effectively solve traditional carpet craft gum
The problem of glue is not easy to permeate in the process, while omitting traditional gum process.The weft yarn composite yarn for hanging pile covers shape using double-contracting
Formula, the first clad select normal polypropylene filament fiber or spun yarn, fusing point at 160 DEG C or more, in hot pressing process due to
Hot pressing temperature will not melt between 130 DEG C -160 DEG C, heart yarn surface is wound in always with fiber condition, in mechanical force
Under the action of firmly combined with heart yarn;Since meldable fibre strand and polypropylene fiber strand contain identical flexible fat
Segment, therefore there is preferable compatibility and affinity, and when heating melting, meldable fibre moieties chain and polypropylene fiber
Moieties chain can mutually be wound, while meldable fibre strand and the partially flexible fat segment of polypropylene fiber strand can be sent out
Raw exchange reaction, further enhances the binding force of meldable fibre material and polypropylene fibre material.Therefore the first clad weft yarn with
Play the role of preferable bridge joint during pile heat bonding.
And distance is hooked using big seal wire when the first clad cladding, the first clad fiber can be made used in big rotation
Property power under the action of heart yarn is fettered close, enhance the rigidity and stiffness of weft yarn, and then enhance the stiffness of carpet and conformal
Property.Meanwhile heart yarn be bound it is close after infiltration of the melt to heart yarn when can reduce meldable fibre heating melting, increase melt to suede
The infiltration capacity of head improves the extraction strength of carpet pile.First clad filament fiber or spun yarn are with side arranged in parallel
Formula is wound in heart yarn surface, and the regularity of arrangement is preferable, and regular arrangement can enhance the first clad filament fiber or spun yarn
Between and long filament or the interfibrous capillary effect of spun yarn, the Wicking of melt when being conducive to enhance meldable fibre heating melting
Effect increases the bonding force with the first clad after melt cures.
Second clad, i.e. clad made of meldable fibre hook distance when cladding using small seal wire, and when cladding rotates
Inertia is relatively low, the second clad fiber can be made to be coated on the first cover surface with more fluffy state, due to the second clad
More fluffy, its internal/external heating is more uniform when hot pressing, can make fiber while melt, and reduces the melting delay of inner fiber, contracting
Short hot pressing time improves hot pressing process production efficiency;Simultaneously because the second clad is more fluffy, meldable fibre is along perpendicular to core
The direction of yarn is more sprawled, and is conducive to increase the contact area of melt and pile after meldable fibre melts, enhancing melt is to pile
Infiltration infiltration increases the extraction strength of pile after solidification.
Due to containing ethene-vinyl acetate-methacrylic acid contracting in selected hot melt ethylene-vinyl acetate co-polymer fiber
Water glyceride, ethylene-maleic acid-methacrylic dehydrated glyceride, ethylene-methyl acrylate-Glycidyl methacrylate are sweet
Grease, ethylene-ethylacrylate-glycidyl methacrylate, ethylene/n-butyl acrylate-Glycidyl methacrylate are sweet
Grease, polypropylene grafted glycidyl methacrylate, polyethylene to graft glycidyl methacrylate, ethylene/butylene
Copolymer grafted glycidyl methacrylate, ethylene/octene graft glycidyl methacrylate, benzene second
Alkene/ethylene/butadiene block copolymer graft glycidyl methacrylate, ethylene-methyl acrylate-maleic anhydride tercopolymer
Copolymer, ethylene-ethyl acrylate-maleic anhydride copolymer, ethylene/n-butyl acrylate-maleic anhydride tercopolymer copolymerization
Object, maleic anhydride grafted ethene-vinyl acetate co-polymer, maleic anhydride grafted polyethylene, ethylene/octene are grafted horse
Carry out acid anhydrides, ethylene/butylene copolymers connect one or more in school maleic anhydride, ethylene-acrylic acid copolymer, each bonding additives
Contain flexible fat segment similar with flexible fat segment in ethylene-vinyl acetate co-polymer strand in strand,
Therefore each bonding additives have preferable compatibility and binding force, especially ethylene-with ethylene-vinyl acetate co-polymer material
Contain and ethylene-in vinyl acetate-glycidyl methacrylate, maleic anhydride grafted ethene-vinyl acetate co-polymer
The segment of vinyl acetate co-polymer material identical, binding force between the two is stronger, while in each bonding additives strand
Containing the active anhydride group of chemical property or epoxy group, in the granulation of the second master batch, hot melt ethylene-vinyl acetate co-polymer
When high-temperature fusion occurs for fibre spinning and carpet heat pressure adhesive, anhydride group or epoxy group on bonding additives strand can
The epoxy group on hydrogen bond, especially bonding additives strand is formed with the ester group on ethylene-vinyl acetate co-polymer strand
Group can in ethylene-vinyl acetate co-polymer terminal hydroxy group and end carboxyl form hydrogen bond and/or covalent bond, further enhance viscous
Connect the cementability of auxiliary agent and ethylene-vinyl acetate co-polymer material.Furthermore the addition of bonding additives can reduce ethylene-acetic acid
The surface tension of vinyl ester copolymers melt is conducive to ethylene-vinyl acetate co-polymer melt to suede in carpet heat pressure adhesive
The infiltration of gauze kerchief worn on a woman's head fiber increases the contact area of ethylene-vinyl acetate co-polymer melt and pile yarn fiber, enhances ethylene-
After vinyl acetate co-polymer melt cooling and solidifying with the mechanical bonding force of pile yarn fiber and spread interfacial molecular active force, into
And increase the extraction strength of carpet pile.
Using composite yarn as weft yarn, tightens heart yarn enhancing in the first clad and the second clad cladding and hang pile filling rigidity
And while stiffness, enhance the stretch modulus of composite yarn, and then reduce the lower machine broadwise crimp after the weaving of embryo blanket, mitigates carpet
The working strength of weaving process designer, increases the carpet manufacture breadth of loom, mitigates that carpet weaving breadth is limited to be brought
Waste.
Since selected pile yams are Quality Pure Cotton Yarn Production, cotton fiber mixed yarn, viscose fiber filament yarn, viscose rayon staple yarns
One kind in yarn, viscose rayon staple blended yarn containing primary hydroxyl and secondary hydroxyl isoreactivity group in strand, in carpet hot pressing
In process, hot melt ethylene-vinyl acetate co-polymer it is fiber-heated melting become melt infiltration cotton fiber and viscose rayon it is same
When, anhydride group or epoxy group in melt in bonding additives strand can be with the primary hydroxyls in cotton fiber and viscose glue strand
Covalent bond and/or hydrogen bond are formed with secondary hydroxyl, while molecular melt chain can mutually be wound with the strand for stretching out pile yarn fiber,
Carry out the machinery consolidation of molecule interchain.Active force, bonding additives between pile yams and bonding additives and ethylene-vinyl acetate
Between active force, the second clad between ester copolymer and the active force between the first clad, the first clad and heart yarn
Active force collective effect under, ensure that pile yams extraction strength.Meanwhile pile yams after cutting off due to its length compared with
It is short, and two head ends are free end, therefore easily voluntarily backtwisting, and then suede yarn is made to become fluffy, be conducive to melt infiltration, have after solidification
The increase of strength is bonded conducive to pile.
And hot pressing process is carried out by the way of first preheating multiple tracks hot pressing again, the uniformity of embryo blanket heating can be improved in preheating,
And improve the processing efficiency of hot pressing process;Multiple tracks hot pressing can enhance the mobility of melt after meldable fibre melts and be oozed to pile
Permeability improves the extraction strength of pile, while after preceding road pressure roller hot pressing, during the melt after meldable fibre can be made to melt is with heart yarn
Heart flowing expansion, while under pressure close to the pile yams part for hanging pile filling, being formed by plane and becoming in melt
Shape flattens, and then increases the contact area of melt and pile;It is acted on simultaneously in pressure close to the pile yams part for hanging pile filling
Air is extruded discharge between lower fiber, after carpet leaves pressure roller, since pile yarn fiber has certain resilience, in rebound
Negative pressure is formed inside pile yams, and then enhances infiltration of the melt to pile yams, increases the extraction strength of pile yams after melt solidification.
Using meldable fibre without adding organic solvent, reduces environmental pollution, ensure that carpet manufacture personnel and carpet use
The health of personnel;The warp thread hung the weft yarn of pile and intersected therewith can be consolidated after meldable fibre melt-flow resolidification
Knot, and then enhance the conformality and dimensional stability of carpet;The heat preservation that certain time is carried out after hot pressing, can be improved high molecular material
Crystallinity, and then improve carpet pile extraction strength.
Description of the drawings
Fig. 1 is the structural schematic diagram of the heat roller tube in autoclaving process in the present invention.
Specific implementation mode
The present invention provides a kind of preparation methods of the woven carpet without gum operating process, to make the mesh of the present invention
, technical solution and effect it is clearer, clear, the present invention is described in more detail below.It should be appreciated that described herein
Specific embodiment be only used to explain the present invention, be not intended to limit the present invention.
The present invention provides a kind of preparation method of the woven carpet without gum operating process, the carpet include base fabric,
Pile yams, weft yarn and warp thread, and the weft yarn includes hanging pile filling and not hanging pile filling, hang pile filling and do not hang pile
The ratio of weft yarn is 1:1-1:2, pile yams be Quality Pure Cotton Yarn Production, cotton fiber mixed yarn, viscose fiber filament yarn, viscose rayon it is pure spin it is short
One kind in silvalin, viscose rayon staple blended yarn, the extension pile filling are composite yarn, and composite yarn is by heart yarn and clad group
At the heart yarn is the normal weft for meeting carpet requirement, which includes the first clad and the second clad, the second cladding
Layer is meldable fibre long filament or spun yarn, and the first clad is polypropylene fiber long filament or spun yarn, and the second clad accounts for composite yarn
The 20%-50% of gross mass, the first clad account for the 10%-15% of composite yarn gross mass, and surplus is heart yarn;
Above-mentioned meldable fibre is hot melt ethylene-vinyl acetate co-polymer fiber, and the hot melt ethylene-vinylacetate is total
Polymer fibre includes ethylene-vinyl acetate co-polymer material and inorganic nano material, the ethylene-for being 60 DEG C -70 DEG C with fusing point
Vinyl acetate co-polymer material is (60-70) in mass ratio with surface-modified inorganic nano material:The ratio of (30-40)
Melt blending is granulated, and the first master batch is made;With fusing point be 60 DEG C -70 DEG C ethylene-vinyl acetate co-polymer material with it is Nian Jie
Auxiliary agent is (50-60) in mass ratio:The ratio melt blending of (40-50) is granulated, and the second master batch is made, and then pressing design requirement will
Ethylene-vinyl acetate co-polymer material molten spinning that first master batch, the second master batch are 80 DEG C -110 DEG C with fusing point is made
State hot melt ethylene-vinyl acetate co-polymer fiber.
Heating ethylene-vinyl acetate co-polymer fiber, there is amorphous-crystalline state structure, the presence of crystal region to make fiber
With certain strength;And the presence of amorphous region makes the macromolecular chain of fiber can move freely, to make the property of fiber connect
It is bordering on amorphous high polymer, has glass when there are some physical state features possessed by Amorphous Polymers, therefore being heated
State, elastomeric state, viscous state, therefore hot melt ethylene-vinyl acetate co-polymer fiber can carry out melt-processed, and again through cooling
There is certain strength and flexibility, using hot melt ethylene-vinyl acetate co-polymer fiber as adhesives after solidification
When producing non-adhesive carpet, and pile yams made of cooperation cotton fiber and viscose rayon, when hot melt ethylene-is vinyl acetate copolymerized
Fibres are melted when hot pressing process is heated to its fusing point or more, and fiber Macromolecular chain configuration changes, and passes through segment
Transition, so that entire macromolecular chain is slid, VISCOUS FLOW occur, passes through the capillarity and fiber of glued Inter-fiber voids
Surface tension effects, the melt flowed sprawls infiltration in fiber surface, after cooling and solidifying again, passes through mechanical adhesion power
With the active force binder fibre of diffusion interfacial molecular, weft yarn and warp thread are effectively consolidated after solidification, enhance the conformal of carpet
Property and the stability of size keep carpet obtained more environmentally friendly to which the gum process in carpet preparation process be omitted.
Further, above-mentioned bonding additives are ethene-vinyl acetate-glycidyl methacrylate, ethylene-Malaysia
Anhydride-methyl acrylic acid dehydrated glyceride, ethylene-methyl acrylate-glyceryl methacrylate, ethylene-acrylic acid second
Ester-glycidyl methacrylate, ethylene/n-butyl acrylate-glycidyl methacrylate, polypropylene grafted methyl
Glycidyl acrylate, polyethylene to graft glycidyl methacrylate, ethylene/butylene copolymers grafted methacrylic acid
Ethylene oxidic ester, ethylene/octene graft glycidyl methacrylate, styrene/ethylene/butadiene block copolymer
Object graft glycidyl methacrylate, ethylene-methyl acrylate-maleic anhydride terpolymer, ethylene-acrylic acid second
Ester-maleic anhydride terpolymer, ethylene/n-butyl acrylate-maleic anhydride terpolymer, maleic anhydride grafted ethene-
Vinyl acetate co-polymer, maleic anhydride grafted polyethylene, ethylene/octene grafted maleic anhydride, ethylene/butylene copolymerization
Object connects one or more in school maleic anhydride, ethylene-acrylic acid copolymer;Above-mentioned inorganic nano material is silica, carbon
One or more in sour calcium, montmorillonite, titanium dioxide, which is 15 nanometers -20 nanometers, specific surface area
For 150 ± l0m2/g.With silane coupling agent, titanate coupling agent, aluminate coupling agent, phosphate coupling agent etc. to inorganic nano
Material carries out surface modification, and one layer of organic matter, enhancing inorganic nano material and ethylene-acetic acid are covered on inorganic nano material surface
The compatibility and bonding force of vinyl ester copolymers material, and enhancing inorganic nano material is in ethylene-vinyl acetate co-polymer
Dispersibility in material;With fusing point be 60 DEG C -70 DEG C ethylene-vinyl acetate co-polymer material with it is surface-modified inorganic
Nano material melt blending is granulated, and the first master batch is made, since fusing point is 60 DEG C -70 DEG C of ethylene-vinyl acetate co-polymer
Viscosity lazy flow is good when material molten, inorganic nano material can be made to have in heating ethylene-vinyl acetate ester fiber preferable
Dispersibility, be conducive to follow-up spinning process.
And the advance structure design of carpet is pressed, embryo blanket is made after pile yams, weft yarn and warp thread are interweaved, at embryo blanket hot pressing
Reason makes clad fusing flowing, through cooling and solidifying, bonding pile yams and weft yarn and weft yarn and warp thread, then after subsequent processing
To above-mentioned carpet.
It in another preferred embodiment of the present invention, can be to embryo blanket hot pressing in order to further improve the performance of carpet
Processing is using progress hot-rolling pressurization after far infrared or hot-air preheating.As shown in Figure 1,1 table of heat roller tube can be entered in embryo blanket 3
In front, first far infrared or hot-air 4 is used to preheat embryo blanket, 1 surface of heat roller tube is provided with 1-3 pressure roller 2, heat roller tube
1 is dynamic for main turn, and pressure roller 2 is driven rotation, and embryo blanket 3 is slave drive, and 1 surface temperature of heat roller tube is 130 DEG C -160 DEG C, hot-rolling
Cylinder 1 generally uses 135 DEG C or 155 DEG C, further improves the bonding of carpet pile and composite weft after carpet hot pressing
The stiffness of degree and carpet.Embryo blanket 3 carries out hot pressurization by different pressure rollers 2 successively;Embryo blanket 3 is being pressed during hot pressing
Under the collective effect of roller 2 and heat roller tube 1, the seepage velocity and infiltration capacity after the second clad hot melt are further improved, is made
Second clad is more conducive to bonding pile yams and weft yarn and weft yarn and warp thread after melting resolidification, and bonding has been effectively ensured and has made
With.Embryo blanket 3 enters progress isothermal crystal in heat preservation zone after leaving hot-rolling, and the temperature of heat preservation zone is generally between 50 DEG C -90 DEG C.This
The hot pressing process of invention is carried out by the way of first preheating multiple tracks hot pressing again, and the uniformity of embryo blanket heating can be improved in preheating, and carries
The processing efficiency of high hot pressing process;Multiple tracks hot pressing can enhance the mobility of melt and the infiltration to pile after meldable fibre melts
Property, the extraction strength of pile is improved, while after preceding road pressure roller hot pressing, the melt after meldable fibre can be made to melt is centered on heart yarn
Flowing expansion, while under pressure close to the pile yams part for hanging pile filling, plane internal deformation is formed by melt
Flattening, and then increase the contact area of melt and pile;Simultaneously under pressure close to the pile yams part of extension pile filling
Air is extruded discharge between fiber, after carpet leaves pressure roller, since pile yarn fiber has certain resilience, and the suede in rebound
Negative pressure is formed inside gauze kerchief worn on a woman's head, and then enhances infiltration of the melt to pile yams, increases the extraction strength of pile yams after melt solidification.
And the composite yarn of above-mentioned extension pile filling is the composite yarn being machined into using coating machine or fancy twist yarn.Than
Such as with polypropylene fiber long filament or spun yarn for the first clad, to heat ethylene-vinyl acetate co-polymer fiber filament or short
Fine yarn is the second clad, and it is 10 centimetre -20 that when coating the first clad, the seal wire of coating machine or Novelty twisters, which hooks distance,
Centimetre, it is 1 centimetre -15 centimetres that when coating the second clad, the seal wire of coating machine or Novelty twisters, which hooks distance, and the second layer
Low 5 centimetres of the distance or more that seal wire hooks when the distance that seal wire hooks when cladding is coated than first layer;
First clad is wrapped in compact state on heart yarn, and the second clad is wrapped in the first clad in soft fluffy state
On surface, above-mentioned extension pile filling is made after carrying out first layer cladding and second layer cladding to the heart yarn for hanging pile filling.
The weft yarn composite yarn for hanging pile covers form using double-contracting, and the first clad selects the first cladding made of polypropylene fiber
Layer, fusing point, since its hot pressing temperature is between 130 DEG C -160 DEG C in hot pressing process, will not be melted at 160 DEG C or more
Melt, heart yarn surface is wound in fiber condition always, is firmly combined with heart yarn under the action of mechanical force;Hot melt is fine when heated
Dimension melting, because meldable fibre and the first clad are same based material, molecular radical having the same, therefore with fine compatibility
And cementability, the two can be carried out strong bonded by the winding of macromolecular chain, intermolecular force, hydrogen bond etc..Therefore the first packet
Coating plays the role of preferable bridge joint during weft yarn and pile heat bonding.
And distance is hooked using big seal wire when the first clad cladding, the first clad fiber can be made used in big rotation
Property power under the action of heart yarn is fettered close, enhance the rigidity of weft yarn, and then enhance the stiffness and conformality of carpet.Meanwhile
Infiltration of the melt to heart yarn, increases infiltration of the melt to pile heart yarn can reduce meldable fibre heating melting after being bound closely when
Amount improves the extraction strength of carpet pile.First clad filament fiber or spun yarn are wound in a manner of arranged in parallel
The regularity on heart yarn surface, arrangement is preferable, and regular arrangement can enhance between the first clad filament fiber or spun yarn and long
Silk or the interfibrous capillary effect of spun yarn, the Wicking effect of melt, increases when being conducive to enhance meldable fibre heating melting
Bonding force after adding melt to cure with the first clad.
Second clad, i.e. clad made of meldable fibre hook distance when cladding using small seal wire, and when cladding rotates
Inertia is relatively low, the second clad fiber can be made to be coated on the first cover surface in the form of more fluffy, due to the second clad
More fluffy, its internal/external heating is more uniform when hot pressing, can make fiber while melt, and reduces the melting delay of inner fiber, contracting
Short hot pressing time improves hot pressing process production efficiency;Simultaneously because the second clad is more fluffy, meldable fibre is along perpendicular to core
The direction of yarn is more sprawled, and is conducive to increase the contact area of melt and pile after meldable fibre melts, enhancing melt is to pile
Infiltration infiltration increases the extraction strength of pile after solidification.
Using composite yarn as weft yarn, tightens heart yarn enhancing in the first clad and the second clad cladding and hang pile filling rigidity
And while stiffness, enhance the stretch modulus of composite yarn, and then reduce the lower machine broadwise crimp after the weaving of embryo blanket, mitigates carpet
The working strength of weaving process designer, increases the carpet manufacture breadth of loom, mitigates that carpet weaving breadth is limited to be brought
Waste.
Certainly in preparation process, above-mentioned carpet can be woven Wilden carpet or woven Axminster carpet, certainly
Carpet made of other modes can also be applied.
Certainly, described above is only that presently preferred embodiments of the present invention is answered the present invention is not limited to enumerate above-described embodiment
When explanation, any technical person familiar with the field is all equivalent substitutes for being made, bright under the introduction of this specification
Aobvious variant, all falls within the essential scope of this specification, ought to be protected by the present invention.
Claims (7)
1. a kind of preparation method of woven carpet without gum operating process, which includes base fabric, pile yams, weft yarn and warp
Yarn, which is characterized in that the weft yarn includes hanging pile filling and not hanging pile filling, pile yams be Quality Pure Cotton Yarn Production, cotton fiber mixed yarn,
One kind in viscose fiber filament yarn, viscose rayon staple yarns yarn, viscose rayon staple blended yarn, the extension pile filling are
Composite yarn, composite yarn are made of heart yarn and clad, which is the normal weft for meeting carpet requirement, which includes the
One clad and the second clad, the second clad are meldable fibre long filament or spun yarn, and the first clad is that polypropylene fiber is long
Silk or spun yarn, the second clad account for the 20%-50% of composite yarn gross mass, and the first clad accounts for composite yarn gross mass
10%-15%, surplus are heart yarn;
Above-mentioned meldable fibre is hot melt ethylene-vinyl acetate co-polymer fiber, and it is total which heats ethylene-vinylacetate
Polymer fibre is composite fibre, which includes ethylene-vinyl acetate co-polymer material, bonding additives and inorganic nano
Material, wherein the mass ratio of ethylene-vinyl acetate co-polymer material, bonding additives and inorganic nano material is (85-
98.5):(1-10):(0.5-5);
Inorganic nano material is carried out using silane coupling agent, titanate coupling agent, aluminate coupling agent or phosphate coupling agent
Surface is modified, and the ethylene-vinyl acetate co-polymer material for being then 60 DEG C -70 DEG C with fusing point inorganic is received with surface-modified
Rice material is (60-70) in mass ratio:The ratio melt blending of (30-40) is granulated, and the first master batch is made;With fusing point be 60 DEG C-
70 DEG C of ethylene-vinyl acetate co-polymer material is (50-60) in mass ratio with bonding additives:The ratio of (40-50) melts
It is blended and is granulated, the second master batch is made, then press the second that the first master batch, the second master batch are 80 DEG C -110 DEG C with fusing point by design requirement
Above-mentioned hot melt ethylene-vinyl acetate co-polymer fiber is made in alkene-vinyl acetate co-polymer material molten spinning.
2. preparation method according to claim 1, which is characterized in that above-mentioned bonding additives are ethene-vinyl acetate-methyl
Glycidyl acrylate, ethylene-maleic acid-methacrylic dehydrated glyceride, ethylene-methyl acrylate-metering system
Acid glycidyl ester, ethylene-ethylacrylate-glycidyl methacrylate, ethylene/n-butyl acrylate-metering system
Acid glycidyl ester, polypropylene grafted glycidyl methacrylate, polyethylene to graft glycidyl methacrylate, second
Alkene/butylene copolymer graft glycidyl methacrylate, ethylene/octene grafted methacrylic acid glycidol
Ester, styrene/ethylene/butadiene block copolymer graft glycidyl methacrylate, ethylene-methyl acrylate-Malaysia
Acid anhydrides terpolymer, ethylene-ethyl acrylate-maleic anhydride copolymer, ethylene/n-butyl acrylate-maleic anhydride
Terpolymer, maleic anhydride grafted ethene-vinyl acetate co-polymer, maleic anhydride grafted polyethylene, ethylene/octene copolymerization
Object grafted maleic anhydride, ethylene/butylene copolymers connect one or more in school maleic anhydride, ethylene-acrylic acid copolymer;On
It is one or more, the inorganic nano material grain in silica, calcium carbonate, montmorillonite, titanium dioxide to state inorganic nano material
Diameter is 15 nanometers -20 nanometers, and specific surface area is 150 ± l0m2/g。
3. preparation method according to claim 1, which is characterized in that the advance structure design of carpet is pressed, by pile yams, weft yarn
Embryo blanket is made after interweaving with warp thread, so that the fusing flowing of the second clad is bonded pile yams through cooling and solidifying embryo blanket hot-pressing processing
With weft yarn and weft yarn and warp thread, then above-mentioned carpet is obtained after subsequent processing.
4. preparation method according to claim 3, which is characterized in that above-mentioned to use far infrared or heat to embryo blanket hot-pressing processing
Hot-rolling pressurization is carried out after air preheat again;Before embryo blanket enters heat roller tube surface, first use far infrared or hot-air to embryo blanket into
Row preheating is provided with 1-3 pressure roller on heat roller tube surface, and heat roller tube is dynamic for main turn, and pressure roller is driven rotation, and embryo blanket is driven
Transmission, hot-rolling drum surface temperature are 130 DEG C -160 DEG C, and embryo blanket carries out hot pressurization by different pressure rollers successively;Embryo blanket leaves hot-rolling
Enter afterwards and carries out isothermal crystal in heat preservation zone.
5. preparation method according to claim 1, which is characterized in that the composite yarn of above-mentioned extension pile filling is using cladding
The composite yarn that machine or fancy twist yarn are machined into.
6. preparation method according to claim 5, which is characterized in that coated for first with polypropylene fiber long filament or spun yarn
Layer, to heat ethylene-vinyl acetate co-polymer fiber filament or spun yarn for the second clad, when coating the first clad
It is 10 centimetres -20 centimetres that the seal wire of coating machine or Novelty twisters, which hooks distance, coating machine or fancy when coating the second clad
It is 1 centimetre -15 centimetres that the seal wire of twisting machine, which hooks distance, and seal wire when the distance that seal wire hooks when the second layer coats is coated than first layer
Low 5 centimetres of distance of hook or more;
First clad is wrapped in compact state on heart yarn, and the second clad is wrapped in the first cover surface in soft fluffy state
On, above-mentioned extension pile filling is made after carrying out first layer cladding and second layer cladding to the heart yarn for hanging pile filling.
7. preparation method according to claim 1, which is characterized in that above-mentioned carpet be woven Wilden carpet or woven Ah
Gram Munster carpet.