CN206204540U - A kind of low-melting fiber towel - Google Patents
A kind of low-melting fiber towel Download PDFInfo
- Publication number
- CN206204540U CN206204540U CN201621192191.7U CN201621192191U CN206204540U CN 206204540 U CN206204540 U CN 206204540U CN 201621192191 U CN201621192191 U CN 201621192191U CN 206204540 U CN206204540 U CN 206204540U
- Authority
- CN
- China
- Prior art keywords
- low
- fiber
- melting
- yarn
- cortex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of low-melting fiber towel, towel include ground weft, pass through and hair through weaving form, the ground weft or/and ground use low-melting fiber covering yarn through whole or interval, the cortex of low-melting fiber covering yarn is the composite fibre comprising low melting point fiber-forming polymer, sandwich layer is long filament or high grade cotton yarn, and the low melting point fiber-forming polymer is COPET or PE or HDPE or LDPE or LLDPE or PP.The utility model knits low-melting fiber covering yarn and makees warp thread or weft yarn due to ginseng, through high-temperature digestion low melting point fiber-forming polymer, commonly will be fixed through weft yarn, it is to avoid hair is through hair loss, hook silk plucking in machine washing and use.
Description
Technical field
The utility model is related to textile production technology field, and in particular to a kind of low-melting fiber towel.
Background technology
The towel that top grade hotel, club use at present is cleaned, and is typically all washed by force using large scale industry washing machine, by force
Wash operation towel damage comparison big, be particularly easy to hair loss occur, hook hair phenomenon, very influence is used and appearance, is high-grade
What place was feared.
Utility model content
The technical problems to be solved in the utility model is to provide a kind of low-melting fiber towel, and ginseng knits low-melting fiber cored
Yarn makees warp thread or weft yarn, through high-temperature digestion low melting point fiber-forming polymer, commonly will be fixed through weft yarn, it is to avoid hair in machine washing and use
Through hair loss, hook hair.
The utility model is achieved through the following technical solutions:
A kind of low-melting fiber towel, including ground weft, pass through and hair through weaving form, the ground weft or/and ground through whole
Or interval uses low-melting fiber covering yarn, the cortex of low-melting fiber covering yarn is compound comprising low melting point fiber-forming polymer
Fiber, sandwich layer be long filament or high grade cotton yarn, the low melting point fiber-forming polymer be COPET or PE or HDPE or LDPE or
LLDPE or PP.
The further improvement project of the utility model is that the cortex of the low-melting fiber covering yarn is core-sheath low melting point
Fiber, cortex and the sandwich layer of core-sheath low-melting fiber are fiber-forming polymers, and the melting temperature of its cortex is less than sandwich layer
Melting temperature.
The further improvement project of the utility model is, the cortex of the core-sheath low-melting fiber for OPET or PE or
HDPE or LDPE or LLDPE or PP, sandwich layer PET or PA or PP.
Modified poly ester(COPET), polyethylene(PE), high density polyethylene (HDPE)(HDPE), low density polyethylene (LDPE)(LDPE), line style
Bottom density polyethylene(LLDPE), polypropylene(PP)Etc. low melting point into a more conventional fiber-forming polymer polyester of high polymer melting temperature
(PET), polyamide(PA)It is low, during hot melt pre-setting, cortex fusing bonding hair warp, polypropylene(PP)Fusing point low PET higher than PE,
Therefore PP and PET arranges in pairs or groups, and can make cortex, is arranged in pairs or groups with PE and can make sandwich layer again.
Another further improvement project of the utility model is that the cortex of the low-melting fiber covering yarn is multiple with core-skin
Conjunction low-melting fiber is cortex, and cotton fiber is the covering yarn of sandwich layer, and the cortex of the core-sheath low-melting fiber is equal with sandwich layer
It is fiber-forming polymer, the melting temperature of the melting temperature less than sandwich layer of its cortex.
The utility model another further improvement project is that the cortex of the low-melting fiber covering yarn is with one-component
Low melting point fiber-forming polymer fiber is cortex, and cotton fiber is the covering yarn of sandwich layer.
The further improvement project of the utility model is that the sandwich layer long filament of the low-melting fiber covering yarn refers to terylene long
Silk or terylene low elastic interlaced yarn or chinlon filament or polyamide fibre low elastic interlaced yarn or PLA(PLA)Long filament or PLA
(PLA)Low elastic interlaced yarn or super imitative cotton modified dacron long filament or super imitative cotton modified dacron low elastic interlaced yarn;The core-spun yarn core
Layer high grade cotton yarn is pure cotton high-count yarns or polyester-cotton blend high grade cotton yarn or the super imitative cotton high count yarn of terylene.
The further improvement project of the utility model is, the low-melting fiber covering yarn 1.3~3.3dtex of fineness, length
35~51mm.
The processing method of above-mentioned low-melting fiber towel, including spinning, weaving and dyeing and finishing process, in first of dyeing and finishing process
Or hot melt pre-setting treatment is finally carried out together in dyeing and finishing process, setting temperature is higher than used low melting point fiber-forming polymer
5-25 DEG C of fusing point, shaping time 30-120s.Low melting point fiber-forming polymer is heated hair through being bonded together, and will be common through weft yarn
It is fixed, towel in machine washing and use not hair loss, hair is not hooked, while avoiding bonding portion from entirely knitting group all becomes very hard
, influence feel.
The utility model compared with prior art, with following obvious advantage:
The utility model knits low-melting fiber covering yarn and makees warp thread or weft yarn due to ginseng, through high-temperature digestion low melting point into fine height
Polymers, commonly will fix through weft yarn, it is to avoid hair is through hair loss, hook silk plucking in machine washing and use.
Brief description of the drawings
Fig. 1 is the low-melting fiber covering yarn end section schematic diagram of the utility model embodiment 1.
Fig. 2 is the utility model towel cross-sectional view.
Specific embodiment
Embodiment 1
As shown in Figure 1 and Figure 2, a kind of low-melting fiber towel described in the utility model, including ground weft 1, through 2 and hair
Formed through 3 weavings, all using low-melting fiber covering yarn, the cortex 11 of low-melting fiber covering yarn is core-skin to the ground weft 1
Composite low melting point fiber, sandwich layer 12 is polyester filament.Wherein the cortex 111 of core-sheath low-melting fiber is HDPE, sandwich layer 112
It is PET.Low-melting fiber covering yarn fineness 1.5 dtex, length 38mm(Fineness is in 1.3~3.3dtex, 35~51mm of length
The fineness length of spinning can be gone up).
Its processing method, successively including spinning, weaving and dyeing and finishing process, first started in dyeing and finishing process is heated
Pre-setting treatment, remaining dyeing and finishing treatment normal operating.Hot melt pre-setting temperature is higher than 5-25 DEG C of HDPE fusing points, shaping time 30-
120s。
Embodiment 2
Describedly through 2 all using low-melting fiber covering yarn, the cortex of low-melting fiber covering yarn is with core-sheath
Low-melting fiber is cortex, and cotton fiber is the covering yarn of sandwich layer, and sandwich layer is PLA low elastic interlaced yarns.Wherein core-sheath low melting point
The cortex of fiber is COPET, and sandwich layer is PA.Low-melting fiber covering yarn fineness 3dtex, length 45mm.Remaining is such as embodiment 1.
Its processing method, successively including spinning, weaving and dyeing and finishing process, dyeing and finishing process it is last carry out heating together it is pre-
Heat treatment, remaining dyeing and finishing treatment normal operating.Hot melt pre-setting temperature is higher than 5-25 DEG C of COPET fusing points, shaping time 30-
120s。
Embodiment 3
The interval of the ground weft 1 uses low-melting fiber covering yarn, and the cortex of the low-melting fiber covering yarn is with single group
Part low melting point fiber-forming polymer fiber PP is cortex, and cotton fiber is the covering yarn of sandwich layer, and sandwich layer is the super imitative cotton high count yarn of terylene, low
Melting-point fibers covering yarn fineness 2dtex, length 38mm.Remaining and processing method are as implemented 1.
Embodiment 4
The ground weft 1 and ground use low-melting fiber covering yarn through 2 intervals, and the cortex of low-melting fiber covering yarn is core-skin
Composite low melting point fiber, sandwich layer is pure cotton high-count yarns.Wherein the cortex of core-sheath low-melting fiber is PE, and sandwich layer is PA.Its
Remaining and processing method is as implemented 1.
Each 100 of the low-melting fiber towel that example 1 to 4 is produced, being put into large scale industry washing machine carries out by force that to wash 1 small
When, there is hair loss, hook hair, plucking phenomenon in none.
Claims (7)
1. a kind of low-melting fiber towel, including ground weft(1), pass through(2)Passed through with hair(3)Weaving is formed, it is characterised in that:It is described
Ground weft(1)Or/and ground warp(2)Whole or interval uses low-melting fiber covering yarn, the cortex of low-melting fiber covering yarn(11)
It is the composite fibre comprising low melting point fiber-forming polymer, sandwich layer(12)It is long filament or high grade cotton yarn, the low melting point fiber-forming polymer
It is COPET or PE or HDPE or LDPE or LLDPE or PP.
2. a kind of low-melting fiber towel according to claim 1, it is characterised in that:The low-melting fiber covering yarn
Cortex is core-sheath low-melting fiber, and cortex and the sandwich layer of core-sheath low-melting fiber are fiber-forming polymer, its cortex
Melting temperature less than sandwich layer melting temperature.
3. a kind of low-melting fiber towel according to claim 2, it is characterised in that:The core-sheath low-melting fiber
Cortex be OPET or PE or HDPE or LDPE or LLDPE or PP, sandwich layer PET or PA or PP.
4. a kind of low-melting fiber towel according to claim 1, it is characterised in that:The low-melting fiber covering yarn
Cortex is that, with core-sheath low-melting fiber as cortex, cotton fiber is the covering yarn of sandwich layer, the core-sheath low-melting fiber
Cortex and sandwich layer be fiber-forming polymer, the melting temperature of the melting temperature less than sandwich layer of its cortex.
5. a kind of low-melting fiber towel according to claim 1, it is characterised in that:The low-melting fiber covering yarn
Cortex is that, with one-component low melting point fiber-forming polymer fiber as cortex, cotton fiber is the covering yarn of sandwich layer.
6. a kind of low-melting fiber towel according to claim 1, it is characterised in that:The low-melting fiber covering yarn
Sandwich layer long filament refer to polyester filament or terylene low elastic interlaced yarn or chinlon filament or polyamide fibre low elastic interlaced yarn or PLA long filaments,
Or PLA low elastic interlaced yarns or super imitative cotton modified dacron long filament or super imitative cotton modified dacron low elastic interlaced yarn;The core-spun yarn core
Layer high grade cotton yarn is pure cotton high-count yarns or polyester-cotton blend high grade cotton yarn or the super imitative cotton high count yarn of terylene.
7. a kind of low-melting fiber towel according to claim 1, it is characterised in that:The low-melting fiber covering yarn is thin
Degree 1.3~3.3dtex, 35~51mm of length.