CN108395761A - A kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing - Google Patents
A kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing Download PDFInfo
- Publication number
- CN108395761A CN108395761A CN201810284509.1A CN201810284509A CN108395761A CN 108395761 A CN108395761 A CN 108395761A CN 201810284509 A CN201810284509 A CN 201810284509A CN 108395761 A CN108395761 A CN 108395761A
- Authority
- CN
- China
- Prior art keywords
- white
- acquisition system
- dimensional imaging
- layer manufacturing
- painting layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing, includes the following steps：White gouache color and liquid detergent are poured into vessel；Uniform stirring for the first time is carried out to the inside of vessel；It will be in alcohol dispenser ware；Uniform second is carried out to the inside of vessel to stir, and obtains white spray；White spray loading flusher is sprayed.The painting layer manufacturing method thereof enables to spray-on coating thin, and without particle, strong adhesive force is not easy to be left out and is very easy to cleaning, and smell is small.
Description
Technical field
The present invention relates to the technical fields of stereo shaping, more particularly to one kind to be examined for three-dimensional imaging acquisition system and infiltration
The painting layer manufacturing method thereof of survey.
Background technology
Three-dimensional imaging acquisition system is in order to acquiring minute surface at present（It is high reflective）And extinction（Black）Body surface number
According to it is usually to use contrast enhancement agents or dye check agent that body surface, which is required for one layer of white coating of spray, coating,.
Contrast enhancement agents are high with dye check agent price；Spraying out the coating come has fine-particulate shape, the number of acquisition
According to granular effect can be collected, original effect is just not achieved, having the coating layer thickness that graininess sprays thicker, to production
Product size fluctuation is too big, and also influencing the too small product in gap can not permeate, and accomplish that overall permeation detects；Product has prodigious pungent
Smell is not easy to air environment protection and is not easy to human body contact use, especially human nose contact pair for a long time for a long time
Nose has prodigious injury.
Wherein contrast enhancement agents adhesive force is too strong, can not be cleaned up to the coating of spraying, even if using dedicated cleaning
Agent can not also reach the effect before not spraying；Dye check agent adhesive force is too weak, as long as at a touch can be the coating of spraying
It is left out, omitted position can not just collect data, and being easy to be left out to also result in acquires pasted index point（Anchor point）It is de-
Leakage, can not thus be acquired again.
Therefore, it is unsatisfactory using contrast enhancement agents or dye check agent.
Invention content
It is an object of the present invention to：It provides a kind of for the making of the coating of three-dimensional imaging acquisition system and Liquid penetrant testing
Method, which enables to spray-on coating thin, and without particle, strong adhesive force is not easy to be left out and be very easy to clear
It washes, smell is small.
For this purpose, the present invention uses following technical scheme：One kind being used for three-dimensional imaging acquisition system and Liquid penetrant testing
Painting layer manufacturing method thereof, include the following steps：
White gouache color and liquid detergent are poured into vessel；
Uniform stirring for the first time is carried out to the inside of vessel；
It will be in alcohol dispenser ware；
Uniform second is carried out to the inside of vessel to stir, and obtains white spray；
White spray loading flusher is sprayed.
As a kind of perferred technical scheme, the time of the first time stirring is 3 minutes.
As a kind of perferred technical scheme, the time of second of stirring is 5 minutes.
As a kind of perferred technical scheme, the quality hundred of the white gouache color, the liquid detergent and the alcohol
Divide than being respectively 62.52%, 21.21% and 16.27%.
As a kind of perferred technical scheme, described to spray white spray loading flusher, specially：
White spray is packed into flusher；
Flusher is arranged in distance by spray object preset distance；
Start flusher to be sprayed.
As a kind of perferred technical scheme, the preset distance is 15-30cm.
As a kind of perferred technical scheme, the startup flusher is sprayed, and further includes later：
It is stood by spray object in setting time, waits the dry tack free for being sprayed object and infiltration.
As a kind of perferred technical scheme, the setting time is 5-10 minutes.
As a kind of perferred technical scheme, the ingredient of the white gouache color includes that colorant, glue consolidate agent, are soaked
Agent, preservative and filler.
As a kind of perferred technical scheme, the filler is white lead, titanium white, white magnetic soil or zinc white.
Beneficial effects of the present invention are：A kind of coating making side for three-dimensional imaging acquisition system and Liquid penetrant testing is provided
Method, which enables to spray-on coating thin, and without particle, strong adhesive force is not easy cleaning of being left out and be very easy to,
Smell is small.
Description of the drawings
Below according to drawings and examples, invention is further described in detail.
Fig. 1 is a kind of stream for three-dimensional imaging acquisition system and the painting layer manufacturing method thereof of Liquid penetrant testing described in embodiment
Cheng Tu.
Specific implementation mode
Technical solution to further illustrate the present invention below with reference to the accompanying drawings and specific embodiments.
As shown in Figure 1, in this present embodiment, a kind of coating making side for three-dimensional imaging acquisition system and Liquid penetrant testing
Method includes the following steps：
White gouache color and liquid detergent are poured into vessel；
Uniform stirring for the first time is carried out to the inside of vessel；
It will be in alcohol dispenser ware；
Uniform second is carried out to the inside of vessel to stir, and obtains white spray；
White spray loading flusher is sprayed.
White gouache color is a kind of water compatible pigment.Main ingredient have toner, bonding agent, glycerine, preservative, rock sugar,
Honey, lime acid, bile, starch etc..Its color variety is abundant, there is certain covering power.Pigment applicability is wide, cheap, table
Existing power is strong, and is easy to hold and use.But have when in use it is dry very fast, be not easy to color linking and color it is dry after it is variable
The shortcomings of color.
It is mainly the very fine and smooth of white gouache color that white gouache color is selected in this method, is sprayed onto the object for needing to acquire
Body surface face is very smooth, not the effect of particle；Due to there is no particle, the effect of ejection very thin yet；White water-borne pigment exists
Under dry situation, it is not easy to be left out；Pigment smell is very small, will not cause the injury of environment and human body；It is very easy to cleaning.
It is mainly the viscosity for increasing white spray that liquid detergent is selected in this method, reduces the mobility of white spray, increases
The adhesive force on strong surface, also for preferably cleaning the object sprayed.
Alcohol is selected to primarily serve an easily dry, reconciliation and diluted effect in this method.
In this present embodiment, the time of the first time stirring is 3 minutes.
In this present embodiment, the time of second of stirring is 5 minutes.
In this present embodiment, the white gouache color, the liquid detergent and the alcohol mass percent be respectively
62.52%, 21.21% and 16.27%.
In this present embodiment, described to spray white spray loading flusher, specially：
White spray is packed into flusher；
Flusher is arranged in distance by spray object preset distance；
Start flusher to be sprayed.
In this present embodiment, the preset distance is 15cm.In other embodiment, the preset distance can also be 17
Cm, 20 cm or 30 cm.
In this present embodiment, the startup flusher is sprayed, and further includes later：
It is stood by spray object in setting time, waits the dry tack free for being sprayed object and infiltration.
In this present embodiment, the setting time is 5 minutes.In other embodiment, the setting time can also be 7
Minute, 8 minutes or 10 minutes.
In this present embodiment, the ingredient of the white gouache color include colorant, glue consolidate agent, wetting agent, preservative and
Filler.
Colorant, using ball mill barreling at superfine pigment powder.
Glue consolidates agent, dextrin, natural gum etc..
Wetting agent, rock sugar, glycerine etc..
Preservative, carbolic acid or formalin.
Filler, mainly various white pigments or wheaten starch etc..
In this present embodiment, the filler is white lead.In other embodiment, the filler can also be titanium
In vain, white magnetic soil or zinc white.
White lead is lily artificial mineral matter pigment.Other pigment other than pure white lead and cadmium yellow mix all
Be it is very fast light with it is firm.
Titanium white is a kind of magnificent sterling white, belongs to artificial mineral matter pigment.No matter simple titanium white or with other pigment
Mixing is all fast light and lasting.
White magnetic soil, i.e. barium white, are pure barium sulfate, are people's dressing substance pigment, have special light resistance and outside of contending with
The robustness of influence, being mixed with other pigment has lasting and firm characteristic.
Zinc white is a kind of slightly colder white, fast light and lasting artificial mineral matter pigment.Its critical defect is color
Layer fragility lacks flexibility, and is easily cracked and is scattered；And easily the moisture absorption, appearance are hot；Covering power is also weaker.After the regular hour, especially
Be by solar heat and it is moist influenced, will significantly lose covering power, color is not also pure, mainly as manufacture quality and
The additives of the lower gouache color of grade.
In this present embodiment, a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing：Specific step
Suddenly it is：
1, the mass percent for matching white gouache color, liquid detergent and alcohol is respectively 62.52%, 21.21% and 16.27%；
2, white gouache color and liquid detergent are poured into vessel；
3, uniform stirring in 3 minutes is carried out to the inside of vessel；
It 4, will be in alcohol dispenser ware；
5, uniform stirring in 5 minutes is carried out to the inside of vessel, obtains white spray；
6, white spray is packed into flusher；
7, flusher is arranged in distance by the position of spray object 15cm；
8, start flusher to be sprayed；
9, the dry tack free for being waited being sprayed object by spray object and infiltration are stood in 5 minutes.
It is to be understood that above-mentioned specific implementation mode is only that presently preferred embodiments of the present invention and institute's application technology are former
Reason, in technical scope disclosed in this invention, variation that any one skilled in the art is readily apparent that or
It replaces, should all cover within the scope of the present invention.
Claims (10)
1. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing, which is characterized in that including following step
Suddenly：
White gouache color and liquid detergent are poured into vessel；
Uniform stirring for the first time is carried out to the inside of vessel；
It will be in alcohol dispenser ware；
Uniform second is carried out to the inside of vessel to stir, and obtains white spray；
White spray loading flusher is sprayed.
2. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 1,
It is characterized in that, the time of the first time stirring is 3 minutes.
3. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 1,
It is characterized in that, the time of second of stirring is 5 minutes.
4. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 1,
It is characterized in that, the mass percent of the white gouache color, the liquid detergent and the alcohol is respectively 62.52%, 21.21%
With 16.27%.
5. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 1,
It is characterized in that, it is described to spray white spray loading flusher, specially：
White spray is packed into flusher；
Flusher is arranged in distance by spray object preset distance；
Start flusher to be sprayed.
6. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 5,
It is characterized in that, the preset distance is 15-30cm.
7. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 5,
It is characterized in that, the startup flusher is sprayed, and further includes later：
It is stood by spray object in setting time, waits the dry tack free for being sprayed object and infiltration.
8. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 7,
It is characterized in that, the setting time is 5-10 minutes.
9. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 1,
It is characterized in that, the ingredient of the white gouache color includes that colorant, glue consolidate agent, wetting agent, preservative and filler.
10. a kind of painting layer manufacturing method thereof for three-dimensional imaging acquisition system and Liquid penetrant testing according to claim 9,
It is characterized in that, the filler is white lead, titanium white, white magnetic soil or zinc white.