CN108394057A - A kind of preparation method of wood moulding floor tile for gardens pavement - Google Patents
A kind of preparation method of wood moulding floor tile for gardens pavement Download PDFInfo
- Publication number
- CN108394057A CN108394057A CN201810067285.9A CN201810067285A CN108394057A CN 108394057 A CN108394057 A CN 108394057A CN 201810067285 A CN201810067285 A CN 201810067285A CN 108394057 A CN108394057 A CN 108394057A
- Authority
- CN
- China
- Prior art keywords
- brick body
- floor tile
- preparation
- wood moulding
- auxiliary
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of preparation method of wood moulding floor tile for gardens pavement includes the preparation of the preparation of wood moulding floor tile base-material, the preparation and auxiliary brick body of main brick body, the specific steps are:The recipe ingredient of wood moulding floor tile is taken to melt to obtain liquid wood moulding base-material;By partially liq wood moulding base-material compression moulding winner brick body, main brick body is smeared by wire drawing process, beeswax, and the main brick body is cuboid, and the lower part of the main brick body both sides is provided with the rectangular recess for the insertion of auxiliary brick body;It takes partially liq wood moulding base-material to be put into molding die again and auxiliary brick body is made, auxiliary brick body forms uniform beeswax layer by the beeswax smearing processing of different modes twice, and auxiliary brick body includes rectangle brick body and the drainage trough that is arranged above rectangle brick body.The present invention realizes creative production in the floor tile production method of pavement; change the independently installed mode of traditional floor tile; increase the glossiness and protectiveness of floor tile using the smearing of beeswax, the processing of wire drawing helps to improve the antiskid function of floor tile, extends the service life of floor tile.
Description
Technical field
The invention belongs to technical field of floor, the more particularly to a kind of preparation side of wood moulding floor tile for gardens pavement
Method.
Background technology
Currently, in finishing field, outdoor either flooring pavement material is generally various wood floors or compound
The feel on floor, wood floors is more comfortable, but in use since dilatancy, cracking etc. often occurs in its physical property
Various problems, and Wood-plastic floor refer to using polyethylene, polypropylene and polyvinyl chloride etc., instead of common resin adhesive, with
Be mixed into new wood materials more than the useless plant fiber such as the wood powder of 35%-70% or more, rice husk, stalk, then through extruding, molding,
The plank or proximate matter that the plastic processings such as injection molding are produced have the performance and feature of timber and plastics concurrently, have epipodium
Guarantor, fungus-proof antisepsis, it is indeformable do not crack, the advantages that good mechanical property, processing performance are good, at low cost, timber and plastics can be substituted
Novel environment friendly hitech materials, mainly apply the industries such as building materials, furniture, logistics packaging.
With the development of the times, the demand of some special floors is also increasing, such as gardens pavement floor tile requires tool
There are preferable skid resistance, wearability etc., prior art wood moulding floor tile type is various, and the selectable leeway of people is very big, however mesh
Preceding existing pavement floor tile is generally independent brick body, and after screed is levelling, floor tile is laid with one by one, however
It being corroded for a long time by rainwater and pedestrian tramples rear screed and easily loosens for a long time, the binding force in turn resulting in floor tile and ground weakens,
Loose phenomenon is generated, rainwater often accumulates in the gap of adjacent two pieces of floor tiles at this time, the floor tile of loosening, ground once pedestrian steps on
The rainwater and sludge accumulated below brick will splash and drench, pollute on clothes suddenly, and this phenomenon has become gardens pedestrian
The disadvantage of road floor tile, in addition to this, the cost of the maintenance consumption in later stage are very high.
Invention content
The object of the present invention is to provide a kind of preparation method of the wood moulding floor tile for gardens pavement, solved with this
State the deficiency of technical problem.
In order to achieve the goal above, the technical solution adopted in the present invention is:A kind of wood moulding for gardens pavement
The preparation method of brick includes the preparation of the preparation of wood moulding floor tile base-material, the preparation and auxiliary brick body of main brick body, includes the following steps:
Step 1: the preparation of wood moulding floor tile base-material:The recipe ingredient for taking wood moulding floor tile is put into high-speed mixer uniformly
Mixing, mixed material obtained are melted in the case where temperature is 100-150 DEG C, pressure is 13-17MPa, obtain liquid wood moulding base-material, standby
With;
Step 2: the preparation of main brick body:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, pressed sizing
22-30min takes out after cooling and shaping, winner's brick body, and the main brick body is rectangle brick body, and the lower part of the main brick body both sides is set
Be equipped with height be main brick body height 1/5th to a quarter rectangular recess;
B, first the main brick body in step a is put into wire drawing machine, the carry out table in the case where temperature is 280-320 DEG C, power is 26-30Hz
Face depth is the wire drawing process of 0.08-0.12cm, then will immerse and is equipped with after the main brick body progress sanding and polishing after wire drawing process
In the vacuum tank of beeswax, heat-insulation pressure keeping impregnates 2-3h, will be formed in the main brick body merging vacuum dryer of beeswax layer, in temperature
Baking 5-8h is carried out under conditions of being 0.1-0.008MPa for 150-180 DEG C, pressure, is taken out after cooling and is carried out at stock removal polishing again
Reason, it is spare;
Step 3: the preparation of auxiliary brick body:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, pressed sizing
30-40min is demoulded after cooling and shaping, and auxiliary brick body is obtained after sanding and polishing processing, and the auxiliary brick body includes that rectangle brick body and setting exist
The both ends of drainage trough above rectangle brick body, the rectangle brick body are corresponding with the rectangular recess of main brick body and can be embedded in rectangle recessed
In slot, the drainage trough is along including vertical section and linkage section, and the vertical section is connected with the linkage section, and vertical section is even
The lower section for connecing section, after auxiliary brick body both ends are embedded in main brick body, drainage trough start to the top of main brick body along main brick body madial wall and
Extend close to the direction of madial wall, it is spare;
B, on the inner wall for the molding die for being applied to auxiliary brick body after heating solid beeswax, auxiliary brick body is put into after beeswax cooling
In molding die, by molding die together with being fired in auxiliary brick body merging Muffle furnace, auxiliary brick body is taken out after cooling, and by auxiliary brick body table
The extra beeswax layer in face is rejected, and is smeared processing mode according still further to the beeswax of main brick body in step 2 and is carried out benefit wax, after sanding and polishing
It puts it into and conserves 1-2d in curing box.
It advanced optimizes, 65-75 DEG C is increased to 8-10 DEG C of heating rate when heat-insulation pressure keeping impregnates in the step 1,
And the range of control pressure is in 0.6-0.8MPa.
It advanced optimizes, the wire drawing process in the step 2 is straight line wire drawing process.
It advanced optimizes, the beeswax layer thickness of main brick body is 0.23-0.33mm in the step 2.
It advanced optimizes, the rectangle brick body in the step 2 is hollow brick body.
It advanced optimizes, offers rectangle water inlet in the step 2 at the top of rectangle brick body, bottom is provided with row
The mouth of a river.
It advanced optimizes, the final beeswax layer thickness of auxiliary brick body is 0.28-0.38mm in the step 3.
It advanced optimizes, first sprays releasing agent in the step 3 before the demoulding of auxiliary brick body into molding die, then will be at
Pattern tool, which is placed on bobbing machine, vibrates 1-2min.
Advanced optimize, in the step 3 Muffle furnace firing temperature be 150-180 DEG C, heating rate be 10-12 DEG C/
Min keeps the temperature 10-12h.
In terms of beneficial effects of the present invention are broadly divided into following four:
One, wire drawing process carries out straight line wire drawing on the surface of main brick body, not only facilitates the non-skid property for improving floor tile,
It is alternatively arranged as the diversion trench of ponding, helps that ponding is guided to be discharged in time;
Two, the structure of auxiliary brick body is more complex, be easy to cause when smearing beeswax dead angle smear it is uneven, using means of different twice
Smearing mode, uniform beeswax layer can be formed on the surface of auxiliary brick body;
Three, the both ends of auxiliary brick body are embedded in main brick body, and the two checks and balance, and is not easy to loosen, and effectively improves the stability of floor tile, main
The wire drawing of brick body upper surface setting has certain depth, effectively ponding can be guided to flow to;
Four, auxiliary brick body includes rectangle brick body and drainage trough, and the vertical section of drainage trough connects to form staircase-type with vertical section, guiding master
The ponding of brick body upper surface flows to auxiliary brick body, effectively reduces the ponding of tile surface, alleviates the pressure of ponding discharge with this;
In conclusion the present invention's is simple for process, operability is strong, and creativeness is realized in the floor tile production method of pavement
Production is changed the independently installed mode of traditional floor tile, is increased the glossiness and protectiveness of floor tile using the smearing of beeswax, wire drawing
Processing helps to improve the antiskid function of floor tile, extends the service life of floor tile.
Description of the drawings
Fig. 1 is the structural schematic diagram of pavement floor tile;
Fig. 2 is the structural schematic diagram of main brick body;
The structural schematic diagram of brick body supplemented by Fig. 3;
It is marked in figure:1, main brick body, 2, auxiliary brick body, 3, rectangular recess, 4, rectangle brick body, 5, drainage trough, 501, vertical section,
502, linkage section, 6, water inlet, 7, discharge outlet.
Specific implementation mode
Technological means, creation characteristic, reached purpose and advantageous effect to make the present invention realize are easy to understand, under
Face combines specific implementation mode, and the present invention is further explained.
A kind of preparation method of wood moulding floor tile for gardens pavement includes preparation, the main brick body of wood moulding floor tile base-material
Preparation and auxiliary brick body preparation, include the following steps:
Step 1: the preparation of wood moulding floor tile base-material:The recipe ingredient for taking wood moulding floor tile is put into high-speed mixer uniformly
Mixing, mixed material obtained are melted in the case where temperature is 100-150 DEG C, pressure is 13-17MPa, obtain liquid wood moulding base-material, standby
With;
Step 2: the preparation of main brick body 1:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 22-30min takes out after cooling and shaping, winner's brick body 1, and the main brick body 1 is cuboid, the lower part of 1 both sides of main brick body
Be provided with height be 1 height of main brick body 1/5th to a quarter rectangular recess 3;
B, first the main brick body 1 in step a is put into wire drawing machine, is carried out in the case where temperature is 280-320 DEG C, power is 26-30Hz
Case depth is the wire drawing process of 0.08-0.12cm, immerses dress after the main brick body 1 after wire drawing process is then carried out sanding and polishing
Have in the vacuum tank of beeswax, heat-insulation pressure keeping impregnates 2-3h, will be formed in the main brick body merging vacuum dryer of beeswax layer, in temperature
Baking 5-8h is carried out under conditions of degree is 150-180 DEG C, pressure is 0.1-0.008MPa, is taken out after cooling and is carried out stock removal polishing again
Processing, it is spare;
Step 3: the preparation of auxiliary brick body 2:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 30-40min is demoulded after cooling and shaping, and auxiliary brick body 2 is obtained after sanding and polishing processing, and the auxiliary brick body 2 includes 4 He of rectangle brick body
The both ends of the drainage trough 5 being arranged above rectangle brick body 4, the rectangle brick body 4 are corresponding with the rectangular recess 3 of main brick body 1 simultaneously
It can be embedded in rectangular recess 3, the drainage trough 5 includes vertical section 501 and linkage section 502, the vertical section 501 and the connection
Section 502 is connected, and vertical section 501 is in the lower section of linkage section 502, after 2 both ends of auxiliary brick body are embedded in main brick body 1, drainage trough 5
One end extends along 1 madial wall of main brick body to the top-direction of main brick body 1;
B, on the inner wall for the molding die for being applied to auxiliary brick body 2 after heating solid beeswax, auxiliary brick body 2 is put after beeswax cooling
Enter in molding die, molding die is placed in together with auxiliary brick body 2 in Muffle furnace and is fired, take out auxiliary brick body 2 after cooling, and by auxiliary brick
The beeswax layer of 2 excess surface of body is rejected, and is carried out benefit wax according still further to the beeswax smearing processing mode of main brick body 1 in step 2, is polished
It is put it into after polishing and conserves 1-2d in curing box.
It advanced optimizes, 65-75 DEG C is increased to 8-10 DEG C of heating rate when heat-insulation pressure keeping impregnates in the step 1,
And the range of control pressure is in 0.6-0.8MPa.
It advanced optimizes, the wire drawing process in the step 2 is straight line wire drawing process.
It advanced optimizes, the beeswax layer thickness of main brick body 1 is 0.23-0.33mm in the step 2.
It advanced optimizes, the final beeswax layer thickness of auxiliary brick body 2 is 0.28-0.38mm in the step 3.
It advanced optimizes, first sprays releasing agent into molding die before the demoulding of auxiliary brick body 2 in the step 3, then will be at
Pattern tool, which is placed on bobbing machine, vibrates 1-2min.
Advanced optimize, in the step 3 Muffle furnace firing temperature be 150-180 DEG C, heating rate be 10-12 DEG C/
Min keeps the temperature 10-12h.
Embodiment 1:
A kind of preparation method of wood moulding floor tile for gardens pavement includes the system of the preparation of wood moulding floor tile base-material, main brick body
The preparation of standby and auxiliary brick body, includes the following steps:
Step 1: the preparation of wood moulding floor tile base-material:The recipe ingredient for taking wood moulding floor tile available on the market is put into high speed
It is uniformly mixed in mixing machine, mixed material obtained is melted in the case where temperature is 100 DEG C, pressure is 13MPa, obtains liquid wood moulding base
Material, it is spare;
Step 2: the preparation of main brick body 1:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 22min takes out after cooling and shaping, winner's brick body 1, and the main brick body 1 is cuboid, and the lower part of 1 both sides of main brick body is set
Be equipped with height be 1 height of main brick body 1/5th to a quarter rectangular recess 3;
B, first the main brick body 1 in step a is put into wire drawing machine, case depth is carried out in the case where temperature is 280 DEG C, power is 26Hz
For the straight line wire drawing process of 0.08cm, immersed equipped with honey after the main brick body 1 after straight line wire drawing process is then carried out sanding and polishing
In the vacuum tank of wax, it is 0.6MPa, is increased to heat-insulation pressure keeping under conditions of temperature is 65 DEG C with 8 DEG C of heating rate in pressure
2h is impregnated, the main brick body 1 that thickness is 0.23mm beeswax layers will be formed and be placed in vacuum dryer, temperature is 150 DEG C, pressure is
Baking 5h is carried out under conditions of 0.1MPa, is taken out after cooling and is carried out stock removal polishing processing again, it is spare;
Step 3: the preparation of auxiliary brick body 2:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 30min after cooling and shaping, first sprays releasing agent into molding die, then molding die is placed on bobbing machine and vibrates 1min
It is demoulded, auxiliary brick body 2 is obtained after sanding and polishing processing, the auxiliary brick body 2 includes rectangle brick body 4 and is arranged above rectangle brick body
Drainage trough 5, the rectangle brick body 4 is hollow brick body, and the top of rectangle brick body 4 offers rectangle water inlet 6, bottom setting
There is discharge outlet 7, the ponding by drawing the guiding of the chute 5 enters rectangular tiles intracoelomic cavity by water inlet 6, and in time from discharge outlet 7
Discharge, the both ends of rectangle brick body 4 are corresponding with the rectangular recess 3 of main brick body 1 and can be embedded in rectangular recess 3, and drainage trough 5 includes
Vertical section 501 and linkage section 502, the vertical section 501 are connected with the linkage section 502, and vertical section 501 is in linkage section
502 lower section, after 2 both ends of auxiliary brick body are embedded in main brick body 1, one end of drainage trough 5 is connect with water inlet 7, and the other end is along main brick
1 madial wall of body extends to the top-direction of main brick body 1;
B, it is applied on the inner wall of 2 mold of auxiliary brick body after heating solid beeswax, auxiliary brick body 2 is put into auxiliary brick after beeswax cooling
In mould, by mold together with auxiliary brick body 2 be placed in Muffle furnace in fire, firing temperature be 150 DEG C, heating rate be 10 DEG C/
Min keeps the temperature 10h, auxiliary brick body 2 is taken out after cooling, and the beeswax layer of 2 excess surface of auxiliary brick body is rejected, according still further in step 2
The beeswax of main brick body 1 smears processing mode and carries out benefit wax, is put it into after sanding and polishing and conserves 1d in curing box.
Embodiment 2
A kind of preparation method of wood moulding floor tile for gardens pavement includes the system of the preparation of wood moulding floor tile base-material, main brick body
The preparation of standby and auxiliary brick body, includes the following steps:
Step 1: the preparation of wood moulding floor tile base-material:The recipe ingredient for taking wood moulding floor tile available on the market is put into high speed
It is uniformly mixed in mixing machine, mixed material obtained is melted in the case where temperature is 125 DEG C, pressure is 15MPa, obtains liquid wood moulding base
Material, it is spare;
Step 2: the preparation of main brick body 1:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 26min takes out after cooling and shaping, winner's brick body 1, and the main brick body 1 is cuboid, and the lower part of 1 both sides of main brick body is set
Be equipped with height be 1 height of main brick body 1/5th to a quarter rectangular recess 3;
B, first the main brick body 1 in step a is put into wire drawing machine, case depth is carried out in the case where temperature is 300 DEG C, power is 28Hz
For the straight line wire drawing process of 0.1cm, immersed equipped with beeswax after the main brick body 1 after straight line wire drawing process is then carried out sanding and polishing
Vacuum tank in, be 0.7MPa, heat-insulation pressure keeping is increased under conditions of temperature is 70 DEG C with 9 DEG C of heating rate soaks in pressure
2.5h is steeped, the main brick body 1 that thickness is 0.28mm beeswax layers will be formed and be placed in vacuum dryer, temperature is 165 DEG C, pressure is
Baking 6.5h is carried out under conditions of 0.054MPa, is taken out after cooling and is carried out stock removal polishing processing again, it is spare;
Step 3: the preparation of auxiliary brick body 2:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 35min after cooling and shaping, first sprays releasing agent into molding die, then molding die is placed on bobbing machine and is vibrated
1.5min is demoulded, and auxiliary brick body 2 is obtained after sanding and polishing processing, and the auxiliary brick body 2 includes rectangle brick body 4 and is arranged in rectangular tiles
Drainage trough 5 above body, the rectangle brick body 4 are hollow brick body, and the top of rectangle brick body 4 offers rectangle water inlet 6, bottom
Portion is provided with discharge outlet 7, and the ponding by drawing the guiding of the chute 5 enters rectangular tiles intracoelomic cavity by water inlet 6, and in time from row
The mouth of a river 7 is discharged, and the both ends of rectangle brick body 4 are corresponding with the rectangular recess 3 of main brick body 1 and can be embedded in rectangular recess 3, drainage trough
5 include vertical section 501 and linkage section 502, and the vertical section 501 is connected with the linkage section 502, and vertical section 501 is even
The lower section for connecing section 502, after 2 both ends of auxiliary brick body are embedded in main brick body 1, one end of drainage trough 5 is connect with water inlet 7, other end edge
1 madial wall of main brick body extends to the top-direction of main brick body 1;
B, it is applied on the inner wall of 2 mold of auxiliary brick body after heating solid beeswax, auxiliary brick body 2 is put into auxiliary brick after beeswax cooling
In mould, by mold together with auxiliary brick body 2 be placed in Muffle furnace in fire, firing temperature be 165 DEG C, heating rate be 11 DEG C/
Min keeps the temperature 11h, auxiliary brick body 2 is taken out after cooling, and the beeswax layer of 2 excess surface of auxiliary brick body is rejected, according still further in step 2
The beeswax of main brick body 1 smears processing mode and carries out benefit wax, is put it into after sanding and polishing and conserves 1.5d in curing box.
Embodiment 3
A kind of preparation method of wood moulding floor tile for gardens pavement includes the system of the preparation of wood moulding floor tile base-material, main brick body
The preparation of standby and auxiliary brick body, includes the following steps:
Step 1: the preparation of wood moulding floor tile base-material:The recipe ingredient for taking wood moulding floor tile available on the market is put into high speed
It is uniformly mixed in mixing machine, mixed material obtained is melted in the case where temperature is 150 DEG C, pressure is 17MPa, obtains liquid wood moulding base
Material, it is spare;
Step 2: the preparation of main brick body 1:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 30min takes out after cooling and shaping, winner's brick body 1, and the main brick body 1 is cuboid, and the lower part of 1 both sides of main brick body is set
Be equipped with height be 1 height of main brick body 1/5th to a quarter rectangular recess 3;
B, first the main brick body 1 in step a is put into wire drawing machine, case depth is carried out in the case where temperature is 320 DEG C, power is 30Hz
For the straight line wire drawing process of 0.12cm, immersed equipped with honey after the main brick body 1 after straight line wire drawing process is then carried out sanding and polishing
In the vacuum tank of wax, it is 0.8MPa, is increased to keep the temperature under conditions of temperature is 75 DEG C with 10 DEG C of heating rate and protect in pressure
Pressure impregnates 3h, will form the main brick body 1 that thickness is 0.33mm beeswax layers and is placed in vacuum dryer, is 180 DEG C, pressure in temperature
To carry out baking 8h under conditions of 0.1MPa, is taken out after cooling and carry out stock removal polishing processing again, it is spare;
Step 3: the preparation of auxiliary brick body 2:A, the partially liq wood moulding base-material in step 1 is taken to be put into molding die, compacting is fixed
Type 40min after cooling and shaping, first sprays releasing agent into molding die, then molding die is placed on bobbing machine and vibrates 2min
It is demoulded, auxiliary brick body 2 is obtained after sanding and polishing processing, the auxiliary brick body 2 includes rectangle brick body 4 and is arranged above rectangle brick body
Drainage trough 5, the rectangle brick body 4 is hollow brick body, and the top of rectangle brick body 4 offers rectangle water inlet 6, bottom setting
There is discharge outlet 7, the ponding by drawing the guiding of the chute 5 enters rectangular tiles intracoelomic cavity by water inlet 6, and in time from discharge outlet 7
Discharge, the both ends of rectangle brick body 4 are corresponding with the rectangular recess 3 of main brick body 1 and can be embedded in rectangular recess 3, and drainage trough 5 includes
Vertical section 501 and linkage section 502, the vertical section 501 are connected with the linkage section 502, and vertical section 501 is in linkage section
502 lower section, after 2 both ends of auxiliary brick body are embedded in main brick body 1, one end of drainage trough 5 is connect with water inlet 7, and the other end is along main brick
1 madial wall of body extends to the top-direction of main brick body 1;
B, it is applied on the inner wall of 2 mold of auxiliary brick body after heating solid beeswax, auxiliary brick body 2 is put into auxiliary brick after beeswax cooling
In mould, by mold together with auxiliary brick body 2 be placed in Muffle furnace in fire, firing temperature be 180 DEG C, heating rate be 12 DEG C/
Min keeps the temperature 12h, auxiliary brick body 2 is taken out after cooling, and the beeswax layer of 2 excess surface of auxiliary brick body is rejected, according still further in step 2
The beeswax of main brick body 1 smears processing mode and carries out benefit wax, is put it into after sanding and polishing and conserves 2d in curing box.
Main feature, application method, basic principle and the advantages of the present invention of the present invention has been shown and described above.This
Industry technology personnel are it should be appreciated that the present invention is not limited to the above embodiments, described in the above embodiment and specification
It is to illustrate the principle of the present invention, without departing from the spirit and scope of the present invention, the present invention can also have according to actual conditions
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
It is defined by the appending claims and its equivalent thereof.
Claims (7)
1. a kind of preparation method of wood moulding floor tile for gardens pavement, which is characterized in that include the system of wood moulding floor tile base-material
The preparation of the preparation and auxiliary brick body of standby, main brick body, includes the following steps:
Step 1: the preparation of wood moulding floor tile base-material:The recipe ingredient for taking wood moulding floor tile is put into high-speed mixer uniformly
Mixing, mixed material obtained are melted in the case where temperature is 100-150 DEG C, pressure is 13-17MPa, obtain liquid wood moulding base-material, standby
With;
Step 2: main brick body(1)Preparation:A, it takes the partially liq wood moulding base-material in step 1 to be put into molding die, suppresses
Shape 22-30min, is taken out after cooling and shaping, winner's brick body(1), the main brick body(1)For cuboid, the main brick body(1)Two
It is main brick body that the lower part of side, which is provided with height,(1)/ 5th of height to a quarter rectangular recess(3);
B, first by the main brick body in step a(1)Be put into wire drawing machine, in the case where temperature is 280-320 DEG C, power is 26-30Hz into
Row case depth is the wire drawing process of 0.08-0.12cm, then by the main brick body after wire drawing process(1)It is soaked after carrying out sanding and polishing
Entering in the vacuum tank equipped with beeswax, heat-insulation pressure keeping impregnates 2-3h, will be formed in the main brick body merging vacuum dryer of beeswax layer,
Baking 5-8h is carried out under conditions of temperature is 150-180 DEG C, pressure is 0.1-0.008MPa, is taken out and is carried out again once after cooling
Polishing treatment, it is spare;
Step 3: auxiliary brick body(2)Preparation:A, it takes the partially liq wood moulding base-material in step 1 to be put into molding die, suppresses
Shape 30-40min, is demoulded after cooling and shaping, and auxiliary brick body is obtained after sanding and polishing processing(2), the auxiliary brick body(2)Including rectangular tiles
Body(4)With the drainage trough being arranged above rectangle brick body(5), the rectangle brick body(4)Both ends and main brick body(1)Rectangle it is recessed
Slot(3)It is corresponding and rectangular recess can be embedded in(3)It is interior, the drainage trough(5)Including vertical section(501)And linkage section(502), institute
State vertical section(501)With the linkage section(502)It is connected, and vertical section(501)In linkage section(502)Lower section, when auxiliary brick
Body(2)Both ends are embedded in main brick body(1)Afterwards, drainage trough(5)One end along main brick body(1)Madial wall is to main brick body(1)Top side
To extension;
B, auxiliary brick body is applied to after heating solid beeswax(2)Molding die inner wall on, by auxiliary brick body after beeswax cooling
(2)It is put into molding die, by molding die together with auxiliary brick body(2)It is placed in Muffle furnace and fires, auxiliary brick body is taken out after cooling
(2), and by auxiliary brick body(2)The beeswax layer of excess surface is rejected, according still further to main brick body in step 2(1)Beeswax smear processing side
Formula carries out benefit wax, is put it into after sanding and polishing and conserves 1-2d in curing box.
2. the preparation method of a kind of wood moulding floor tile for gardens pavement according to claim 1, which is characterized in that described
It is increased to 65-75 DEG C with 8-10 DEG C of heating rate when heat-insulation pressure keeping impregnates in step 1, and the range of control pressure is in 0.6-
0.8MPa。
3. the preparation method of a kind of wood moulding floor tile for gardens pavement according to claim 1, which is characterized in that described
Wire drawing process in step 2 is straight line wire drawing process.
4. the preparation method of a kind of wood moulding floor tile for gardens pavement according to claim 1, which is characterized in that described
Main brick body in step 2(1)Beeswax layer thickness be 0.23-0.33mm.
5. the preparation method of a kind of wood moulding floor tile for gardens pavement according to claim 1, which is characterized in that described
Auxiliary brick body in step 3(2)Final beeswax layer thickness be 0.28-0.38mm.
6. the preparation method of a kind of wood moulding floor tile for gardens pavement according to claim 1, which is characterized in that described
Auxiliary brick body in step 3(2)Releasing agent is first sprayed into molding die before demoulding, then molding die is placed on bobbing machine and is shaken
Dynamic 1-2min.
7. the preparation method of a kind of wood moulding floor tile for gardens pavement according to claim 1, which is characterized in that described
Muffle furnace firing temperature is 150-180 DEG C in step 3, and heating rate is 10-12 DEG C/min, keeps the temperature 10-12h.