CN108384123A - A kind of plastic bolt of power cable connector - Google Patents
A kind of plastic bolt of power cable connector Download PDFInfo
- Publication number
- CN108384123A CN108384123A CN201810164554.3A CN201810164554A CN108384123A CN 108384123 A CN108384123 A CN 108384123A CN 201810164554 A CN201810164554 A CN 201810164554A CN 108384123 A CN108384123 A CN 108384123A
- Authority
- CN
- China
- Prior art keywords
- parts
- poured
- spare
- mixed solution
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of plastic bolt of power cable connector, is made of 68 parts of 46 parts of 79 parts of 24 parts of 13 parts of 68 parts of 13 parts of 8 10 parts of 24 parts of 57 parts of 8 10 parts of 9 11 parts of 13 15 parts of atactic copolymerized polypropene, polyethylene glycol stearate, ethoxylated dodecyl alcohol, polyethylene terephthalate, polyester fiber, polymethyl methacrylate, methyl phenyl ethers anisole, polyvinyl chloride, zirconium dioxide, diamond dust, polysulfones, silicone oil, the lignite wax and 46 parts of stearic acid that match in parts by weight；There is outstanding water resistance using the power cable connector of the plastic bolt.
Description
The application is original application day on May 12nd, 2016, application number 201610318316.4, applicant's stone strategy, invention
Create a kind of divisional application of entitled power cable connector.
Technical field
The present invention relates to a kind of plastic bolts of power cable connector.
Background technology
Cable connector is also known as end.After cable laying is good, in order to become a continuous circuit, each section of line is necessary
It is connected as an entirety, these tie points are known as cable connector.During the cable connector at position is known as among cable run indirectly
Head, and the cable connector of two end of circuit is known as terminals.Cable connector is for locking and fixing inlet-outlet line, play dust-proof anti-
The effect of vibrations.
Its main function is to keep circuit unobstructed, so that cable is kept sealing, and ensure the class of insulation at cable connector, makes
It safely and reliably runs.If poor sealing, moisture fire moisture can invade inside cable, make decreasing insulating.
However current power cable connector poor waterproof properties on the market, it is easy to make decreasing insulating, or even leave peace
Full hidden danger.
Invention content
The technical problem to be solved in the present invention is to provide a kind of power cable connectors with outstanding water resistance.
To solve the above problems, the present invention adopts the following technical scheme that：
A kind of plastic bolt of power cable connector, by 13-15 parts of the atactic copolymerized polypropene, poly- matched in parts by weight
9-11 parts of ethylene glycol stearate, 8-10 parts of ethoxylated dodecyl alcohol, 5-7 parts of polyethylene terephthalate, polyester are fine
2-4 parts of dimension, 8-10 parts of polymethyl methacrylate, 1-3 parts of methyl phenyl ethers anisole, 6-8 parts of polyvinyl chloride, 1-3 parts of zirconium dioxide, diamond dust
4-6 parts of 2-4 parts, 7-9 parts of polysulfones, 4-6 parts of silicone oil, 6-8 parts of lignite wax and stearic acid are made.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt, is included the following steps：
1) 6-8 parts of 4-6 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that
6-8 parts of lignite wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, 1-3 parts of zirconium dioxide, diamond dust 2- is then added
4 parts and 2-4 parts of polyester fiber, 4-6 parts of progress surface-active-treatments of stearic acid are added after stirring keeps surface tension aobvious
It writes and declines, suspension is made, it is spare；
3) by methyl phenyl ethers anisole 1-3 parts be placed in reaction kettle, 8-10 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C,
It is sufficiently stirred until 8-10 part of polymethyl methacrylate 7-9 parts of polysulfones of addition and cools the temperature to 145 DEG C after being completely dissolved, makes
It obtains 7-9 parts of polysulfones to be completely dissolved, mixed solution is made, it is spare；
4) together by 13-15 parts of 5-7 parts of ethylene glycol terephthalate, 6-8 parts of polyvinyl chloride and atactic copolymerized polypropene
It is poured into heating vessel and is subsequently poured into mixed solution made from step 3) and is heated to 250 DEG C, then holding 30 minutes is added
8-10 parts of 9-11 parts of polyethylene glycol stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is standby
With；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Description of the drawings
Fig. 1 is a kind of overall structure diagram of the power cable connector of the application plastic bolt of the present invention.
Specific implementation mode
Embodiment one：
As shown in Figure 1, a kind of power cable connector of the application plastic bolt, including shell 1 and branch sleeve 2, it is described
1 left and right ends of shell are both provided with silicon rubber loop 3, and the silicon rubber loop 3 is threadedly coupled with shell 1, is pacified on the silicon rubber loop 3
Equipped with hose clamp 4, becket 5 is provided on the shell 1, the becket 5 is bolted with shell 1, is set on the becket 5
It is equipped with rubber block 6, plastic nut 7 is inlaid on the shell 1, plastic bolt 8, the modeling are provided on the plastic nut 7
Material bolt 8 is arranged through becket 5,8 end of plastic bolt setting geared surface clamp pad (not shown), on the shell 1
It is provided with stress cone 9, the stress cone 9 is threadedly coupled with shell 1, and the branch sleeve 2 is installed on stress cone 9, the company
Epoxy resins insulation part 10 is installed on female connector cylinder 2.
It is provided with wavy anti-skid chequer (not shown) on the rubber block 6, there is good antiskid effect, it can the company of preventing
The cable connect falls off.
It is coated with Anti-static paint (not shown) on the shell 1, there are the spies such as antistatic, dust-proof, mould proof, wear-resisting, acid and alkali-resistance
Point, it is durable, do not generate electrostatic.
It is coated with electromagnetic screen coating (not shown) on the epoxy resins insulation part 10, electromagnetic-wave leakage can be effectively prevent
And cause Contamination of Electromagnetic Wave.
2 surface of the branch sleeve is silver-plated setting, can increase conductivity and thermal conductivity, and be also prevented from connection
Sleeve 2 is corroded.
Be provided between the plastic nut 7 and plastic bolt 8 conductive fabric liner (not shown), can with release electrostatic, and
And also there is good sealing performance.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt.
To solve the above problems, the present invention adopts the following technical scheme that：
By match in parts by weight 9 parts of 15 parts of atactic copolymerized polypropene, polyethylene glycol stearate, laruyl alcohol polyoxy second
8 parts of alkene ether, 2 parts of polyester fiber, 8 parts of polymethyl methacrylate, 1 part of methyl phenyl ethers anisole, gathers 5 parts of polyethylene terephthalate
4 parts of 6 parts of vinyl chloride, 1 part of zirconium dioxide, 2 parts of diamond dust, 7 parts of polysulfones, 4 parts of silicone oil, 6 parts of lignite wax and stearic acid compositions, including
Following steps：
1) 6 parts of 4 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that lignite
6 parts of wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, 1 part of zirconium dioxide, 2 parts of diamond dust is then added
With 2 parts of polyester fiber, 4 parts of progress surface-active-treatments of stearic acid are added after stirring makes surface tension be remarkably decreased,
Suspension is made, it is spare；
3) by methyl phenyl ethers anisole 1 part be placed in reaction kettle, 8 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, is fully stirred
It mixes until 8 parts of polymethyl methacrylate is added 7 parts of polysulfones and cools the temperature to 145 DEG C after being completely dissolved so that 7 parts of polysulfones is complete
Mixed solution is made in fully dissolved, spare；
4) 15 parts of 5 parts of ethylene glycol terephthalate, 6 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into together and are added
It is subsequently poured into mixed solution made from step 3) in hot vessel and is heated to 250 DEG C, then polyethylene glycol is added in holding 30 minutes
8 parts of 9 parts of stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Embodiment two：
As shown in Figure 1, a kind of power cable connector of the application plastic bolt, including shell 1 and branch sleeve 2, it is described
1 left and right ends of shell are both provided with silicon rubber loop 3, and the silicon rubber loop 3 is threadedly coupled with shell 1, is pacified on the silicon rubber loop 3
Equipped with hose clamp 4, becket 5 is provided on the shell 1, the becket 5 is bolted with shell 1, is set on the becket 5
It is equipped with rubber block 6, plastic nut 7 is inlaid on the shell 1, plastic bolt 8, the modeling are provided on the plastic nut 7
Material bolt 8 is arranged through becket 5,8 end of plastic bolt setting geared surface clamp pad (not shown), on the shell 1
It is provided with stress cone 9, the stress cone 9 is threadedly coupled with shell 1, and the branch sleeve 2 is installed on stress cone 9, the company
Epoxy resins insulation part 10 is installed on female connector cylinder 2.
It is provided with wavy anti-skid chequer (not shown) on the rubber block 6, there is good antiskid effect, it can the company of preventing
The cable connect falls off.
It is coated with Anti-static paint (not shown) on the shell 1, there are the spies such as antistatic, dust-proof, mould proof, wear-resisting, acid and alkali-resistance
Point, it is durable, do not generate electrostatic.
It is coated with electromagnetic screen coating (not shown) on the epoxy resins insulation part 10, electromagnetic-wave leakage can be effectively prevent
And cause Contamination of Electromagnetic Wave.
2 surface of the branch sleeve is silver-plated setting, can increase conductivity and thermal conductivity, and be also prevented from connection
Sleeve 2 is corroded.
Be provided between the plastic nut 7 and plastic bolt 8 conductive fabric liner (not shown), can with release electrostatic, and
And also there is good sealing performance.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt.
To solve the above problems, the present invention adopts the following technical scheme that：
By 11 parts of 13 parts of atactic copolymerized polypropene, polyethylene glycol stearate, the laruyl alcohol polyoxy matched in parts by weight
10 parts of vinethene, 7 parts of polyethylene terephthalate, 4 parts of polyester fiber, 10 parts of polymethyl methacrylate, methyl phenyl ethers anisole 3
Part, 8 parts of polyvinyl chloride, 3 parts of zirconium dioxide, 4 parts of diamond dust, 9 parts of polysulfones, 6 parts of silicone oil, 8 parts of lignite wax and 6 parts of groups of stearic acid
At including the following steps：
1) 8 parts of 6 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that lignite
8 parts of wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, 3 parts of zirconium dioxide, 4 parts of diamond dust is then added
With 4 parts of polyester fiber, 6 parts of progress surface-active-treatments of stearic acid are added after stirring makes surface tension be remarkably decreased,
Suspension is made, it is spare；
3) by methyl phenyl ethers anisole 3 parts be placed in reaction kettle, 10 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, fully
Stirring is until 10 parts of polymethyl methacrylate is added 9 parts of polysulfones and cools the temperature to 145 DEG C after being completely dissolved so that polysulfones 9
Part is completely dissolved, and mixed solution is made, spare；
4) 13 parts of 7 parts of ethylene glycol terephthalate, 8 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into together and are added
It is subsequently poured into mixed solution made from step 3) in hot vessel and is heated to 250 DEG C, then polyethylene glycol is added in holding 30 minutes
10 parts of 11 parts of stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Embodiment three：
As shown in Figure 1, a kind of power cable connector of the application plastic bolt, including shell 1 and branch sleeve 2, it is described
1 left and right ends of shell are both provided with silicon rubber loop 3, and the silicon rubber loop 3 is threadedly coupled with shell 1, is pacified on the silicon rubber loop 3
Equipped with hose clamp 4, becket 5 is provided on the shell 1, the becket 5 is bolted with shell 1, is set on the becket 5
It is equipped with rubber block 6, plastic nut 7 is inlaid on the shell 1, plastic bolt 8, the modeling are provided on the plastic nut 7
Material bolt 8 is arranged through becket 5,8 end of plastic bolt setting geared surface clamp pad (not shown), on the shell 1
It is provided with stress cone 9, the stress cone 9 is threadedly coupled with shell 1, and the branch sleeve 2 is installed on stress cone 9, the company
Epoxy resins insulation part 10 is installed on female connector cylinder 2.
It is provided with wavy anti-skid chequer (not shown) on the rubber block 6, there is good antiskid effect, it can the company of preventing
The cable connect falls off.
It is coated with Anti-static paint (not shown) on the shell 1, there are the spies such as antistatic, dust-proof, mould proof, wear-resisting, acid and alkali-resistance
Point, it is durable, do not generate electrostatic.
It is coated with electromagnetic screen coating (not shown) on the epoxy resins insulation part 10, electromagnetic-wave leakage can be effectively prevent
And cause Contamination of Electromagnetic Wave.
2 surface of the branch sleeve is silver-plated setting, can increase conductivity and thermal conductivity, and be also prevented from connection
Sleeve 2 is corroded.
Be provided between the plastic nut 7 and plastic bolt 8 conductive fabric liner (not shown), can with release electrostatic, and
And also there is good sealing performance.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt.
To solve the above problems, the present invention adopts the following technical scheme that：
By 10 parts of 14 parts of atactic copolymerized polypropene, polyethylene glycol stearate, the laruyl alcohol polyoxy matched in parts by weight
9 parts of vinethene, 6 parts of polyethylene terephthalate, 3 parts of polyester fiber, 9 parts of polymethyl methacrylate, 2 parts of methyl phenyl ethers anisole,
5 parts of 7 parts of polyvinyl chloride, 2 parts of zirconium dioxide, 3 parts of diamond dust, 8 parts of polysulfones, 5 parts of silicone oil, 7 parts of lignite wax and stearic acid compositions, packet
Include following steps：
1) 7 parts of 5 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that lignite
7 parts of wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, 2 parts of zirconium dioxide, 3 parts of diamond dust is then added
With 3 parts of polyester fiber, 5 parts of progress surface-active-treatments of stearic acid are added after stirring makes surface tension be remarkably decreased,
Suspension is made, it is spare；
3) by methyl phenyl ethers anisole 2 parts be placed in reaction kettle, 9 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, is fully stirred
It mixes until 9 parts of polymethyl methacrylate is added 8 parts of polysulfones and cools the temperature to 145 DEG C after being completely dissolved so that 8 parts of polysulfones is complete
Mixed solution is made in fully dissolved, spare；
4) 14 parts of 6 parts of ethylene glycol terephthalate, 7 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into together and are added
It is subsequently poured into mixed solution made from step 3) in hot vessel and is heated to 250 DEG C, then polyethylene glycol is added in holding 30 minutes
9 parts of 10 parts of stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Beneficial effects of the present invention are：By being provided with silicon rubber loop, and hose clamp is installed on silicon rubber loop, Ke Yizeng
Add the sealing effect between silicon rubber loop and cable, prevents moisture and vapor from entering in shell, by being provided with becket
And plastic bolt, and geared surface clamp pad is set on plastic bolt, the rubber block on complexed metal ring has good damping
And fixed function, it can prevent cable from falling off and influence to use.
Experimental example：
Using the power cable connector of the present invention as experimental group, existing conventional power cable connector carries out as a control group
Test, concrete outcome are as shown in the table：
By being detected to 2 groups of experiments, the power cable connector of experimental group and existing conventional power cable connector phase
Than not only good fixing effect, but also there is outstanding waterproof and damping performance.
Beneficial effects of the present invention are：By being provided with silicon rubber loop, and hose clamp is installed on silicon rubber loop, Ke Yizeng
Add the sealing effect between silicon rubber loop and cable, prevents moisture and vapor from entering in shell, by being provided with becket
And plastic bolt, and geared surface clamp pad is set on plastic bolt, the rubber block on complexed metal ring has good damping
And fixed function, it can prevent cable from falling off and influence to use.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
The change or replacement expected without creative work, should be covered by the protection scope of the present invention.
Claims (2)
1. a kind of plastic bolt of power cable connector, it is characterised in that：By the atactic copolymerized polypropene matched in parts by weight
13-15 parts, 9-11 parts of polyethylene glycol stearate, 8-10 parts of ethoxylated dodecyl alcohol, polyethylene terephthalate 5-7
Part, 2-4 parts of polyester fiber, 8-10 parts of polymethyl methacrylate, 1-3 parts of methyl phenyl ethers anisole, 6-8 parts of polyvinyl chloride, zirconium dioxide 1-3
Part, 2-4 parts of diamond dust, 7-9 parts of polysulfones, 4-6 parts of silicone oil, 6-8 parts of lignite wax and 4-6 parts of stearic acid are made.
2. the manufacturing method of plastic bolt as described in claim 1, it is characterised in that：Include the following steps：
1) 6-8 parts of 4-6 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that lignite
6-8 parts of wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, 1-3 parts of zirconium dioxide, 2-4 parts of diamond dust is then added
With 2-4 parts of polyester fiber, it is added after stirring under 4-6 part of stearic acid progress surface-active-treatments keep surface tension notable
Suspension is made in drop, spare；
3) by methyl phenyl ethers anisole 1-3 parts be placed in reaction kettle, 8-10 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, fully
Stirring is until 8-10 parts of polymethyl methacrylate is added 7-9 parts of polysulfones and cools the temperature to 145 DEG C after being completely dissolved so that poly-
7-9 parts of sulfone is completely dissolved, and mixed solution is made, spare；
4) 13-15 parts of 5-7 parts of ethylene glycol terephthalate, 6-8 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into together
To being subsequently poured into mixed solution made from step 3) in heating vessel and being heated to 250 DEG C, then poly- second is added in holding 30 minutes
8-10 parts of 9-11 parts of glycol stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into together in emulsification agitated kettle,
It carries out emulsification treatment 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.