CN108242793A - A kind of power cable connector - Google Patents
A kind of power cable connector Download PDFInfo
- Publication number
- CN108242793A CN108242793A CN201810160382.2A CN201810160382A CN108242793A CN 108242793 A CN108242793 A CN 108242793A CN 201810160382 A CN201810160382 A CN 201810160382A CN 108242793 A CN108242793 A CN 108242793A
- Authority
- CN
- China
- Prior art keywords
- parts
- shell
- poured
- cable connector
- power cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of power cable connector, including shell and branch sleeve, the shell left and right ends are both provided with silicon rubber loop, the silicon rubber loop is connect with outer casing screw, hose clamp is installed on the silicon rubber loop, becket is provided on the shell, the becket is connect with housing bolts, rubber block is provided on the becket, plastic nut is inlaid on the shell, plastic bolt is provided on the plastic nut, the plastic bolt is set through becket, the plastic bolt end sets geared surface clamp pad, stress cone is provided on the shell, the stress cone is connect with outer casing screw, the branch sleeve is installed on stress cone, epoxy resins insulation part is installed on the branch sleeve；The power cable connector has outstanding water resistance.
Description
The application is original application day on May 12nd, 2016, application number 201610318316.4, applicant's stone strategy, invention
Create a kind of divisional application of entitled power cable connector.
Technical field
The present invention relates to a kind of power cable connectors.
Background technology
Cable connector is also known as end.After cable laying is good, in order to become a continuous circuit, each section of line is necessary
An entirety is connected as, these tie points are known as cable connector.During the cable connector at position is known as among cable run indirectly
Head, and the cable connector of two end of circuit is known as terminals.Cable connector is for locking and fixing inlet-outlet line, play dust-proof anti-
The effect of vibrations.
Its main function is to make circuit unobstructed, cable is made to keep sealing, and ensure the class of insulation at cable connector, made
It safely and reliably runs.If poor sealing, moisture fire moisture can be invaded inside cable, make decreasing insulating.
However current power cable connector poor waterproof properties on the market, easily make decreasing insulating or even leave peace
Full hidden danger.
Invention content
The technical problem to be solved in the present invention is to provide a kind of power cable connectors with outstanding water resistance.
To solve the above problems, the present invention adopts the following technical scheme that：
A kind of power cable connector, including shell and branch sleeve, the shell left and right ends are both provided with silicon rubber loop,
The silicon rubber loop is connect with outer casing screw, and hose clamp is equipped on the silicon rubber loop, and becket, institute are provided on the shell
It states becket to connect with housing bolts, rubber block is provided on the becket, plastic nut is inlaid on the shell, it is described
Plastic bolt is provided on plastic nut, the plastic bolt is set through becket, and the plastic bolt end setting is with teeth
Face clamp pad is provided with stress cone on the shell, and the stress cone is connect with outer casing screw, and the branch sleeve is installed on should
On power cone, epoxy resins insulation part is installed on the branch sleeve.
Preferably, being provided with wavy anti-skid chequer on the rubber block, there is good antiskid effect, it can the company of preventing
The cable connect comes off.
Preferably, being coated with Anti-static paint on the shell, there are the spies such as antistatic, dust-proof, mould proof, wear-resisting, acid and alkali-resistance
Point, it is durable, do not generate electrostatic.
Preferably, being coated with electromagnetic screen coating on the epoxy resins insulation part, electromagnetic-wave leakage can be effectively prevent
And cause Contamination of Electromagnetic Wave.
Preferably, the branch sleeve surface is silver-plated setting, conductivity and thermal conductivity can be increased, but also can be with
Branch sleeve is prevented to be corroded.
Preferably, be provided between the plastic nut and plastic bolt conductive fabric liner, can with release electrostatic, and
Also there is good sealing performance.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt.
To solve the above problems, the present invention adopts the following technical scheme that：
By 9-11 parts of 13-15 parts of atactic copolymerized polypropene, polyethylene glycol stearate, the laruyl alcohol matched in parts by weight
8-10 parts of polyoxyethylene ether, 5-7 parts of polyethylene terephthalate, 2-4 parts of polyester fiber, polymethyl methacrylate 8-10
It is part, 1-3 parts of methyl phenyl ethers anisole, 6-8 parts of polyvinyl chloride, 1-3 parts of zirconium dioxide, 2-4 parts of diamond dust, 7-9 parts of polysulfones, 4-6 parts of silicone oil, brown
4-6 parts of compositions of 6-8 parts of coal wax and stearic acid, include the following steps：
1) 6-8 parts of 4-6 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that
6-8 parts of lignite wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, then adds in 1-3 parts of zirconium dioxide, diamond dust 2-
4 parts and 2-4 parts of polyester fiber, 4-6 parts of progress surface-active-treatments of stearic acid are added in after stirring shows surface tension
It writes and declines, suspension is made, it is spare；
3) by methyl phenyl ethers anisole 1-3 parts be placed in reaction kettle, 8-10 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C,
It is sufficiently stirred until 8-10 part of polymethyl methacrylate 7-9 parts of polysulfones of addition and cools the temperature to 145 DEG C after being completely dissolved, makes
It obtains 7-9 parts of polysulfones to be completely dissolved, mixed solution is made, it is spare；
4) by 13-15 parts of 5-7 parts of ethylene glycol terephthalate, 6-8 parts of polyvinyl chloride and atactic copolymerized polypropene together
It is poured into heating vessel and is subsequently poured into mixed solution made from step 3) and is heated to 250 DEG C, then holding 30 minutes adds in
8-10 parts of 9-11 parts of polyethylene glycol stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is standby
With；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Beneficial effects of the present invention are：By being provided with silicon rubber loop, and hose clamp is installed on silicon rubber loop, Ke Yizeng
Add the sealing effect between silicon rubber loop and cable, prevent moisture and vapor from entering in shell, by being provided with becket
And plastic bolt, and geared surface clamp pad is set on plastic bolt, the rubber block on complexed metal ring has good damping
And fixed function, it can prevent cable from coming off and influence to use.
Description of the drawings
Fig. 1 is a kind of overall structure diagram of power cable connector of the present invention.
Specific embodiment
Embodiment one：
As shown in Figure 1, a kind of power cable connector, including shell 1 and branch sleeve 2,1 left and right ends of shell are all provided with
Silicon rubber loop 3 is equipped with, the silicon rubber loop 3 is threadedly coupled with shell 1, and hose clamp 4 is equipped on the silicon rubber loop 3, described outer
Becket 5 is provided on shell 1, the becket 5 is bolted with shell 1, and rubber block 6 is provided on the becket 5, described
Plastic nut 7 is inlaid on shell 1, plastic bolt 8 is provided on the plastic nut 7, the plastic bolt 8 runs through becket
5 settings, 8 end of plastic bolt sets geared surface clamp pad (not shown), stress cone 9 is provided on the shell 1, described
Stress cone 9 is threadedly coupled with shell 1, and the branch sleeve 2 is installed on stress cone 9, and epoxy is equipped on the branch sleeve 2
Insulation resin part 10.
Wavy anti-skid chequer (not shown) is provided on the rubber block 6, there is good antiskid effect, it can the company of preventing
The cable connect comes off.
Anti-static paint (not shown) is coated on the shell 1, there are the spies such as antistatic, dust-proof, mould proof, wear-resisting, acid and alkali-resistance
Point, it is durable, do not generate electrostatic.
Electromagnetic screen coating (not shown) is coated on the epoxy resins insulation part 10, electromagnetic-wave leakage can be effectively prevent
And cause Contamination of Electromagnetic Wave.
2 surface of branch sleeve is silver-plated setting, can increase conductivity and thermal conductivity, and be also prevented from connecting
Sleeve 2 is corroded.
Be provided between the plastic nut 7 and plastic bolt 8 conductive fabric liner (not shown), can with release electrostatic, and
And also there is good sealing performance.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt.
To solve the above problems, the present invention adopts the following technical scheme that：
By match in parts by weight 9 parts of 15 parts of atactic copolymerized polypropene, polyethylene glycol stearate, laruyl alcohol polyoxy second
8 parts of alkene ether, 2 parts of polyester fiber, 8 parts of polymethyl methacrylate, 1 part of methyl phenyl ethers anisole, gathers 5 parts of polyethylene terephthalate
4 parts of 6 parts of vinyl chloride, 1 part of zirconium dioxide, 2 parts of diamond dust, 7 parts of polysulfones, 4 parts of silicone oil, 6 parts of lignite wax and stearic acid compositions, including
Following steps：
1) 6 parts of 4 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that lignite
6 parts of wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, then adds in 1 part of zirconium dioxide, 2 parts of diamond dust
With 2 parts of polyester fiber, 4 parts of progress surface-active-treatments of stearic acid are added in after stirring is remarkably decreased surface tension,
Suspension is made, it is spare；
3) by methyl phenyl ethers anisole 1 part be placed in reaction kettle, 8 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, is fully stirred
It mixes until 8 parts of polymethyl methacrylate adds in 7 parts of polysulfones and cools the temperature to 145 DEG C after being completely dissolved so that 7 parts of polysulfones is complete
Mixed solution is made in fully dissolved, spare；
4) 15 parts of 5 parts of ethylene glycol terephthalate, 6 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into together and added
Mixed solution made from step 3) is subsequently poured into hot vessel and is heated to 250 DEG C, then holding 30 minutes adds in polyethylene glycol
8 parts of 9 parts of stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Embodiment two：
As shown in Figure 1, a kind of power cable connector, including shell 1 and branch sleeve 2,1 left and right ends of shell are all provided with
Silicon rubber loop 3 is equipped with, the silicon rubber loop 3 is threadedly coupled with shell 1, and hose clamp 4 is equipped on the silicon rubber loop 3, described outer
Becket 5 is provided on shell 1, the becket 5 is bolted with shell 1, and rubber block 6 is provided on the becket 5, described
Plastic nut 7 is inlaid on shell 1, plastic bolt 8 is provided on the plastic nut 7, the plastic bolt 8 runs through becket
5 settings, 8 end of plastic bolt sets geared surface clamp pad (not shown), stress cone 9 is provided on the shell 1, described
Stress cone 9 is threadedly coupled with shell 1, and the branch sleeve 2 is installed on stress cone 9, and epoxy is equipped on the branch sleeve 2
Insulation resin part 10.
Wavy anti-skid chequer (not shown) is provided on the rubber block 6, there is good antiskid effect, it can the company of preventing
The cable connect comes off.
Anti-static paint (not shown) is coated on the shell 1, there are the spies such as antistatic, dust-proof, mould proof, wear-resisting, acid and alkali-resistance
Point, it is durable, do not generate electrostatic.
Electromagnetic screen coating (not shown) is coated on the epoxy resins insulation part 10, electromagnetic-wave leakage can be effectively prevent
And cause Contamination of Electromagnetic Wave.
2 surface of branch sleeve is silver-plated setting, can increase conductivity and thermal conductivity, and be also prevented from connecting
Sleeve 2 is corroded.
Be provided between the plastic nut 7 and plastic bolt 8 conductive fabric liner (not shown), can with release electrostatic, and
And also there is good sealing performance.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt.
To solve the above problems, the present invention adopts the following technical scheme that：
By 11 parts of 13 parts of atactic copolymerized polypropene, polyethylene glycol stearate, the laruyl alcohol polyoxy matched in parts by weight
10 parts of vinethene, 7 parts of polyethylene terephthalate, 4 parts of polyester fiber, 10 parts of polymethyl methacrylate, methyl phenyl ethers anisole 3
Part, 8 parts of polyvinyl chloride, 3 parts of zirconium dioxide, 4 parts of diamond dust, 9 parts of polysulfones, 6 parts of silicone oil, 8 parts of lignite wax and 6 parts of groups of stearic acid
Into including the following steps：
1) 8 parts of 6 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that lignite
8 parts of wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, then adds in 3 parts of zirconium dioxide, 4 parts of diamond dust
With 4 parts of polyester fiber, 6 parts of progress surface-active-treatments of stearic acid are added in after stirring is remarkably decreased surface tension,
Suspension is made, it is spare；
3) by methyl phenyl ethers anisole 3 parts be placed in reaction kettle, 10 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, fully
Stirring is until 10 parts of polymethyl methacrylate adds in 9 parts of polysulfones and cools the temperature to 145 DEG C after being completely dissolved so that polysulfones 9
Part is completely dissolved, and mixed solution is made, spare；
4) 13 parts of 7 parts of ethylene glycol terephthalate, 8 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into together and added
Mixed solution made from step 3) is subsequently poured into hot vessel and is heated to 250 DEG C, then holding 30 minutes adds in polyethylene glycol
10 parts of 11 parts of stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Embodiment three：
As shown in Figure 1, a kind of power cable connector, including shell 1 and branch sleeve 2,1 left and right ends of shell are all provided with
Silicon rubber loop 3 is equipped with, the silicon rubber loop 3 is threadedly coupled with shell 1, and hose clamp 4 is equipped on the silicon rubber loop 3, described outer
Becket 5 is provided on shell 1, the becket 5 is bolted with shell 1, and rubber block 6 is provided on the becket 5, described
Plastic nut 7 is inlaid on shell 1, plastic bolt 8 is provided on the plastic nut 7, the plastic bolt 8 runs through becket
5 settings, 8 end of plastic bolt sets geared surface clamp pad (not shown), stress cone 9 is provided on the shell 1, described
Stress cone 9 is threadedly coupled with shell 1, and the branch sleeve 2 is installed on stress cone 9, and epoxy is equipped on the branch sleeve 2
Insulation resin part 10.
Wavy anti-skid chequer (not shown) is provided on the rubber block 6, there is good antiskid effect, it can the company of preventing
The cable connect comes off.
Anti-static paint (not shown) is coated on the shell 1, there are the spies such as antistatic, dust-proof, mould proof, wear-resisting, acid and alkali-resistance
Point, it is durable, do not generate electrostatic.
Electromagnetic screen coating (not shown) is coated on the epoxy resins insulation part 10, electromagnetic-wave leakage can be effectively prevent
And cause Contamination of Electromagnetic Wave.
2 surface of branch sleeve is silver-plated setting, can increase conductivity and thermal conductivity, and be also prevented from connecting
Sleeve 2 is corroded.
Be provided between the plastic nut 7 and plastic bolt 8 conductive fabric liner (not shown), can with release electrostatic, and
And also there is good sealing performance.
Another technical problem to be solved by the invention is to provide a kind of manufacturing method of plastic bolt.
To solve the above problems, the present invention adopts the following technical scheme that：
By 10 parts of 14 parts of atactic copolymerized polypropene, polyethylene glycol stearate, the laruyl alcohol polyoxy matched in parts by weight
9 parts of vinethene, 6 parts of polyethylene terephthalate, 3 parts of polyester fiber, 9 parts of polymethyl methacrylate, 2 parts of methyl phenyl ethers anisole,
5 parts of 7 parts of polyvinyl chloride, 2 parts of zirconium dioxide, 3 parts of diamond dust, 8 parts of polysulfones, 5 parts of silicone oil, 7 parts of lignite wax and stearic acid compositions, packet
Include following steps：
1) 7 parts of 5 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that lignite
7 parts of wax is completely dissolved, and thick liquid is made, spare；
2) thick liquid made from step 1) is poured into agitated kettle, then adds in 2 parts of zirconium dioxide, 3 parts of diamond dust
With 3 parts of polyester fiber, 5 parts of progress surface-active-treatments of stearic acid are added in after stirring is remarkably decreased surface tension,
Suspension is made, it is spare；
3) by methyl phenyl ethers anisole 2 parts be placed in reaction kettle, 9 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, is fully stirred
It mixes until 9 parts of polymethyl methacrylate adds in 8 parts of polysulfones and cools the temperature to 145 DEG C after being completely dissolved so that 8 parts of polysulfones is complete
Mixed solution is made in fully dissolved, spare；
4) 14 parts of 6 parts of ethylene glycol terephthalate, 7 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into together and added
Mixed solution made from step 3) is subsequently poured into hot vessel and is heated to 250 DEG C, then holding 30 minutes adds in polyethylene glycol
9 parts of 10 parts of stearate and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into emulsification stirring together
In pot, emulsification treatment is carried out 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
Beneficial effects of the present invention are：By being provided with silicon rubber loop, and hose clamp is installed on silicon rubber loop, Ke Yizeng
Add the sealing effect between silicon rubber loop and cable, prevent moisture and vapor from entering in shell, by being provided with becket
And plastic bolt, and geared surface clamp pad is set on plastic bolt, the rubber block on complexed metal ring has good damping
And fixed function, it can prevent cable from coming off and influence to use.
Experimental example：
Using the power cable connector of the present invention as experimental group, existing conventional power cable connector carries out as a control group
Test, concrete outcome are as shown in the table：
By being detected to 2 groups of experiments, the power cable connector of experimental group and existing conventional power cable connector phase
Than not only good fixing effect, but also with outstanding waterproof and damping performance.
Beneficial effects of the present invention are：By being provided with silicon rubber loop, and hose clamp is installed on silicon rubber loop, Ke Yizeng
Add the sealing effect between silicon rubber loop and cable, prevent moisture and vapor from entering in shell, by being provided with becket
And plastic bolt, and geared surface clamp pad is set on plastic bolt, the rubber block on complexed metal ring has good damping
And fixed function, it can prevent cable from coming off and influence to use.
The above description is merely a specific embodiment, but protection scope of the present invention is not limited thereto, any
The change or replacement expected without creative work, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of power cable connector, it is characterised in that：Including shell and branch sleeve, the shell left and right ends are both provided with
Silicon rubber loop, the silicon rubber loop are connect with outer casing screw, and hose clamp is equipped on the silicon rubber loop, is provided on the shell
Becket, the becket are connect with housing bolts, and rubber block is provided on the becket, plastics are inlaid on the shell
Nut is provided with plastic bolt on the plastic nut, and the plastic bolt is set through becket, the plastic bolt end
Geared surface clamp pad is set, is provided with stress cone on the shell, the stress cone is connect with outer casing screw, the branch sleeve
It is installed on stress cone, epoxy resins insulation part is installed, the plastic bolt by matching in parts by weight on the branch sleeve
8 parts of 9 parts of 15 parts of atactic copolymerized polypropene, polyethylene glycol stearate, the ethoxylated dodecyl alcohol of ratio, poly terephthalic acid second
5 parts of diol ester, 2 parts of polyester fiber, 8 parts of polymethyl methacrylate, 1 part of methyl phenyl ethers anisole, 6 parts of polyvinyl chloride, 1 part of zirconium dioxide,
4 parts of 2 parts of diamond dust, 7 parts of polysulfones, 4 parts of silicone oil, 6 parts of lignite wax and stearic acid compositions, include the following steps：
1) 6 parts of 4 parts of silicone oil and lignite wax are poured into vessel and are heated to 90 DEG C together, be sufficiently stirred so that 6 parts of lignite wax
It is completely dissolved, thick liquid is made, it is spare；
2) thick liquid made from step 1) is poured into agitated kettle, then adds in 1 part of zirconium dioxide, 2 parts of diamond dust and gathered
2 parts of ester fiber, 4 parts of progress surface-active-treatments of stearic acid are added in after stirring is remarkably decreased surface tension, is made
Suspension, it is spare；
3) by methyl phenyl ethers anisole 1 part be placed in reaction kettle, 8 parts of polymethyl methacrylate is poured into after being heated to 155 DEG C, is sufficiently stirred straight
7 parts of polysulfones is added in after being completely dissolved to 8 parts of polymethyl methacrylate and cools the temperature to 145 DEG C so that 7 parts of polysulfones is completely molten
Mixed solution is made in solution, spare；
4) 15 parts of 5 parts of ethylene glycol terephthalate, 6 parts of polyvinyl chloride and atactic copolymerized polypropene are poured into heater together
Mixed solution made from step 3) is subsequently poured into ware and is heated to 250 DEG C, then it is stearic to add in polyethylene glycol for holding 30 minutes
8 parts of 9 parts of acid esters and ethoxylated dodecyl alcohol are sufficiently stirred, and are made, and sticky mixed solution is spare；
5) suspension made from mixed solution and step 2) sticky made from step 4) is poured into together in emulsification agitated kettle,
It carries out emulsification treatment 30 minutes, emulsion is made, it is spare；
6) emulsion made from step 5) is poured into injection mold, then through cooling treatment, you can use.
2. power cable connector as described in claim 1, it is characterised in that：It is provided on the rubber block wavy anti-skidding
Line.
3. power cable connector as claimed in claim 2, it is characterised in that：Anti-static paint is coated on the shell.
4. power cable connector as claimed in claim 3, it is characterised in that：Electromagnetic screen is coated on the epoxy resins insulation part
Cover coating.
5. power cable connector as claimed in claim 4, it is characterised in that：The branch sleeve surface is silver-plated setting.
6. power cable connector as claimed in claim 5, it is characterised in that：It is set between the plastic nut and plastic bolt
There is conductive fabric liner.