CN108374164A - Aluminum alloy surface anti-oxidation treatment method - Google Patents
Aluminum alloy surface anti-oxidation treatment method Download PDFInfo
- Publication number
- CN108374164A CN108374164A CN201810252522.9A CN201810252522A CN108374164A CN 108374164 A CN108374164 A CN 108374164A CN 201810252522 A CN201810252522 A CN 201810252522A CN 108374164 A CN108374164 A CN 108374164A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminum alloy
- treatment method
- oxidation treatment
- surface anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of aluminum alloy surface anti-oxidation treatment method.The method of the present invention includes(1)Processing of rust removing is carried out to Al-alloy parts surface;(2)Degreasing cleaning is carried out to Al-alloy parts surface;(3)Al-alloy parts after degreasing is cleaned are dried;(4)7.5 parts of the concentrated sulfuric acid, 22 parts of potassium bichromate is taken to be configured to the mixed solution that mass percentage concentration is 45 65% in parts by weight;(5)Al-alloy parts after drying are immersed in the mixed solution configured, 10 30min are kept the temperature at 60 65 DEG C;(6)Low temperature drying after cleaning.The method treatment process of the present invention is simple and environmental-friendly, and aluminum alloy surface is beautiful after processing, good in oxidation resistance.
Description
Technical field:
The present invention relates to a kind of aluminum alloy surface anti-oxidation treatment methods, belong to field of metal surface treatment technology.
Background technology:
Simple aluminium is to be very easy to oxidation, and not only influencing beauty also influences intensity, so good industrial aluminum profile factory
Family can all be handled in Surface of profile, and most common surface treatment mode is exactly anodic oxidation, mat surface, this mode
Proximate matter after processed is beautiful and generous.
Existing oxidation processes, complex process, and environmental pollution is larger.
Invention content:
The purpose of the present invention is provide a kind of aluminum alloy surface anti-oxidation treatment method, treatment process in view of the above problems
Simple and environmental-friendly, aluminum alloy surface is beautiful after processing, good in oxidation resistance.
Above-mentioned purpose is realized by following technical scheme:
Aluminum alloy surface anti-oxidation treatment method, this method comprises the following steps:
(1)Processing of rust removing is carried out to Al-alloy parts surface;
(2)Degreasing cleaning is carried out to Al-alloy parts surface;
(3)Al-alloy parts after degreasing is cleaned are dried;
(4)7.5 parts of the concentrated sulfuric acid, 22 parts of potassium bichromate is taken to be configured to the mixing that mass percentage concentration is 45-65% in parts by weight
Solution;
(5)Al-alloy parts after drying are immersed in the mixed solution configured, 10-30min is kept the temperature at 60-65 DEG C;
(6)Low temperature drying after cleaning.
The aluminum alloy surface anti-oxidation treatment method, step(1)Described in processing of rust removing use blasting treatment.
The aluminum alloy surface anti-oxidation treatment method, step(2)Described in degreasing cleaning use trichloro ethylene
Cotton wipes Al-alloy parts surface.
The aluminum alloy surface anti-oxidation treatment method, step(3)Described in drying using 45-55 DEG C temperature dry
It is dry.
The aluminum alloy surface anti-oxidation treatment method, step(6)Described in low temperature drying temperature be 30 DEG C.
Advantageous effect:
The present invention will use rational technique, and treatment process is simple and environmental-friendly, and aluminum alloy surface is beautiful after processing, antioxygen
The property changed is good.
Specific implementation mode:
Embodiment 1:
Aluminum alloy surface anti-oxidation treatment method, this method comprises the following steps:
(1)Processing of rust removing is carried out to Al-alloy parts surface;
(2)Degreasing cleaning is carried out to Al-alloy parts surface;
(3)Al-alloy parts after degreasing is cleaned are dried;
(4)7.5 parts of the concentrated sulfuric acid, 22 parts of potassium bichromate is taken to be configured to the mixing that mass percentage concentration is 45-65% in parts by weight
Solution;
(5)Al-alloy parts after drying are immersed in the mixed solution configured, 10-30min is kept the temperature at 60-65 DEG C;
(6)Low temperature drying after cleaning.
The aluminum alloy surface anti-oxidation treatment method, step(3)Described in drying using 45-55 DEG C temperature dry
It is dry.
The aluminum alloy surface anti-oxidation treatment method, step(6)Described in low temperature drying temperature be 30 DEG C.
Embodiment 2:
Aluminum alloy surface anti-oxidation treatment method described in the present embodiment, step(1)Described in processing of rust removing use sandblasting
Processing.
Embodiment 3:
Aluminum alloy surface anti-oxidation treatment method described in the present embodiment, step(2)Described in degreasing cleaning use three
Vinyl chloride cotton wipes Al-alloy parts surface.
The technical means disclosed in the embodiments of the present invention is not limited to the technical means disclosed in the above technical means, and further includes
The technical solution being made of the above technical characteristic equivalent replacement.The unaccomplished matter of the present invention, belongs to those skilled in the art's
Common knowledge.
Claims (5)
1. a kind of aluminum alloy surface anti-oxidation treatment method, it is characterized in that:This method comprises the following steps:
(1)Processing of rust removing is carried out to Al-alloy parts surface;
(2)Degreasing cleaning is carried out to Al-alloy parts surface;
(3)Al-alloy parts after degreasing is cleaned are dried;
(4)7.5 parts of the concentrated sulfuric acid, 22 parts of potassium bichromate is taken to be configured to the mixing that mass percentage concentration is 45-65% in parts by weight
Solution;
(5)Al-alloy parts after drying are immersed in the mixed solution configured, 10-30min is kept the temperature at 60-65 DEG C;
(6)Low temperature drying after cleaning.
2. aluminum alloy surface anti-oxidation treatment method according to claim 1, it is characterized in that:Step(1)Described in remove
Rust processing uses blasting treatment.
3. aluminum alloy surface anti-oxidation treatment method according to claim 1, it is characterized in that:Step(2)Described in go
Grease cleaning is using trichloro ethylene cotton wiping Al-alloy parts surface.
4. aluminum alloy surface anti-oxidation treatment method according to claim 1, it is characterized in that:Step(3)Described in baking
It is dry to be dried using 45-55 DEG C of temperature.
5. aluminum alloy surface anti-oxidation treatment method according to claim 1, it is characterized in that:Step(6)Described in it is low
The temperature of temperature drying is 30 DEG C.