CN108359071A - A kind of germanic underwear chest pad and preparation method thereof - Google Patents
A kind of germanic underwear chest pad and preparation method thereof Download PDFInfo
- Publication number
- CN108359071A CN108359071A CN201810133777.3A CN201810133777A CN108359071A CN 108359071 A CN108359071 A CN 108359071A CN 201810133777 A CN201810133777 A CN 201810133777A CN 108359071 A CN108359071 A CN 108359071A
- Authority
- CN
- China
- Prior art keywords
- parts
- germanic
- underwear
- chest pad
- sponge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of germanic underwear chest pad, raw material includes the component of following parts by weight：20 30 parts of toluene di-isocyanate(TDI), 15 25 parts of diisocyanate, 0.3 0.5 parts of polymerization catalyst, 55 75 parts of polyether polyol, 0.6 5 parts of fire retardant, 0.5 8 parts of foaming agent, 10 20 parts of germanite powder and distilled water several pieces.This product is the underwear chest pad made of germanic sponge; germanic sponge has injury caused by inhibiting radioactive ray; restore the effect of the cell injured; germanic sponge contributes to the ionic equilibrium of adjustment biology simultaneously; keep the abnormal restoring of body neuron circuit normal, there is the sense of discomfort for preventing and improving body and massage and other effects；Women has above-mentioned health-care effect when wearing the underwear made of this product, and to be conducive to the health of wearer, and germanium also has the function of deodorization and quick conductive energy, and the underwear of wearer is enabled to not sticked by sweat；Germanium has warming temperature raising, the effect for promoting blood circulation, lessening fatigue, to improve the comfort level of female wearer simultaneously.
Description
Technical field
The present invention relates to underwear field, specifically a kind of germanic underwear chest pad and preparation method thereof.
Background technology
Sponge is one kind of polyurethane foam plastics, belongs to flexible polyurethane foam.Because there is the cellular knot of cellular
Structure is widely used in sofa, mattress, underwear, clothes so having the characteristics that excellent flexibility, elasticity, water imbibition, water resistance
The industries such as dress, flexible package.
Germanium contributes to the ionic equilibrium of adjustment biology, keeps the abnormal restoring of body neuron circuit normal, has and prevents
With the sense of discomfort and massage hot spring effect and other effects that improve body, germanium also has the function of adjusting the abnormal current potential of human body, thin in cancer
When born of the same parents' current potential is ramping up, Germanium can capture the electronics of cancer cell, so that its current potential is declined, inhibit the deterioration of illness.
Existing underwear chest pad is extensive to which underwear chest pad does not have injury caused by inhibiting radioactive ray without germanous layer
The effect of the multiple cell injured promotes, and does not have and promote blood circulation, lessen fatigue, boosting metabolism, accelerates to exclude
The functions such as waste cannot be conducive to the health of wearer to which underwear protection pad does not have the effect of health care；And existing underwear chest
Pad can be sticked without germanous layer from the function without deodorization and quick conductive energy, the underwear of wearer by sweat, to
Influence the comfort level of wearer.
Invention content
The purpose of the present invention is to provide a kind of germanic underwear chest pads and preparation method thereof, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides the following technical solutions：
A kind of germanic underwear chest pad, which is characterized in that its raw material includes the component of following parts by weight：Toluene diisocynate
20-30 parts of ester, 15-25 parts of diisocyanate, 0.3-0.5 parts of polymerization catalyst, 55-75 parts of polyether polyol, fire retardant 0.6-5
Part, 0.5-8 parts of foaming agent, 10-20 parts of germanite powder and distilled water several pieces.
As a further solution of the present invention：The polymerization catalyst uses stannous octoate or dibutyl tin.
A kind of preparation method of germanic underwear chest pad, is as follows：
(1) germanite powder is added in grinding machinery and carries out fine gtinding, obtain the germanite powder after fine gtinding；
(2) by toluene di-isocyanate(TDI), diisocyanate, distilled water, polymerization catalyst, polyether polyol, fire retardant, hair
The raw material such as the germanite powder after infusion and fine gtinding are added sequentially in Mixing Machine；
(3) start Mixing Machine, stir 30-60s, and the temperature in Mixing Machine is 25 DEG C -35 DEG C, stirring blade turns
Speed is 900-1100r/min；
(4) mixture after stirring is rapidly added forming box, chain growth, foaming, crosslinking, solidification is completed in forming box
Deng reaction, then the product after curing molding is cooled down by cooling device；
(5) sponge or sponge produced after being cooled and shaped and cloth pasting are made by cutting, xeothermic compression molding
Sponge sheet material becomes underwear chest pad after thermoplastic deformation occurs.
As a further solution of the present invention：The grinding precision of germanite powder is 0.06mm-0.1mm in the step (1).
Chain propagation reaction in above-mentioned shaping box is：Polymer is will produce after said mixture mixing, in polymer chain not
It is saturated monomer molecule and increases an active site additionally increased, to form chain growth.
Foamable reaction in above-mentioned shaping box is：By heating so that foaming agent is heated, to be allowed to decompose release outlet
Body and foam.
Cross-linking reaction in above-mentioned shaping box is：Two or more molecules (generally linear molecule) in said mixture
It is mutually bonded the relatively stable molecule (build molecule) for being cross-linked into network structure, to line style or the transformation of the macromolecular of slight branched chain type
At tridimensional network, the performances such as intensity, heat resistance, wearability, solvent resistance are improved with this.
Curing reaction in above-mentioned shaping box is：Toluene di-isocyanate(TDI), diisocyanate in said mixture with it is poly-
Ethoxylated polyhydric alcohol, it is uniformly mixed by continuously stirring under the action of suitable catalyst (stannous octoate or dibutyl tin), most
Post-consumer polymer forms firming body.
Compared with prior art, the beneficial effects of the invention are as follows：This product is the underwear chest pad made of germanic sponge, is contained
After germanium sponge has injury caused by inhibiting radioactive ray, restores the effect of the cell injured, and cell restores, the blood in blood
Glomus cell increases, and is increased by blood cell and is supplied oxygen, so that blood is cleaner, to blood such as liver cancer, lung cancer, gastric cancers
The treatment that pipe enriches the diseases such as the cancer and breathing problem at position, asthma and skin disease has special curative effect, while germanic
Sponge contributes to the ionic equilibrium of adjustment biology, keeps the abnormal restoring of body neuron circuit normal, has and prevents and improve body
Sense of discomfort and massage and other effects；Germanium also has the function of adjusting the abnormal current potential of human body, when cancer cell current potential is ramping up, germanium
Element can capture the electronics of cancer cell, so that its current potential is declined, inhibit the deterioration of illness, to which women is made in wearing of this product
Underwear when there is above-mentioned health-care effect, to be conducive to the health of wearer, and germanium also with deodorization and quick conductive can
Function enables to the underwear of wearer not sticked by sweat, to improve the wear comfort of wearer；Germanium, which has, simultaneously protects
Warm temperature raising, to promote blood circulation, lessen fatigue, boost metabolism, accelerate to exclude the functions such as waste, to further carry
The comfort level of high female wearer.
Specific implementation mode
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is only
It is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill people
The every other embodiment that member is obtained without making creative work, shall fall within the protection scope of the present invention.
Embodiment 1
In the embodiment of the present invention, a kind of germanic underwear chest pad, raw material includes the component of following parts by weight：Toluene two is different
20 parts of cyanate, 15 parts of diisocyanate, 0.3 part of polymerization catalyst, 55 parts of polyether polyol, 0.6 part of fire retardant, foaming agent
0.5 part, 10 parts of germanite powder and distilled water several pieces.
The polymerization catalyst uses stannous octoate or dibutyl tin.
A kind of preparation method of germanic underwear chest pad, is as follows：
(1) germanite powder is added in grinding machinery and carries out fine gtinding, obtain the germanite powder after fine gtinding；
(2) by toluene di-isocyanate(TDI), diisocyanate, distilled water, polymerization catalyst, polyether polyol, fire retardant, hair
The raw material such as the germanite powder after infusion and fine gtinding are added sequentially in Mixing Machine；
(3) start Mixing Machine, stir 30-60s, and the temperature in Mixing Machine is 25 DEG C, the rotating speed of stirring blade is
900r/min；
(4) mixture after stirring is rapidly added forming box, chain growth, foaming, crosslinking, solidification is completed in forming box
Deng reaction, then the product after curing molding is cooled down by cooling device；
(5) sponge or sponge produced after being cooled and shaped and cloth pasting are made by cutting, xeothermic compression molding
Sponge sheet material becomes underwear chest pad after thermoplastic deformation occurs.
The grinding precision of germanite powder is 0.06mm-0.1mm in the step (1).
Embodiment 2
In the embodiment of the present invention, a kind of germanic underwear chest pad, raw material includes the component of following parts by weight：Toluene two is different
25 parts of cyanate, 20 parts of diisocyanate, 0.4 part of polymerization catalyst, 65 parts of polyether polyol, 3 parts of fire retardant, 2 parts of foaming agent,
15 parts of germanite powder and distilled water several pieces.
The polymerization catalyst uses stannous octoate or dibutyl tin.
A kind of preparation method of germanic underwear chest pad, is as follows：
(1) germanite powder is added in grinding machinery and carries out fine gtinding, obtain the germanite powder after fine gtinding；
(2) by toluene di-isocyanate(TDI), diisocyanate, distilled water, polymerization catalyst, polyether polyol, fire retardant, hair
The raw material such as the germanite powder after infusion and fine gtinding are added sequentially in Mixing Machine；
(3) start Mixing Machine, stir 30-60s, and the temperature in Mixing Machine is 30 DEG C, the rotating speed of stirring blade is
1000r/min；
(4) mixture after stirring is rapidly added forming box, chain growth, foaming, crosslinking, solidification is completed in forming box
Deng reaction, then the product after curing molding is cooled down by cooling device；
(5) sponge or sponge produced after being cooled and shaped and cloth pasting are made by cutting, xeothermic compression molding
Sponge sheet material becomes underwear chest pad after thermoplastic deformation occurs.
The grinding precision of germanite powder is 0.06mm-0.1mm in the step (1).
Embodiment 3
In the embodiment of the present invention, a kind of germanic underwear chest pad, raw material includes the component of following parts by weight：Toluene two is different
30 parts of cyanate, 25 parts of diisocyanate, 0.5 part of polymerization catalyst, 75 parts of polyether polyol, 5 parts of fire retardant, 8 parts of foaming agent,
20 parts of germanite powder and distilled water several pieces.
The polymerization catalyst uses stannous octoate or dibutyl tin.
A kind of preparation method of germanic underwear chest pad, is as follows：
(1) germanite powder is added in grinding machinery and carries out fine gtinding, obtain the germanite powder after fine gtinding；
(2) by toluene di-isocyanate(TDI), diisocyanate, distilled water, polymerization catalyst, polyether polyol, fire retardant, hair
The raw material such as the germanite powder after infusion and fine gtinding are added sequentially in Mixing Machine；
(3) start Mixing Machine, stir 30-60s, and the temperature in Mixing Machine is 35 DEG C, the rotating speed of stirring blade is
1100r/min；
(4) mixture after stirring is rapidly added forming box, chain growth, foaming, crosslinking, solidification is completed in forming box
Deng reaction, then the product after curing molding is cooled down by cooling device；
(5) sponge or sponge produced after being cooled and shaped and cloth pasting are made by cutting, xeothermic compression molding
Sponge sheet material becomes underwear chest pad after thermoplastic deformation occurs.
The grinding precision of germanite powder is 0.06mm-0.1mm in the step (1).
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art,
It still can be with technical scheme described in the above embodiments is modified, or is carried out to which part technical characteristic etc.
With replacing, all within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in this
Within the protection domain of invention.
Claims (4)
1. a kind of germanic underwear chest pad, which is characterized in that its raw material includes the component of following parts by weight：Toluene di-isocyanate(TDI)
20-30 parts, 15-25 parts of diisocyanate, 0.3-0.5 parts of polymerization catalyst, 55-75 parts of polyether polyol, fire retardant 0.6-5
Part, 0.5-8 parts of foaming agent, 10-20 parts of germanite powder and distilled water several pieces.
2. a kind of germanic underwear chest pad according to claim 1, which is characterized in that the polymerization catalyst is using octanoic acid
Stannous or dibutyl tin.
3. according to a kind of preparation method of any germanic underwear chest pads of claim 1-2, which is characterized in that it is described its
It is as follows：
(1) germanite powder is added in grinding machinery and carries out fine gtinding, obtain the germanite powder after fine gtinding；
(2) by toluene di-isocyanate(TDI), diisocyanate, distilled water, polymerization catalyst, polyether polyol, fire retardant, foaming agent
And the raw material such as germanite powder after fine gtinding are added sequentially in Mixing Machine；
(3) start Mixing Machine, stir 30-60s, and the temperature in Mixing Machine is 25 DEG C -35 DEG C, the rotating speed of stirring blade is
900-1100r/min；
(4) mixture after stirring is rapidly added forming box, it is anti-that chain growth, foaming, crosslinking, solidification etc. is completed in forming box
It answers, then the product after curing molding is cooled down by cooling device；
(5) sponge or sponge produced after being cooled and shaped and cloth pasting make sponge by cutting, xeothermic compression molding
Sheet material becomes underwear chest pad after thermoplastic deformation occurs.
4. a kind of germanic underwear chest pad according to claim 3, which is characterized in that germanite powder in the step (1)
Grinding precision is 0.06mm-0.1mm.